CN104387926A - Scratching-resistant automobile powder coating with high adhesive force - Google Patents
Scratching-resistant automobile powder coating with high adhesive force Download PDFInfo
- Publication number
- CN104387926A CN104387926A CN201410733096.2A CN201410733096A CN104387926A CN 104387926 A CN104387926 A CN 104387926A CN 201410733096 A CN201410733096 A CN 201410733096A CN 104387926 A CN104387926 A CN 104387926A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder coating
- good
- saturated polyester
- sticking power
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a scratching-resistant automobile powder coating with high adhesive force. The scratching-resistant automobile powder coating consists of the following components in parts by weight: 15-30 parts of linear hydroxyl saturated polyester resin, 3-5 parts of epoxy resin, 20-30 parts of slight branched-chain hydroxyl saturated polyester resin, 15-20 parts of modified rosin resin, 15-20 parts of titanium dioxide, 3-6 parts of fast yellow, 5-10 parts of organosilicone, 2-4 parts of a curing agent, 0.1-1 part of a stabilizer and 2-5 parts of a flatting agent. The coating disclosed by the invention is high in adhesive force and good in scratching resistance.
Description
Technical field
The present invention relates to automotive powder coating.
Background technology
At present, along with the develop rapidly of global industry, the environmental problem caused also becomes increasingly conspicuous.How to carry out the important topic that environmental protection work has become urgently people's research.Some western countries development research that Environmental awareness is strong goes out to have the car paint of low volatile organic, and puts into production in a large number and use.Along with the development of automobile industry, in order to beautify the appearance of film of automobile, alleviating the environmental pollution that it causes, improving vehicle spray painting technology and seeming particularly important.
For automotive powder coating, the sticking power of powder is extremely important, if the sticking power of powder coating is little, then the paint film sprayed easily drops off, and affects the life-span.
Summary of the invention
In order to improve sticking power and the anti scuffing performance of powder coating, the invention provides the anti scuffing automotive powder coating that a kind of sticking power is good.
For achieving the above object, the anti scuffing automotive powder coating that sticking power is good, count by weight, be made up of the hydroxyl saturated polyester resin of the linear hydroxyl saturated polyester resin of 15-30 part, 3-5 part epoxy resin, 20-30 part is slight collateralization, 15-20 part modified rosin resin, 15-20 part titanium dioxide, 3-6 part permanent yellow, 5-10 part organosilicon, 2-4 part solidifying agent, 0.1-1 part stablizer and 2-5 part flow agent.
Further, described solidifying agent is fatty polyamide type amine.
Further, described stablizer is Zinic stearas.
Further, described flow agent selects dimethyl siloxane.
The invention has the beneficial effects as follows: add organosilicon and can reduce epoxy resin internal stress, the performances such as epoxy resin toughness, high thermal resistance can be improved again.In the process forming powder coating, the fusing point of modified rosin resin is low, and under the effect of organosilicon and epoxy resin, make the particle of powder coating close to spherical, like this, just can improve the sticking power of paint film, paint film is not easy to drop, long service life.Due to the hydroxyl saturated polyester resin containing linear hydroxyl saturated polyester resin, epoxy resin, slight collateralization, therefore, the anti scuffing performance of this coating is good.
Embodiment
Below in conjunction with embodiment, the present invention is further elaborated.
The anti scuffing automotive powder coating that sticking power is good, count by weight, be made up of the hydroxyl saturated polyester resin of the linear hydroxyl saturated polyester resin of 15-30 part, 3-5 part epoxy resin, 20-30 part is slight collateralization, 15-20 part modified rosin resin, 15-20 part titanium dioxide, 3-6 part permanent yellow, 5-10 part organosilicon, 2-4 part solidifying agent, 0.1-1 part stablizer and 2-5 part flow agent.Described solidifying agent is fatty polyamide type amine.Described stablizer is Zinic stearas.Described flow agent selects dimethyl siloxane.
Embodiment 1.
The anti scuffing automotive powder coating that sticking power is good, comprises the following steps,
(1) count by weight, the hydroxyl saturated polyester resin of the linear hydroxyl saturated polyester resin of 15 parts, 3 parts of epoxy resin, 20 parts of slight collateralizations, 15 parts of modified rosin resins, 15 parts of titanium dioxides, 3-part permanent yellow, 5 parts of organosilicons, 2 parts of solidifying agent, 0.1 part of stablizer and 2 parts of flow agents are mixed.
(2) adopt twin screw extruder to adopt 75 DEG C-85 DEG C in front end to batch mixing extruding, by forcing machine extrusion molding after stage casing temperature brings up to 110 DEG C-120 DEG C, after pulverizing, obtain powder coating.
Embodiment 2.
The anti scuffing automotive powder coating that sticking power is good, comprises the following steps,
(1) count by weight, the hydroxyl saturated polyester resin of the linear hydroxyl saturated polyester resin of 30 parts, 5 parts of epoxy resin, 30 parts of slight collateralizations, 20 parts of modified rosin resins, 20 parts of titanium dioxides, 6 parts of permanent yellows, 10 parts of organosilicons, 4 parts of solidifying agent, 1 part of stablizer and 5 parts of flow agents are mixed.
(2) adopt twin screw extruder to adopt 75 DEG C-85 DEG C in front end to batch mixing extruding, by forcing machine extrusion molding after stage casing temperature brings up to 110 DEG C-120 DEG C, after pulverizing, obtain powder coating.
Embodiment 3.
The anti scuffing automotive powder coating that sticking power is good, comprises the following steps,
(1) count by weight, the hydroxyl saturated polyester resin of the linear hydroxyl saturated polyester resin of 20 parts, 4 parts of epoxy resin, 25 parts of slight collateralizations, 17 parts of modified rosin resins, 17 parts of titanium dioxides, 5 parts of permanent yellows, 8 parts of organosilicons, 3 parts of solidifying agent, 0.5 part of stablizer and 3.5 parts of flow agents are mixed.
(2) adopt twin screw extruder to adopt 75 DEG C-85 DEG C in front end to batch mixing extruding, by forcing machine extrusion molding after stage casing temperature brings up to 110 DEG C-120 DEG C, after pulverizing, obtain powder coating.
Powder coating of the present invention, adds organosilicon and can reduce epoxy resin internal stress, can improve the performances such as epoxy resin toughness, high thermal resistance again.In the process forming powder coating, the fusing point of modified rosin resin is low, and under the effect of organosilicon and epoxy resin, make the particle of powder coating close to spherical, like this, just can improve the sticking power of paint film, paint film is not easy to drop, long service life.Due to the hydroxyl saturated polyester resin containing linear hydroxyl saturated polyester resin, epoxy resin, slight collateralization, therefore, the anti scuffing performance of this coating is good.
Claims (4)
1. the anti scuffing automotive powder coating that sticking power is good, it is characterized in that: count by weight, be made up of the hydroxyl saturated polyester resin of the linear hydroxyl saturated polyester resin of 15-30 part, 3-5 part epoxy resin, 20-30 part is slight collateralization, 15-20 part modified rosin resin, 15-20 part titanium dioxide, 3-6 part permanent yellow, 5-10 part organosilicon, 2-4 part solidifying agent, 0.1-1 part stablizer and 2-5 part flow agent.
2. the anti scuffing automotive powder coating that sticking power according to claim 1 is good, is characterized in that: described solidifying agent is fatty polyamide type amine.
3. the anti scuffing automotive powder coating that sticking power according to claim 1 is good, is characterized in that: described stablizer is Zinic stearas.
4. the anti scuffing automotive powder coating that sticking power according to claim 1 is good, is characterized in that: described flow agent selects dimethyl siloxane.