CN105754130A - Plastic surface hardening treatment method - Google Patents
Plastic surface hardening treatment method Download PDFInfo
- Publication number
- CN105754130A CN105754130A CN201610231435.6A CN201610231435A CN105754130A CN 105754130 A CN105754130 A CN 105754130A CN 201610231435 A CN201610231435 A CN 201610231435A CN 105754130 A CN105754130 A CN 105754130A
- Authority
- CN
- China
- Prior art keywords
- dry
- temperature
- 3min
- spray
- surface hardening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention relates to the technical field of plastic products and discloses a plastic surface hardening treatment method.The method includes steps: cleaning a to-be-treated plastic part in deionized water at 50-60 DEG C for 15-20min, spraying and drying; filtering photocuring paint through a 600-1200-mesh screen, performing infrared drying for 20-25min at 60-65 DEG C, and performing cooling and leveling for 1-3min at the room temperature, wherein a spray coating pressure is 32-38kg/cm<2>; subjecting a formed coating to ultraviolet curing for 1-3min at 40-50 DEG C.By the plastic surface hardening treatment method, the problems of high cost and high paint waste in existing plastic surface hardening are solved.
Description
Technical field
The present invention relates to plastic products technology field, the hardening process of especially a kind of frosting.
Background technology
Plastics because of its light weight, will not the excellent performance such as corrosion, shock-resistant, easy processing, and be widely used in producing or in the articles for daily use.But; plastics are compared to metal; its case hardness is relatively low; surface is easily subject to damage, especially as the working of plastics of the electronic product display screen such as mobile phone, camera or lens etc., if its case hardness is relatively low; after long-term use; plastic part surface easily scratches, scratches, and has a strong impact on visual effect and surface optical performance, thus this kind of plastic plate would generally be carried out Surface hardening treatment.Existing frosting cure process mainly has two kinds of technology, one is to soak plastics with chemical agent and dry hardening, another kind is to spray hardened layer at frosting, there is poisonous and harmful substance in former, it is unfavorable for environmental protection, the hardening mode that the latter UV of employing solidifies more, but its problem that to there is paint waste more, relatively costly.
Summary of the invention
It is an object of the invention to provide the hardening process of a kind of frosting, this method can solve the hardening of existing frosting and there is the problem that paint waste is more and cost is high.
In order to solve the problems referred to above, the technical solution used in the present invention is: the hardening process of this frosting comprises the following steps:
A, pending working of plastics is put in the deionized water that water temperature is 50~60 DEG C cleaning 15~20min, after spray, be dried;
B, with 600~1200 order net filtration photocuring paint vehicles, spray pressure 32~38kg/cm2, use infrared drying 20~25min when 60~65 DEG C, under room temperature, cool down levelling 1~3min;
C, with the ultraviolet light polymerization step B film formed, solidification temperature is 40~50 DEG C, and the time is 1~3min.
In the technical scheme of the hardening process of above-mentioned frosting, technical scheme is it may also is that the spray temperature of step B is 40~45 DEG C more specifically, dry and carry out at twice, first time baking temperature 58~62 DEG C, dry 5~8min, at room temperature dries 5~10min, carries out second time dry, baking temperature 62~65 DEG C, dry 3~5min.
Further, the wavelength of the ultraviolet light in step C is 260~272nm.
Owing to have employed technique scheme, the present invention compared with prior art has the advantages that the hardness improving frosting, coating hardness can reach 6H, so that its surface is more resistant to delineation and scraping, having good optics anti-scratch performance, coating surface performance is good, without doing over again, save coating consumption, and without expensive equipment, reduce production cost.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described:
Embodiment 1
The hardening process of the frosting of the present embodiment comprises the following steps: comprise the following steps:
A, pending working of plastics is put in the deionized water that water temperature is 50 DEG C cleaning 20min, spraying subsequently, spray temperature is 40 DEG C, after spray, it is dried again, dry and carry out at twice, first time baking temperature 62 DEG C, dry 5min, at room temperature dry 5min, carry out second time dry, baking temperature 65 DEG C, dry 3min;
B, with 1000 order net filtration photocuring paint vehicles, spray pressure 32kg/cm2, use infrared drying 20min when 60 DEG C, under room temperature, cool down levelling 3min;
C, with the ultraviolet light polymerization step B that wavelength the is 260nm film formed, solidification temperature is 40 DEG C, and the time is 3min.
Embodiment 2
A, pending working of plastics is put in the deionized water that water temperature is 60 DEG C cleaning 15min, spraying subsequently, spray temperature is 45 DEG C, after spray, it is dried again, dry and carry out at twice, first time baking temperature 58 DEG C, dry 8min, at room temperature dry 10min, carry out second time dry, baking temperature 62 DEG C, dry 5min;
B, with 600 order net filtration photocuring paint vehicles, spray pressure 38kg/cm2, use infrared drying 25min when 65 DEG C, under room temperature, cool down levelling 1min;
C, with the ultraviolet light polymerization step B that wavelength the is 272nm film formed, solidification temperature is 50 DEG C, and the time is 1min.
Embodiment 3
A, pending working of plastics is put in the deionized water that water temperature is 55 DEG C cleaning 18min, spraying subsequently, spray temperature is 42 DEG C, after spray, it is dried again, dry and carry out at twice, first time baking temperature 60 DEG C, dry 7min, at room temperature dry 8min, carry out second time dry, baking temperature 63 DEG C, dry 4min;
B, with 1200 order net filtration photocuring paint vehicles, spray pressure 35kg/cm2, use infrared drying 23min when 63 DEG C, under room temperature, cool down levelling 2min;
C, with the ultraviolet light polymerization step B that wavelength the is 265nm film formed, solidification temperature is 45 DEG C, and the time is 2min.
Claims (3)
1. the hardening process of a frosting, it is characterised in that comprise the following steps:
A, pending working of plastics is put in the deionized water that water temperature is 50~60 DEG C cleaning 15~20min, after spray, be dried;
B, with 600~1200 order net filtration photocuring paint vehicles, spray pressure 32~38kg/cm2, use infrared drying 20~25min when 60~65 DEG C, under room temperature, cool down levelling 1~3min;
C, with the ultraviolet light polymerization step B film formed, solidification temperature is 40~50 DEG C, and the time is 1~3min.
2. the hardening process of frosting according to claim 1, it is characterized in that: the spray temperature of step B is 40~45 DEG C, dry and carry out at twice, first time baking temperature 58~62 DEG C, dry 5~8min, at room temperature dries 5~10min, carries out second time dry, baking temperature 62~65 DEG C, dry 3~5min.
3. the hardening process of frosting according to claim 1 and 2, it is characterised in that: the wavelength of the ultraviolet light in step C is 260~272nm.