CN105713380A - 热固性酚醛树脂包覆长玻璃纤维增强聚酰胺复合材料制备方法 - Google Patents
热固性酚醛树脂包覆长玻璃纤维增强聚酰胺复合材料制备方法 Download PDFInfo
- Publication number
- CN105713380A CN105713380A CN201410731020.6A CN201410731020A CN105713380A CN 105713380 A CN105713380 A CN 105713380A CN 201410731020 A CN201410731020 A CN 201410731020A CN 105713380 A CN105713380 A CN 105713380A
- Authority
- CN
- China
- Prior art keywords
- phenolic resin
- long glass
- composite material
- thermosetting phenolic
- glass fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供热固性酚醛树脂包覆长玻璃纤维增强聚酰胺复合材料制备方法，首先将长玻璃纤维进行烧蚀以去除表面残留有机物，再采用KH550硅烷偶联剂对其进行表面改性；然后采用酚醛树脂-乙醇溶液均匀喷涂于玻璃纤维表面，经晾晒、烘干，得到热固性酚醛树脂包覆长玻璃纤维；最后采用单螺杆挤出机挤出造粒，制得长玻璃纤维增强聚酰胺复合材料。本发明方法工艺简单，复合材料中玻璃纤维和聚酰胺之间的界面结合力强，力学性能良好。
Description
技术领域
本发明属于纤维增强复合材料领域，涉及热固性酚醛树脂包覆长玻璃纤维增强聚酰胺复合材料制备方法。
背景技术
玻璃纤维增强复合材料是以聚合物为基体以玻璃纤维为增强材料而制成的高性能复合材料，其综合了聚合物和玻璃纤维的性能。玻璃纤维可用于增强聚酰胺、ABS、PET、PP、PE等多种塑料，玻璃纤维增强塑料具有拉伸性能好、比强度高、耐腐蚀、隔热、成型收缩率小等优点。玻璃纤维增强复合材料的关键是如何提高玻璃纤维与聚合物基体的界面结合力。
发明内容
本发明的目的在于提供热固性酚醛树脂包覆长玻璃纤维增强聚酰胺复合材料制备方法，该方法工艺简单，制备的玻璃纤维增强聚酰胺复合材料的力学性能优良。
为实现上述目的，本发明采用的技术方案为：
热固性酚醛树脂包覆长玻璃纤维增强聚酰胺复合材料制备方法，其特征在于，包括以下步骤：
（1）将长玻璃纤维在500℃下烧蚀1h，以去除表面残留有机物，然后将10%浓度的KH550硅烷偶联剂水溶液喷涂于长玻璃纤维表面上进行表面改性，烘干；
（2）配制10～30%浓度的酚醛树脂-乙醇溶液，将其均匀喷涂于经过步骤（1）得到的长玻璃纤维表面，酚醛树脂与长玻璃纤维的质量比为0.1～0.5：1，自然条件下晾晒2h后移入真空烘箱中于160℃烘干1h，得到热固性酚醛树脂包覆长玻璃纤维；
（3）将聚酰胺原料预先干燥，采用单螺杆挤出机挤出造粒，在通过挤拉包覆口模时加入步骤得到的热固性酚醛树脂包覆长玻璃纤维，挤出料经过水冷和切粒，制得热固性酚醛树脂包覆长玻璃纤维增强聚酰胺复合材料。
本发明所具有的有益效果：
本发明提供了热固性酚醛树脂包覆长玻璃纤维增强聚酰胺复合材料制备方法，该制备方法工艺简单，便于推广；该制备方法是采用热固性酚醛树脂对长玻璃纤维预先进行包覆，增强了玻璃纤维和聚酰胺的界面粘结，提高了两者之间的界面结合力，复合材料的力学性能良好。
具体实施方式
下面结合具体实施例对本发明作进一步说明，但不限定本发明的保护范围。
实施例1
热固性酚醛树脂包覆长玻璃纤维增强聚酰胺复合材料制备方法，包括以下步骤：
（1）将长玻璃纤维在500℃下烧蚀1h，以去除表面残留有机物，然后将10%浓度的KH550硅烷偶联剂水溶液喷涂于长玻璃纤维表面上进行表面改性，烘干；
（2）配制30%浓度的酚醛树脂-乙醇溶液，将其均匀喷涂于经过步骤（1）得到的长玻璃纤维表面，酚醛树脂与长玻璃纤维的质量比为0.5：1，自然条件下晾晒2h后移入真空烘箱中于160℃烘干1h，得到热固性酚醛树脂包覆长玻璃纤维；
（3）将聚酰胺原料预先干燥，采用单螺杆挤出机挤出造粒，在通过挤拉包覆口模时加入步骤得到的热固性酚醛树脂包覆长玻璃纤维，挤出料经过水冷和切粒，制得热固性酚醛树脂包覆长玻璃纤维增强聚酰胺复合材料。
实施例2
热固性酚醛树脂包覆长玻璃纤维增强聚酰胺复合材料制备方法，包括以下步骤：
（1）将长玻璃纤维在500℃下烧蚀1h，以去除表面残留有机物，然后将10%浓度的KH550硅烷偶联剂水溶液喷涂于长玻璃纤维表面上进行表面改性，烘干；
（2）配制10%浓度的酚醛树脂-乙醇溶液，将其均匀喷涂于经过步骤（1）得到的长玻璃纤维表面，酚醛树脂与长玻璃纤维的质量比为0.2：1，自然条件下晾晒2h后移入真空烘箱中于160℃烘干1h，得到热固性酚醛树脂包覆长玻璃纤维；
（3）将聚酰胺原料预先干燥，采用单螺杆挤出机挤出造粒，在通过挤拉包覆口模时加入步骤得到的热固性酚醛树脂包覆长玻璃纤维，挤出料经过水冷和切粒，制得热固性酚醛树脂包覆长玻璃纤维增强聚酰胺复合材料。
以上所述，仅是本发明的较佳实施例而已，并非对本发明的技术方案作任何形式上的限制。凡是依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明的技术方案的范围内。
Claims (1)
1.热固性酚醛树脂包覆长玻璃纤维增强聚酰胺复合材料制备方法，其特征在于，包括以下步骤：
（1）将长玻璃纤维在500℃下烧蚀1h，以去除表面残留有机物，然后将10%浓度的KH550硅烷偶联剂水溶液喷涂于长玻璃纤维表面上进行表面改性，烘干；
（2）配制10～30%浓度的酚醛树脂-乙醇溶液，将其均匀喷涂于经过步骤（1）得到的长玻璃纤维表面，酚醛树脂与长玻璃纤维的质量比为0.1～0.5:1，自然条件下晾晒2h后移入真空烘箱中于160℃烘干1h，得到热固性酚醛树脂包覆长玻璃纤维；
（3）将聚酰胺原料预先干燥，采用单螺杆挤出机挤出造粒，在通过挤拉包覆口模时加入步骤得到的热固性酚醛树脂包覆长玻璃纤维，挤出料经过水冷和切粒，制得热固性酚醛树脂包覆长玻璃纤维增强聚酰胺复合材料。