CN105860042A - PET (polyethylene terephthalate) slice formula for heat pot bottle - Google Patents
PET (polyethylene terephthalate) slice formula for heat pot bottle Download PDFInfo
- Publication number
- CN105860042A CN105860042A CN201610254031.9A CN201610254031A CN105860042A CN 105860042 A CN105860042 A CN 105860042A CN 201610254031 A CN201610254031 A CN 201610254031A CN 105860042 A CN105860042 A CN 105860042A
- Authority
- CN
- China
- Prior art keywords
- pet
- acid
- bottle
- meg
- pta
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention aims at providing a PET (polyethylene terephthalate) slice formula for a heat pot bottle with the advantages of low cost, use safety, high melting point and high strength. Through being calculated by producing one ton of PET slices, the formula comprises 839 to 866Kg of PTA (pure terephthalic acid), 1.0 to 4.0Kg of IPA (iso propyle alcohol), 332 to 333Kg of MEG (mono ethylene glycol), 2 to 6Kg of DEG (diethylene glycol) and 2 to 5Kg of phosphoric acid. The formula can be applied to the technical field of the PET slice formula for the heat pot bottle.
Description
Technical field
The present invention relates to a kind of hot tank bottle PET slice formulation.
Background technology
PET is milky highly crystalline polymer, smooth surface and glossy, its most resistance to creep, antifatigue and resistance to
Mill property is preferable, and wear away little, hardness is high, resistance to pressure is strong, has the toughness of maximum in thermoplastic；Meanwhile, its electric insulation
Property good, temperature influence is less, nontoxic and chemical proof good stability, weak acid resistant and organic solvent.At present, poly-to benzene two
Formic acid ethylene glycol fat (PET) be widely used in cushion, carbonated beverage bottle, edible oil bottle, cruet, drug bottle and
Bottle for cosmetics etc. manufacture.In terms of the composition and proportioning of PET, tradition bottle blowing PET(bottle level PET) composition and proportioning be nothing
Method is used for high-level product, is mainly reflected in the inherent viscosity of PET, fusing point and intensity, so we need existing
Bottle level PET is modified so that it is can make quality and well and produce the finished proprietary item that yields is high.
Summary of the invention
The technical problem to be solved is to overcome the deficiencies in the prior art, it is desirable to provide a kind of low cost, use
The hot tank bottle PET slice formulation that safety, fusing point are high, intensity is big.
In the present invention, a kind of hot tank bottle PET slice formulation be the technical scheme is that a kind of hot tank bottle PET cuts into slices
Formula, is calculated by 1 ton of PET of output section, and it includes following raw material:
Terephthalic acid (TPA) (PTA) 839～866Kg
M-phthalic acid (IPA) 1.0～4.0Kg
Ethylene glycol (MEG) 332～333Kg
Diethylene glycol (DEG) (DEG) 2～6Kg
Phosphoric acid 2～5Kg.
Preferably, a kind of hot tank bottle PET slice formulation, calculate by 1 ton of PET of output section, it includes following raw material:
Terephthalic acid (TPA) (PTA) 838～867Kg
M-phthalic acid (IPA) 2～3Kg
Ethylene glycol (MEG) 331～333Kg
Diethylene glycol (DEG) (DEG) 3～5Kg
Phosphoric acid 3～4Kg.
It is furthermore preferred that a kind of hot tank bottle PET slice formulation, calculating by 1 ton of PET section of output, it includes following raw material:
Terephthalic acid (TPA) (PTA) 857.5Kg
M-phthalic acid (IPA) 2.5Kg
Ethylene glycol (MEG) 332Kg
Diethylene glycol (DEG) (DEG) 4Kg
Phosphoric acid 3.5Kg.
The invention has the beneficial effects as follows: owing to the present invention is calculated by 1 ton of PET section of output, it includes terephthalic acid (TPA)
(PTA) 839～866Kg, M-phthalic acid (IPA) 1.0～4.0Kg, ethylene glycol (MEG) 332～333Kg, diethylene glycol (DEG) (DEG) 2
～6Kg, phosphoric acid 2～5Kg, so the present invention is for the composition and proportioning of PET of the prior art, the present invention can improve
Properties of product, cost-effective, moreover it is possible to reduce cost, use safety, improve fusing point, add intensity.
Detailed description of the invention
Embodiment one:
A kind of hot tank bottle PET slice formulation, is calculated by 1 ton of PET section of output, and it includes following raw material:
Terephthalic acid (TPA) (PTA) 839Kg
M-phthalic acid (IPA) 4Kg
Ethylene glycol (MEG) 332Kg
Diethylene glycol (DEG) (DEG) 6Kg
Phosphoric acid 5Kg
Testing result: (seeing table 1)
(table 1)
Embodiment two:
A kind of hot tank bottle PET slice formulation, is calculated by 1 ton of PET section of output, and it includes following raw material:
Terephthalic acid (TPA) (PTA) 857.5Kg
M-phthalic acid (IPA) 2.5Kg
Ethylene glycol (MEG) 332Kg
Diethylene glycol (DEG) (DEG) 4Kg
Phosphoric acid 3.5Kg.
Testing result: (seeing table 2)
(table 2)
Embodiment three:
A kind of hot tank bottle PET slice formulation, is calculated by 1 ton of PET section of output, and it includes following raw material:
Terephthalic acid (TPA) (PTA) 866Kg
M-phthalic acid (IPA) 1Kg
Ethylene glycol (MEG) 333Kg
Diethylene glycol (DEG) (DEG) 2Kg
Phosphoric acid 2Kg.
Testing result: (seeing table 3)
(table 3)
The testing result obtained from above table and embodiment, the composition proportion scope gone out given in the claims in the present invention
And preparation technology parameter scope all can reach the quality standard that high standard product is produced.
Present invention can apply to the technical field of hot tank bottle PET slice formulation.
Claims (3)
1. a hot tank bottle PET slice formulation, it is characterised in that: calculating by 1 ton of PET of output section, it includes following raw material:
Terephthalic acid (TPA) (PTA) 839～866Kg
M-phthalic acid (IPA) 1.0～4.0Kg
Ethylene glycol (MEG) 332～333Kg
Diethylene glycol (DEG) (DEG) 2～6Kg
Phosphoric acid 2～5Kg.
One the most according to claim 1 hot tank bottle PET slice formulation, it is characterised in that: by 1 ton of PET section of output
Calculating, it includes following raw material:
Terephthalic acid (TPA) (PTA) 838～867Kg
M-phthalic acid (IPA) 2～3Kg
Ethylene glycol (MEG) 331～333Kg
Diethylene glycol (DEG) (DEG) 3～5Kg
Phosphoric acid 3～4Kg.
One the most according to claim 1 and 2 hot tank bottle PET slice formulation, it is characterised in that: cut by 1 ton of PET of output
Sheet calculates, and it includes following raw material:
Terephthalic acid (TPA) (PTA) 857.5Kg
M-phthalic acid (IPA) 2.5Kg
Ethylene glycol (MEG) 332Kg
Diethylene glycol (DEG) (DEG) 4Kg
Phosphoric acid 3.5Kg.