CN105719725A - 发光型太阳能正面电极浆料 - Google Patents
发光型太阳能正面电极浆料 Download PDFInfo
- Publication number
- CN105719725A CN105719725A CN201610042756.1A CN201610042756A CN105719725A CN 105719725 A CN105719725 A CN 105719725A CN 201610042756 A CN201610042756 A CN 201610042756A CN 105719725 A CN105719725 A CN 105719725A
- Authority
- CN
- China
- Prior art keywords
- electrode slurry
- light emitting
- front electrode
- solar energy
- type solar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
发光型太阳能正面电极浆料，包括银粉，剩余组分为有机粘接剂1?3%、无机粘接剂3?8%、溶剂3?5%及发光体；所述发光体含量为0.5?2%，为CaMgSi2O6:Eu、(Ba,Eu)MgAl10O17、(Zn,Mn)2SiO4、(Y,Gd,Tb)BO3、Ba(Mg,Mn)Al10O17、(Y,Gd,Eu)BO3、(Y,Eu)(PV)O4中的一种或几种，所述发光体为粒径在1?1.5微米的粉体；所述百分比均为重量百分比。本发明在正面电极银浆料中增加了发光体组分，这些发光体组分可以吸收太阳能辐射并激发出光，并被半导体材料所就近吸收，二次发光显著提高了太阳能电池的光电转化效率。
Description
技术领域
本发明属于电子领域，涉及太阳能电池制造原料，具体涉及一种发光型太阳能正面电极浆料。
背景技术
太阳能电池是可以有效吸收太阳能，并将其转化成电能的半导体部件。用半导体硅﹑硒等材料将太阳的光能变成电能的器件。具有可靠性高﹐寿命长﹐转换效率高等优点﹐可做人造卫星﹑航标灯﹑晶体管收音机等的电源。太阳能电池中的电极采用以银粉为主体的银浆料，正面电极印刷在太阳能电池正面，用于直接收集阳光照射半导体材料所转化出的电流，正面电极基本要求是印刷性能好，高宽比高，同时能与硅晶片形成良好的欧姆接触，降低接触电阻，从而使电池片具有较高的光电转换效率。
太阳能电池的光电转化效率是衡量太阳能电池的基本指标，光照辐射在半导体材料表面产生光生电流，现有技术中，围绕如何提高光电转化效率的手段主要在提高半导体材料性能本身，研发成本较高。
发明内容
为克服现有技术存在的技术缺陷，提高太阳能电池发电效率，本发明公开了一种发光型太阳能正面电极浆料。
本发明所述发光型太阳能正面电极浆料，包括银粉，剩余组分为有机粘接剂1-3%、无机粘接剂3-8%、溶剂3-5%及发光体；所述发光体含量为0.5-2%，为CaMgSi2O6:Eu、(Ba,Eu)MgAl10O17、(Zn,Mn)2SiO4、(Y,Gd,Tb)BO3Ba(Mg,Mn)Al10O17、(Y,Gd,Eu)BO3、(Y,Eu)(PV)O4中的一种或几种，所述发光体为粒径在1-1.5微米的粉体；所述百分比均为重量百分比。
优选的，所述有机粘结剂为环氧树脂、丙烯配树脂、聚酰亚胺树脂、聚氨酯树脂当中的一种。
优选的，所述溶剂为柠檬烯、十一酸乙酯、己二酸二甲酯、戊二酸二甲酯中的一种或几种。
优选的，所述无机粘结剂由以下组分组成：Bi2S3为20-40%、Pb3O4为30-40%、TeSO4为10-20%、GeTe为0-5%；无机粘结剂各个组分为粒径1-2微米的粉体，所述各个百分比均为重量百分比。
采用本发明所述的发光型太阳能正面电极浆料，在正面电极银浆料中增加了发光体组分，这些发光体组分可以吸收太阳能辐射并激发出光，并被半导体材料所就近吸收，二次发光显著提高了太阳能电池的光电转化效率，且该改进手段成本相对半导体材料的改进更加低廉，并且不影响半导体材料对光电转化效率的提高，使得生产出的太阳能电池效率高于同类产品。
具体实施方式
下面对本发明的具体实施方式作进一步的详细说明。
发光型太阳能正面电极浆料，包括银粉，剩余组分为有机粘接剂1-3%、无机粘接剂3-8%、溶剂3-5%及发光体；所述发光体含量为0.5-2%，为CaMgSi2O6:Eu、(Ba,Eu)MgAl10O17、(Zn,Mn)2SiO4、(Y,Gd,Tb)BO3Ba(Mg,Mn)Al10O17、(Y,Gd,Eu)BO3、(Y,Eu)(PV)O4中的一种或几种，所述发光体为粒径在1-1.5微米的粉体；所述百分比均为重量百分比。
银粉通常为直径1.5-2.5微米的微型银球，因此发光体粒径也设置为与银粉大小相仿的粉体，粒径在1-1.5微米。在CaMgSi2O6:Eu、(Ba,Eu)MgAl10O17、(Zn,Mn)2SiO4、(Y,Gd,Tb)BO3Ba(Mg,Mn)Al10O17、(Y,Gd,Eu)BO3、(Y,Eu)(PV)O4中选择任意一种或多种作为发光体添加至银浆料中。发光型太阳能正面电极浆料，在正面电极银浆料中增加了发光体组分，这些发光体组分可以吸收太阳能辐射并激发出光，并被半导体材料所就近吸收，二次发光显著提高了太阳能电池的光电转化效率。
有机粘结剂可以选择为环氧树脂、丙烯配树脂、聚酰亚胺树脂、聚氨酯树脂当中的一种，利于电极在烘干或固化后成膜。
溶剂可以选择为柠檬烯、十一酸乙酯、己二酸二甲酯、戊二酸二甲酯中的一种或几种，溶剂将有机粘结剂溶解后以提高银浆的稠度。
银浆中无机粘结剂的作用是在电极制造的高温烧结过程中固化成形为电极形状，优选设置为以下组分：Bi2S3为20-40%、Pb3O4为30-40%、TeSO4为10-20%、GeTe为0-5%；无机粘结剂各个组分为粒径1-2微米的粉体，所述各个百分比均为重量百分比。采用以上成分的无机粘结剂在高温烧结后比现有技术更好好烧穿氮化硅层，让浆料中的导电主体银与作为半导体激发材料的硅更好的形成硅银合金，提高二者之间的电导，减少损耗；同时该无机粘结剂中的Bi2S3、GeTe等组分为半导体材料，在发光体的二次光电转化作用中光照后还可以产生二次光源，照射太阳能电池硅片，进一步提高光电转化效率。
具体实施例1
发光型太阳能正面电极浆料，包括银粉，剩余组分为有机粘接剂3%、无机粘接剂3%、溶剂5%及发光体2%；发光体为CaMgSi2O6:Eu。
其中有机粘结剂为环氧树脂，环氧树脂、丙烯配树脂、聚酰亚胺树脂、聚氨酯树脂。溶剂为柠檬烯、十一酸乙酯、己二酸二甲酯、戊二酸二甲酯。
具体实施例2
发光型太阳能正面电极浆料，包括银粉，剩余组分为有机粘接剂1.5%、无机粘接剂8%、溶剂4%及发光体1%；发光体为CaMgSi2O6:Eu、(Ba,Eu)MgAl10O17、(Zn,Mn)2SiO4混合物，各占重量的1/3。
其中有机粘结剂为聚酰亚胺树脂、聚氨酯树脂。溶剂为己二酸二甲酯。
具体实施例3
发光型太阳能正面电极浆料，包括银粉，剩余组分为有机粘接剂1%、无机粘接剂4%、溶剂3%及发光体0.5%；发光体为(Y,Gd,Eu)BO3、(Y,Eu)(PV)O4混合物（PV为磷矾分子团），各占重量的1/2。
其中有机粘结剂为聚酰亚胺树脂、聚氨酯树脂。溶剂为己二酸二甲酯。
无机粘结剂为以下组分：Bi2S3为20-40%、Pb3O4为30-40%、TeSO4为10-20%、GeTe为0-5%。
前文所述的为本发明的各个优选实施例，各个优选实施例中的优选实施方式如果不是明显自相矛盾或以某一优选实施方式为前提，各个优选实施方式都可以任意叠加组合使用，所述实施例以及实施例中的具体参数仅是为了清楚表述发明人的发明验证过程，并非用以限制本发明的专利保护范围，本发明的专利保护范围仍然以其权利要求书为准，凡是运用本发明的说明书内容所作的等同结构变化，同理均应包含在本发明的保护范围内。
Claims (4)
1.发光型太阳能正面电极浆料，包括银粉，其特征在于，剩余组分为有机粘接剂1-3%、无机粘接剂3-8%、溶剂3-5%及发光体；所述发光体含量为0.5-2%，为CaMgSi2O6:Eu、(Ba,Eu)MgAl10O17、(Zn,Mn)2SiO4、(Y,Gd,Tb)BO3Ba(Mg,Mn)Al10O17、(Y,Gd,Eu)BO3、(Y,Eu)(PV)O4中的一种或几种，所述发光体为粒径在1-1.5微米的粉体；所述百分比均为重量百分比。
2.如权利要求1所述的发光型太阳能正面电极浆料，其特征在于，所述有机粘结剂为环氧树脂、丙烯配树脂、聚酰亚胺树脂、聚氨酯树脂当中的一种。
3.如权利要求1所述的发光型太阳能正面电极浆料，其特征在于，所述溶剂为柠檬烯、十一酸乙酯、己二酸二甲酯、戊二酸二甲酯中的一种或几种。
4.如权利要求1所述的发光型太阳能正面电极浆料，其特征在于，所述无机粘结剂由以下组分组成：Bi2S3为20-40%、Pb3O4为30-40%、TeSO4为10-20%、GeTe为0-5%；无机粘结剂各个组分为粒径1-2微米的粉体，所述各个百分比均为重量百分比。