CN105819841B - A kind of refractory aggregate being used to prepare skimming equipment - Google Patents
A kind of refractory aggregate being used to prepare skimming equipment Download PDFInfo
- Publication number
- CN105819841B CN105819841B CN201610127805.1A CN201610127805A CN105819841B CN 105819841 B CN105819841 B CN 105819841B CN 201610127805 A CN201610127805 A CN 201610127805A CN 105819841 B CN105819841 B CN 105819841B
- Authority
- CN
- China
- Prior art keywords
- skimming
- skimming equipment
- refractory aggregate
- equipment
- blast furnace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of refractory aggregates for being used to prepare skimming equipment, belong to slag iron separation equipment technical field during blast furnace casting.A kind of refractory aggregate being used to prepare skimming equipment of the invention, is made of corundum brick, mullite, zircon, Suzhou soil, coke, converter wind quenching slag, Newman powder and copper ore.Refractory aggregate of the invention passes through creative component proportion, so that skimming equipment made of toasting has good wearability, thermal shock resistance and corrosion resistance, service life reaches 50 days or so in the case that skimming equipment is not repaired, substantially increase the service life of skimming equipment, it preferably ensure that conditions of blast furnace stabilization and direct motion, reduce the production cost of iron and steel enterprise.
Description
Present patent application is for application No. is 2014104438797 divisional application, the applyings date of original application
Are as follows: 2014-09-02, invention and created name are as follows: the skimming equipment during a kind of blast furnace casting.
Technical field
The present invention relates to slag iron separation equipment technical fields during blast furnace casting, are used for more specifically to one kind
Prepare the refractory aggregate of skimming equipment.
Background technique
Blast furnace ironmaking is most widely used iron-smelting process, and the high temperature liquid iron through blast furnace process and clinker mix simultaneously
It is flowed out by iron mouth, molten iron is being transported to converter station by ladle, torpedo tank car after blast furnace casting, carries out pneumatic steelmaking.For
It prevents the harmful components in clinker to be again introduced into molten iron, needs the slag iron separation equipment to high temperature sludge during blast furnace casting
Iron is separated.The slag iron separation equipment mainly used in the prior art is skimming tool, also known as sand mouth;Blast furnace is connect on skimming tool
Sow, under connect branch iron runner, bypass connection slag runner, during tapping, the clinker in sow is with molten iron because of its density difference
Natural layering.Clinker floats on the upper surface of molten iron because density is small, after being blocked by skimming tool then flows to slag runner;Molten iron is big because of its density
It sinks in the following, and flowing to iron runner by the gap between skimming tool and sow.Slag, the iron of high-temperature liquid state during realization tapping
Efficiently separate.Skimming tool is in core node position on cast house, is the exclusive node for guaranteeing slag iron and efficiently separating, and is to promote
The device that high-temperature liquid furnace slag, molten iron efficiently separate during into blast furnace casting.
But skimming tool undergos the mechanical erosion of high temperature liquid iron, the chemical erosion of high temperature furnace slag during military service
It is corroded with intermittent thermal shock.And three kinds of factor alternating actions, mutually reinforce, greatly reduces the service life of skimming tool.It is existing
Some skimming tools generally use the materials such as corundum, silicon carbide, alumina powder and pitch to be made, and the antiscour of skimming tool resists and invades
Erosion ability, antistrip performance and thermal shock resistance are poor, so that the service life of skimming tool only has 1-2 months, and every 10-15 days
Just need feed supplement primary.The frequent repairing of skimming tool, usually influences tapping on schedule, leads to the checking underproduction, and coke ratio increases.
The service life of existing skimming tool is shorter, repairing is frequent, directly affects blast furnace tapping on schedule, extends molten iron and deposit
The furnace time not only increases a ton iron cost, heavy financial burden is brought to iron and steel enterprise, and it is hidden to bring serious safety
Suffer from.Therefore, need to improve the material composition of slag iron separation equipment during blast furnace casting so that skimming equipment have it is good anti-
It washes away, anti-scour property, to improve the service life of skimming equipment.
Through patent retrieval, there is relevant technical solution to disclose.Such as: a kind of blast-furnace iron runner skimmer precast lintel
(CN200910143657.2, data of publication of application: 2010-12-01), lintel castable refractory is prefabricated to be formed, and by drying
It comes into operation after roasting, prefabricated component top future insufficiency, although this application prevents precast lintel when in use because lower part is heated
Elongated the problem of causing top tension to crack is expanded, extends skimming tool service life, but this application only improves slash
The structure of slag device, there is no the material compositions to skimming tool to improve, and the service life of skimming tool needs to be further increased.
In addition, a kind of blast furnace with reclaimed sand mouth material and preparation method thereof (CN201210187866.9, data of publication of application:
2013-12-11), component and weight percent content are as follows: its component and weight percent content are as follows: granularity≤0.088mm
Discarded sial material 15-20%, granularity are quartz sand 20-30%, the granularity≤0.088mm quartz sand 10-20% of 1-3mm,
Granularity≤0.074mm clay powder 8-15%, granularity≤1.0mm pitch 3-10%, granularity≤2.0mm coke powder 7-15%,
The discarded iron runner material fine powder 10-20% of granularity≤0.088mm, non-hydrate sodium metasilicate: 0.1-3%.Although this application reduces
The production cost of skimming equipment, and high-alumina brick for making the silicon material containing aluminium etc. and iron runner material are comprehensively utilized, but skimming equipment
Material composition need service life that is further perfect, and further increasing skimming equipment.
Summary of the invention
1. technical problems to be solved by the inivention
It is an object of the invention to overcome in the prior art skimming service life of equipment it is short, repairing, replacement frequency are big not
Foot, provides a kind of refractory aggregate for being used to prepare skimming equipment, and skimming equipment of the invention passes through creative raw material components
Proportion, not only substantially increases the service life of equipment, ensure that the normal production order of blast furnace, and manufacture simple and convenient.
2. technical solution
In order to achieve the above objectives, technical solution provided by the invention are as follows:
Skimming equipment of the invention, is made of refractory aggregate and bonding agent, and the quality of the bonding agent is refractory aggregate
Quality 6%-8%.
Further, the refractory aggregate each component is formed by following mass parts:
Further, the bonding agent each component is formed by following mass parts:
Further, the granularmetric composition of the corundum brick are as follows: granularity≤0.074mm:30%, 0.074-1.0mm:
50%, 1-3mm:20%;The granularmetric composition of the mullite are as follows: granularity≤0.074mm:20%, 0.074-1.5mm:40%,
1.5-3.5mm:40%.
Further, granularity≤0.074mm of the coke.
3. beneficial effect
Using technical solution provided by the invention, compared with existing well-known technique, there is following remarkable result:
Pitch used by bonding agent of the invention is pelletted pitch, improves skimming equipment using higher carbon content
Erosion-resisting characteristics, and remain more carbon in the gap of skimming equipment pouring material, so that skimming equipment is finer and close, and tie
Creative supplying phenolic resin, guar gum, polyurethanes, cellulose acetate, butyl acrylate and melon rubber in mixture,
Skimming equipment is made according to specific proportion, so that being made in itself and refractory aggregate by the adhesive property for substantially increasing bonding agent
Skimming equipment enhanced strength, thermoplasticity is high, and stability is good;
The corundum brick and mullite of refractory aggregate of the invention use different granularmetric composition, so that the granularity of refractory aggregate
It is more reasonable to form, and zircon, Suzhou soil, coke, converter wind quenching slag, Newman powder and copper ore are added in refractory aggregate,
So that toast made of skimming equipment can resist the mechanical erosion of high temperature liquid iron and the erosion of slag iron, have good wearability,
Thermal shock resistance and corrosion resistance greatly reduce the labor intensity of stokehold, preferably to improve the service life of skimming equipment
Ground ensure that conditions of blast furnace stabilization and direct motion.
Specific embodiment
To further appreciate that the contents of the present invention, the present invention will be further described with reference to the examples below.
Embodiment 1
The skimming equipment of the present embodiment, is made of refractory aggregate and bonding agent, and the quality of the bonding agent is fire resisting bone
The 8% of the quality of material;The refractory aggregate each component is formed by following mass parts: corundum brick 90kg, mullite 80kg, zirconium English
Stone 18kg, Suzhou soil 15kg, coke 12kg, converter wind quenching slag 8kg, Newman powder 2kg and copper ore 2kg.
And it is illustrated herein, the granularmetric composition of the corundum brick are as follows: granularity≤0.074mm:30% (quality percentage
Number), 0.074-1.0mm:50% (mass percent), 1-3mm:20% (mass percent);The granularity group of the mullite
Become: granularity≤0.074mm:20% (mass percent), 0.074-1.5mm:40% (mass percent), 1.5-3.5mm:
40% (mass percent);Granularity≤0.074mm of the coke.The granularity of the zircon of the present embodiment is 0.5-2.0mm,
The zircon of supplying special ratios improves the thermal shock resistance of refractory aggregate, improves service life;The Suzhou soil is
Medium-low temperature fluid alteration remnants type kaolin, the mass percentage of ingredient are as follows: Al2O3: 38.5%, SiO2: 46.6%,
He: 14.9%;Suzhou soil granularity≤the 2.0mm.
In addition, above-mentioned converter wind quenching slag is the vessel slag of liquid after vessel slag is transported to wind quenching station by slag ladle and carriage
It flows out from the pans of slag ladle and carriage, then is dispelled by the air that Laval nozzle sprays, being broken into graininess is converter wind quenching
Slag, the quality percentage of the ingredient of the converter wind quenching slag are as follows: Al2O3: 3.26%, CaO:45.02%, MgO:12.85%, MnO:
0.71%, Si2O:14.61%, TFe:21.22%, f-CaO:0.48%, remaining is inevitable impurity.Above-mentioned Newman
The mass percentage of meal component are as follows: TFe:62.02%, SiO2: 5.03%, CaO:0.23%, MnO:0.15%, Al2O3:
0.67%, remaining is inevitable impurity, and the granularity of the Newman powder is 2.0-3.5mm.The copper ore is from copper mine
Mined, then become higher, the fine sand shape copper mine of cupric quality by ore dressing, the granularity of copper ore is 0.5-
1.5mm, the copper ore are the copper ore of black.
The bonding agent each component of the present embodiment is formed by following mass parts: pitch 80kg, phenolic resin 25kg, guar gum
9kg, polyurethanes 8kg, cellulose acetate 10kg, butyl acrylate 3kg and melon rubber 2kg.It is worth noting that described
Pitch be pelletted pitch, the polyurethanes, be on main chain containing repeat carbamate groups macromolecular
The general designation of object is closed, it is to be formed by organic diisocyanate or polyisocyanates with dihydroxy or polyol addition polymerization.
In addition, the cellulose acetate of the present embodiment is the chemical modification obtained after hydroxyl acetic acid esterified in cellulosic molecule
Natural high polymer, and acetyl content be 38%.The guar gum is water soluble polymer, its chemical name is
Guar hydroxypropyltrimonium ammonium chloride.
A kind of skimming equipment during the blast furnace casting of the present embodiment, it is specific the preparation method is as follows:
Step 1: refractory aggregate is prepared
(1) corundum brick 90kg, mullite 80kg, zircon 18kg, Suzhou soil 15kg and coke are weighed by mass fraction
Said components are added sequentially in blender by 12kg, and in stirrer for mixing 25min, blender revolving speed is 250r/min,
Mixture A is obtained after mixing;
(2) converter wind quenching slag 8kg, Newman powder 2kg and copper ore 2kg are weighed by mass fraction, and successively by said components
It is added in step (1) in mixture A obtained, blender continuess to mix stirring 20min, and refractory aggregate is prepared;
Step 2: bonding agent is prepared
(1) pitch 80kg, phenolic resin 25kg, guar gum 9kg and polyurethanes 8kg are weighed by mass fraction, according to
It is secondary to be added in reaction kettle, and 55 DEG C at a temperature of be stirred 20min, then reaction kettle is first with the heating of 1 DEG C/min speed
Degree heating 15min keeps the temperature 10min, then with the heating rate heating 5min of 2 DEG C/min, is warming up to 80 DEG C, mixture is prepared
B;
(2) cellulose acetate 10kg, butyl acrylate 3kg and melon rubber 2kg are weighed by mass fraction, is added sequentially to stir
It mixes in machine, and stirs 20min, be uniformly mixed to obtain mixture C;
(3) mixture C obtained in step (2) is added in step (1) in mixture B obtained, and continues to stir
30min is mixed to get bonding agent;
Step 3: the bonding agent that step 2 is prepared is added in the blender in step 1, wherein bonding agent
Quality is the 8% of the quality of refractory aggregate, continuess to mix stirring 40min, is uniformly mixed and obtains skimming equipment pouring material;
Step 4: skimming equipment pouring material made of step 3 being poured into mold, then is toasted, wherein toast
Method is as follows:
(1) heating treatment
Firstly, being warming up to 150 DEG C with the heating rate of 10 DEG C/h, 3h is kept the temperature;
Second, being warming up to 650 DEG C with the heating rate of 25 DEG C/h, 5h is kept the temperature;
Third, being warming up to 1100 DEG C with the heating rate of 35 DEG C/h, 14h is kept the temperature;
Finally, being warming up to 1500 DEG C with the heating rate of 30 DEG C/h, 10h is kept the temperature;
(2) cooling is handled
Firstly, cooling to 1200 DEG C with the cooling rate of 25 DEG C/h, 5h is kept the temperature;
Second, cooling to 700 DEG C with the cooling rate of 40 DEG C/h, 2h is kept the temperature;
Third, cooling to 300 DEG C with the cooling rate of 20 DEG C/h, 2h is kept the temperature;
Finally, being air-cooled to room temperature, through polishing deburring processing, that is, skimming equipment is prepared.
Skimming equipment during a kind of blast furnace casting of the present embodiment has been incorporated zirconium due to creative in refractory aggregate
Diamond stone, Suzhou soil, converter wind quenching slag, Newman powder and copper ore enhance the resistant to high temperatures of the skimming equipment, thermal shock resistance and resist
Erosion performance, the corundum brick and mullite of the refractory aggregate use different granularmetric composition, so that the granularmetric composition of refractory aggregate
More rationally;Pitch used by the bonding agent of the present embodiment is pelletted pitch, improves skimming using higher carbon content
The erosion-resisting characteristics of equipment, and more carbon is remained in the gap of skimming equipment pouring material, so that skimming equipment is finer and close,
And creative supplying phenolic resin, guar gum, polyurethanes, cellulose acetate, butyl acrylate and melon in bonding agent
Youngster's glue substantially increases the adhesive property of bonding agent.
Skimming equipment during a kind of blast furnace casting of the invention, refractory aggregate and bonding agent pass through creative component
Proportion, the perfect pouring material of skimming equipment, then by the obtained skimming equipment of specific sintering method, which has
Good wearability, thermal shock resistance and corrosion resistance.The service life of blast furnace skimming equipment is substantially increased, skimming equipment is not
Service life reaches 48 days in the case where repairing, and does not need feed supplement in use, easy for installation, not only greatly reduces
The labor intensity of stokehold, and for blast furnace, tapping is provided safeguard on schedule, ensure that conditions of blast furnace stabilization and direct motion.
Embodiment 2
The basic content of the present embodiment with embodiment 1, the difference is that: the quality of the bonding agent of the present embodiment be it is resistance to
The 7.5% of the quality of fiery aggregate;The refractory aggregate each component is formed by following mass parts: corundum brick 85kg, mullite
75kg, zircon 16kg, Suzhou soil 14kg, coke 10kg, converter wind quenching slag 6kg, Newman powder 1kg and copper ore 1kg.This implementation
The bonding agent each component of example is formed by following mass parts: pitch 75kg, phenolic resin 20kg, guar gum 8kg, polyurethanes
6kg, cellulose acetate 8kg, butyl acrylate 2kg and melon rubber 1kg.
A kind of skimming equipment during the blast furnace casting of the present embodiment, it is specific the preparation method is as follows:
Step 1: refractory aggregate is prepared
(1) corundum brick 85kg, mullite 75kg, zircon 16kg, Suzhou soil 14kg and coke are weighed by mass fraction
Said components are added sequentially in blender by 10kg, and in stirrer for mixing 22min, blender revolving speed is 250r/min,
Mixture A is obtained after mixing;
(2) converter wind quenching slag 6kg, Newman powder 1kg and copper ore 1kg are weighed by mass fraction, and successively by said components
It is added in step (1) in mixture A obtained, blender continuess to mix stirring 20min, and refractory aggregate is prepared;
Step 2: bonding agent is prepared
(1) pitch 75kg, phenolic resin 20kg, guar gum 8kg and polyurethanes 6kg are weighed by mass fraction, according to
It is secondary to be added in reaction kettle, and 55 DEG C at a temperature of be stirred 20min, then reaction kettle is first with the heating of 1 DEG C/min speed
Degree heating 15min keeps the temperature 10min, then with the heating rate heating 5min of 2 DEG C/min, is warming up to 80 DEG C, mixture is prepared
B;
(2) cellulose acetate 8kg, butyl acrylate 2kg and melon rubber 1kg are weighed by mass fraction, is added sequentially to stir
It mixes in machine, and stirs 20min, be uniformly mixed to obtain mixture C;
(3) mixture C obtained in step (2) is added in step (1) in mixture B obtained, and continues to stir
30min is mixed to get bonding agent;
Step 3: the bonding agent that step 2 is prepared is added in the blender in step 1, wherein bonding agent
Quality is the 7.5% of the quality of refractory aggregate, continuess to mix stirring 35min, is uniformly mixed and obtains skimming equipment pouring material;
Step 4: skimming equipment pouring material made of step 3 being poured into mold, then is toasted, wherein toast
Method is as follows:
(1) heating treatment
Firstly, being warming up to 150 DEG C with the heating rate of 10 DEG C/h, 3h is kept the temperature;
Second, being warming up to 650 DEG C with the heating rate of 25 DEG C/h, 5h is kept the temperature;
Third, being warming up to 1100 DEG C with the heating rate of 35 DEG C/h, 14h is kept the temperature;
Finally, being warming up to 1500 DEG C with the heating rate of 30 DEG C/h, 10h is kept the temperature;
(2) cooling is handled
Firstly, cooling to 1200 DEG C with the cooling rate of 25 DEG C/h, 5h is kept the temperature;
Second, cooling to 700 DEG C with the cooling rate of 40 DEG C/h, 2h is kept the temperature;
Third, cooling to 300 DEG C with the cooling rate of 20 DEG C/h, 2h is kept the temperature;
Finally, being air-cooled to room temperature, through polishing deburring processing, that is, skimming equipment is prepared.
Skimming equipment during a kind of blast furnace casting of the invention, refractory aggregate and bonding agent pass through creative component
Proportion, the perfect pouring material of skimming equipment, then by the obtained skimming equipment of specific sintering method, which has
Good wearability, thermal shock resistance and corrosion resistance.The service life of blast furnace skimming equipment is substantially increased, skimming equipment is not
Service life reaches 51 days in the case where repairing, and does not need feed supplement in use, easy for installation, not only greatly reduces
The labor intensity of stokehold, and for blast furnace, tapping is provided safeguard on schedule, ensure that conditions of blast furnace stabilization and direct motion.
Embodiment 3
The basic content of the present embodiment with embodiment 1, the difference is that: the quality of the bonding agent of the present embodiment be it is resistance to
The 6% of the quality of fiery aggregate;The refractory aggregate each component is formed by following mass parts: corundum brick 80kg, mullite 60kg,
Zircon 14kg, 12 parts of Suzhou soil, coke 8kg, converter wind quenching slag 5kg, Newman powder 1kg and copper ore 1kg;The knot of the present embodiment
Mixture each component is formed by following mass parts: pitch 70kg, phenolic resin 10kg, guar gum 5kg, polyurethanes 5kg, vinegar
Acid cellulose 7kg, butyl acrylate 2kg and melon rubber 1kg.
A kind of skimming equipment during the blast furnace casting of the present embodiment, it is specific the preparation method is as follows:
Step 1: refractory aggregate is prepared
(1) corundum brick 80kg, mullite 60kg, zircon 14kg, Suzhou soil 12kg and coke are weighed by mass fraction
Said components are added sequentially in blender by 8kg, and in stirrer for mixing 20min, blender revolving speed is 250r/min,
Mixture A is obtained after mixing;
(2) converter wind quenching slag 5kg, Newman powder 1kg and copper ore 1kg are weighed by mass fraction, and successively by said components
It is added in step (1) in mixture A obtained, blender continuess to mix stirring 20min, and refractory aggregate is prepared;
Step 2: bonding agent is prepared
(1) pitch 70kg, phenolic resin 10kg, guar gum 5kg and polyurethanes 5kg are weighed by mass fraction, according to
It is secondary to be added in reaction kettle, and 55 DEG C at a temperature of be stirred 20min, then reaction kettle is first with the heating of 1 DEG C/min speed
Degree heating 15min keeps the temperature 10min, then with the heating rate heating 5min of 2 DEG C/min, is warming up to 80 DEG C, mixture is prepared
B;
(2) cellulose acetate 7kg, butyl acrylate 2kg and melon rubber 1kg are weighed by mass fraction, is added sequentially to stir
It mixes in machine, and stirs 20min, be uniformly mixed to obtain mixture C;
(3) mixture C obtained in step (2) is added in step (1) in mixture B obtained, and continues to stir
30min is mixed to get bonding agent;
Step 3: the bonding agent that step 2 is prepared is added in the blender in step 1, wherein bonding agent
Quality is the 6% of the quality of refractory aggregate, continuess to mix stirring 30min, is uniformly mixed and obtains skimming equipment pouring material;
Step 4: skimming equipment pouring material made of step 3 being poured into mold, then is toasted, wherein toast
Method is as follows:
(1) heating treatment
Firstly, being warming up to 150 DEG C with the heating rate of 10 DEG C/h, 3h is kept the temperature;
Second, being warming up to 650 DEG C with the heating rate of 25 DEG C/h, 5h is kept the temperature;
Third, being warming up to 1100 DEG C with the heating rate of 35 DEG C/h, 14h is kept the temperature;
Finally, being warming up to 1500 DEG C with the heating rate of 30 DEG C/h, 10h is kept the temperature;
(2) cooling is handled
Firstly, cooling to 1200 DEG C with the cooling rate of 25 DEG C/h, 5h is kept the temperature;
Second, cooling to 700 DEG C with the cooling rate of 40 DEG C/h, 2h is kept the temperature;
Third, cooling to 300 DEG C with the cooling rate of 20 DEG C/h, 2h is kept the temperature;
Finally, being air-cooled to room temperature, through polishing deburring processing, that is, skimming equipment is prepared.
Skimming equipment during a kind of blast furnace casting of the invention, refractory aggregate and bonding agent pass through creative component
Proportion, the perfect pouring material of skimming equipment, then by the obtained skimming equipment of specific sintering method, which has
Good wearability, thermal shock resistance and corrosion resistance.The service life of blast furnace skimming equipment is substantially increased, skimming equipment is not
Service life reaches 47 days in the case where repairing, and does not need feed supplement in use, easy for installation, not only greatly reduces
The labor intensity of stokehold, and for blast furnace, tapping is provided safeguard on schedule, ensure that conditions of blast furnace stabilization and direct motion.
Claims (3)
1. a kind of refractory aggregate for being used to prepare skimming equipment, it is characterised in that: the refractory aggregate each component presses following matter
Measure part composition:
The wherein mass percent of the ingredient of converter wind quenching slag are as follows: Al2O3: 3.26%, CaO:45.02%, MgO:12.85%,
MnO:0.71%, Si2O:14.61%, TFe:21.22%, f-CaO:0.48%, remaining is inevitable impurity.
2. a kind of refractory aggregate for being used to prepare skimming equipment according to claim 1, it is characterised in that: the corundum
The granularmetric composition of brick are as follows: granularity≤0.074mm:30%, 0.074-1.0mm:50%, 1-3mm:20%;The mullite
Granularmetric composition are as follows: granularity≤0.074mm:20%, 0.074-1.5mm:40%, 1.5-3.5mm:40%.
3. a kind of refractory aggregate for being used to prepare skimming equipment according to claim 1, it is characterised in that: the coke
Granularity≤0.074mm.