CN105802202A - Modified polyamide-filled plastic - Google Patents
Modified polyamide-filled plastic Download PDFInfo
- Publication number
- CN105802202A CN105802202A CN201610318365.8A CN201610318365A CN105802202A CN 105802202 A CN105802202 A CN 105802202A CN 201610318365 A CN201610318365 A CN 201610318365A CN 105802202 A CN105802202 A CN 105802202A
- Authority
- CN
- China
- Prior art keywords
- good
- parts
- modified polyamide
- filled plastic
- filled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses modified polyamide-filled plastic, which is prepared from the following ingredients in parts by mass: 20 parts of polyamide, 2-5 parts of glass fibers, 2-4 parts of barium sulfate, 2-4 parts of silicon dioxide, 1-2 parts of calcium silicate, 1-2 parts of magnesium silicate and 0.5-1 part of an ethylene-octylene copolymer. In the manner, the modified polyamide-filled plastic has the advantages of light specific gravity, good impact strength, good tensile property, high strength, good fillibility, good abrasive resistance, good self-lubricating property, good solvent resistance, safety, practicability and the like, and has a wide market prospect in popularization of the modified polyamide-filled plastic.
Description
Technical field
The present invention relates to engineering plastics field, particularly relate to a kind of modified polyamide filled-type plastics.
Background technology
Engineering plastics can be made engineering material and replace metal to manufacture the plastics of element part etc..Engineering plastics have excellent combination property, rigidity is big, creep is little, mechanical strength is high, heat-resist, electrical insulating property is good, can use for a long time in harsher chemistry, physical environment, alternative metal uses as structural timber, but the tensile property of existing engineering plastics and impact property do not reach high requirement.
Summary of the invention
The technical problem that present invention mainly solves is to provide a kind of modified polyamide filled-type plastics, by using the materials such as barium sulfate, silicon dioxide, barium silicate to be filled into polyamide substrate, light specific gravity, impact strength are good, tensile property is good, intensity is high, fillibility is good, wearability is good, self lubricity is good, solvent resistance is good, safe and practical, have market prospect widely popularizing of modified polyamide filled-type plastics.
For solving above-mentioned technical problem, the present invention provides a kind of modified polyamide filled-type plastics, and the quality proportioning of composition includes:
Polyamide 20 parts,
Glass fibre 2-5 part,
Barium sulfate 2-4 part,
Silicon dioxide 2-4 part,
Calcium silicates 1-2 part,
Magnesium silicate 1-2 part,
Ethylene-octene copolymer 0.5-1 part.
In a preferred embodiment of the present invention, described modified polyamide filled-type plastics include additive.
In a preferred embodiment of the present invention, described additive include dispersant, stabilizer, lubricant one or more.
In a preferred embodiment of the present invention, the cross-sectional area of described glass fibre is polygon.
The invention has the beneficial effects as follows: modified polyamide filled-type plastics of the present invention have the advantages such as light specific gravity, impact strength is good, tensile property is good, intensity is high, fillibility is good, wearability is good, self lubricity is good, solvent resistance is good, safe and practical have market prospect widely popularizing of modified polyamide filled-type plastics.
Detailed description of the invention
Technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based on the embodiment in the present invention, all other embodiments that those of ordinary skill in the art are obtained under not making creative work premise, broadly fall into the scope of protection of the invention.
The embodiment of the present invention includes:
A kind of modified polyamide filled-type plastics, the quality proportioning of composition includes:
Polyamide 20 parts,
Glass fibre 2-5 part,
Barium sulfate 2-4 part,
Silicon dioxide 2-4 part,
Calcium silicates 1-2 part,
Magnesium silicate 1-2 part,
Ethylene-octene copolymer 0.5-1 part.
Preferably, described modified polyamide filled-type plastics include additive.
Preferably, described additive include dispersant, stabilizer, lubricant one or more.
Preferably, the cross-sectional area of described glass fibre is polygon.
Modified polyamide filled-type plastics of the present invention provide the benefit that:
By using the materials such as barium sulfate, silicon dioxide, barium silicate to be filled into polyamide substrate, light specific gravity, impact strength are good, tensile property is good, intensity is high, fillibility is good, wearability is good, self lubricity is good, solvent resistance is good, safe and practical.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every equivalent structure utilizing description of the invention content to be made or equivalence flow process conversion; or directly or indirectly it is used in other relevant technical field, the most in like manner it is included in the scope of patent protection of the present invention.
Claims (4)
1. modified polyamide filled-type plastics, it is characterised in that the quality proportioning of composition includes:
Polyamide 20 parts,
Glass fibre 2-5 part,
Barium sulfate 2-4 part,
Silicon dioxide 2-4 part,
Calcium silicates 1-2 part,
Magnesium silicate 1-2 part,
Ethylene-octene copolymer 0.5-1 part.
Modified polyamide filled-type plastics the most according to claim 1, it is characterised in that described modified polyamide filled-type plastics include additive.
Modified polyamide filled-type plastics the most according to claim 2, it is characterised in that described additive include dispersant, stabilizer, lubricant one or more.
Modified polyamide filled-type plastics the most according to claim 1, it is characterised in that the cross-sectional area of described glass fibre is polygon.