CN105712677A - High-end light wall using diatomite as base material and production method of high-end light wall - Google Patents
High-end light wall using diatomite as base material and production method of high-end light wall Download PDFInfo
- Publication number
- CN105712677A CN105712677A CN201510061117.5A CN201510061117A CN105712677A CN 105712677 A CN105712677 A CN 105712677A CN 201510061117 A CN201510061117 A CN 201510061117A CN 105712677 A CN105712677 A CN 105712677A
- Authority
- CN
- China
- Prior art keywords
- light wall
- base material
- kieselguhr
- end light
- diatomite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to novel high-end building materials and particularly relates to a high-end light wall using diatomite as base material and a production method of the high-end light wall. The high-end light wall using the diatomite as the base material comprises, by weight percentage, 40-70% of diatomite, 25-40% of Portland cement, 2-5% of quick lime, 2-10% of montmorillonite, 0.5-1% of glass fibers and 1-3% of additives. The high-end light wall using the diatomite as the base material has the advantages that the light wall is novel high-end environment-friendly light building material, the natural properties of the diatomite are brought into full play, an automatic moisture absorbing and discharging function is provided, indoor air humidity can be adjusted, harmful gases such as formaldehyde and smoke can be absorbed, indoor air quality can be improved, and the wall is light, fireproof, soundproof, and convenient in construction.
Description
Technical field
The invention belongs to Novel high-end construction material, particularly a kind of be base material with kieselguhr high-end Light Wall and preparation method thereof.
Background technology
The construction material that traditional lightweight wall board is is base material with silicate, its main component is by cement, flyash, slag, and additive forms, quality weight, tight.With the main component of Light Wall that kieselguhr is base material it is: kieselguhr content accounts for 40-70%, and all the other are adjuvant.
Kieselguhr is that diatom developed, through 1 years, the inorganic mineral formed, and main chemical compositions is silicon dioxide, and its multi-cellular structure gives the useful performance of the multiple excellence of kieselguhr, and proportion is little, has good environmental-protecting performance.Therefore prepare high-end Light Wall with kieselguhr for base material and there is the features such as light weight, automatic moisture adsorption and releasing, sound insulation, insulation, absorption harmful gas.It is the New Building Materials of a kind of high-end green building environmental protection.
Summary of the invention
The present invention it is important that in Light Wall formula vast scale add kieselguhr, kieselguhr content accounts for 40-70%, its adjuvant use environmental and ecological raw material.
It is an object of the invention to, it is provided that there is excellent environmental-protecting performance, a kind of be base material with kieselguhr high-end environmental protection Light Wall and preparation method thereof.
The purpose of the present invention is achieved through the following technical solutions: a kind of be base material with kieselguhr high-end Light Wall and preparation method thereof, the high-end Light Wall being base material with kieselguhr, its material prescription is by weight percentage: kieselguhr 40-70%, portland cement 25-40%, quick lime 2-5%, montmorillonite 2-10%, glass fibre 0.5-1%, additive 1-3% forms；
Described additive is: higher fatty acids is received, sodium sulfate, 801 Petropols；
Its preparation method is: according to above-mentioned prescription, and the water mixing of the weight ratios such as use is made into liquid concrete slip, slip casting method injection molding, vibration material base, heating 45 degrees Celsius in mould, the precuring demoulding in 18 hours, indoor 35-40 degree Celsius of maintenance of curing room 30 days, obtains manufactured goods.
The Light Wall of the present invention is a kind of Novel high-end construction material, due to kieselguhr for base material, give full play to kieselguhr natural attribute, there is automatic moisture adsorption and releasing function, regulate indoor air humidity, the harmful gas such as formaldehyde adsorption, flue gas, improve IAQ (indoor air quality), lightweight, fire prevention, sound insulation, easy construction, be a kind of high-end environmental protection light building material.
Detailed description of the invention
It is as follows that this experiment has carried out 3 embodiments
Embodiment 1, a kind of be base material with kieselguhr high-end Light Wall and preparation method thereof, its material prescription is:
| Component | Formula (weight portion) |
| Kieselguhr | 45 |
| Portland cement | 40 |
| Quick lime | 5 |
| Montmorillonite | 8 |
| Glass fibre | 0.5 |
| Higher fatty acids is received | 0.5 |
| Sodium sulfate | 0.5 |
| 801 Petropols | 0.5 |
| Add up to | 100 |
A kind of be base material with kieselguhr high-end Light Wall and preparation method thereof, above prescription is prepared as follows:
1, kieselguhr, more than porosity 1um, particle diameter 200-400 order.
Squeeze into after kieselguhr after milled and other adjuvants are measured by formula siccative in sealing siccative blender, stir 15 minutes, add the water of weight ratio 1: 1.5, stirring slurry 20 minutes, inject mould.
2 inject mould after vibration increases degree of compaction in 10 minutes, and mould heats 45 degrees Celsius, precuring 18 hours, the demoulding.
Light Wall after 3 demouldings, is pushed into indoor 35-45 degree Celsius of maintenance of curing room 30 days.
4 finished product packing warehouse-ins.
Embodiment 2, a kind of be base material with kieselguhr high-end Light Wall and preparation method thereof, its material prescription is:
| Component | Formula (weight portion) |
| Kieselguhr | 55 |
| Portland cement | 35 |
| Quick lime | 3 |
| Montmorillonite | 5 |
| Glass fibre | 0.5 |
| Higher fatty acids is received | 0.5 |
| Sodium sulfate | 0.5 |
| 801 Petropols | 0.5 |
| Add up to | 100 |
A kind of be base material with kieselguhr high-end Light Wall and preparation method thereof, above prescription is prepared as follows:
1, kieselguhr, more than porosity 1um, particle diameter 200-400 order.
Squeeze into after kieselguhr after milled and other adjuvants are measured by formula siccative in sealing siccative blender, stir 15 minutes, add the water of weight ratio 1: 1.5, stirring slurry 20 minutes, inject mould.
2 inject mould after vibration increases degree of compaction in 10 minutes, and mould heats 45 degrees Celsius, precuring 18 hours, the demoulding.
Light Wall after 3 demouldings, is pushed into indoor 35-45 degree Celsius of maintenance of curing room 30 days.
4 finished product packing warehouse-ins.
Embodiment 3, a kind of be base material with kieselguhr high-end Light Wall and preparation method thereof, its material prescription is:
| Component | Formula (weight portion) |
| Kieselguhr | 60 |
| Portland cement | 34 |
| Quick lime | 2 |
| Montmorillonite | 2 |
| Glass fibre | 0.5 |
| Higher fatty acids is received | 0.5 |
| Sodium sulfate | 0.5 |
| 801 Petropols | 0.5 |
| Add up to | 100 |
A kind of be base material with kieselguhr high-end Light Wall and preparation method thereof, above prescription is prepared as follows:
1, kieselguhr, more than porosity 1um, particle diameter 200-400 order.
Squeeze into after kieselguhr after milled and other adjuvants are measured by formula siccative in sealing siccative blender, stir 15 minutes, add the water of weight ratio 1: 1.5, stirring slurry 20 minutes, inject mould.
2 inject mould after vibration increases degree of compaction in 10 minutes, and mould heats 45 degrees Celsius, precuring 18 hours, the demoulding.
Light Wall after 3 demouldings, is pushed into indoor 35-45 degree Celsius of maintenance of curing room 30 days.
4 finished product packing warehouse-ins.
Claims (3)
1. high-end Light Wall that a kind is base material with kieselguhr and preparation method thereof, the high-end Light Wall being base material with kieselguhr, it is characterized in that: its material prescription by weight percentage: kieselguhr 40-70%, portland cement 25-40%, quick lime 2-5%, montmorillonite 2-10%, glass fibre 0.5-1%, additive 1-3% forms.
2. according to claim 1 a kind of be base material with kieselguhr high-end Light Wall and preparation method thereof, it is characterised in that: described additive be higher fatty acids receive, sodium sulfate, 801 Petropols.
3. according to claim 1 a kind of be base material with kieselguhr high-end Light Wall and preparation method thereof, it is characterized in that: its preparation method is according to above-mentioned prescription, with etc. weight ratio water mixing be made into liquid concrete slip, slip casting method injection molding, vibration material base, heating 45 degrees Celsius in mould, the precuring demoulding in 18 hours, indoor 35-40 degree Celsius of maintenance of curing room 30 days, obtain manufactured goods.