CN105860731A - Internal wall latex paint and preparation method thereof - Google Patents
Internal wall latex paint and preparation method thereof Download PDFInfo
- Publication number
- CN105860731A CN105860731A CN201610251803.3A CN201610251803A CN105860731A CN 105860731 A CN105860731 A CN 105860731A CN 201610251803 A CN201610251803 A CN 201610251803A CN 105860731 A CN105860731 A CN 105860731A
- Authority
- CN
- China
- Prior art keywords
- parts
- emulsion
- latex paint
- internal wall
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides internal wall latex paint and a preparation method thereof. A recipe of the internal wall latex paint comprises the following raw materials in part by weight: 5 parts of shielding emulsion OP-62B, 30 parts of organosilicone modified acrylate emulsion, 20 parts of styrene-acrylic emulsion, 25 parts of rutile titanium dioxide, 0.7 part of SUPER PB-1 wetting dispersants, 8 parts of talcum powder, 5 parts of kaolin, 5 parts of calcium carbonate, 4 parts of diatomite, trace of rare earth additives, 0.3 part of defoaming agents BYK-022, 0.5 part of thickening agents, 0.2 part of anti-mildew bactericide Kathon and 35 parts of water. The product is suitable for decorating indoor plaster walls, concrete and brick and stone buildings, can also be used for decorating gypsum and brick walls, and belongs to the latex paint capable of being widely applied to surface decoration of wood plates and asbestos plates. The product has the advantages that the freezing temperature is low; the anti-freezing performance is good; the anti-tensioning and anti-shearing intensity is high; the water-resistant performance and the ventilation performance are realized; the sterilization effect is achieved; the alkali resistance is good; the shielding power is high; the water washing and smearing can be realized; the cost is low.
Description
Technical field
The present invention relates to latex paint field, be specifically related to one be applicable to decorate indoor plaster walls, concrete,
Masonry is it can also be used to gauge stuff, brick wall；Also can be widely used to the surface dress of plank, asbestos board
The latex paint of decorations.
Background technology
Latex paint, also known as emulsion paint.It is to be scattered in the fines of 1.1～0.5um by synthetic resin
Water is formed emulsion, and with emulsion as main film forming substance, adds suitable pigment, filler and auxiliary material
After, ground.Mediation is made up by latex paint of aqueous dispersed polymer emulsion and pigment water.Breast
The fineness of glue coating refers to the size of the particle such as pigment, extender pigment in colored paint or mill base or scattered uniform journey
Degree, represents with micron.The quality of latex paint fineness will affect the paint film things such as the gloss of paint film, water penetration
Reason mechanical performance.Latex paint, according to its feature, the most also needs to add thickener and improves bin stability and change
Kind workability；Add defoamer, improve appearance of film；Add polyalcohol and improve freeze-thaw stability；Due to
The easy mildew of emulsion paint, also needs to add mould inhibitor.Latex paint is divided into latex paint for building and metal by purposes
By the big class of latex paint two.Latex paint for building is mainly used in interior wall and exterior wall and ground is covered with paint, lacquer, colour wash, etc.；Metal is used
Latex paint can be made on the priming paint of industrial maintenance coatings and finish paint and some engineering goods.Latex paint is current
Most popular, the most popular a kind of building coating, is one of the developing direction of building coating.Latex paint
There is graceful, pure and fresh decorative effect, nontoxic, tasteless environmental protection feature.
Summary of the invention
It is an object of the invention to provide one to be applicable to decorate indoor plaster walls, concrete, masonry,
Can also be used for gauge stuff, brick wall；The latex of the incrustation that also can be widely used to plank, asbestos board is coated with
Material, has nontoxic, non-environmental-pollution, and rich color is beautiful, and flow leveling is remarkable, strong covering power；
Also there is excellent water-fast, the good result of alkaline resistance properties.
Present invention employs such technical scheme: raw material and weight proportion in the formula of described invention are distinguished
Be: covering emulsion OP-62B 5 parts, organosilicon-modified acrylic emulsion 30 parts, styrene-acrylic emulsion 20 parts,
Rutile type titanium white 25 parts, SUPER PB-1 wetting dispersing agent 0.7 part, talcum powder 8 parts, kaolin 5
Part, 5 parts of calcium carbonate, 4 parts of diatomite, rare earth addition trace, defoamer BYK-0220.3 part, thickening
Agent 0.5 part, antimildew disinfectant Kathon 0.2 part, 35 parts of water.
Thickener of the present invention can be selected for hydroxy ethyl fiber degree/AES-60/TT-935/RW-8/BR-125P
Deng raw material.Filler granularity is 200-400 mesh, can be selected for precipitated calcium carbonate, talcum powder, kaolin and diatom
Soil etc..
The present invention is applicable to decorate indoor plaster walls, concrete, masonry it can also be used to gauge stuff, brick
Wall；Also can be widely used to the latex paint of the incrustation of plank, asbestos board.
This product solidification point is low, freeze-proof good, tension and shear strength high；There is water repellent and gas permeability,
Sterilization sterilizing；Alkali resistance is good, strong covering power, and available washing is smeared；Cost is relatively low.
Detailed description of the invention
Described a kind of internal wall emulsion coating and preparation method, raw material in its formula and weight proportion be respectively:
Covering emulsion OP-62B 5 parts, organosilicon-modified acrylic emulsion 30 parts, styrene-acrylic emulsion 20 parts, golden red
Stone-type titanium dioxide 25 parts, SUPER PB-1 wetting dispersing agent 0.7 part, talcum powder 8 parts, kaolin 5 parts,
5 parts of calcium carbonate, 4 parts of diatomite, rare earth addition trace, defoamer BYK-0220.3 part, thickener 0.5
Part, antimildew disinfectant Kathon 0.2 part, 35 parts of water.Its preparation method is:
Step one: add water, stirring in stainless steel dispersion cylinder, then weigh various thing exactly by formula
Material, adds wetting dispersing agent, the defoamer of 2/3, thickener, rutile type titanium white in the case of stirring,
Stirring at low speed 5min, adds talcum powder, kaolin and diatomite, and high-speed stirred is disperseed, and temperature rises to
50℃；
Step 2: transfer in paint mixing tank by the slurry of gained, adds covering emulsion, organosilicon under low speed
Modified acrylic acid emulsion, residue defoamer and other auxiliary agent paint；
Step 3: resulting articles uses the 400 mesh vibratory sieves of a diameter of 450mm filter, removes impurity grain
The color stuffing particle of son and not up to fineness, finally packs.
Claims (2)
1. an internal wall emulsion coating and preparation method, it is characterised in that in formula, raw material and weight proportion divide
Not: covering emulsion OP-62B 5 parts, organosilicon-modified acrylic emulsion 30 parts, styrene-acrylic emulsion 20 parts,
Rutile type titanium white 25 parts, SUPER PB-1 wetting dispersing agent 0.7 part, talcum powder 8 parts, kaolin 5
Part, 5 parts of calcium carbonate, 4 parts of diatomite, rare earth addition trace, defoamer BYK-022 0.3 part, thickening
Agent 0.5 part, antimildew disinfectant Kathon 0.2 part, 35 parts of water.
2. according to the latex paint described in claim 1, it is characterised in that described a kind of internal wall emulsion coating
And the preparation method of preparation method is:
Step one: add water, stirring in stainless steel dispersion cylinder, then weigh various thing exactly by formula
Material, adds wetting dispersing agent, the defoamer of 2/3, thickener, rutile type titanium white in the case of stirring,
Stirring at low speed 5min, adds talcum powder, kaolin and diatomite, and high-speed stirred is disperseed, and temperature rises to
50℃；
Step 2: transfer in paint mixing tank by the slurry of gained, adds covering emulsion, organosilicon under low speed
Modified acrylic acid emulsion, residue defoamer and other auxiliary agent paint；
Step 3: resulting articles uses the 400 mesh vibratory sieves of a diameter of 450mm filter, removes foreign particle
And the color stuffing particle of not up to fineness, finally pack.