CN105729313A - Stainless steel rubberizing and coloring treatment method - Google Patents
Stainless steel rubberizing and coloring treatment method Download PDFInfo
- Publication number
- CN105729313A CN105729313A CN201610102743.9A CN201610102743A CN105729313A CN 105729313 A CN105729313 A CN 105729313A CN 201610102743 A CN201610102743 A CN 201610102743A CN 105729313 A CN105729313 A CN 105729313A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- adhesive tape
- steel substrate
- pasted
- colouring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a stainless steel rubberizing and coloring treatment method which comprises the following steps: A, pasting a layer of adhesive tape on the surface of a stainless steel substrate; B, graving a blank area on the layer of adhesive tape pasted on the stainless steel substrate; C, carrying out sand blasting treatment on the surface of the stainless steel substrate pasted with the adhesive tape; and D, carrying out oxidation treatment on the surface of the stainless steel substrate subjected to sand blasting treatment, and carrying out coloring treatment on an oxidation film formed by oxidation treatment, wherein the blank area is not pasted with the adhesive tape, step A and step B are performed for a plurality of times alternatively, and the blank areas of the plurality of adhesive tapes are increased layer by layer according to the pasting time sequence. According to the invention, different areas are distinguished by using a manner of pasting adhesive tapes, no or fewer layers of adhesive tapes are pasted on areas requiring great roughness degree, and in same time, the adhesive tape is subjected to sand blasting removal to expose the stainless steel surface and then is subjected to sand blasting polishing to form time delay, and the sand blasting time of each area can be controlled by the layer number of the adhesive tapes, so as to form area styles with different roughness.
Description
Technical field
The present invention relates to a kind of rustless steel processing method, particularly relate to a kind of rustless steel rubberizing colouring processing method.
Background technology
Existing stainless steel surfaces colouring processes technique all once can only form unified colouring style for one whole rustless steel, and the depth degree of colouring many times uses the degree of roughness into stainless steel surfaces different in coloring process, and the surface oxidation degree that causes due to degree of roughness difference is different, for needing to form different sandblasting effects whole stainless steel surfaces zones of different and then form different Colors, that is: the region not sandblasting having, the degree of roughness of some surface sand-blastings is different, to form different region sandblasting styles at same stainless steel surfaces, and then form the coloured differently depth.Particularly on the same face, between zones of different, the style of sandblasting gradual change is difficult to completing in a sandblasting procedures, namely the fade effect of dyeing is difficult to one step completed.
Summary of the invention
Instant invention overcomes the deficiencies in the prior art, it is provided that a kind of rustless steel rubberizing colouring processing method.
For reaching above-mentioned purpose, the technical solution used in the present invention is: a kind of rustless steel rubberizing colouring processing method, it is characterised in that comprise the following steps:
A, one layer tape is pasted on stainless steel substrate surface;
B, the one layer tape being attached on stainless steel substrate is depicted it is left white area;
C, the stainless steel substrate surface posting adhesive tape is carried out blasting treatment;
D, the stainless steel substrate surface after blasting treatment being carried out oxidation processes, the oxide-film then oxidation processes formed carries out colouring process;
The described area that is left white is that the area not having adhesive tape of paste, step A and step B hocket several times, and number of times is equal with the adhesive tape number of plies, and the area that is left white of some layers of adhesive tape successively increases according to pasting time sequencing.
In a preferred embodiment of the present invention, described adhesive tape is the tinfoil paper with mucigel or the aluminium foil with mucigel.
In a preferred embodiment of the present invention, what the described adhesive tape first pasted depicted be left white area will not by after the described adhesive tape pasted shelter from.
In a preferred embodiment of the present invention, described stainless steel substrate surface is planar structure or globoidal structure.
In a preferred embodiment of the present invention, in step D, colouring processes: by concentration 5%-10% sulfuric acid solution, stainless steel substrate surface is carried out activation processing and obtains oxide-film, is then immersed by stainless steel substrate in coloring liquid and soaks.
In a preferred embodiment of the present invention, described sandblasting adopts the ceramic sand of 30-60 order, zircon sand or corundum.
The invention solves the defect existed in background technology, the present invention possesses following beneficial effect:
1, the mode taped is used zones of different to be made a distinction, the regional choice that degree of roughness is bigger is needed not paste or paste which floor adhesive tape less, regional choice which floor adhesive tape of many patches needing degree of roughness less, so within the identical time, the stainless steel surfaces that adhesive tape exposes after being grit blasted removal, then can being grit blasted polishing thus forming time dilation, just can be controlled the time that is grit blasted in each region by the adhesive tape number of plies, form different rough region style.
2, by producing different rough region style, so just can form corresponding oxidation effectiveness, and then form corresponding upper chromatic effect.
What the described adhesive tape 3, first pasted depicted be left white area will not by after the described adhesive tape pasted shelter from, so just reasonably can quickly distribute sand blasted area, the simultaneously open-and-shut length knowing each region blast time.
4, the metal forming such as tinfoil paper or aluminium foil to a certain extent, can resist the polishing from sandblasting within a certain period of time, well plays the effect of time delay sandblasting.
Certain adhesive tape can also adopt common adhesive tape.Colouring also needs to be thermally dried after terminating, in order to solidify color.
Detailed description of the invention
Presently in connection with embodiment, the present invention is further detailed explanation.
A kind of rustless steel rubberizing colouring processing method, comprises the following steps:
A, one layer tape is pasted on stainless steel substrate surface;
B, the one layer tape being attached on stainless steel substrate is depicted it is left white area;
C, the stainless steel substrate surface posting adhesive tape is carried out blasting treatment;
D, the stainless steel substrate surface after blasting treatment being carried out oxidation processes, the oxide-film then oxidation processes formed carries out colouring process;
Being left white area is that the area not having adhesive tape of paste, step A and step B hocket several times, and number of times is equal with the adhesive tape number of plies, and the area that is left white of some layers of adhesive tape successively increases according to pasting time sequencing.
Adhesive tape is the tinfoil paper with mucigel or the aluminium foil with mucigel.
What the described adhesive tape first pasted depicted be left white area will not by after the described adhesive tape pasted shelter from.
Stainless steel substrate surface is planar structure or globoidal structure.
In step D, colouring processes: by concentration 5%-10% sulfuric acid solution, stainless steel substrate surface is carried out activation processing and obtains oxide-film, is then immersed by stainless steel substrate in coloring liquid and soaks.
Sandblasting adopts the ceramic sand of 30-60 order, zircon sand or corundum.
The mode taped is used zones of different to be made a distinction, the regional choice that degree of roughness is bigger is needed not paste or paste which floor adhesive tape less, regional choice which floor adhesive tape of many patches needing degree of roughness less, so within the identical time, the stainless steel surfaces that adhesive tape exposes after being grit blasted removal, then can being grit blasted polishing thus forming time dilation, just can be controlled the time that is grit blasted in each region by the adhesive tape number of plies, form different rough region style.
By producing different rough region style, so just can form corresponding oxidation effectiveness, and then form corresponding upper chromatic effect.
What the described adhesive tape first pasted depicted be left white area will not by after the described adhesive tape pasted shelter from, so just reasonably can quickly distribute sand blasted area, the simultaneously open-and-shut length knowing each region blast time.
The metal forming such as tinfoil paper or aluminium foil to a certain extent, can resist the polishing from sandblasting within a certain period of time, well plays the effect of time delay sandblasting.
Certain adhesive tape can also adopt common adhesive tape.Colouring also needs to be thermally dried after terminating, in order to solidify color.
Above according to the desirable embodiment of the present invention for enlightening, by above-mentioned description, related personnel in the scope not necessarily departing from this invention technological thought, can carry out various change and amendment completely.The technical scope of this invention is not limited to the content in description, it is necessary to determine technical scope according to right.
Claims (6)
1. a rustless steel rubberizing colouring processing method, it is characterised in that comprise the following steps:
A, one layer tape is pasted on stainless steel substrate surface;
B, the one layer tape being attached on stainless steel substrate is depicted it is left white area;
C, the stainless steel substrate surface posting adhesive tape is carried out blasting treatment;
D, the stainless steel substrate surface after blasting treatment being carried out oxidation processes, the oxide-film then oxidation processes formed carries out colouring process;
The described area that is left white is that the area not having adhesive tape of paste, step A and step B hocket several times, and number of times is equal with the adhesive tape number of plies, and the area that is left white of some layers of adhesive tape successively increases according to pasting time sequencing.
2. rustless steel rubberizing according to claim 1 colouring processing method, it is characterised in that: described adhesive tape is the tinfoil paper with mucigel or the aluminium foil with mucigel.
3. rustless steel rubberizing according to claim 1 colouring processing method, it is characterised in that: what the described adhesive tape first pasted depicted be left white area will not by after the described adhesive tape pasted shelter from.
4. rustless steel rubberizing according to claim 1 colouring processing method, it is characterised in that: described stainless steel substrate surface is planar structure or globoidal structure.
5. rustless steel rubberizing according to claim 1 colouring processing method, it is characterized in that: in step D, colouring processes: by concentration 5%-10% sulfuric acid solution, stainless steel substrate surface is carried out activation processing and obtains oxide-film, is then immersed by stainless steel substrate in coloring liquid and soaks.
6. rustless steel rubberizing according to claim 1 colouring processing method, it is characterised in that: described sandblasting adopts the ceramic sand of 30-60 order, zircon sand or corundum.