CN105712337A - Stripping solution for graphene stripping - Google Patents
Stripping solution for graphene stripping Download PDFInfo
- Publication number
- CN105712337A CN105712337A CN201410711139.7A CN201410711139A CN105712337A CN 105712337 A CN105712337 A CN 105712337A CN 201410711139 A CN201410711139 A CN 201410711139A CN 105712337 A CN105712337 A CN 105712337A
- Authority
- CN
- China
- Prior art keywords
- graphene
- parts
- stripping
- stripper
- peeled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a stripping solution for graphene stripping. The stripping solution comprises the following components by weight: 100 parts of an alcohol solvent, 50-80 parts of polyacrylic ester or polyacrylic ester derivative, 0.5-5 parts of rubber powder, and 0.5-5 parts of a water soluble salt. According to the invention, polyacrylic ester or polyacrylic ester derivative with glue adhesiveness is added into the stripping solution, the combined solution can be used in coordination with grinding or stirring so as to reduce the requirement for grinding or stirring speed, and stripping of graphene can be realized without ultra high-speed shearing to a flake graphite layer. Through cooperation with rubber powder with high friction coefficient, a stripping force generated to graphite can be increased. In addition, the water-soluble salt added into the system can improve the conductivity of the system, superimposition of stripped graphene together again due to static electricity can be avoided, especially static electricity on the surface of the rubber powder can be eliminated, so that the stripped graphene can maintain a disperse state.
Description
Technical field
The present invention relates to Graphene production technical field, being specifically related to a kind of for graphite being peeled off the stripper for Graphene.
Background technology
Graphene is a kind of two-dimensional material with good flexibility, electrical property.You need to add is that, stricti jurise is said, Graphene is the lamellar of a kind of monolayer；But due to the preparation difficulty of single-layer graphene, generally also the form the few-layer graphene alkene with similar performance is also ranged in the category of Graphene.
At present, the method that prepared by Graphene mainly has: chemically grown method and physics stripping method.Low compared to efficiency, be not suitable for the chemically grown method of industrialized mass production; it is raw material that physics stripping method mainly adopts cheap graphite; make graphite layers peeling-off by graphite crystal is applied mechanical force; break the Van der Waals force of graphite layers; forming monolithic graphite alkene or form the few-layer graphene alkene, this physical separation methods has more industrial prospect and applicable large-scale production.
In Graphene stripping process, it is necessary to add some auxiliary agents, to increase the interlayer distance of graphite or so-called intercalation, so that graphite is peeled off better.As adopted nitric acid, potassium permanganate, chromic acid or hydrogen peroxide as oxidant, concentrated sulphuric acid, as intercalator, introduces the oxy radicals such as hydroxyl, epoxide group and carboxyl at graphite layers or edge, increase graphite layers from, be beneficial to follow-up graphite layers and peel off.But this chemical substance intercalated technique acid consumption is big, production process has the pollution of the harmful gass such as SOx, NOx or heavy metal ion, product there is sulfur remain, the Graphene finally given is easily generated defect, and in the application equipment there is is corrosion, reduce the service life of equipment, add production cost.
Summary of the invention
It is an object of the invention to overcome the defect existed in prior art, it is provided that the stripper that a kind of Graphene is peeled off, this stripper cooperative mechanical is ground, it is possible to be efficiently peeled off graphite, and the structural deterioration of Graphene is little.
For realizing the purpose of the present invention, the technical scheme is that the stripper that a kind of Graphene is peeled off, the composition of this stripper includes:
Alcohols solvent 100 parts,
Polyacrylate or polyacrylate derivatives 50～80 parts,
Rubber powder 0.5～5 part,
Water soluble salt 0.5～5 part；
Wherein, each component is in its parts by weight.
Preferred technical scheme is, the particle diameter of described rubber powder is 2～20 microns.
Preferred technical scheme is, described alcohols solvent is one or more in ethanol, normal propyl alcohol, n-butyl alcohol, propylene glycol and terpineol.
Preferred technical scheme is, the number-average molecular weight of described polyacrylate or polyacrylate derivatives is more than 100000.
Preferred technical scheme is, described water soluble salt is the one in lithium fluoride, sodium fluoride, sodium chloride, lithium chloride.
Prior art is compared, the stripper that Graphene of the present invention is peeled off by adding polyacrylate or the polyacrylate derivatives with glue viscosity in stripper, use this combination liquid to coordinate to grind or stirring, the requirement to grinding or mixing speed can be reduced, it is not necessary to graphite flake layer ultra high shear can be realized the stripping to Graphene；Coordinate the rubber powder with great friction coefficient, it is possible to improve the peeling force that graphite is produced；It addition, the water soluble salt added in system can improve the electric conductivity of system, it is to avoid the Graphene of stripping, because electrostatic is superimposed together again, particularly eliminates the electrostatic on rubber powder surface, the Graphene after stripping is made to keep the dispersity after peeling off.This stripper is being peeled off while Graphene, and not etching apparatus does not damage graphene-structured.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following example are only for clearly illustrating technical scheme, and can not limit the scope of the invention with this.
Embodiment 1
The present invention is the stripper that a kind of Graphene is peeled off, and the composition of the stripper that this Graphene is peeled off includes: ethanol 100 parts by weight, polyacrylate 50 parts by weight, neoprene rubber powder 0.5 parts by weight, lithium fluoride 2 parts by weight.Wherein, the particle diameter of neoprene rubber powder is 2～20 microns；The number-average molecular weight of polyacrylate is more than 100000.
Embodiment 2
The present invention is the stripper that a kind of Graphene is peeled off, and the composition of the stripper that this Graphene is peeled off includes: ethanol 50 parts by weight, normal propyl alcohol 50 parts by weight, polyurethane-modified polyacrylate 80 parts by weight, sbr powder 5 parts by weight, sodium fluoride 5 parts by weight.Wherein, the particle diameter of sbr powder is 2～20 microns；The number-average molecular weight of polyurethane-modified polyacrylate is more than 100000.
Embodiment 3
The present invention is the stripper that a kind of Graphene is peeled off, and the composition of the stripper that this Graphene is peeled off includes: n-butyl alcohol 40 parts by weight, propylene glycol 60 parts by weight, polyurethane-modified polyacrylate 60 parts by weight, ABS rubber powder 2 parts by weight, sodium chloride 0.5 parts by weight.Wherein, the particle diameter of ABS rubber powder is 2～20 microns；The number-average molecular weight of polyurethane-modified polyacrylate is more than 100000.
Embodiment 4
The present invention is the stripper that a kind of Graphene is peeled off, and the composition of the stripper that this Graphene is peeled off includes: terpineol 100 parts by weight, polyacrylate 70 parts by weight, butyl rubber powder 4 parts by weight, lithium chloride 3 parts by weight.Wherein, the particle diameter of butyl rubber powder is 2～20 microns；The number-average molecular weight of polyacrylate is more than 100000.
The above is only the preferred embodiment of the present invention; it should be pointed out that, for those skilled in the art, under the premise without departing from the technology of the present invention principle; can also making some improvements and modifications, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (5)
1. the stripper that a Graphene is peeled off, it is characterised in that the composition of this stripper includes:
Alcohols solvent 100 parts,
Polyacrylate or polyacrylate derivatives 50～80 parts,
Rubber powder 0.5～5 part,
Water soluble salt 0.5～5 part；
Wherein, each component is in its parts by weight.
2. the stripper that Graphene as claimed in claim 1 is peeled off, it is characterised in that the particle diameter of described rubber powder is 2～20 microns.
3. the stripper that Graphene as claimed in claim 1 is peeled off, it is characterised in that described alcohols solvent is one or more in ethanol, normal propyl alcohol, n-butyl alcohol, propylene glycol and terpineol.
4. the stripper that Graphene as claimed in claim 1 is peeled off, it is characterised in that the number-average molecular weight of described polyacrylate or polyacrylate derivatives is more than 100000.
5. the stripper that Graphene as claimed in claim 1 is peeled off, it is characterised in that described water soluble salt is the one in lithium fluoride, sodium fluoride, sodium chloride, lithium chloride.