CN105778064A - Polyester resin for direct-fired boiler tolerant powder coating and preparation method thereof - Google Patents
Polyester resin for direct-fired boiler tolerant powder coating and preparation method thereof Download PDFInfo
- Publication number
- CN105778064A CN105778064A CN201610161489.XA CN201610161489A CN105778064A CN 105778064 A CN105778064 A CN 105778064A CN 201610161489 A CN201610161489 A CN 201610161489A CN 105778064 A CN105778064 A CN 105778064A
- Authority
- CN
- China
- Prior art keywords
- polyester resin
- antioxidant
- color inhibition
- inhibition agent
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a polyester resin for direct-fired boiler tolerant powder coating and a preparation method thereof. This polyester resin is made from the following materials: 0-15 parts of ethylene glycol, 20-40 parts of neopentyl glycol, 0-30 parts of trimethylolpropane, 30-60 parts of terephthalic acid, 0-30 parts of isophthalic acid, and 1-20 parts of adipic acid; the polyester resin also comprises an antioxidant and a yellowing resistant, the antioxidant is antioxidant 168, the yellowing resistant is yellowing resistant 1300, and addition of the antioxidant and yellowing resistant is 0.4-1.2% of total weight of the polyester resin. The polyester resin for direct-fired boiler tolerant powder coating is tolerant to direct-fired boiler baking by adding the antioxidant 168 and yellowing resistant 1200 and reasonably making their ratio.
Description
Technical field
The invention belongs to polymeric material field, relate to a kind of polyester resin, particularly to a kind of resistance to direct combustion
Stove polyester resin for powder coating.
Background technology
Powdery paints has solvent-free, pollution-free, recyclable, environmental protection, the saving energy and resource, alleviates
Labour intensity and film mechanical strength high, thus be rapidly developed, be widely used in household electrical appliances,
Car paint, aluminum alloy doors and windows and metal and nonmetallic external decoration coating protection.
Mode of heating in paint line substantially has three kinds at present: electrical heating, gas heating and combustion
Oil heating.The most regional in China, owing to commercial power is shorter and expensive, therefore, in paint line
Heater be widely used diesel oil, natural gas etc. as thermal source.But directly heated by gas furnace,
The baking of combustion gas can affect the surface color of powdery paints, thus affects final painting effect.
Summary of the invention
The present invention is to solve the problems referred to above, it is provided that a kind of polyester resin for powder coating of resistance to direct-combustion furnace, reach
To the powdery paints preparing the heating of resistance to direct-combustion furnace so that in the case of paint line uses gas heating
The purpose of surface color is not interfered with yet.
For achieving the above object, the present invention is by the following technical solutions:
A kind of polyester resin for powder coating of resistance to direct-combustion furnace, described polyester resin includes following parts by weight
Raw material:
Described polyester resin also includes antioxidant and color inhibition agent, and described antioxidant is irgasfos 168;Resistance to
Xanthochromia agent is color inhibition agent 1300, and the addition of described antioxidant and color inhibition agent is polyester resin gross weight
0.4-1.2%.
Further, described polyester resin includes the raw material of following parts by weight:
Described polyester resin also includes antioxidant and color inhibition agent, and described antioxidant is irgasfos 168;Resistance to Huang
Change agent is color inhibition agent 1300.Wherein irgasfos 168 is: three [2.4-di-tert-butyl-phenyl] phosphite ester,
Color inhibition agent 1300 is double (N, N-dimethyl)-1,6-hexamethyl trap phosphinylidynes.
The addition of described antioxidant and color inhibition agent is the 0.6-1% of polyester resin gross weight.
Further, described polyester resin includes the raw material of following parts by weight:
Described polyester resin also includes antioxidant and color inhibition agent, and described antioxidant is irgasfos 168;Resistance to
Xanthochromia agent is color inhibition agent 1300, and the addition of described antioxidant and color inhibition agent is polyester resin gross weight
1%.
Further, the interpolation mass ratio of antioxidant and color inhibition agent is 1:2-2:1.
Further, the interpolation mass ratio of antioxidant and color inhibition agent is 1:2.
The present invention also provides for the preparation method of a kind of described polyester resin for powder coating of resistance to direct-combustion furnace, including
Following steps:
Synthesis reactor temperature is risen to 90-100 DEG C, add ethylene glycol, neopentyl glycol, trimethylolpropane,
Terephthalic acid (TPA), adipic acid, M-phthalic acid, Mono-n-butyltin, rise under the protection of reaction nitrogen
240-245 DEG C of maintenance of temperature, until the acid number of thing is 10-20mgkoh/g, is cooled to 210-220 DEG C, puts into
End-capping reagent M-phthalic acid, or/and adipic acid, is warming up to 242-245 DEG C of maintenance, until reactant acid number is
46-49mgkoh/g, carries out vacuumizing, until reactant acid number is 32-36mgkoh/g, is cooled to
205-210 DEG C, put into curing accelerator quaternary ammonium salt, antioxidant and color inhibition agent, maintain 15-30 minute i.e.
Can discharging.
Compared with prior art, the technical program has the advantage that
The polyester resin for powder coating of resistance to direct-combustion furnace of the present invention is by adding irgasfos 168 and color inhibition agent
1300, and the ratio both reasonable preparation, prepared polyester resin good weatherability, significantly improve simultaneously
The xanthochromia performance of baking in gas furnace, protecting light rate is more than 50 (240h QUV/%), and aberration is less than 0.3
(200℃*10min)。
Further, by adjusting the rational proportion of each raw material further, the ratio when 168 and 1300 is 1:
2;When the gross weight of antioxidant and color inhibition agent is the 1% of polyester resin, protecting light rate is more than 50 (240h
QUV/%), aberration is only 0.13 (200 DEG C of * 10min).
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention will be further described.
Embodiment 1:
First, on the premise of without antioxidant and color inhibition agent, weigh former by following mass fraction
Material, prepares polyester resin
Synthesis reactor temperature is risen to 90-100 DEG C, add ethylene glycol, neopentyl glycol, trimethylolpropane,
Terephthalic acid (TPA), adipic acid, M-phthalic acid, Mono-n-butyltin, rise under the protection of reaction nitrogen
240-245 DEG C of maintenance of temperature, until the acid number of thing is 10-20mgkoh/g, is cooled to 210-220 DEG C, puts into
End-capping reagent M-phthalic acid, or/and adipic acid, is warming up to 242-245 DEG C of maintenance, until reactant acid number is
46-49mgkoh/g, carries out vacuumizing, until reactant acid number is 32-36mgkoh/g, is cooled to
205-210 DEG C, put into curing accelerator quaternary ammonium salt, maintain and get final product discharging in 15-30 minute.
Embodiment 2-8 is as shown in the table:
The proportioning table of table 1 embodiment 2-8
Its major parameter acid value of polyester resin, viscosity and the Tg that prepare by upper table 1 are as shown in table 2.
The polyester resin prepared adds filler, levelling agent, optical brightener, curing agent, through squeezing after mixing
Go out machine extrusion, use flour mill abrasive dust, be then screened into powdery paints.The powder prepared through this kind of method is coated with
The condition of cure of material is 200 DEG C/10-20min, easy construction, it is simple to reclaim, energy-conserving and environment-protective.
Table 2 embodiment 2-8 prepare polyester resin and powder process after performance parameter
As above, shown in table 2, the use of ethylene glycol can reduce the ageing properties of polyester resin;M-phthalic acid
The ageing-resistant performance of polyester resin can be increased, but impact property is bad;The adipic acid glass to polyester resin
The impact of glass temperature is very big, and the consumption increasing adipic acid can reduce vitrification point.Embodiment 8 obtains
Sample combination property optimal.On the basis of the sample of embodiment 8, add irgasfos 168 and color inhibition
Agent 1300 is tested.
In following table, the amount of antioxidant is antioxidant and the ratio of color inhibition agent.Both add total amount is poly-
The 1% of ester resin.
The different antioxidant of table 3 and color inhibition agent are with the use of the impact on prepared polyester resin performance
From upper table 3 it can be seen that antioxidant 168 and color inhibition agent 1300 with the use of substantially carrying
The high xanthochromia performance of baking in gas furnace, and the ratio of antioxidant 168 and color inhibition agent 1300 is
1:2 is with the use of best results.
Although the present invention is open as above with preferred embodiment, but it is not for limiting the present invention, appoints
What those skilled in the art without departing from the spirit and scope of the present invention, may be by the disclosure above
Technical solution of the present invention is made possible variation and amendment by method and technology contents, therefore, every does not takes off
From the content of technical solution of the present invention, it is any that above example is made by the technical spirit of the foundation present invention
Simple modification, equivalent variations and modification, belong to the protection domain of technical solution of the present invention.
Claims (6)
1. the polyester resin for powder coating of resistance to direct-combustion furnace, it is characterised in that described polyester resin includes
The raw material of following parts by weight:
Described polyester resin also includes antioxidant and color inhibition agent, and described antioxidant is irgasfos 168;Resistance to Huang
Change agent is color inhibition agent 1300, and the addition of described antioxidant and color inhibition agent is polyester resin gross weight
0.4-1.2%.
Polyester resin the most according to claim 1, it is characterised in that described polyester resin include with
The raw material of lower parts by weight:
Described polyester resin also includes antioxidant and color inhibition agent, and described antioxidant is irgasfos 168;Resistance to
Xanthochromia agent is color inhibition agent 1300, and the addition of described antioxidant and color inhibition agent is polyester resin gross weight
The 0.6-1% of amount.
Polyester resin the most according to claim 2, it is characterised in that described polyester resin include with
The raw material of lower parts by weight:
Described polyester resin also includes antioxidant and color inhibition agent, and described antioxidant is irgasfos 168;Resistance to
Xanthochromia agent is color inhibition agent 1300, and the addition of described antioxidant and color inhibition agent is polyester resin gross weight
The 1% of amount.
4. according to the polyester resin described in claim 1-3 any one, it is characterised in that antioxidant and resistance to
The interpolation mass ratio of xanthochromia agent is 1:2-2:1.
Polyester resin the most according to claim 4, it is characterised in that antioxidant and color inhibition agent
Interpolation mass ratio is 1:2.
The preparation method of the polyester resin for powder coating of resistance to direct-combustion furnace the most as claimed in claim 1, its feature
It is, comprises the following steps:
Synthesis reactor temperature is risen to 90-100 DEG C, adds ethylene glycol, neopentyl glycol, trimethylolpropane, right
Phthalic acid, adipic acid, M-phthalic acid, Mono-n-butyltin, rise under the protection of reaction nitrogen
240-245 DEG C of maintenance of temperature, until the acid number of thing is 10-20mgkoh/g, is cooled to 210-220 DEG C, throws
Enter end-capping reagent M-phthalic acid or/and adipic acid, be warming up to 242-245 DEG C of maintenance, until reactant is sour
Value is 46-49mgkoh/g, carries out vacuumizing, until reactant acid number is 32-36mgkoh/g, and fall
Temperature, to 205-210 DEG C, puts into curing accelerator quaternary ammonium salt, antioxidant and color inhibition agent, maintains 15-30
Minute get final product discharging.