Teflon and stiffening technology and guide roller cleaning technology after use of teflon and stiffening technology Download PDFInfo
- Publication number
- CN105755715A CN105755715A CN201610297797.5A CN201610297797A CN105755715A CN 105755715 A CN105755715 A CN 105755715A CN 201610297797 A CN201610297797 A CN 201610297797A CN 105755715 A CN105755715 A CN 105755715A
- Authority
- CN
- China
- Prior art keywords
- stiffening
- technology
- guide roller
- padding
- deflector roll
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a teflon and stiffening technology. The teflon and stiffening technology of a fabric is finished through the steps of preparing padding fluid, performing padding, performing drying and performing baking. A guide roller cleaning technology after use of the teflon and stiffening technology needs to be performed under a no-cold-water state, a padding fluid forming membrane coats the outer surface of the guide roller, when the thickness of the membrane formed by the padding fluid is 0.5 mm or above, the membrane formed by the padding fluid at the edge of the guide roller is directly torn and separated from the guide roller, and then the whole membrane on the guide roller is torn; when the thickness of the membrane formed by the padding fluid is 0.5 mm or below, the membrane is directly wiped by using cloth, and the membrane is wiped down from the guide roller. The teflon and stiffening technology and the guide roller cleaning technology which are disclosed by the invention have the advantages that the formula of the padding fluid is reasonably improved, and technology parameters are reasonably adjusted, so that the water resistance, the oil resistance, the stain resistance and the stiffening effect of the fabric after the after-finish technology are good; under the no-cold-water state, after being used, a machine is immediately cleaned, the membrane formed by the padding fluid is torn down from the surface of the guide roller, and time and labor are saved.
Description
Technical field
The invention belongs to weaving face fabric processed technology, deflector roll cleaning after being specifically related to a kind of polytetrafluoroethylene and stiffening technique and using.
Background technology
Currently, along with the civilization and progress of society and improving constantly of people's living standard, the demand of dress ornament is broken through it and hides body, cold-proof, warming original basic function by people already, but develops to the diversified direction pursuing personalized, stylization and functionalization.For adapting to the development and change of above-mentioned situation, textile printing and dyeing industry and color additive industry have all carried out substantial amounts of research and exploration, the new textile that new material, new technique, new technology produce is adopted to continue to bring out in a large number, daily life that they improve day by day except meeting people and except taking demand, also penetrate into the various aspects of social production, seek to new survival and development space for textile.This is wherein, to all kinds of flat textile product, as cotton, fiber crops, polyester-cotton blend, chemical fibre and blend fabric, yarn dyed fabric etc. carry out different types of functional topical finishing, it is made to possess on the basis of fibril weaving characteristic, give more excellent wearability and other purposes functions widely, the function making textile is extended and is developed, and is one of important approach.
But after polytetrafluoroethylene and stiffening Final finishing, usually can form film in guide roller surface, will lump immediately after running into cold water, be difficult to be carried out, cause the use affecting fabric below, even directly result in the damage of plant equipment.
Summary of the invention
Present invention aims to the deficiencies in the prior art, deflector roll cleaning after simple, the easy to operate polytetrafluoroethylene of a kind of technique and stiffening technique being now provided and using.
For solving above-mentioned technical problem, the technical solution used in the present invention is: the invention discloses a kind of polytetrafluoroethylene and stiffening technique, its innovative point is in that: through padding liquid preparation, pad, dry and bake step, complete the polytetrafluoroethylene of fabric and stiffening technique；Described specifically comprise the following steps that
(1) preparation of padding liquid: polytetrafluoroethylene reagent C P-SLA, stiffening agent GM-710 and neutralization acid are put in water, prepare impregnation liquid, the consumption of described polytetrafluoroethylene reagent C P-SLA is 60g/L, and the consumption of described stiffening agent GM-710 is 30g/L, and described antacid consumption is 10g/L；
(2) pad: adopt an immersing and rolling technique, described in pad speed be 25m/min；
(3) dry: the speed of described stenter is 30m/min, and described drying temperature is 110-120 DEG C；
(4) bake: the speed of described forming machine is 30m/min, and described baking temperature is 185-190 DEG C, described in bake the time be 1min.
Another object of the present invention is deflector roll cleaning after open a kind of use, its innovative point is in that: described cleaning must carry out under without cold water state, described padding liquid forms film and is coated on deflector roll outer surface, the thickness of the film that described padding liquid is formed is more than 0.5mm, the film padding liquid at deflector roll edge formed directly is torn with deflector roll and is separated, and is then torn by the whole film on deflector roll；The thickness of the film that described padding liquid is formed is below 0.5mm, uses cloth to carry out direct wiping, is got off from wiping deflector roll by film.
Beneficial effects of the present invention is as follows:
(1) present invention is by rationally improving the formula of padding liquid, by Reasonable adjustment technological parameter so that pass through the three anti-and stiffening effects of fabric of this postfinishing process more preferably；
(2) present invention is by without under cold water state, and board uses after terminating and just cleans immediately, is torn from guide roller surface by the film that padding liquid is formed, time saving and energy saving.
Detailed description of the invention
By particular specific embodiment, embodiments of the present invention being described below, those skilled in the art the content disclosed by this specification can understand other advantages and effect of the present invention easily.
Deflector roll cleaning after a kind of use, cleaning must carry out under without cold water state, padding liquid forms film and is coated on deflector roll outer surface, the thickness of the film that padding liquid is formed is more than 0.5mm, the film padding liquid at deflector roll edge formed directly is torn with deflector roll and is separated, and is then torn by the whole film on deflector roll；The thickness of the film that padding liquid is formed is below 0.5mm, uses cloth to carry out direct wiping, is got off from wiping deflector roll by film.
Embodiment 1
A kind of polytetrafluoroethylene and stiffening technique, through padding liquid preparation, pad, dry and bake step, complete the polytetrafluoroethylene of fabric and stiffening technique；Specifically comprise the following steps that
(1) preparation of padding liquid: being put in water by polytetrafluoroethylene reagent C P-SLA, stiffening agent GM-710 and neutralization acid, prepare impregnation liquid, the consumption of polytetrafluoroethylene reagent C P-SLA is 60g/L, and the consumption of stiffening agent GM-710 is 30g/L, and antacid consumption is 10g/L；
(2) padding: adopt an immersing and rolling technique, padding speed is 25m/min；
(3) drying: the speed of stenter is 30m/min, drying temperature is 110 DEG C；
(4) baking: the speed of forming machine is 30m/min, baking temperature is 185 DEG C, and the time of baking is 1min.
Product after being processed by the present embodiment can be reached to wash rear defence oil index at 10 times and reach 5 grades.
Embodiment 2
A kind of polytetrafluoroethylene and stiffening technique, through padding liquid preparation, pad, dry and bake step, complete the polytetrafluoroethylene of fabric and stiffening technique；Specifically comprise the following steps that
(1) preparation of padding liquid: being put in water by polytetrafluoroethylene reagent C P-SLA, stiffening agent GM-710 and neutralization acid, prepare impregnation liquid, the consumption of polytetrafluoroethylene reagent C P-SLA is 60g/L, and the consumption of stiffening agent GM-710 is 30g/L, and antacid consumption is 10g/L；
(2) padding: adopt an immersing and rolling technique, padding speed is 25m/min；
(3) drying: the speed of stenter is 30m/min, drying temperature is 120 DEG C；
(4) baking: the speed of forming machine is 30m/min, baking temperature is 190 DEG C, and the time of baking is 1min.
Product after being processed by the present embodiment can be reached to wash rear defence oil index at 10 times and reach 5 grades.
Embodiment 3
A kind of polytetrafluoroethylene and stiffening technique, through padding liquid preparation, pad, dry and bake step, complete the polytetrafluoroethylene of fabric and stiffening technique；Specifically comprise the following steps that
(1) preparation of padding liquid: being put in water by polytetrafluoroethylene reagent C P-SLA, stiffening agent GM-710 and neutralization acid, prepare impregnation liquid, the consumption of polytetrafluoroethylene reagent C P-SLA is 60g/L, and the consumption of stiffening agent GM-710 is 30g/L, and antacid consumption is 10g/L；
(2) padding: adopt an immersing and rolling technique, padding speed is 25m/min；
(3) drying: the speed of stenter is 30m/min, drying temperature is 115 DEG C；
(4) baking: the speed of forming machine is 30m/min, baking temperature is 187 DEG C, and the time of baking is 1min.
Product after being processed by the present embodiment can be reached to wash rear defence oil index at 10 times and reach 5 grades.
The present invention is by rationally improving the formula of padding liquid, by Reasonable adjustment technological parameter so that pass through the three anti-and stiffening effects of fabric of this postfinishing process more preferably；The present invention is by without under cold water state, and board uses after terminating and just cleans immediately, is torn from guide roller surface by the film that padding liquid is formed, time saving and energy saving.
Above-described embodiment is presently preferred embodiments of the present invention; it it is not the restriction to technical solution of the present invention; as long as without the technical scheme that creative work can realize on the basis of above-described embodiment, be regarded as falling within the scope of the rights protection of patent of the present invention.
Claims (2)
1. a polytetrafluoroethylene and stiffening technique, it is characterised in that: through padding liquid preparation, pad, dry and bake step, complete the polytetrafluoroethylene of fabric and stiffening technique；Described specifically comprise the following steps that
(1) preparation of padding liquid: polytetrafluoroethylene reagent C P-SLA, stiffening agent GM-710 and neutralization acid are put in water, prepare impregnation liquid, the consumption of described polytetrafluoroethylene reagent C P-SLA is 60g/L, and the consumption of described stiffening agent GM-710 is 30g/L, and described antacid consumption is 10g/L；
(2) pad: adopt an immersing and rolling technique, described in pad speed be 25m/min；
(3) dry: the speed of described stenter is 30m/min, and described drying temperature is 110-120 DEG C；
(4) bake: the speed of described forming machine is 30m/min, and described baking temperature is 185-190 DEG C, described in bake the time be 1min.
2. deflector roll cleaning after the use described in a claim 1, it is characterized in that: described cleaning must carry out under without cold water state, described padding liquid forms film and is coated on deflector roll outer surface, the thickness of the film that described padding liquid is formed is more than 0.5mm, the film padding liquid at deflector roll edge formed directly is torn with deflector roll and is separated, and is then torn by the whole film on deflector roll；The thickness of the film that described padding liquid is formed is below 0.5mm, uses cloth to carry out direct wiping, is got off from wiping deflector roll by film.