CN105712333A - Physical striping method of graphene - Google Patents
Physical striping method of graphene Download PDFInfo
- Publication number
- CN105712333A CN105712333A CN201410711017.8A CN201410711017A CN105712333A CN 105712333 A CN105712333 A CN 105712333A CN 201410711017 A CN201410711017 A CN 201410711017A CN 105712333 A CN105712333 A CN 105712333A
- Authority
- CN
- China
- Prior art keywords
- graphene
- parts
- filter cake
- physics
- peels
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a physical striping method of graphene. The method consists of: S1. injecting flake graphite and a stripping solution into a ball milling tank, wherein the stripping solution is composed of 100 parts of an alcohol solvent, 3-20 parts of hydroxy acrylic resin, and 1-30 parts of sheet metal powder; S2. conducting ball milling for 4-48h, and controlling the rotation speed of the ball mill above 2000rpm/min; S3. at the end of reaction, discharging a suspension solution to a storage tank and performing standing for 24h; S4. conveying the graphene suspension solution into a centrifuge to conduct centrifugation, then taking the supernatant and performing vacuum filtration to obtain a filter cake; and S5. washing the filter cake and conducting freeze drying, thus obtaining a graphene product. The stripping method can efficiently strip graphene.
Description
Technical field
The present invention relates to Graphene production technical field, be specifically related to a kind of method that Graphene is peeled off.
Background technology
Graphene is a kind of two-dimensional material with good flexibility, electrical property.You need to add is that, stricti jurise is said, Graphene is the lamellar of a kind of monolayer；But due to the preparation difficulty of single-layer graphene, generally also the form the few-layer graphene alkene with similar performance is also ranged in the category of Graphene.
At present, the method that prepared by Graphene mainly has: chemically grown method and physics stripping method.Low compared to efficiency, be not suitable for the chemically grown method of industrialized mass production; it is raw material that physics stripping method mainly adopts cheap graphite; make graphite layers peeling-off by graphite crystal is applied mechanical force; break the Van der Waals force of graphite layers; forming monolithic graphite alkene or form the few-layer graphene alkene, this physical separation methods has more industrial prospect and applicable large-scale production.
In Graphene stripping means, it is necessary to add some auxiliary agents to increase the interlayer distance of graphite or so-called intercalation, so that graphite is peeled off better.As adopted nitric acid, potassium permanganate, chromic acid or hydrogen peroxide as oxidant, concentrated sulphuric acid, as intercalator, introduces the oxy radicals such as hydroxyl, epoxide group and carboxyl at graphite layers or edge, increase graphite layers from, be beneficial to follow-up graphite layers and peel off.But this chemical substance intercalated technique acid consumption is big, production process has the pollution of the harmful gass such as SOx, NOx or heavy metal ion, product there is sulfur remain, the Graphene finally given is easily generated defect, and in the application equipment there is is corrosion, reduce the service life of equipment, add production cost.
Summary of the invention
It is an object of the invention to overcome the defect existed in prior art, it is provided that a kind of physics peels off the method for Graphene, and the method can be efficiently peeled off graphite, and the structural deterioration of Graphene is little.
For realizing the purpose of the present invention, the technical scheme is that a kind of method that physics peels off Graphene, the method comprises the following steps:
S1. by purity more than 98%, particle diameter is that 30 ~ 500 μm of graphite flakes and stripper inject in ball grinder according to the weight ratio of 1:2～5, wherein the consisting of of stripper:
Alcohols solvent 100 parts,
Hydroxylated acrylic resin 3～20 parts,
Flake metal powder 1～30 part；
Wherein, each component is in its parts by weight.
S2. ball milling 4～48h, the rotating speed of ball mill is more than 2000rpm/min；
S3. by discharging opening, suspension is expelled in storage tank after stopped reaction, stands 24h head product derived above；
S4. the graphene suspension in the storage tank obtained by step S3 is delivered in centrifuge, and centrifuge speed is 1000-6000rpm/min, and centrifugation time 10min-2h takes the supernatant, and in vacuum apparatus, vacuum is filtrated to get filter cake；
S5. filter cake step S4 obtained with appropriate distilled water wash, filter cake more than lyophilization 3h in freeze drying plant, namely obtain graphene product.
Preferred technical scheme is, in step sl, described alcohols solvent is one or more in ethanol, normal propyl alcohol, n-butyl alcohol, propylene glycol and terpineol.
Preferred technical scheme is, in step sl, described flake metal powder is one or more in zinc powder, nikel powder, argentum powder.
It is preferred that technical scheme be that in step sl, described flake metal powder is of a size of 3～10 microns.
Preferred technical scheme is, in step sl, the number-average molecular weight of described Hydroxylated acrylic resin is 10000～20000.
Prior art is compared, physics of the present invention peels off the method for Graphene by adopting special stripper for the stripping of Graphene, adopting flake metal powder as abrasive media in this stripper, this abrasive media coordinates conventional ball mill medium, it is possible to produce uniform peeling force on graphite flake layer；Flake metal powder coordinates the alcohols solvent and Hydroxylated acrylic resin that can penetrate in graphite flake layer, by forming hydrogen bond between alcohols solvent and Hydroxylated acrylic resin, the heat produced by ball milling makes hydrogen bond destroy, thus graphite linings is produced impulsive force, form inside and outside pincer attack, be effectively facilitated the efficient stripping of Graphene.
Detailed description of the invention
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following example are only for clearly illustrating technical scheme, and can not limit the scope of the invention with this.
Embodiment 1
The present invention is a kind of method that physics peels off Graphene, and the method comprises the following steps:
S1. by purity more than 98%, particle diameter is that 30 ~ 500 μm of graphite flakes and stripper inject in ball grinder, wherein the consisting of of stripper: ethanol 100 parts by weight, Hydroxylated acrylic resin 3 parts by weight, zinc flake 1 parts by weight.Wherein, zinc flake is of a size of 3～10 microns；The number-average molecular weight of Hydroxylated acrylic resin is 10000～20000.The weight ratio of graphite flakes and stripper is 1:5.
S2. ball milling 4h, the rotating speed of ball mill is 6000rpm/min.
S3. by discharging opening, suspension is expelled in storage tank after stopped reaction, stands 24h head product derived above.
S4. the graphene suspension in the storage tank obtained by step S3 is delivered in centrifuge, and centrifuge speed is 1000rpm/min, and centrifugation time 2h takes the supernatant, and in vacuum apparatus, vacuum is filtrated to get filter cake.
S5. filter cake step S4 obtained with appropriate distilled water wash, filter cake more than lyophilization 3h in freeze drying plant, namely obtain graphene product.
Embodiment 2
The present invention is a kind of method that physics peels off Graphene, and the method comprises the following steps:
S1. by purity more than 98%, particle diameter is that 30 ~ 500 μm of graphite flakes and stripper inject in ball grinder, wherein the consisting of of stripper: normal propyl alcohol 100 parts by weight, Hydroxylated acrylic resin 10 parts by weight, Nickel Powder 20 parts by weight.Wherein, Nickel Powder is of a size of 3～10 microns；The number-average molecular weight of Hydroxylated acrylic resin is 10000～20000.The weight ratio of graphite flakes and stripper is 1:4.
S2. ball milling 8h, the rotating speed of ball mill is 4000rpm/min.
S3. by discharging opening, suspension is expelled in storage tank after stopped reaction, stands 24h head product derived above.
S4. the graphene suspension in the storage tank obtained by step S3 is delivered in centrifuge, and centrifuge speed is 4000rpm/min, and centrifugation time 20min takes the supernatant, and in vacuum apparatus, vacuum is filtrated to get filter cake.
S5. filter cake step S4 obtained with appropriate distilled water wash, filter cake more than lyophilization 3h in freeze drying plant, namely obtain graphene product.
Embodiment 3
The present invention is a kind of method that physics peels off Graphene, and the method comprises the following steps:
S1. by purity more than 98%, particle diameter is that 30 ~ 500 μm of graphite flakes and stripper inject in ball grinder, wherein the consisting of of stripper: n-butyl alcohol 70 parts by weight, propylene glycol 30 parts by weight, Hydroxylated acrylic resin 15 parts by weight, flake silver powder 30 parts by weight.Wherein, flake silver powder is of a size of 3～10 microns；The number-average molecular weight of Hydroxylated acrylic resin is 10000～20000.The weight ratio of graphite flakes and stripper is 1:3.
S2. ball milling 12h, the rotating speed of ball mill is 3000rpm/min.
S3. by discharging opening, suspension is expelled in storage tank after stopped reaction, stands 24h head product derived above.
S4. the graphene suspension in the storage tank obtained by step S3 is delivered in centrifuge, and centrifuge speed is 6000rpm/min, and centrifugation time 10min takes the supernatant, and in vacuum apparatus, vacuum is filtrated to get filter cake.
S5. filter cake step S4 obtained with appropriate distilled water wash, filter cake more than lyophilization 3h in freeze drying plant, namely obtain graphene product.
Embodiment 4
The present invention is a kind of method that physics peels off Graphene, and the method comprises the following steps:
S1. by purity more than 98%, particle diameter is that 30 ~ 500 μm of graphite flakes and stripper inject in ball grinder, wherein the consisting of of stripper: terpineol 100 parts by weight, Hydroxylated acrylic resin 20 parts by weight, flake silver powder 10 parts by weight, Nickel Powder 10 parts.Wherein, flake silver powder and Nickel Powder are of a size of 3～10 microns；The number-average molecular weight of Hydroxylated acrylic resin is 10000～20000.The weight ratio of graphite flakes and stripper is 1:1.
S2. ball milling 48h, the rotating speed of ball mill is 2000rpm/min.
S3. by discharging opening, upper strata suspension is expelled in storage tank after stopped reaction, stands 24h head product derived above.
S4. the graphene suspension in the storage tank obtained by step S3 is delivered in centrifuge, and centrifuge speed is 2000rpm/min, and centrifugation time 1h takes the supernatant, and in vacuum apparatus, vacuum is filtrated to get filter cake.
S5. filter cake step S4 obtained with appropriate distilled water wash, filter cake more than lyophilization 3h in freeze drying plant, namely obtain graphene product.
The above is only the preferred embodiment of the present invention; it should be pointed out that, for those skilled in the art, under the premise without departing from the technology of the present invention principle; can also making some improvements and modifications, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (5)
1. the method that a physics peels off Graphene, it is characterised in that the method comprises the following steps:
S1. by purity more than 98%, particle diameter is that 30 ~ 500 μm of graphite flakes and stripper inject in ball grinder according to the weight ratio of 1:2～5, wherein the consisting of of stripper:
Alcohols solvent 100 parts,
Hydroxylated acrylic resin 3～20 parts,
Flake metal powder 1～30 part；
Wherein, each component is in its parts by weight；
S2. ball milling 4～48h, the rotating speed of ball mill is more than 2000rpm/min；
S3. by discharging opening, suspension is expelled in storage tank after stopped reaction, stands 24h head product derived above；
S4. the graphene suspension in the storage tank obtained by step S3 is delivered in centrifuge, and centrifuge speed is 1000-6000rpm/min, and centrifugation time 10min-2h takes the supernatant, and in vacuum apparatus, vacuum is filtrated to get filter cake；
S5. filter cake step S4 obtained with appropriate distilled water wash, filter cake more than lyophilization 3h in freeze drying plant, namely obtain graphene product.
2. the method that physics as claimed in claim 1 peels off Graphene, it is characterised in that in described step S1, described alcohols solvent is one or more in ethanol, normal propyl alcohol, n-butyl alcohol, propylene glycol and terpineol.
3. the method that physics as claimed in claim 1 peels off Graphene, it is characterised in that in described step S1, described flake metal powder is one or more in zinc powder, nikel powder, argentum powder.
4. the method that physics as claimed in claim 3 peels off Graphene, it is characterised in that in described step S1, described flake metal powder is of a size of 3～10 microns.
5. the method that physics as claimed in claim 1 peels off Graphene, it is characterised in that in described step S1, the number-average molecular weight of described Hydroxylated acrylic resin is 10000～20000.