CN104356879A - Fireproof powder paint - Google Patents
Fireproof powder paint Download PDFInfo
- Publication number
- CN104356879A CN104356879A CN201410735863.3A CN201410735863A CN104356879A CN 104356879 A CN104356879 A CN 104356879A CN 201410735863 A CN201410735863 A CN 201410735863A CN 104356879 A CN104356879 A CN 104356879A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire
- powder
- epoxy resin
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fireproof powder paint which is composed of the following components in parts by weight: 10-20 parts of bisphenol F epoxy resin, 30-45 parts of aliphatic glycidol ether epoxy resin, 15-18 parts of poly(methyl) acrylic resin with free carboxyl group, 15-20 parts of FEVE fluorocarbon resin, 4-8 parts of ammonium polyphosphate, 1-2 parts of magnesium carbonate, 4-8 parts of rubber powder, 8-12 parts of carbon black, 3-5 parts of aluminum powder, 3-5 parts of iron oxide red, 5-8 parts of curing agent, 1-2 parts of stabilizer and 1-2 parts of leveling agent. The powder paint has the advantages of moderate volume resistance, high surface resistance and favorable fire resistance.
Description
Technical field
The present invention relates to powder coating.
Background technology
At present, along with the develop rapidly of global industry, the environmental problem caused also becomes increasingly conspicuous.How to carry out the important topic that environmental protection work has become urgently people's research.Some western countries development research that Environmental awareness is strong goes out to have the car paint of low volatile organic, and puts into production in a large number and use.Along with the development of automobile industry, in order to beautify the appearance of film of automobile, alleviating the environmental pollution that it causes, improving vehicle spray painting technology and seeming particularly important.
For automotive powder coating, if the volume resistance of powder coating is too high, powder is not easily adsorbed on base material, and volume resistance is too low, causes powder not easily charged.If the surface resistivity of powder coating is too low, be just easy to cause the electric charge being positioned at base material edges and corners to leak, thus the powder coating on base material is come off.
In coating, fire resistance also very important.
Summary of the invention
The invention provides a kind of volume resistance moderate, surface resistivity is high, the powder coating that fire resistance is good.
For achieving the above object, a kind of fire-proof powdery paint, count by weight, poly-(methyl) acrylic resin, 15-20 part FEVE fluorocarbon resin, 4-8 part ammonium polyphosphate, 1-2 part magnesiumcarbonate, 4-8 part rubber powder, 8-12 part carbon black, 3-5 part aluminium powder, 3-5 part red iron oxide, 5-8 part solidifying agent, 1-2 part stablizer and 1-2 part flow agent by 10-20 part bisphenol F epoxy resin, 30-45 part aliphatic glycidyl ether epoxy resin, 15-18 part with free carboxyl group form.
Further, described solidifying agent is TGIC.
Further, described stablizer is organic tin stablizer.
Further, described flow agent selects the product of Dow Corning Corporation, and model is 5T.
The invention has the beneficial effects as follows: adopt raw material of the present invention when preparing powder coating, owing to containing aliphatic glycidyl ether epoxy resin in raw material, there is poly-(methyl) acrylic resin, rubber powder, carbon black and the aluminium powder of free carboxyl group, when sprayed coating, carbon black and aluminium powder is made to deposit in powder, more rubber powder is had to separate out, therefore, make the surface resistivity of powder coating high, volume resistance is moderate, like this, not easily there is charge leakage in the edges and corners of base material in the powder coating of spraying, powder coating is easily attached on base material.The present invention adopts FEVE fluorocarbon resin to coordinate with poly-(methyl) acrylic resin with free carboxyl group, containing as lively as a cricket epoxy group(ing) in product of the present invention, also containing fluoroolefin, hydroxyl etc., it to most of material as timber, metal, glass, plastics, rubber, leather, pottery, fiber etc. have good bonding force.Product after solidification, has excellent chemical resistance, thermotolerance, resistance to acids and bases and good electrical insulating property, has good sticking power, non-corrosibility and physical strength; The present invention has splendid closure, and flame-retardant composition can not move to coat side, and therefore its fire resistance is less by the impact of time and environment.
Embodiment
Below in conjunction with embodiment, the present invention is further elaborated.
Fire-proof powdery paint, count by weight, poly-(methyl) acrylic resin, 15-20 part FEVE fluorocarbon resin, 4-8 part ammonium polyphosphate, 1-2 part magnesiumcarbonate, 4-8 part rubber powder, 8-12 part carbon black, 3-5 part aluminium powder, 3-5 part red iron oxide, 5-8 part solidifying agent, 1-2 part stablizer and 1-2 part flow agent by 10-20 part bisphenol F epoxy resin, 30-45 part aliphatic glycidyl ether epoxy resin, 15-18 part with free carboxyl group form.Described solidifying agent is TGIC.Described stablizer is organic tin stablizer.Described flow agent selects the product of Dow Corning Corporation, and model is 5T.
Embodiment 1.
The preparation method of fire-proof powdery paint, comprises the following steps,
(1) count by weight, by 10 parts of bisphenol F epoxy resins, 30 parts of aliphatic glycidyl ether epoxy resin, 15 parts have poly-(methyl) acrylic resin of free carboxyl group, 15 parts of FEVE fluorocarbon resins, 4 parts of ammonium polyphosphates, 1 part of magnesiumcarbonate, 4 parts of rubber powders, 8 parts of carbon blacks, 3 parts of aluminium powders, 3 parts of red iron oxides, 5 parts of solidifying agent, 1 part of stablizer and 1 part of flow agent mix.
(2) adopt twin screw extruder to adopt 70 DEG C-80 DEG C in front end to batch mixing extruding, by forcing machine extrusion molding after stage casing temperature brings up to 120 DEG C-130 DEG C, after pulverizing, obtain powder coating.
Embodiment 2.
The preparation method of fire-proof powdery paint, comprises the following steps,
(1) count by weight, by 20 parts of bisphenol F epoxy resins, 45 parts of aliphatic glycidyl ether epoxy resin, 18 parts have poly-(methyl) acrylic resin of free carboxyl group, 20 parts of FEVE fluorocarbon resins, 8 parts of ammonium polyphosphates, 2 parts of magnesiumcarbonate, 8 parts of rubber powders, 12 parts of carbon blacks, 5 parts of aluminium powders, 5 parts of red iron oxides, 8 parts of solidifying agent, 2 parts of stablizers and 2 parts of flow agents mix.
(2) adopt twin screw extruder to adopt 70 DEG C-80 DEG C in front end to batch mixing extruding, by forcing machine extrusion molding after stage casing temperature brings up to 120 DEG C-130 DEG C, after pulverizing, obtain powder coating.
Embodiment 3.
The preparation method of fire-proof powdery paint, comprises the following steps,
(1) count by weight, by 15 parts of bisphenol F epoxy resins, 37 parts of aliphatic glycidyl ether epoxy resin, 16 parts have poly-(methyl) acrylic resin of free carboxyl group, 18 parts of FEVE fluorocarbon resins, 6 parts of ammonium polyphosphates, 1.3 parts of magnesiumcarbonate, 5 parts of rubber powders, 10 parts of carbon blacks, 4 parts of aluminium powders, 4 parts of red iron oxides, 7 parts of solidifying agent, 1.2 parts of stablizers and 1.5 parts of flow agents mix.
(2) adopt twin screw extruder to adopt 70 DEG C-80 DEG C in front end to batch mixing extruding, by forcing machine extrusion molding after stage casing temperature brings up to 120 DEG C-130 DEG C, after pulverizing, obtain powder coating.
Adopt raw material of the present invention when preparing powder coating, owing to containing aliphatic glycidyl ether epoxy resin in raw material, there is poly-(methyl) acrylic resin, rubber powder, carbon black and the aluminium powder of free carboxyl group, when sprayed coating, carbon black and aluminium powder is made to deposit in powder, more rubber powder is had to separate out, therefore, make the surface resistivity of powder coating high, volume resistance is moderate, like this, not easily there is charge leakage in the edges and corners of base material in the powder coating of spraying, powder coating is easily attached on base material.The present invention adopts FEVE fluorocarbon resin to coordinate with poly-(methyl) acrylic resin with free carboxyl group, containing as lively as a cricket epoxy group(ing) in product of the present invention, also containing fluoroolefin, hydroxyl etc., it to most of material as timber, metal, glass, plastics, rubber, leather, pottery, fiber etc. have good bonding force.Product after solidification, has excellent chemical resistance, thermotolerance, resistance to acids and bases and good electrical insulating property, has good sticking power, non-corrosibility and physical strength; The present invention has splendid closure, and flame-retardant composition can not move to coat side, and therefore its fire resistance is less by the impact of time and environment.
Claims (4)
1. a fire-proof powdery paint, it is characterized in that: count by weight, poly-(methyl) acrylic resin, 15-20 part FEVE fluorocarbon resin, 4-8 part ammonium polyphosphate, 1-2 part magnesiumcarbonate, 4-8 part rubber powder, 8-12 part carbon black, 3-5 part aluminium powder, 3-5 part red iron oxide, 5-8 part solidifying agent, 1-2 part stablizer and 1-2 part flow agent by 10-20 part bisphenol F epoxy resin, 30-45 part aliphatic glycidyl ether epoxy resin, 15-18 part with free carboxyl group form.
2. fire-proof powdery paint according to claim 1, is characterized in that: described solidifying agent is TGIC.
3. fire-proof powdery paint according to claim 1, is characterized in that: described stablizer is organic tin stablizer.
4. fire-proof powdery paint according to claim 1, is characterized in that: described flow agent selects the product of Dow Corning Corporation, and model is 5T.