CN104387952A - Anti-corrosion automobile powder coating with good adhesive force - Google Patents

Anti-corrosion automobile powder coating with good adhesive force Download PDF

Info

Publication number
CN104387952A
CN104387952A CN201410733100.5A CN201410733100A CN104387952A CN 104387952 A CN104387952 A CN 104387952A CN 201410733100 A CN201410733100 A CN 201410733100A CN 104387952 A CN104387952 A CN 104387952A
Authority
CN
China
Prior art keywords
parts
powder coating
good
sticking power
anticorrosion
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410733100.5A
Other languages
Chinese (zh)
Inventor
李永志
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410733100.5A priority Critical patent/CN104387952A/en
Publication of CN104387952A publication Critical patent/CN104387952A/en
Pending legal-status Critical Current

Abstract

The invention discloses an anti-corrosion automobile powder coating with a good adhesive force. The anti-corrosion automobile powder coating comprises the components in parts by weight: 45-50 parts of polyamide resin, 1-2 parts of bisphenol A epoxy resin, 15-25 parts of modified rosin resin, 20-25 parts of titanium dioxide, 3-6 parts of lead chromate, 5-10 parts of organosilicone, 2-3 parts of phenolic aldehyde amine, 0.3-0.6 part of dibutyltin dilaurate, 2-3 parts of curing agent, 0.5-1 part of stabilizer and 2-2.5 parts of flatting agent. The anti-corrosion automobile powder coating has the good adhesive force and corrosion resistance.

Description

The anticorrosion automotive powder coating that sticking power is good
Technical field
The present invention relates to automotive powder coating.
Background technology
At present, along with the develop rapidly of global industry, the environmental problem caused also becomes increasingly conspicuous.How to carry out the important topic that environmental protection work has become urgently people's research.Some western countries development research that Environmental awareness is strong goes out to have the car paint of low volatile organic, and puts into production in a large number and use.Along with the development of automobile industry, in order to beautify the appearance of film of automobile, alleviating the environmental pollution that it causes, improving vehicle spray painting technology and seeming particularly important.
For automotive powder coating, the sticking power of powder is extremely important, if the sticking power of powder coating is little, then the paint film sprayed easily drops off, and affects the life-span.
Summary of the invention
In order to improve sticking power and the antiseptic property of powder coating, the invention provides the anticorrosion automotive powder coating that a kind of sticking power is good.
For achieving the above object, the anticorrosion automotive powder coating that sticking power is good, count by weight, be made up of the polyamide resin of 45-50 part, 1-2 part bisphenol A epoxide resin, 15-25 part modified rosin resin, 20-25 part titanium dioxide, 3-6 part chrome yellow, 5-10 part organosilicon, 2-3 part phenolic aldehyde amine, 0.3-0.6 part dibutyl tin dilaurate, 2-3 part solidifying agent, 0.5-1 part stablizer and 2-2.5 part flow agent.
Further, described solidifying agent is hydroxyalkyl amide.
Further, described stablizer is Zinic stearas.
Further, described flow agent selects the product of Dow Corning Corporation, and model is 5T.
The invention has the beneficial effects as follows: add organosilicon and can reduce bisphenol A epoxide resin internal stress, the performances such as bisphenol A epoxide resin toughness, high thermal resistance can be improved again.In the process forming powder coating, the fusing point of polyamide resin and modified rosin resin is low, under the effect of organosilicon and bisphenol A epoxide resin, make the particle of powder coating close to spherical, like this, just can improve the sticking power of paint film, paint film is not easy to drop, long service life.Phenolic aldehyde amine as solidifying agent, under the effect of bisphenol A epoxide resin, can fast setting at low ambient temperatures, and there is good antiseptic property.
Embodiment
Below in conjunction with embodiment, the present invention is further elaborated.
The anticorrosion automotive powder coating that sticking power is good, count by weight, be made up of the polyamide resin of 45-50 part, 1-2 part bisphenol A epoxide resin, 15-25 part modified rosin resin, 20-25 part titanium dioxide, 3-6 part chrome yellow, 5-10 part organosilicon, 2-3 part phenolic aldehyde amine, 0.3-0.6 part dibutyl tin dilaurate, 2-3 part solidifying agent, 0.5-1 part stablizer and 2-2.5 part flow agent.Described solidifying agent is hydroxyalkyl amide.Described stablizer is Zinic stearas.Described flow agent selects the product of Dow Corning Corporation, and model is 5T.
Embodiment 1.
The preparation method of the anticorrosion automotive powder coating that sticking power is good, comprises the following steps,
(1) count by weight, the polyamide resin of 45 parts, 1 part of bisphenol A epoxide resin, 5 parts of organosilicons, 2 parts of phenolic aldehyde amine, 2 parts of solidifying agent and 2 parts of flow agents are mixed and obtain batch mixing A.
(2) 15 parts of modified rosin resins, 20 parts of titanium dioxides, 3 parts of chrome yellow, 0.3 part of dibutyl tin dilaurate, 0.5 part of stablizer are mixed and obtain mixed material B.
(3) adopt twin screw extruder to adopt in front end 75 DEG C-85 DEG C to extrude batch mixing A, forcing machine is added mixed material B after temperature is brought up to 110 DEG C-120 DEG C by stage casing, and extrusion molding, after pulverizing, obtain powder coating.
Embodiment 2.
The preparation method of the anticorrosion automotive powder coating that sticking power is good, comprises the following steps,
(1) count by weight, the polyamide resin of 50 parts, 2 parts of bisphenol A epoxide resins, 10 parts of organosilicons, 3 parts of phenolic aldehyde amine, 3 parts of solidifying agent and 2.5 parts of flow agents are mixed and obtain batch mixing A.
(2) 25 parts of modified rosin resins, 25 parts of titanium dioxides, 6 parts of chrome yellow, 0.6 part of dibutyl tin dilaurate, 1 part of stablizer are mixed and obtain mixed material B.
(3) adopt twin screw extruder to adopt in front end 75 DEG C-85 DEG C to extrude batch mixing A, forcing machine is added mixed material B after temperature is brought up to 110 DEG C-120 DEG C by stage casing, and extrusion molding, after pulverizing, obtain powder coating.
Embodiment 3.
The preparation method of the anticorrosion automotive powder coating that sticking power is good, comprises the following steps,
(1) count by weight, the polyamide resin of 48 parts, 1.5 parts of bisphenol A epoxide resins, 8 parts of organosilicons, 2.5 parts of phenolic aldehyde amine, 2.5 parts of solidifying agent and 2.3 parts of flow agents are mixed and obtain batch mixing A.
(2) 20 parts of modified rosin resins, 22 parts of titanium dioxides, 5 parts of chrome yellow, 0.4 part of dibutyl tin dilaurate, 0.7 part of stablizer are mixed and obtain mixed material B.
(3) adopt twin screw extruder to adopt in front end 75 DEG C-85 DEG C to extrude batch mixing A, forcing machine is added mixed material B after temperature is brought up to 110 DEG C-120 DEG C by stage casing, and extrusion molding, after pulverizing, obtain powder coating.
Powder coating of the present invention, adds organosilicon and can reduce bisphenol A epoxide resin internal stress, can improve the performances such as bisphenol A epoxide resin toughness, high thermal resistance again.In the process forming powder coating, the fusing point of polyamide resin and modified rosin resin is low, under the effect of organosilicon and bisphenol A epoxide resin, make the particle of powder coating close to spherical, like this, just can improve the sticking power of paint film, paint film is not easy to drop, long service life.Phenolic aldehyde amine as solidifying agent, under the effect of bisphenol A epoxide resin, can fast setting at low ambient temperatures, and there is good antiseptic property.

Claims (4)

1. the anticorrosion automotive powder coating that sticking power is good, it is characterized in that: count by weight, be made up of the polyamide resin of 45-50 part, 1-2 part bisphenol A epoxide resin, 15-25 part modified rosin resin, 20-25 part titanium dioxide, 3-6 part chrome yellow, 5-10 part organosilicon, 2-3 part phenolic aldehyde amine, 0.3-0.6 part dibutyl tin dilaurate, 2-3 part solidifying agent, 0.5-1 part stablizer and 2-2.5 part flow agent.
2. the anticorrosion automotive powder coating that sticking power according to claim 1 is good, is characterized in that: described solidifying agent is hydroxyalkyl amide.
3. the anticorrosion automotive powder coating that sticking power according to claim 1 is good, is characterized in that: described stablizer is Zinic stearas.
4. the anticorrosion automotive powder coating that sticking power according to claim 1 is good, is characterized in that: described flow agent selects the product of Dow Corning Corporation, and model is 5T.
CN201410733100.5A 2014-12-07 2014-12-07 Anti-corrosion automobile powder coating with good adhesive force Pending CN104387952A (en)