CN105801969A - Polyethylene pipe formula - Google Patents
Polyethylene pipe formula Download PDFInfo
- Publication number
- CN105801969A CN105801969A CN201610224184.9A CN201610224184A CN105801969A CN 105801969 A CN105801969 A CN 105801969A CN 201610224184 A CN201610224184 A CN 201610224184A CN 105801969 A CN105801969 A CN 105801969A
- Authority
- CN
- China
- Prior art keywords
- parts
- formula
- neoprene
- vinyl acetate
- ethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a polyethylene pipe formula. The formula is prepared from raw materials in parts by weight as follows: 66-75 parts of high-density polyethylene, 5-12 parts of neoprene, 5-12 parts of polyvinyl butyral, 5-9 parts of an ethylene-vinyl acetate copolymer, 2-6 parts of nonylphenol polyoxyethylene ether, 4-8 parts of diphenyl octyl phosphite, 3-5 parts of carbon nanotubes, 3-5 parts of bis(1-tert-butylperoxy)-1-methylethyl)-benzene and 2-4 parts of acetyl tributyl citrate. The strength, hardness and rigidity of a polyethylene pipe prepared with the formula are improved, the preparation process is simple and easy, the pipe can be better adapted to the harsh working environments, and the service life is long.
Description
Technical field
Present invention relates particularly to a kind of polyvinyl piping materials formula.
Technical background
Plastic pipe is the chemical building material that high-tech is composited, and chemical building material be continue steel,
After timber, cement, the fourth-largest class New Building Materials that the present age is emerging.Chemical building material is at me
State achieves being widely used of rapid progress fast development, especially novel environment friendly plastics tubing,
Start a sound and substitute the revolution of traditional construction material.Plastic pipe because of have current loss little, energy-conservation,
The advantage such as material-saving, protecting ecology, completion are convenient, be widely used in building water supply and drainage, cities and towns to
The field such as draining and Gas Pipe, becomes the main force of new century urban construction pipe network.
Plastic pipe, compared with the pipelines such as traditional cast iron pipe, coating steel pipe, pipe of cement, has
Energy-saving material-saving, environmental protection, high-strength light, corrosion-resistant, inner wall smooth non-scaling, construct and keep in repair
The advantages such as simplicity, length in service life, are widely used in building water supply and drainage, town and country plumbing, city
The building industry such as city's combustion gas, electric power and cable jacket, industrial fluids conveying, agricultural irrigation, municipal administration,
Industry and agriculture field.
Plastics are different with traditional material, technological progress paces faster, constantly occur is new
Technology, new material, new technology make the advantage of the relatively conventional material of plastic tube more and more prominent.Mould
Material tubing, compared with traditional metal tube and pipe of cement, has lightweight, is typically only metal tube
1/6-1/10, have preferable corrosion resistance, shock resistance and tensile strength, plastic tube inner surface
Than cast iron pipe smooth many, coefficient of friction is little, fluid resistance is little, can reduce water delivery energy consumption 5%
Above, synthesis energy saving is good, manufactures the right reduction of energy consumption 75%, convenient transportation, installs simple, makes
With the life-span up to 30-50.Plastic pipe develops quickly in countries in the world, and developed country is giving
It is not only a large amount of for replacing that water field and gas burning field application have accounted for absolute advantage plastic pipe
Traditional steel pipe, cast iron pipe etc., reason is that technological innovation.On the one hand material has great
Progressive;On the other hand application technology has new development, makes traditional piping material this side of applicable employing
The occasion of method does not has competitiveness at all.A lot of new materials, new technique is also had to study, or
Found out on probation examine to, can affirm, the technology of 10 years plastic tubes is entered from now on
Step will promote plastic tube more quickly to develop, more extensively.
China's plastic conduit develops quickly, and quality is improving constantly.At present, preliminarily formed with
Polrvinyl chloride (PVC-U) pipe, polyethylene (PE) pipe and polypropylene (PP-R) Guan Weizhu's
Plastic tube industry.Wherein polyethylene (PE) pipe due to himself uniqueness advantage by widely should
For building water supply, construction drainage, buried drain pipe, building and heating, gas transmission and distribution, gas transmission
Pipe, electrician and telecommunication protection sleeve pipe, industrial pipe, agricultural pipe etc..It is mainly used in city
City's water supply, city gas supply and field irrigation.PE, is polyethylene (Polyethylene of
The english abbreviation of raised temperature resistance), general PE tubing feed pipe
The range of application in road is the temperature less than 40 DEG C, it is impossible to for delivery pipeline.PE tubing
It it is a kind of degree of crystallinity thermoplastic resin high, nonpolar.The milky appearance of ortho states HDPE,
It is a certain degree of translucent in meagre cross section.PE have excellent resistance to great majority life and
The characteristic of chemicals for industrial use.
The production technology of China's new material falls behind, and most equipment all needs import, adds external
The impact of enterprise so that manufacturing enterprise of China faces the market test of sternness.But it is as various
New material, new equipment and new technology are constantly emerged in large numbers, and the plastic pipe of China will be promoted towards product
Kind of variation, customizations and possess multi-functional plastic pipe direction and develop.Therefore, poly-second
Alkene (PE) pipe application is the most constantly expanding, but due to the material of polyethylene tube self
Material characteristic so that not as metallic conduit in terms of intensity and hardness, thus in some application scenarios
Limited.It is modified the most on its basis, develops high-performance, and meet international standard
Product, can largely expand its use field.
Summary of the invention
To achieve these goals, the invention provides a kind of polyvinyl piping materials formula.
It is an object of the invention to be achieved through the following technical solutions:
A kind of polyvinyl piping materials formula, this formula each raw material weight component is: high density polyethylene (HDPE)
66-75 part, neoprene 5-12 part, polyvinyl butyral resin 5-12 part, ethyl vinyl acetate
Ethylene copolymer 5-9 part, NPE 2-6 part, octyl diphenyl phosphite 4-8
Part, CNT 3-5 part, dual-tert-butyl peroxy isopropyl base benzene 3-5 part and acetyl tributyl citrate three
Butyl ester 2-4 part.
One of preferred version: this formula each raw material weight component is: high density polyethylene (HDPE) 66 parts,
Neoprene 5 parts, polyvinyl butyral resin 5 parts, ethylene-vinyl acetate copolymer 5 parts,
NPE 2 parts, octyl diphenyl phosphite 4 parts, CNT 3 parts, double uncle
Butylperoxyisopropyl benzene 3 parts and tributyl 2-acetylcitrate 2 parts.
The two of preferred version: this formula each raw material weight component is: high density polyethylene (HDPE) 75 parts,
Neoprene 12 parts, polyvinyl butyral resin 12 parts, ethylene-vinyl acetate copolymer 9 parts,
NPE 6 parts, octyl diphenyl phosphite 8 parts, CNT 5 parts, double uncle
Butylperoxyisopropyl benzene 5 parts and tributyl 2-acetylcitrate 4 parts.
The three of preferred version: this formula each raw material weight component is: high density polyethylene (HDPE) 68 parts,
Neoprene 6 parts, polyvinyl butyral resin 6 parts, ethylene-vinyl acetate copolymer 6 parts,
NPE 3 parts, octyl diphenyl phosphite 5 parts, CNT 4 parts, double uncle
Butylperoxyisopropyl benzene 4 parts and tributyl 2-acetylcitrate 3 parts.
The four of preferred version: this formula each raw material weight component is: high density polyethylene (HDPE) 72 parts,
Neoprene 11 parts, polyvinyl butyral resin 10 parts, ethylene-vinyl acetate copolymer 7 parts,
NPE 5 parts, octyl diphenyl phosphite 6 parts, CNT 4 parts, double uncle
Butylperoxyisopropyl benzene 4 parts and tributyl 2-acetylcitrate 3 parts.
This formula prepares the method for tubing: at low-speed mixer after being mixed in proportion by each raw material
In be stirred 10-12 minute, the batch mixing feeding single screw extrusion machine that then will prepare, add
Work temperature controls at 160-210 DEG C, and screw speed controls at 60-90rpm, extruding pipe material.
The method have the advantages that the polyethylene that the formula provided by the present invention is prepared
Tubing intensity enhancing, hardness and rigidity increase, and preparation process is simple, can preferably fit
Working environment that should be severe, service life is long.
Detailed description of the invention
The following stated is only the preferred embodiments of the present invention, is not limited to the present invention,
Although the present invention being described in detail with reference to previous embodiment, for the technology of this area
For personnel, the technical scheme described in foregoing embodiments still can be modified by it,
Or wherein portion of techniques feature is carried out equivalent.All the spirit and principles in the present invention it
In, any modification, equivalent substitution and improvement etc. made, should be included in the protection of the present invention
Within the scope of.
Embodiment 1
A kind of polyvinyl piping materials formula, this formula each raw material weight component is: high density polyethylene (HDPE)
66 parts, neoprene 5 parts, polyvinyl butyral resin 5 parts, ethylene-vinyl acetate copolymer
5 parts, NPE 2 parts, octyl diphenyl phosphite 4 parts, CNT 3 parts,
Dual-tert-butyl peroxy isopropyl base benzene 3 parts and tributyl 2-acetylcitrate 2 parts.
Embodiment 2
A kind of polyvinyl piping materials formula, this formula each raw material weight component is: high density polyethylene (HDPE)
75 parts, neoprene 12 parts, polyvinyl butyral resin 12 parts, ethene-vinyl acetate copolymerization
Thing 9 parts, NPE 6 parts, octyl diphenyl phosphite 8 parts, CNT 5
Part, dual-tert-butyl peroxy isopropyl base benzene 5 parts and tributyl 2-acetylcitrate 4 parts.
Embodiment 3
A kind of polyvinyl piping materials formula, this formula each raw material weight component is: high density polyethylene (HDPE)
68 parts, neoprene 6 parts, polyvinyl butyral resin 6 parts, ethylene-vinyl acetate copolymer
6 parts, NPE 3 parts, octyl diphenyl phosphite 5 parts, CNT 4 parts,
Dual-tert-butyl peroxy isopropyl base benzene 4 parts and tributyl 2-acetylcitrate 3 parts.
Embodiment 4
A kind of polyvinyl piping materials formula, this formula each raw material weight component is: high density polyethylene (HDPE)
72 parts, neoprene 11 parts, polyvinyl butyral resin 10 parts, ethene-vinyl acetate copolymerization
Thing 7 parts, NPE 5 parts, octyl diphenyl phosphite 6 parts, CNT 4
Part, dual-tert-butyl peroxy isopropyl base benzene 4 parts and tributyl 2-acetylcitrate 3 parts.
Claims (5)
1. a polyvinyl piping materials formula, it is characterised in that this formula each raw material weight component is:
High density polyethylene (HDPE) 66-75 part, neoprene 5-12 part, polyvinyl butyral resin 5-12 part,
Ethylene-vinyl acetate copolymer 5-9 part, NPE 2-6 part, phosphorous acid two
Benzene monooctyl ester 4-8 part, CNT 3-5 part, dual-tert-butyl peroxy isopropyl base benzene 3-5 part and second
Acyl tributyl citrate 2-4 part.
A kind of polyvinyl piping materials formula the most according to claim 1, it is characterised in that should
Formula each raw material weight component is: high density polyethylene (HDPE) 66 parts, neoprene 5 parts, poly-second
Enol butyral 5 parts, ethylene-vinyl acetate copolymer 5 parts, NPE 2
Part, octyl diphenyl phosphite 4 parts, CNT 3 parts, dual-tert-butyl peroxy isopropyl base benzene 3
Part and tributyl 2-acetylcitrate 2 parts.
A kind of polyvinyl piping materials formula the most according to claim 1, it is characterised in that should
Formula each raw material weight component is: high density polyethylene (HDPE) 75 parts, neoprene 12 parts, poly-second
Enol butyral 12 parts, ethylene-vinyl acetate copolymer 9 parts, NPE 6
Part, octyl diphenyl phosphite 8 parts, CNT 5 parts, dual-tert-butyl peroxy isopropyl base benzene 5
Part and tributyl 2-acetylcitrate 4 parts.
A kind of polyvinyl piping materials formula the most according to claim 1, it is characterised in that should
Formula each raw material weight component is: high density polyethylene (HDPE) 68 parts, neoprene 6 parts, poly-second
Enol butyral 6 parts, ethylene-vinyl acetate copolymer 6 parts, NPE 3
Part, octyl diphenyl phosphite 5 parts, CNT 4 parts, dual-tert-butyl peroxy isopropyl base benzene 4
Part and tributyl 2-acetylcitrate 3 parts.
A kind of polyvinyl piping materials formula the most according to claim 1, it is characterised in that should
Formula each raw material weight component is: high density polyethylene (HDPE) 72 parts, neoprene 11 parts, poly-second
Enol butyral 10 parts, ethylene-vinyl acetate copolymer 7 parts, NPE 5
Part, octyl diphenyl phosphite 6 parts, CNT 4 parts, dual-tert-butyl peroxy isopropyl base benzene 4
Part and tributyl 2-acetylcitrate 3 parts.