CN105731960A - Gypsum-based mortar - Google Patents
Gypsum-based mortar Download PDFInfo
- Publication number
- CN105731960A CN105731960A CN201610050701.5A CN201610050701A CN105731960A CN 105731960 A CN105731960 A CN 105731960A CN 201610050701 A CN201610050701 A CN 201610050701A CN 105731960 A CN105731960 A CN 105731960A
- Authority
- CN
- China
- Prior art keywords
- gypsum
- mortar
- cement
- parts
- based mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses gypsum-based mortar which is prepared by mixing the following ingredients in parts by weight: 400-550 parts of gypsum powder, 450-600 aggregates, 3-5 a retarder, 4.5-5.5 parts of latex powder, 4-5 parts of cellulose and 0.5-1.5 parts of a high-molecular polymer. The gypsum-based mortar has the advantages and beneficial effects that use of existing cement is reduced or even replaced on the basis of meeting the physicochemical characteristics of cement mortar; waste of cement and energy required for producing the cement and the damage to the environment in the cement production process are avoided, so that compared with traditional cement mortar, the gypsum-based mortar is more environment-friendly; and meanwhile, according to the technical scheme, the coagulation time is also shortened, the construction efficiency is improved, and the construction period is shortened. The gypsum-based mortar is suitable for bonding of a lightweight ceramic tile, skimming and leveling of exterior wall concrete and bonding of an insulated plastic extrusion plate and a foam plate. Compared with existing cement mortar and gypsum mortar, the gypsum-based mortar has wider applicability.
Description
Technical field
The present invention relates to a kind of mortar, particularly to a kind of gypsum base mortar.
Background technology
Entering decades, science and technology leap is progressive, and the productivity develops rapidly.Cement is as one of construction material requisite in architectural engineering, and it is widely used in preparation building, the industry such as ornament materials.But impact and the pollution of environment be can not be ignored by a large amount of dust of producing in process of production of cement and harmful substance thereof.The raw material of traditional cement mortar relies primarily on cement to be prepared production, and reasoning is extremely wide, and the application remote-effects of traditional cement mortar Cement Market supply and demand amount just, and what a large amount of productions of cement brought with it is bigger disposal of pollutants therewith.
Summary of the invention
In order to solve the problems referred to above, the present invention provides a kind of gypsum base mortar.The technical program is by utilizing Gypsum Fibrosum and aggregate as major ingredient, achieve compared with traditional cement mortar, ensure that there is the physical property that cement mortar has, reduce the use even replaced current cement, and then reduce the environmental disruption brought due to the production of cement at present;Meanwhile, the technical program can be used for the bonding of lightweight ceramic tile, the granted full of exterior wall concrete and levelling, and the bonding of insulating extruded board and cystosepiment, compared with existing cement mortar and gypsum mortar, has the suitability widely.
A kind of gypsum base mortar in the present invention, is mixed by the dispensing of following weight proportion:
In such scheme, described aggregate is quartz sand.
In such scheme, described Gypsum Fibrosum powder is desulfurization gypsum powder.
In such scheme, described latex powder is redispersible latex powder.
In such scheme, described high molecular polymer is polyvinyl alcohol 2488.
In such scheme, described cellulose is hydroxypropyl methyl cellulose, and the viscosity of hydroxypropyl methyl cellulose is 100000~200000mPa.s.In such scheme, also can add stabilizer.
Advantages of the present invention and having the beneficial effects that: the present invention provides a kind of gypsum base mortar, and has following beneficial effect:
1, meeting on the basis of physicochemical property of cement mortar, reduce the use even replaced current cement, avoid the waste of cement and the energy produced needed for cement, and produce in cement process the destruction to environment, therefore more environmentally-friendly compared with traditional cement mortar, meanwhile, the technical program also shortens setting time, improve efficiency of construction, shorten the construction time;
2, the technical program can be used for the bonding of lightweight ceramic tile, the granted full of exterior wall concrete and levelling, and the bonding of insulating extruded board and cystosepiment, compared with existing cement mortar and gypsum mortar, has the suitability widely.
Detailed description of the invention
Example below, is further described the specific embodiment of the present invention.Following example are only for clearly illustrating technical scheme, and can not limit the scope of the invention with this.
Embodiment 1:
Preparation method
After the above-mentioned various raw material of formula accurate measurement, mixing, positive mechanical formula stir and obtain target product, can use after being mixed with water by target product;Wherein, the viscosity of hydroxypropyl methyl cellulose is 150000mPa.s, and it is 60 minutes that this target product obtains its setting time by experiment;Gypsum Fibrosum powder in the technical program is desulfurated plaster, under compared with other Gypsum Fibrosum powders, have higher stability, it is to avoid the situation that other gypsum sets times are too fast.
Embodiment 2:
Preparation method
After the above-mentioned various raw material of formula accurate measurement, mixing, positive mechanical formula stir and obtain target product, can use after being mixed with water by target product;Wherein, the viscosity of hydroxypropyl methyl cellulose is 150000mPa.s, it is 70 minutes that this target product obtains its setting time by experiment, Gypsum Fibrosum powder in the technical program is desulfurated plaster, under compared with other Gypsum Fibrosum powders, there is higher stability, it is to avoid the situation that other too fast gypsum sets times.
Embodiment 3:
Preparation method
After the above-mentioned various raw material of formula accurate measurement, mixing, positive mechanical formula stir and obtain target product, can use after being mixed with water by target product;Wherein, the viscosity of hydroxypropyl methyl cellulose is 150000mPa.s, it is 60 minutes that this target product obtains its setting time by experiment, Gypsum Fibrosum powder in the technical program is desulfurated plaster, under compared with other Gypsum Fibrosum powders, there is higher stability, it is to avoid the situation that other too fast gypsum sets times.
Embodiment 4:
Preparation method
After the above-mentioned various raw material of formula accurate measurement, mixing, positive mechanical formula stir and obtain target product, can use after being mixed with water by target product;Wherein, the viscosity of hydroxypropyl methyl cellulose is 150000mPa.s, it is 60 minutes that this target product obtains its setting time by experiment, Gypsum Fibrosum powder in the technical program is desulfurated plaster, under compared with other Gypsum Fibrosum powders, there is higher stability, it is to avoid the situation that other too fast gypsum sets times.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all within the spirit and principles in the present invention, any amendment of making, equivalent replacement, improvement etc., should be included within protection scope of the present invention.
Claims (6)
1. a gypsum base mortar, it is characterised in that be mixed by the dispensing of following weight proportion:
2. a kind of gypsum base mortar according to claim 1, it is characterised in that described aggregate is quartz sand.
3. a kind of gypsum base mortar according to claim 1, it is characterised in that described Gypsum Fibrosum powder is desulfurization gypsum powder.
4. a kind of gypsum base mortar according to claim 1, it is characterised in that described latex powder is redispersible latex powder.
5. a kind of gypsum base mortar according to claim 1, it is characterised in that described high molecular polymer is polyvinyl alcohol 2488.
6. a kind of gypsum base mortar according to claim 1, it is characterised in that described cellulose is hydroxypropyl methyl cellulose, and the viscosity of hydroxypropyl methyl cellulose is 100000~200000mPa.s.