CN105778477A - Casing and manufacturing method thereof - Google Patents
Casing and manufacturing method thereof Download PDFInfo
- Publication number
- CN105778477A CN105778477A CN201610136931.3A CN201610136931A CN105778477A CN 105778477 A CN105778477 A CN 105778477A CN 201610136931 A CN201610136931 A CN 201610136931A CN 105778477 A CN105778477 A CN 105778477A
- Authority
- CN
- China
- Prior art keywords
- powder body
- preparation
- rubber substrate
- plastic rubber
- finish paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a casing and a manufacturing method thereof, belongs to the field of painting of plastic cement products, and particularly relates to a manufacturing method of plastic cement products using a static electricity powder painting technique.
Description
Technical field
The present invention relates to plastic cement products and preparation method thereof, relate to plastic cement products field of coating, especially design the preparation method that plastic cement products uses electrostatic powder body coating technology.
Background technology
Nylon as most important kind maximum in engineering plastics, especially its modified characteristic realizing high performance, PA adds the glass fibre of 30%, the mechanical property of PA, dimensional stability, thermostability, ageing-resistant performance have and clearly improve." to mould Dai Gang, performance brilliance ", purposes is extremely extensive.It has lightweight, intensity is high, self-lubricating, wear-resisting, anticorrosion, the multiple special performance such as insulation.It is widely used engineering plastics, almost spreads over all of industrial circle.But it is single that nylon adds glass material color after molding, but surface physical properties is poor, polarity is low, in spraying coating process, the basic demand of performance is adhesive force one just more difficult control only.Being only capable of realizing pretreating reagent at present and add organic coatings volatile organic compounds, pollute big, efficiency is low.And powder coating is a kind of new technique at environment-protecting asepsis, gather efficient, energy-conservation, the saving advantage such as cost, environmental protection, powder coating is from being worked into finished product almost without the harmful substance such as formaldehyde and VOC, production is not necessary to unnecessary blowdown cost and environmental protection cost, and low-temperature setting powder body is the emphasis direction researched and developed in the industry.
Summary of the invention
The present invention provides a kind of housing and manufacture method thereof, and this housing utilizes nylon to add glass injection mo(u)lding, re-uses powder coating spraying, and technique is simple, and environmental protection.
The present invention provides the special Preparation Method of a kind of housing, including:
Powder body priming paint is formed on plastic rubber substrate surface;
Powder body finish paint is formed at described powder body primed surface.
Saying further, described preparation method also includes: before plastic rubber substrate surface forms powder body priming paint, preheat 3 ~ 5 minutes, and preheating temperature is 85 ~ 95 DEG C;
Saying further, described preparation method also includes: also include: before described powder body primed surface forms powder body finish paint, need to through hot setting, and solidification temperature must at 120 DEG C-140 DEG C;
Saying further, described preparation method also includes: also include: after described powder body finish paint is formed, need to through hot setting, and solidification temperature must at 110 DEG C-130 DEG C;
Saying further, described plastic rubber substrate is added glass by nylon and forms, and ratio is: nylon 65%-75%, glass 25%-35%.
Saying further, described plastic rubber substrate also includes auxiliary agent, including high molecular polymer.
Saying further, described powder body includes low-temperature resins, epoxy resin, firming agent, infrared ray initiator, adjuvant, pigment, and ratio is: 45%-68%, 5%-8%, 3%-15%, 3%-7%, 1%-5%, 8%-23%.
The present invention also provides for a kind of housing, including: plastic rubber substrate, the powder body priming paint being successively set on plastic rubber substrate and powder body finish paint.
Innovative point of the present invention is in that: 1, plastic rubber substrate is to be added glass by nylon to add the making of high molecular polymer auxiliary agent again, improves product surface physical property, improves its mobility and flame resistance.2, the component for powder body improves so that it is just can be successful curing at about 120 DEG C.And temperature required when generally powder coating is by electrostatic painting process formation coating is 180 DEG C-200 DEG C, but plastic cement can deform again at this temperature, forms contradiction.The invention solves this contradiction.It is an advantage of the current invention that: 1. environmental protection completely, reach more than 95% response rate, without pollution problems such as waste water;2. equipment unification, it is simple to volume production;3. processing heavy industry is easy, and raw material scraps reduction;4. getting the raw materials ready simple, handling of goods and materials is concentrated.
Accompanying drawing explanation
In order to be illustrated more clearly that the embodiment of the present invention or technical scheme of the prior art, the accompanying drawing used required in embodiment or description of the prior art will be briefly described below, apparently, and the accompanying drawing in describing is some embodiments of the present invention, to those skilled in the art, under the premise not paying creative work, it is also possible to obtain other accompanying drawings according to these accompanying drawings.
Fig. 1 is inventive shell embodiment cross-sectional view.
Below in conjunction with embodiment, and with reference to accompanying drawing, the realization of the object of the invention, functional characteristics and advantage are described further.
Detailed description of the invention
In order to make purpose, technical scheme and the advantage to invent clearly, below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that, described embodiment is to invent a part of embodiment rather than whole embodiments.Based on the embodiment in the present invention, the every other embodiment that those of ordinary skill in the art obtain under the premise not making creative work, broadly fall into the scope of protection of the invention.
As it is shown in figure 1, the present invention provides a kind of housing.Including: plastic rubber substrate 1, the powder body priming paint 2 being successively set on plastic rubber substrate and powder body finish paint 3.Wherein: plastic rubber substrate is added glass by nylon and forms, ratio is: nylon 65%-75%, glass 25%-35%.It is also added with auxiliary agent, is mainly high molecular polymer, add auxiliary agent and reduce its hygroscopicity, and product surface physical property can be improved, improve its mobility and flame resistance.Powder body priming paint dough-making powder enamel-cover is drawn together: low-temperature resins, epoxy resin, firming agent, infrared ray initiator, adjuvant, pigment, and ratio is: 45%-68%, 5%-8%, 3%-15%, 3%-7%, 1%-5%, 8%-23%, and relatively common injection moulding need to improve mold temperature.
In the present embodiment, manufacture of casing includes: by plastic rubber substrate through the infrared preheating of intermediate waves 4 minutes, preheating temperature is 90 DEG C;By aforementioned plastic rubber substrate electrostatic spraying mode, spraying powder priming paint, by hot setting, solidification temperature is at 130 DEG C.Cooling;With electrostatic spraying mode spraying powder finish paint on aforementioned plastic rubber substrate, then hot setting, solidification temperature 120 DEG C.Last cooling forming.
Above example only in order to technical scheme to be described, is not intended to limit;Although the present invention being described in detail with reference to previous embodiment, it will be understood by those within the art that: the technical scheme described in foregoing embodiments still can be modified by it, or wherein portion of techniques feature is carried out equivalent replacement, and these amendments or replacement, do not make the essence of appropriate technical solution depart from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (9)
1. the present invention provides the special Preparation Method of a kind of housing, including:
Powder body priming paint is formed on plastic rubber substrate surface;
Powder body finish paint is formed at described powder body primed surface.
2. preparation method according to claim 1, it is characterised in that also include: before plastic rubber substrate surface forms powder body priming paint, preheat 3 ~ 5 minutes, preheating temperature is 85 ~ 95 DEG C.
3. preparation method according to claim 1, it is characterised in that also include: before described powder body primed surface forms powder body finish paint, need to through hot setting, and solidification temperature must at 120 DEG C-140 DEG C.
4. preparation method according to claim 1, it is characterised in that also include: after described powder body finish paint is formed, need to through hot setting, and solidification temperature must at 110 DEG C-130 DEG C.
5. preparation method according to claim 1, it is characterised in that described plastic rubber substrate is added glass by nylon and forms, ratio is: nylon 65%-75%, glass 25%-35%.
6. preparation method according to claim 1, it is characterised in that described plastic rubber substrate also includes auxiliary agent, including high molecular polymer.
7. preparation method according to claim 1, it is characterised in that described powder body includes low-temperature resins, epoxy resin, firming agent, infrared ray initiator, adjuvant, pigment, and ratio is: 45%-68%, 5%-8%, 3%-15%, 3%-7%, 1%-5%, 8%-23%.
8. preparation method according to claim 1, it is characterised in that described powder body priming paint and the finish paint of being formed on plastic rubber substrate surface adopts electrostatic painting process to complete.
9. a housing, adopts the arbitrary described preparation method of claim 1-8 to prepare, it is characterised in that to include: plastic rubber substrate, the powder body priming paint being successively set on plastic rubber substrate and powder body finish paint.