CN105754509A - Hot-pressing adhesive tape with beautiful-pattern paper - Google Patents
Hot-pressing adhesive tape with beautiful-pattern paper Download PDFInfo
- Publication number
- CN105754509A CN105754509A CN201410792947.0A CN201410792947A CN105754509A CN 105754509 A CN105754509 A CN 105754509A CN 201410792947 A CN201410792947 A CN 201410792947A CN 105754509 A CN105754509 A CN 105754509A
- Authority
- CN
- China
- Prior art keywords
- adhesive tape
- stricture
- parts
- vagina
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to an adhesive tape and particularly relates to a hot-pressing adhesive tape with beautiful-pattern paper. The adhesive tape comprises a beautiful-pattern paper layer 1, an acrylic acid adhesive layer 2 and a hot melt adhesive layer 3 in order from top to bottom. The adhesive tape is good in retentivity, free of adhesive residue, good in toughness, good in tension resisting effects, high in tensile strength and free of breakage.
Description
Technical field
The present invention relates to adhesive tape, be specifically related to a kind of U.S. stricture of vagina paper hot pressing adhesive tape.
Background technology
Hot pressing adhesive tape is also known as Hot melt adhesive tape.It is different from pressure sensitive adhesive tape, and it is when room temperature, and hot pressing adhesive tape does not show pressure sensitive adhesion, and has resistance to blocking；But through the high temperature hot pressing of moment, just produce the cohesive force of 10 times of pressure sensitive adhesive tapes.But in the adhesive tape of the high thickness of existing needs, multiplex U.S. stricture of vagina paper is as substrate layer, but this substrate layer pastes poor performance with hot melt adhesive layer, it is easy to degumming.
Summary of the invention
It is good that the technical problem to be solved is to provide a kind of bonding force, not easily a kind of U.S. stricture of vagina paper hot pressing adhesive tape of degumming.
The technical problem to be solved is achieved by the following technical programs:
A kind of U.S. stricture of vagina paper hot pressing adhesive tape, is followed successively by U.S. stricture of vagina ply of paper 1, acrylate glue adhensive layer 2, hot melt adhesive layer 3 from top to bottom.
Further, described acrylate glue adhensive layer is made up of the component of following parts by weight:
Methyl methacrylate 40 ~ 50 parts；Hydroxyethyl methylacrylate 20 ~ 30 parts；Stabilizer 1 ~ 3 part；Initiator 1 ~ 3 part；Solvent 10 ~ 25 parts；Stabilizer used, initiator, solvent are that the material that the art is commonly used all can realize the present invention, are not described in detail at this.
Further, described hot melt adhesive layer is made up of the component of following parts by weight:
Ethylene ~ acetate ethylene copolymer 180 ~ 300 parts；Petropols 20 ~ 50 parts；0.2 ~ 4 part of age resistor.
Further, described U.S. stricture of vagina ply of paper thickness is 80 ~ 120 μm.
Further, described acrylate glue adhensive layer thickness is 5 ~ 8 μm.
Further, described hot melt adhesive layer thickness is 10 ~ 15 μm.
In the present invention, U.S. stricture of vagina ply of paper is big with hot melt adhesive layer polarity spectrum, causes that adhesion is poor, it is easy to degumming.Therefore, inventor increases an acrylate glue adhensive layer at U.S. stricture of vagina ply of paper and hot melt adhesive layer cleverly and solves polarity spectrum greatly, and adhesion is poor, it is easy to the problem of degumming.
And in hot melt adhesive layer, the characteristic according to acrylate glue adhensive layer, so that both polarity are similar, it has on acrylate glue adhensive layer and significantly penetrates into effect, it is possible to strengthen adhesion between the two further, strengthens adhesive force.
And age resistor used in inventing is the age resistor that the art is conventional, it is preferred to four (3,5-di-t-butyl-4-hydroxyl) benzenpropanoic acid pentaerythritol ester.
There is advantages that the U.S. stricture of vagina paper hot pressing adhesive tape retentivity of the present invention is good, without cull, good toughness, tension is effective, and tensile strength is high, does not have phenomenon of rupture.
Accompanying drawing explanation
Fig. 1 is U.S. stricture of vagina paper hot pressing adhesive tape structure schematic diagram provided by the invention.
Detailed description of the invention
The preparation technology of the present invention is the routine techniques of the art, does not elaborate at this.
Below in conjunction with drawings and Examples, the present invention will be described in detail.
Embodiment 1
As it is shown in figure 1, U.S. stricture of vagina paper hot pressing adhesive tape provided by the invention, it is followed successively by U.S. stricture of vagina ply of paper 1, acrylate glue adhensive layer 2, hot melt adhesive layer 3 from top to bottom.The formula of described acrylate glue adhensive layer is: methyl methacrylate 40 parts；Hydroxyethyl methylacrylate 30 parts；Stabilizer 2 parts；Initiator 2 parts；Solvent 15 parts.The formula of described hot melt adhesive layer is: ethylene ~ acetate ethylene copolymer 250 parts, Petropols 35 parts；Four (3,5-di-t-butyl-4-hydroxyl) benzenpropanoic acid pentaerythritol ester 2 parts.Described U.S. stricture of vagina ply of paper thickness is 100 μm；Described acrylate glue adhensive layer thickness is 8 μm；Described hot melt adhesive layer thickness is 12 μm.The U.S. stricture of vagina paper hot pressing adhesive tape of the present invention will not produce cull after peeling off.
Embodiment 2
As it is shown in figure 1, U.S. stricture of vagina paper hot pressing adhesive tape provided by the invention, it is followed successively by U.S. stricture of vagina ply of paper 1, acrylate glue adhensive layer 2, hot melt adhesive layer 3 from top to bottom.The formula of described acrylate glue adhensive layer is: methyl methacrylate 50 parts；Hydroxyethyl methylacrylate 20 parts；Stabilizer 1 part；Initiator 3 parts；Solvent 25 parts.The formula of described hot melt adhesive layer is: ethylene ~ acetate ethylene copolymer 200 parts；Petropols 50 parts；Four (3,5-di-t-butyl-4-hydroxyl) benzenpropanoic acid pentaerythritol ester 4 parts.Described U.S. stricture of vagina ply of paper thickness is 120 μm；Described acrylate glue adhensive layer thickness is 5 μm；Described hot melt adhesive layer thickness is 15 μm.The U.S. stricture of vagina paper hot pressing adhesive tape of the present invention will not produce cull after peeling off.
Embodiment 3
As it is shown in figure 1, U.S. stricture of vagina paper hot pressing adhesive tape provided by the invention, it is followed successively by U.S. stricture of vagina ply of paper 1, acrylate glue adhensive layer 2, hot melt adhesive layer 3 from top to bottom.Methyl methacrylate 45 parts；Hydroxyethyl methylacrylate 25 parts；Stabilizer 3 parts；Initiator 13 parts；Solvent 10 parts.The formula of described hot melt adhesive layer is: ethylene ~ acetate ethylene copolymer 300 parts, Petropols 21 parts；Four (3,5-di-t-butyl-4-hydroxyl) benzenpropanoic acid pentaerythritol ester 0.5 part.Described U.S. stricture of vagina ply of paper thickness is 80 μm；Described acrylate glue adhensive layer thickness is 6 μm；Described hot melt adhesive layer thickness is 10 μm.The U.S. stricture of vagina paper hot pressing adhesive tape of the present invention will not produce cull after peeling off.
Embodiment described above only have expressed embodiments of the present invention; it describes comparatively concrete and detailed; but therefore can not be interpreted as the restriction to the scope of the claims of the present invention; in every case the technical scheme adopting the form of equivalent replacement or equivalent transformation to obtain, all should drop within protection scope of the present invention.
Claims (6)
1. a U.S. stricture of vagina paper hot pressing adhesive tape, it is characterised in that: it is followed successively by U.S. stricture of vagina ply of paper (1), acrylate glue adhensive layer (2), hot melt adhesive layer (3) from top to bottom.
2. a kind of U.S. stricture of vagina paper hot pressing adhesive tape according to claim 1, it is characterised in that described acrylate glue adhensive layer is made up of the component of following parts by weight:
Methyl methacrylate 40 ~ 50 parts；
Hydroxyethyl methylacrylate 20 ~ 30 parts；
Stabilizer 1 ~ 3 part；
Initiator 1 ~ 3 part；
Solvent 10 ~ 25 parts.
3. a kind of U.S. stricture of vagina paper hot pressing adhesive tape according to claim 1, it is characterised in that described hot melt adhesive layer is made up of the component of following parts by weight:
Ethylene ~ acetate ethylene copolymer 180 ~ 300 parts；
Petropols 20 ~ 50 parts；
0.2 ~ 4 part of age resistor.
4. a kind of U.S. stricture of vagina paper hot pressing adhesive tape according to claim 1, it is characterised in that: described U.S. stricture of vagina ply of paper thickness is 80 ~ 120 μm.
5. a kind of U.S. stricture of vagina paper hot pressing adhesive tape according to claim 1, it is characterised in that: described acrylate glue adhensive layer thickness is 5 ~ 8 μm.
6. a kind of U.S. stricture of vagina paper hot pressing adhesive tape according to claim 1, it is characterised in that: described hot melt adhesive layer thickness is 10 ~ 15 μm.