CN105802225A - Modified polyphenylene sulfide enhanced plastic - Google Patents

Modified polyphenylene sulfide enhanced plastic Download PDF

Info

Publication number
CN105802225A
CN105802225A CN201610318402.5A CN201610318402A CN105802225A CN 105802225 A CN105802225 A CN 105802225A CN 201610318402 A CN201610318402 A CN 201610318402A CN 105802225 A CN105802225 A CN 105802225A
Authority
CN
China
Prior art keywords
good
parts
enhanced plastic
polyphenylene sulfide
modified polyphenylene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610318402.5A
Other languages
Chinese (zh)
Inventor
徐春华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou New District Huashida Engineering Plastic Co Ltd
Original Assignee
Suzhou New District Huashida Engineering Plastic Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou New District Huashida Engineering Plastic Co Ltd filed Critical Suzhou New District Huashida Engineering Plastic Co Ltd
Priority to CN201610318402.5A priority Critical patent/CN105802225A/en
Publication of CN105802225A publication Critical patent/CN105802225A/en
Pending legal-status Critical Current

Abstract

The invention discloses modified polyphenylene sulfide enhanced plastic which comprises the following components in parts by mass: 20 parts of polyphenylene sulfide, 4-6 parts of glass fiber, 2-3 parts of carbon fiber, 2-3 parts of aramid fiber, 1-2 parts of polyperfluoro ethylene propylene and 1-2 parts of polytetrafluoroethylene. Through the way, the modified polyphenylene sulfide enhanced plastic disclosed by the invention has the advantages of light specific weight, good corrosion resistance, excellent electric property, good mechanical property, good flame retardance, good wear resistance, good self-lubricating property, good solvent resistance, safety and practicability and the like and has a broad application prospect in the popularization of modified polyphenylene sulfide enhanced plastic.

Description

A kind of modified polyphenyl thioether enhanced plastic
Technical field
The present invention relates to engineering plastics field, particularly relate to a kind of modified polyphenyl thioether enhanced plastic.
Background technology
Engineering plastics can be made engineering material and replace metal to manufacture the plastics of element part etc..Engineering plastics have excellent combination property, and rigidity is big, and creep is little, mechanical strength is high, and heat-resist, electrical insulating property is good, can use for a long time in harsher chemistry, physical environment, alternative metal uses as structural timber, but the performance of existing engineering plastics does not reaches high requirement.
Summary of the invention
The technical problem that present invention mainly solves is to provide a kind of modified polyphenyl thioether enhanced plastic, modified enhanced plastic is formed by using several long fibres to be added to polyphenylene sulfide matrix, light specific gravity, thermostability are good, good corrosion resistance, excellent electrical property, good mechanical property, fire resistance are good, wearability is good, self lubricity is good, solvent resistance is good, safe and practical, have market prospect widely popularizing of modified polyphenyl thioether enhanced plastic.
For solving above-mentioned technical problem, the present invention provides a kind of modified polyphenyl thioether enhanced plastic, and the quality proportioning of composition includes:
Polyphenylene sulfide 20 parts,
Glass fibre 4-6 part,
Carbon fiber 2-3 part,
Aramid fiber 2-3 part,
Perfluoroethylene bright alkene 1-2 part,
Politef 1-2 part.
In a preferred embodiment of the present invention, described modified polyphenyl thioether enhanced plastic includes additive.
In a preferred embodiment of the present invention, described additive include dispersant, stabilizer, lubricant one or more.
In a preferred embodiment of the present invention, described glass fibre, carbon fiber, the length range of aramid fiber are 2-10mm.
The invention has the beneficial effects as follows: modified polyphenyl thioether enhanced plastic of the present invention has the advantages such as light specific gravity, thermostability is good, good corrosion resistance, excellent electrical property, good mechanical property, fire resistance are good, wearability is good, self lubricity is good, solvent resistance is good, safe and practical have market prospect widely popularizing of modified polyphenyl thioether enhanced plastic.
Detailed description of the invention
Technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based on the embodiment in the present invention, all other embodiments that those of ordinary skill in the art are obtained under not making creative work premise, broadly fall into the scope of protection of the invention.
The embodiment of the present invention includes:
A kind of modified polyphenyl thioether enhanced plastic, the quality proportioning of composition includes:
Polyphenylene sulfide 20 parts,
Glass fibre 4-6 part,
Carbon fiber 2-3 part,
Aramid fiber 2-3 part,
Perfluoroethylene bright alkene 1-2 part,
Politef 1-2 part.
Preferably, described modified polyphenyl thioether enhanced plastic includes additive.
Preferably, described additive include dispersant, stabilizer, lubricant one or more.
Preferably, described glass fibre, carbon fiber, the length range of aramid fiber are 2-10mm.
Modified polyphenyl thioether enhanced plastic of the present invention provides the benefit that:
Forming modified plastics by using several long fibres to be added to polyphenylene sulfide matrix, light specific gravity, thermostability are good, good corrosion resistance, excellent electrical property, good mechanical property, fire resistance are good, wearability is good, self lubricity is good, solvent resistance is good, safe and practical.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every equivalent structure utilizing description of the invention content to be made or equivalence flow process conversion; or directly or indirectly it is used in other relevant technical field, the most in like manner it is included in the scope of patent protection of the present invention.

Claims (4)

1. a modified polyphenyl thioether enhanced plastic, it is characterised in that the quality proportioning of composition includes:
Polyphenylene sulfide 20 parts,
Glass fibre 4-6 part,
Carbon fiber 2-3 part,
Aramid fiber 2-3 part,
Perfluoroethylene bright alkene 1-2 part,
Politef 1-2 part.
Modified polyphenyl thioether enhanced plastic the most according to claim 1, it is characterised in that described modified polyphenyl thioether enhanced plastic includes additive.
Modified polyphenyl thioether enhanced plastic the most according to claim 2, it is characterised in that described additive include dispersant, stabilizer, lubricant one or more.
Modified polyphenyl thioether enhanced plastic the most according to claim 1, it is characterised in that described glass fibre, carbon fiber, the length range of aramid fiber are 2-10mm.
CN201610318402.5A 2016-05-16 2016-05-16 Modified polyphenylene sulfide enhanced plastic Pending CN105802225A (en)