CN102863163A - Method for preparing acid-proof cement with argil product wastes to serve as main raw material - Google Patents
Method for preparing acid-proof cement with argil product wastes to serve as main raw material Download PDFInfo
- Publication number
- CN102863163A CN102863163A CN2012103814021A CN201210381402A CN102863163A CN 102863163 A CN102863163 A CN 102863163A CN 2012103814021 A CN2012103814021 A CN 2012103814021A CN 201210381402 A CN201210381402 A CN 201210381402A CN 102863163 A CN102863163 A CN 102863163A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- main raw
- argil
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for preparing acid-proof cement with argil product wastes to serve as a main raw material. The method includes weighing 60-65 parts of argil product fragments, 12-15 parts of sodium silicate, 15-17 parts of quick limes and 3-4 parts of calcined gypsums according to weight ratio, mixing, performing mechanical smashing and uniformly stirring the materials. The cement prepared by the method is high in cementing force and intensity, good in acid resistance and heat resistance and capable of being widely used in acid erodent buildings of overwater, underground construction and the like.
Description
Technical field
The invention belongs to building materials field, being specifically related to a kind of is the method that main raw material prepares acid-proof cement with the terra cotta waste.
Background technology
Cement, powdery hydraulicity inorganic coagulation material.Add water and stir rear one-tenth slurry, can in air, harden or better sclerosis in water, and can be together cementing securely materials such as sand, stones.The history of cement can be traced back to lime and the pozzuolanic mixture that the roman uses under construction the earliest, and this mixture is very similar to modern lime pozzolanic cement.With the concrete that its cementing rubble is made, not only intensity is higher after the sclerosis, and can also resist the erosion of fresh water or brackish water.For a long time, it is widely used in the engineerings such as civil construction, water conservancy, national defence as a kind of important gelling material.
Along with the development of technology, the requirement to cement in the reality is also more and more higher, and the water resisting property agent acid corrosion-resistant of cement is had higher requirement, and existing cement can not meet the needs of production.
Summary of the invention
The preparation method who the purpose of this invention is to provide the strong cement of a kind of acid-resistant corrosion.
Technical scheme of the present invention is: a kind of is the method that main raw material prepares acid-proof cement with the terra cotta waste, it is characterized in that, according to weight proportion, take by weighing terra cotta fragment 60-65 part, water glass 12-15 part, unslaked lime 15-17 part and plaster of Paris 3-4 part, machinery shatters after mixing, and stirring gets final product.
Preferably, described terra cotta fragment is 62 parts, and 14 parts of water glass, unslaked lime are 16 parts, and the plaster of Paris is 3 parts.
The present invention compared with prior art has following advantage:
The cement of the present invention preparation, cohesive force is strong, intensity is higher, the buildings of the acid attacks such as that acid resistance, good heat resistance can be widely used in is waterborne, underground works.
Embodiment
A kind of is the method that main raw material prepares acid-proof cement with the terra cotta waste, according to weight proportion, takes by weighing terra cotta fragment 60-65 part, water glass 12-15 part, and unslaked lime 15-17 part and plaster of Paris 3-13 part, machinery shatters after mixing, and stirring gets final product.Preferably, described terra cotta fragment is 62 parts, and 14 parts of water glass, unslaked lime are 16 parts, and the plaster of Paris is 3 parts.
Embodiment 1
Take by weighing 60 parts of terra cotta fragments, 12 parts of water glass, 4 parts of 15 parts of unslaked limes and the plaster of Paris, machinery shatters after mixing, and stirring gets final product.
Embodiment 2
Take by weighing 65 parts of terra cotta fragments, 15 parts of water glass, 3 parts of 17 parts of unslaked limes and the plaster of Paris, machinery shatters after mixing, and stirring gets final product.
Embodiment 3
Take by weighing 62 parts of terra cotta fragments, 14 parts of water glass, 3 parts of 16 parts of unslaked limes and the plaster of Paris, machinery shatters after mixing, and stirring gets final product.
The cement of the present invention preparation, cohesive force is strong, intensity is higher, the buildings of the acid attacks such as that acid resistance, good heat resistance can be widely used in is waterborne, underground works.
Claims (2)
1. one kind is the method that main raw material prepares acid-proof cement with the terra cotta waste, it is characterized in that, according to weight proportion, take by weighing terra cotta fragment 60-65 part, water glass 12-15 part, unslaked lime 15-17 part and plaster of Paris 3-4 part, machinery shatters after mixing, and stirring gets final product.
According to claim 1 a kind of be the method that main raw material prepares acid-proof cement with the terra cotta waste, it is characterized in that: described terra cotta fragment is 62 parts, 14 parts of water glass, unslaked lime are 16 parts, the plaster of Paris is 3 parts.