CN105778587A - Low-temperature photo-curing paint - Google Patents
Low-temperature photo-curing paint Download PDFInfo
- Publication number
- CN105778587A CN105778587A CN201610285524.9A CN201610285524A CN105778587A CN 105778587 A CN105778587 A CN 105778587A CN 201610285524 A CN201610285524 A CN 201610285524A CN 105778587 A CN105778587 A CN 105778587A
- Authority
- CN
- China
- Prior art keywords
- parts
- curing paint
- curing
- temperature photo
- low
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of coating, in particular to low-temperature photo-curing paint. The low-temperature photo-curing paint comprises, by weight, 50-80 parts of perfluoroalkyl ethyl methacrylate, 25-35 parts of methacrylamide, 10-15 parts of ethyl acetate, 20-30 parts of tetraethyl orthosilicate, 25-50 parts of ethyl alcohol, 5-10 parts of trifluoroethyl acrylate, 1-3 parts of antiskinning agent, 5-8 parts of activated carbon powder and 5-7 parts of nanometer iron powder. The low-temperature photo-curing paint is fast in curing, curable at room temperature, high in production efficiency and convenient to produce, cured products are good in performance, prepared test samples after curing have excellent adhesion force, scratch resistance and corrosion resistance, and paint films formed by coating are matt, thick and wide in film formation and high in hardness.
Description
Technical field
The present invention relates to technical field of coatings, specifically about a kind of low temperature photo-curing paint.
Background technology
Acroleic acid polyurethane coating main film forming substance hydroxy-containing resin, because it has desirable physical mechanical ability and excellent protecting light, protect the feature such as color, weatherability and be widely used in the application of the product casing of high-chemical-resistance, such as this thermosetting photocuring finishing varnish may be used in the painting design of packaging, general industry, such as, being widely used in bicycle, motorcycle, automobile, electric refrigerator, washing machine, electric fan, instrument, instrument, precision optical machinery and the application on IT product surface.
Face coat owing to applying need to have outstanding outward appearance in terms of smoothness and glossiness, and need to have outstanding corrosion resistance, so that the coating of heavy dressing has outstanding tack, outstanding repastes tack.But, thermosetting acrylic coating compositions well known in the prior art, it is difficult to the face coat that formation has colored appearance simultaneously, corrosion-resistant, high temperature resistant, wear-resisting and tack is strong.
Summary of the invention
In order to solve above-mentioned technical problem of the prior art, it is an object of the invention to provide a kind of low temperature photo-curing paint with excellent adhesion and solvent resistance.
In order to realize foregoing invention purpose, a kind of low temperature photo-curing paint of the present invention, counts by weight and includes following components: perfluor alkyl ethide methacrylate 50-80 part, Methacrylamide 25-35 part, ethyl acetate 10-15 part, tetraethyl orthosilicate 20-30 part, ethanol 25-50 part, acrylic acid trifluoro ethyl ester 5-10 part, anti-skinning agent 1-3 part, activated carbon powder 5-8 part, nanometer iron powder 5-7 part.
Further, described low temperature photo-curing paint, counts by weight and includes following components: perfluor alkyl ethide methacrylate 60 parts, Methacrylamide 30 parts, ethyl acetate 12 parts, tetraethyl orthosilicate 28 parts, ethanol 35 parts, acrylic acid trifluoro ethyl ester 7 parts, anti-skinning agent 1.5 parts, activated carbon powder 6 parts, nanometer iron powder 5.5 parts.
Further, in described anti-skinning agent Oleum Terebinthinae, dipentene and butyl aldoxime one or more.
Further, described nanometer iron powder granularity is 800-1200 mesh.
Compared with prior art, the method have the advantages that curing rate of the present invention is fast, can be in normal temperature cure, production efficiency is high, easily manufactured, cured product performance is good, the sample prepared after solidification has adhesive force, resistance to marring and the corrosion resistance of excellence, and the paint film one-tenth Asia of application formation is photochromic, become thickness and wide, hardness height.
Detailed description of the invention
Hereinafter the preferred embodiments of the present invention are described in detail.
Embodiment 1
A kind of low temperature photo-curing paint, counts by weight and includes following components: perfluor alkyl ethide methacrylate 50 parts, Methacrylamide 25 parts, ethyl acetate 10 parts, tetraethyl orthosilicate 20 parts, ethanol 25 parts, acrylic acid trifluoro ethyl ester 5 parts, anti-skinning agent 1 part, activated carbon powder 5 parts, nanometer iron powder 5 parts.
Embodiment 2
A kind of low temperature photo-curing paint, counts by weight and includes following components: perfluor alkyl ethide methacrylate 60 parts, Methacrylamide 30 parts, ethyl acetate 12 parts, tetraethyl orthosilicate 28 parts, ethanol 35 parts, acrylic acid trifluoro ethyl ester 7 parts, anti-skinning agent 1.5 parts, activated carbon powder 6 parts, nanometer iron powder 5.5 parts.
Embodiment 3
A kind of low temperature photo-curing paint, counts by weight and includes following components: perfluor alkyl ethide methacrylate 80 parts, Methacrylamide 35 parts, ethyl acetate 15 parts, tetraethyl orthosilicate 30 parts, ethanol 50 parts, acrylic acid trifluoro ethyl ester 10 parts, anti-skinning agent 3 parts, activated carbon powder 8 parts, nanometer iron powder 7 parts.
Although reference be made herein to invention has been described for the explanatory embodiment of the present invention, above-described embodiment is only the present invention preferably embodiment, embodiments of the present invention are also not restricted to the described embodiments, should be appreciated that, those skilled in the art can be designed that a lot of other amendments and embodiment, and these amendments and embodiment will fall within spirit disclosed in the present application and spirit.
Claims (4)
1. a low temperature photo-curing paint, it is characterised in that: count by weight and include following components: perfluor alkyl ethide methacrylate 50-80 part, Methacrylamide 25-35 part, ethyl acetate 10-15 part, tetraethyl orthosilicate 20-30 part, ethanol 25-50 part, acrylic acid trifluoro ethyl ester 5-10 part, anti-skinning agent 1-3 part, activated carbon powder 5-8 part, nanometer iron powder 5-7 part.
Low temperature photo-curing paint the most according to claim 1, it is characterised in that: count by weight and include following components: perfluor alkyl ethide methacrylate 60 parts, Methacrylamide 30 parts, ethyl acetate 12 parts, tetraethyl orthosilicate 28 parts, ethanol 35 parts, acrylic acid trifluoro ethyl ester 7 parts, anti-skinning agent 1.5 parts, activated carbon powder 6 parts, nanometer iron powder 5.5 parts.
Low temperature photo-curing paint the most according to claim 1, it is characterised in that: in described anti-skinning agent Oleum Terebinthinae, dipentene and butyl aldoxime one or more.
Low temperature photo-curing paint the most according to claim 1, it is characterised in that: described nanometer iron powder granularity is 800-1200 mesh.