CN102634128A - Processing modifier for polyvinyl chloride post and telecommunication pipelines - Google Patents
Processing modifier for polyvinyl chloride post and telecommunication pipelines Download PDFInfo
- Publication number
- CN102634128A CN102634128A CN2012101027002A CN201210102700A CN102634128A CN 102634128 A CN102634128 A CN 102634128A CN 2012101027002 A CN2012101027002 A CN 2012101027002A CN 201210102700 A CN201210102700 A CN 201210102700A CN 102634128 A CN102634128 A CN 102634128A
- Authority
- CN
- China
- Prior art keywords
- modifier
- processing
- post
- parts
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a processing modifier for polyvinyl chloride post and telecommunication pipelines. The processing modifier is characterized by comprising the following components in parts by weight: 3-4 parts of stabilizing agent, 0.5-1.5 parts of titanium dioxide, 0.02-0.03 part of carbon black, 0.7-0.9 part of stearic acid, 0.5-1.5 parts of paraffin, 20-30 parts of calcium carbonate and 1.5-3 parts of rubber and plastic modifier. A preparation process of the processing modifier comprises preparation of the components, mixing, stirring, heating, cooling and unloading and packaging. The processing modifier has the following beneficial effects that the processing modifier is reasonable in conception, standard and simple-to-operate in process and low in cost and is pollution-free; the product performances can be improved and the product cost can be reduced when the processing modifier is used for processing the polyvinyl chloride post and telecommunication pipes; and the processing modifier can be industrially produced in quantity and can be widely used in the field of processing of the polyvinyl chloride post and telecommunication pipelines.
Description
Technical field
The present invention relates to a kind of processing of plastic properties-correcting agent that is used for, particularly relate to a kind of modifier that is used for SE post and telecommunications pipeline.
Background technology
As everyone knows, traditional modifier that is used for SE post and telecommunications pipeline is unreasonable because of the auxiliary material and the proportioning thereof of adding, therefore; The SE post and telecommunications tube performance of producing is relatively poor; Cost is higher, is difficult to satisfy the demands of consumers, and has limited it and has applied.
Summary of the invention
The objective of the invention is to research and develop a kind of new auxiliary agent as auxiliary material,, reduce production costs, and a kind of modifier that is used for SE post and telecommunications pipeline is provided in order to improve the performance of SE post and telecommunications pipeline in order to overcome the deficiency of above-mentioned background technology.
The technical scheme of the modifier that is used for SE post and telecommunications pipeline that to achieve these goals, the present invention is alleged is such:
Modifier of the present invention comprises following component and weight part: stablizer 3～4; White titanium pigment 0.5～1.5; Carbon black 0.02～0.03; Triple Pressed Stearic Acid 0.7～0.9; Paraffin 0.5～1.5; Lime carbonate 20～30; Rubber and plastic properties-correcting agent 1.5～3.
Modifier of the present invention comprises following component and weight part: stablizer 3.5; White titanium pigment 1; Carbon black 0.025; Triple Pressed Stearic Acid 0.8; Paraffin 1; Lime carbonate 25; Rubber and plastic properties-correcting agent 2.
Rubber and plastic properties-correcting agent of the present invention is to be composited by ethylene vinyl acetate and aluminic acid lipoprotein coupling agent, and its proportioning is: ethylene vinyl acetate: aluminic acid lipoprotein coupling agent=1.5～2.5: 0.05～0.1.
The proportioning of rubber and plastic properties-correcting agent of the present invention is: ethylene vinyl acetate: aluminic acid lipoprotein coupling agent=2: 0.08.
The modifier that is used for SE post and telecommunications pipeline that the present invention is alleged has following beneficial effect: reasonable idea, technological specification, simple to operate, cheap, pollution-free; The modifier that is used for SE post and telecommunications pipe can improve performance of products, promotes the quality of product, reduces production cost of products.The present invention can form industrialized mass production, can be widely used in the manufacture field of SE post and telecommunications pipeline.
Embodiment
Below in conjunction with embodiment the present invention is made further detailed description, but this embodiment should not be construed as limitation of the present invention.
Embodiment 1
Modifier of the present invention is joined by following processing sequence system:
One, produces the preparation of each component of said modifier and weight part
1, the preparation of rubber and plastic properties-correcting agent:
Get ethylene vinyl acetate 1.5 by described rubber and plastic properties-correcting agent proportioning, aluminic acid lipoprotein coupling agent 0.05 is inserted in the whisking appliance together, under normal temperature condition, stirs, and gets final product discharging, subsequent use after stirring.
2, the preparation of described each component and weight part:
Stablizer 3; White titanium pigment 0.5; Carbon black 0.02; Triple Pressed Stearic Acid 0.7; Paraffin 0.5; Lime carbonate 20; Rubber and plastic properties-correcting agent 1.5, subsequent use.
Two, the preparation of described modifier:
1, batch mixing: above-mentioned each ingredients weight parts for preparing is mixed, drop into mixing and stirring in the kneader together, heating to 135 ℃～140 ℃ can stop to heat, subsequent use;
2, discharging is packed: can discharging packing, i.e. finished product---described modifier packing after the above-mentioned batch mixing that processes is cooled to normal temperature.
Three, the preparation of SE post and telecommunications raw pipeline material
At first get 100 parts of SE and drop in the mixing machines, get in 44 parts of adding mixing machines of the above-mentioned modifier for preparing again, the mixing granulation that promptly is available on the machine becomes the raw material of required SE post and telecommunications pipe.
Embodiment 2
Present embodiment and embodiment 1 are basic identical, and its difference is:
One, the preparation of each component of modifier (being auxiliary agent) and weight part:
1, auxiliary agent rubber and plastic properties-correcting agent preparation:
Get ethylene vinyl acetate 2 by described rubber and plastic properties-correcting agent proportioning, aluminic acid lipoprotein coupling agent 0.08 is inserted in the whisking appliance together, under normal temperature condition, stirs, and gets final product discharging, subsequent use after stirring.
2, the preparation of described each component and weight part:
Stablizer 3.5; White titanium pigment 1; Carbon black 0.025; Triple Pressed Stearic Acid 0.8; Paraffin 1; Lime carbonate 25; Rubber and plastic properties-correcting agent 2, subsequent use.
Embodiment 3
Present embodiment and embodiment 1 are basic identical, and its difference is:
One, the preparation of each component of modifier (being auxiliary agent) and weight part:
1, auxiliary agent rubber and plastic properties-correcting agent preparation:
Get ethylene vinyl acetate 2.5 by described rubber and plastic properties-correcting agent proportioning, aluminic acid lipoprotein coupling agent 0.1 is inserted in the whisking appliance together, under normal temperature condition, stirs, and gets final product discharging, subsequent use after stirring.
2, the preparation of described each component and weight part:
Stablizer 4; White titanium pigment 1.5; Carbon black 0.03; Triple Pressed Stearic Acid 0.9; Paraffin 1.5; Lime carbonate 30; Rubber and plastic properties-correcting agent 3, subsequent use.
Obviously, those skilled in the art can carry out various changes and modification to the present invention and not break away from the spirit and scope of the present invention.Like this, belong within the scope of claim of the present invention and equivalent technologies thereof if of the present invention these are revised with modification, then the present invention also is intended to comprise these changes and modification interior.
The content of not doing in this specification sheets to describe in detail belongs to this area professional and technical personnel's known prior art.
Claims (4)
1. modifier that is used for SE post and telecommunications pipeline, it is characterized in that: described modifier comprises following component and weight part:
Stablizer 3～4; White titanium pigment 0.5～1.5; Carbon black 0.02～0.03; Triple Pressed Stearic Acid 0.7～0.9; Paraffin 0.5～1.5; Lime carbonate 20～30; Rubber and plastic properties-correcting agent 1.5～3.
2. the modifier that is used for SE post and telecommunications pipeline according to claim 1 is characterized in that: described modifier comprises following component and weight part:
Stablizer 3.5; White titanium pigment 1; Carbon black 0.025; Triple Pressed Stearic Acid 0.8; Paraffin 1; Lime carbonate 25; Rubber and plastic properties-correcting agent 2.
3. according to the described modifier that is used for SE post and telecommunications pipeline of arbitrary claim in the claim 1 to 2; It is characterized in that: described rubber and plastic properties-correcting agent is to be composited by ethylene vinyl acetate and aluminic acid lipoprotein coupling agent, and its proportioning is: ethylene vinyl acetate: aluminic acid lipoprotein coupling agent=1.5～2.5: 0.05～0.1.
4. the modifier that is used for SE post and telecommunications pipeline according to claim 3 is characterized in that: described rubber and plastic properties-correcting agent proportioning is an ethylene vinyl acetate: aluminic acid lipoprotein coupling agent=2: 0.08.