CN105678373A - Coating type thermo-print electronic tag and preparation method thereof - Google Patents

Coating type thermo-print electronic tag and preparation method thereof Download PDF

Info

Publication number
CN105678373A
CN105678373A CN201610009288.8A CN201610009288A CN105678373A CN 105678373 A CN105678373 A CN 105678373A CN 201610009288 A CN201610009288 A CN 201610009288A CN 105678373 A CN105678373 A CN 105678373A
Authority
CN
China
Prior art keywords
coating
layer
electronic tag
cloth
coated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610009288.8A
Other languages
Chinese (zh)
Other versions
CN105678373B (en
Inventor
孙海德
张钦永
李亚男
崔若峰
田茂涛
田召普
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Taibao Information Technology Group Co., Ltd
Original Assignee
Shandong Taibao Preventing Counterfeit Product Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Taibao Preventing Counterfeit Product Co Ltd filed Critical Shandong Taibao Preventing Counterfeit Product Co Ltd
Priority to CN201610009288.8A priority Critical patent/CN105678373B/en
Publication of CN105678373A publication Critical patent/CN105678373A/en
Application granted granted Critical
Publication of CN105678373B publication Critical patent/CN105678373B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention belongs to the technical field of electronic tags, and particularly relates to a coating type thermo-print electronic tag and a preparation method thereof. The coating type thermo-print electronic tag comprises a silicone oil layer, a PET layer, a release layer, a medium layer, a two-component glue layer, an inlay layer and a hot melt adhesive film layer, wherein the above layers are connected sequentially from top to bottom. Based on the process combination, a traditional electronic tag is converted into a new thermo-print disc belt-type electronic tag. In this way, the automatic thermo-print is realized and the damage to chips during the compounding and thermo-print process of the electronic tag can be avoided. Therefore, the bidirectional positioning and thermo-print of the electronic tag can be realized.

Description

Cloth of coating-type thermoprint electronic tag and preparation method thereof
Technical field
The invention belongs to electronic label technology field, be specifically related to a kind of cloth of coating-type thermoprint electronic tag and preparation method thereof.
Background technology
Anti-counterfeiting technology can help consumer to differentiate rapidly the true and false of business men in industry-by-industry, protects consumer rights, helps enterprise customer to hit fake products simultaneously; Can stopping batch to copy, protect brand names, maintaining enterprise image, it is to avoid economic loss, electronic tag is with internal memory and the integrated circuit controlling system, is furnished with corresponding antenna circuit simultaneously. Electronic tag can store information, and in the course of the work information is rewritten. It is possible not only to the essential information of record article, article can also be recorded in intermediate links, supervision link and sales section various information together simultaneously. The massive store feature of electronic tag is laid a good foundation for realizing article quality tracing function, the inside chip of each electronic tag all solidifies a globally unique cognizance code simultaneously, this cognizance code solidifies therein in chip production link, once produce, will be unable to modify. Therefore, after an electronic tag and article are bound, it is possible to this cognizance code cognizance code as article, electronic tag and article form the relation of correspondence, thus realizing the antiforge function of article. Additionally electronic tag adopts cordless with external information exchange, have that information interactive speed is fast, precision is high, capacity of resisting disturbance is strong, adapt to the remarkable advantages such as various working environments, be therefore widely used in the fields such as logistics management, transportation, health care, commodity counterfeit prevention, asset management. In recent years, China also reviews in food safety, drug quality, tobacco and wine anti-counterfeit field increases the application work of electronic label technology, state key Safety of Food Quality tracer working application demonstration projects has been started up, meanwhile, many enterprises also begin to one of the important tool that uses electronic tag as commodity counterfeit prevention quality tracing.
Summary of the invention
It is an object of the invention to provide a kind of cloth of coating-type thermoprint electronic tag, there is significantly high false proof exclusivity, greatly strengthen anti-counterfeiting power; The preparation method that invention also provides cloth of coating-type thermoprint electronic tag, scientific and reasonable, simple, achieve automatization's thermoprint.
Cloth of coating-type thermoprint electronic tag of the present invention is that silicon layer, pet layer, release layer, dielectric layer, double-component glue-line, inlay layer and PUR rete are sequentially connected from top to bottom.
The off-type force size of described silicon layer is 90 ° of peel strengths is 0.002-0.004 thousand ns/m, and 90 ° of peel strengths between release layer and pet layer are 0.03-0.05 thousand ns/m, and the thickness of PUR rete is 40-60 μm.
In described inlay layer, the interval between every inlay is equidistant, and all etches equidistant two-way location cursor above every inlay.
Described cloth of coating-type thermoprint electronic tag is dribbling thermoprint electronic tag, inlay to the range deviation≤0.2mm of the range deviation≤between 0.2mm, inlay at dribbling edge.
Hot melt adhesive film is to have elastic hot melt adhesive film, and its thickness is 40-60 μm, and fusing point is 120-130 DEG C, and hardening time is 10-15s, peels off pulling force >=3 f.
Electronic tag thermoprint is to by after on boiling hot thing, and pet layer just strips down at random.
The preparation method of cloth of coating-type thermoprint electronic tag of the present invention, step is as follows:
(1) dribbling film is made
1. one side corona PET is selected;
2. silicon-coating oil reservoir: silicon layer uses compounding machine be coated on the corona surface of pet layer;
3. release layer it is coated with: release layer utilizes compounding machine to be coated at the non-corona surface of pet layer;
4. coated media layer: dielectric layer utilizes compounding machine to be coated in release aspect;
(2) utilize dry compound machine, use two component the medium aspect in the non-chip face of inlay layer Yu dribbling film to be combined with each other;
(3) use solvent-free composite machine at the chip topcoating cloth hot melt adhesive film of inlay layer;
(4) cross cutting: use automatic die cutter to carry out cross cutting, part unnecessary for inlay is drained simultaneously;
(5) bar is divided: use banding machine that the semi-finished product that cross cutting is good are divided into wall scroll and make dribbling thermoprint electronic tag.
The thickness of the PET described in step (1) is 30-50 μm.
Silicon layer described in step (1) is made up of the raw material of following parts by weight:
Release layer described in step (1) is made up of the raw material of following parts by weight:
5017 water wax 0.5-1.5 parts
Water 10-15 part
Ethanol 10-15 part.
Dielectric layer described in step (1) is made up of the raw material of following parts by weight:
In silicon-coating oil reservoir described in step (1), coating is to use machine coating in 200 order metallic roll, and oven temperature is set to 92 DEG C-130 DEG C-143 DEG C-146 DEG C-115 DEG C, and speed is 50-70 m/min; In coating release layer, coating is that the web coatable roller using 200 orders is coated, coating moisture is 4.6 ± 0.3 grams/, it is coated with the leftover of bolt of cloth and uses and scrapes plain-barreled roll, reversal speed is 550 revs/min, drying tunnel temperature is 95 DEG C-125 DEG C-140 DEG C-145 DEG C-120 DEG C, and coating speed is 50-70m/min; In coated media layer, coating is the web coatable roller using 200 orders, coating moisture is 4.6 ± 0.3 grams/, it is coated with the leftover of bolt of cloth and uses and scrapes plain-barreled roll, reversal speed is 550 revs/min, drying tunnel temperature is 95 DEG C-125 DEG C-140 DEG C-145 DEG C-120 DEG C, and coating speed is 50-70m/min.
Two component described in step (2) is made up of the raw material of following parts by weight:
YH953010 part
YH9530B10 part
Ethyl acetate 10-20 part.
Combined temp described in step (2) is 50-60 DEG C, and composite pressure is 1-1.5MPa, and the composite curing time is 12-18 hour.
In coating described in step (3), hot melt adhesive film is 150-160 DEG C at material case melt temperature, is coated with leftover of bolt of cloth temperature and is 130-140 DEG C, and speed is 80-100 m/min, and hardening time is 24-36 hour.
7362,7387 and 4000 is that DOW CORNING (China) Investment Co., Ltd provides, 5017 water waxes, 802 resins and 902 resins are that cumulative packaging material company limited of Foshan City produces, and YH9530 and YH9530B is that Beijing material limited company of high-new alliance provides.
The preparation method of cloth of coating-type thermoprint electronic tag of the present invention, specifically comprises the following steps that
(1) dribbling film is made
1. the one side corona PET selecting thickness to be 30-50 μm.
2. silicon-coating oil reservoir:
Silicon layer is made up of the raw material of following parts by weight:
Batching step:
A. first weigh quantitative toluene, put in stainless steel cask, calculate the weight of required 7362 according to proportioning, put in stainless steel cask and stir 10 minutes with Pneumatic blender.
B. calculate the weight of required 7387 according to proportioning, and put in dispensing stainless steel cask, stir 20 minutes.
C. calculate the weight of required 4000 according to proportioning, and put in dispensing stainless steel cask, stir 10 minutes.
D. compounding machine is used to be coated on the corona surface of pet layer the silicone oil configured.
E. processing parameter: using machine coating in 200 order metallic roll, oven temperature is set to 92 DEG C-130 DEG C-143 DEG C-146 DEG C-115 DEG C, speed 50-70 m/min.
3. release layer it is coated with:
A. the component of release layer and content: 5017 water waxes: 0.5-1.5 part water: 10-15 part ethanol: 10-15 part
B. the releasing layer coating that will configure, utilizes compounding machine at the non-corona surface of pet layer, uses the web coatable roller of 200 orders to be coated, and is coated with moisture: 4.6 ± 0.3 grams/. It is coated with leftover of bolt of cloth use and scrapes plain-barreled roll, reversal speed 550 revs/min. Drying tunnel temperature: 95 DEG C-125 DEG C-140 DEG C-145 DEG C-120 DEG C, coating speed: 50-70m/min.
4. coated media layer:
The component of dielectric layer and content is:
802 resins: 20-25 part 902 resin: 4-6 part butanone: 8-12 part Ketohexamethylene: 2-3 part
The dielectric layer coating that will have configured, utilizes compounding machine in release aspect, uses the web coatable roller of 200 orders, is coated with moisture: 4.6 ± 0.3 grams/. It is coated with leftover of bolt of cloth use and scrapes plain-barreled roll, reversal speed 550 revs/min. Drying tunnel temperature: 95 DEG C-125 DEG C-140 DEG C-145 DEG C-120 DEG C; Coating speed: 50-70m/min.
(2) utilize dry compound machine, use two component the medium aspect in the non-chip face of inlay layer Yu dribbling film to be combined with each other. Combined temp is 50-60 DEG C, and pressure is 1-1.5MPa, and hardening time is 12-18 hour.
Two component is made up of the raw material of following parts by weight:
YH953010 part
YH9530B10 part
Ethyl acetate 10-20 part.
(3) using solvent-free composite machine at the chip topcoating cloth hot melt adhesive film of inlay layer, material case temperature is 150-160 DEG C, is coated with leftover of bolt of cloth temperature and is 130-140 DEG C, speed 80-100 m/min, 24-36 hour hardening time.
(4) cross cutting: use automatic die cutter, carry out cross cutting according to the size of electronic tag, part unnecessary for inlay is drained simultaneously.
(5) bar is divided: use banding machine that the semi-finished product that cross cutting is good are divided into wall scroll and make dribbling thermoprint electronic tag.
The present invention compared with prior art, has the advantages that
1, by process combination, traditional electronic tag is transferred to and turns to a kind of brand-new thermoprint dribbling electronic tag, it is achieved thermoprint way automatically.
2, solve electronic label chip in compound and thermoprint, damage chip problem.
3, the two-way locating thermoprint of electronic tag is realized.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described further.
Embodiment 1
Customer order 1,000,000 pieces
(1) dribbling film is made
1. the one side corona PET selecting thickness to be 30 μm
2. silicon-coating oil reservoir:
Silicon layer is composed as follows:
Batching step:
A. first weigh quantitative toluene, put in stainless steel cask, calculate the weight of required 7362 according to proportioning, put in stainless steel cask and stir 10 minutes with Pneumatic blender.
B. calculate the weight of required 7387 according to proportioning, and put in dispensing stainless steel cask, stir 20 minutes.
C. calculate the weight of required 4000 according to proportioning, and put in dispensing stainless steel cask, stir 10 minutes.
D. compounding machine is used to be coated on the corona surface of pet layer the silicone oil configured.
E. processing parameter: using machine coating in 200 order metallic roll, oven temperature is set to 92 DEG C-130 DEG C-143 DEG C-146 DEG C-115 DEG C, speed 70 ms/min.
3. release layer it is coated with:
A. the component of release layer and content: 5017 water waxes: 0.5kg water: 10kg ethanol: 10kg
B. the releasing layer coating that will configure, utilizes compounding machine at the non-corona surface of pet layer, uses the web coatable roller of 200 orders to be coated, and is coated with moisture: 4.3 grams/. It is coated with leftover of bolt of cloth use and scrapes plain-barreled roll, reversal speed 550 revs/min. Drying tunnel temperature: 95 DEG C-125 DEG C-140 DEG C-145 DEG C-120 DEG C, coating speed: 70m/min.
4. coated media layer:
The component of dielectric layer and content is:
802 resins: 20kg902 resin: 4kg butanone: 8kg Ketohexamethylene: 2kg
The dielectric layer coating that will have configured, utilizes compounding machine in release aspect, uses the web coatable roller of 200 orders, is coated with moisture: 4.3 grams/. It is coated with leftover of bolt of cloth use and scrapes plain-barreled roll, reversal speed 550 revs/min. Drying tunnel temperature: 95 DEG C-125 DEG C-140 DEG C-145 DEG C-120 DEG C; Coating speed: 70m/min.
(2) utilize dry compound machine, use two component the medium aspect in the non-chip face of inlay layer Yu dribbling film to be combined with each other. Combined temp is 50 DEG C, and pressure is 1MPa, and hardening time is 12 hours.
Two component is composed as follows:
YH953010kg
YH9530B10kg
Ethyl acetate 10kg.
(3) using solvent-free composite machine at the chip topcoating cloth hot melt adhesive film of inlay layer, material case temperature is 150 DEG C, and being coated with leftover of bolt of cloth temperature is 130 DEG C, speed 100 ms/min, 36 hours hardening times.
(4) cross cutting: use automatic die cutter, carry out cross cutting according to the size of electronic tag, part unnecessary for inlay is drained simultaneously.
(5) bar is divided: use banding machine that the semi-finished product that cross cutting is good are divided into wall scroll and make dribbling thermoprint electronic tag.
Embodiment 2
Customer order 2,000,000 pieces
(1) dribbling film is made
1. the one side corona PET selecting thickness to be 50 μm
2. silicon-coating oil reservoir:
Silicon layer is composed as follows:
Batching step:
A. first weigh quantitative toluene, put in stainless steel cask, calculate the weight of required 7362 according to proportioning, put in stainless steel cask and stir 10 minutes with Pneumatic blender.
B. calculate the weight of required 7387 according to proportioning, and put in dispensing stainless steel cask, stir 20 minutes.
C. calculate the weight of required 4000 according to proportioning, and put in dispensing stainless steel cask, stir 10 minutes.
D. compounding machine is used to be coated on the corona surface of pet layer the silicone oil configured.
E. processing parameter: using machine coating in 200 order metallic roll, oven temperature is set to 92 DEG C-130 DEG C-143 DEG C-146 DEG C-115 DEG C, speed 60 ms/min.
3. release layer it is coated with:
A. the component of release layer and content: 5017 water waxes: 1kg water: 13kg ethanol: 12kg
B. the releasing layer coating that will configure, utilizes compounding machine at the non-corona surface of pet layer, uses the web coatable roller of 200 orders to be coated, and is coated with moisture: 4.6 grams/. It is coated with leftover of bolt of cloth use and scrapes plain-barreled roll, reversal speed 550 revs/min. Drying tunnel temperature: 95 DEG C-125 DEG C-140 DEG C-145 DEG C-120 DEG C, coating speed: 60m/min.
4. coated media layer:
The component of dielectric layer and content is:
802 resins: 22kg902 resin: 5kg butanone: 10kg Ketohexamethylene: 2.5kg
The dielectric layer coating that will have configured, utilizes compounding machine in release aspect, uses the web coatable roller of 200 orders, is coated with moisture: 4.6 grams/. It is coated with leftover of bolt of cloth use and scrapes plain-barreled roll, reversal speed 550 revs/min. Drying tunnel temperature: 95 DEG C-125 DEG C-140 DEG C-145 DEG C-120 DEG C; Coating speed: 60m/min.
(2) utilize dry compound machine, use two component the medium aspect in the non-chip face of inlay layer Yu dribbling film to be combined with each other. Combined temp is 55 DEG C, and pressure is 1.2MPa, and hardening time is 16 hours.
Two component is composed as follows:
YH953010kg
YH9530B10kg
Ethyl acetate 15kg.
(3) using solvent-free composite machine at the chip topcoating cloth hot melt adhesive film of inlay layer, material case temperature is 155 DEG C, and being coated with leftover of bolt of cloth temperature is 135 DEG C, speed 90 ms/min, 30 hours hardening times.
(4) cross cutting: use automatic die cutter, carry out cross cutting according to the size of electronic tag, part unnecessary for inlay is drained simultaneously.
(5) bar is divided: use banding machine that the semi-finished product that cross cutting is good are divided into wall scroll and make dribbling thermoprint electronic tag.
Embodiment 3
Customer order 3,000,000 pieces
(1) dribbling film is made
1. the one side corona PET selecting thickness to be 50 μm
2. silicon-coating oil reservoir:
Silicon layer is composed as follows:
Batching step:
A. first weigh quantitative toluene, put in stainless steel cask, calculate the weight of required 7362 according to proportioning, put in stainless steel cask and stir 10 minutes with Pneumatic blender.
B. calculate the weight of required 7387 according to proportioning, and put in dispensing stainless steel cask, stir 20 minutes.
C. calculate the weight of required 4000 according to proportioning, and put in dispensing stainless steel cask, stir 10 minutes.
D. compounding machine is used to be coated on the corona surface of pet layer the silicone oil configured.
E. processing parameter: using machine coating in 200 order metallic roll, oven temperature is set to 92 DEG C-130 DEG C-143 DEG C-146 DEG C-115 DEG C, speed 70 ms/min.
3. release layer it is coated with:
A. the component of release layer and content: 5017 water waxes: 1.5kg water: 15kg ethanol: 15kg
B. the releasing layer coating that will configure, utilizes compounding machine at the non-corona surface of pet layer, uses the web coatable roller of 200 orders to be coated, and is coated with moisture: 4.9 grams/. It is coated with leftover of bolt of cloth use and scrapes plain-barreled roll, reversal speed 550 revs/min. Drying tunnel temperature: 95 DEG C-125 DEG C-140 DEG C-145 DEG C-120 DEG C, coating speed: 50m/min.
4. coated media layer:
The component of dielectric layer and content is:
802 resins: 25kg902 resin: 6kg butanone: 12kg Ketohexamethylene: 3kg
The dielectric layer coating that will have configured, utilizes compounding machine in release aspect, uses the web coatable roller of 200 orders, is coated with moisture: 4.9 grams/. It is coated with leftover of bolt of cloth use and scrapes plain-barreled roll, reversal speed 550 revs/min. Drying tunnel temperature: 95 DEG C-125 DEG C-140 DEG C-145 DEG C-120 DEG C; Coating speed: 50m/min.
(2) utilize dry compound machine, use two component the medium aspect in the non-chip face of inlay layer Yu dribbling film to be combined with each other. Combined temp is 60 DEG C, and pressure is 1.5MPa, and hardening time is 18 hours.
Two component is composed as follows:
YH953010kg
YH9530B10kg
Ethyl acetate 20kg.
(3) using solvent-free composite machine at the chip topcoating cloth hot melt adhesive film of inlay layer, material case temperature is 160 DEG C, and being coated with leftover of bolt of cloth temperature is 140 DEG C, speed 100 ms/min, 36 hours hardening times.
(4) cross cutting: use automatic die cutter, carry out cross cutting according to the size of electronic tag, part unnecessary for inlay is drained simultaneously.
(5) bar is divided: use banding machine that the semi-finished product that cross cutting is good are divided into wall scroll and make dribbling thermoprint electronic tag.

Claims (10)

1. a cloth of coating-type thermoprint electronic tag, it is characterised in that silicon layer, pet layer, release layer, dielectric layer, double-component glue-line, inlay layer and PUR rete are sequentially connected from top to bottom.
2. cloth of coating-type thermoprint electronic tag according to claim 1, it is characterized in that the off-type force size of described silicon layer be 90 ° of peel strengths is 0.002-0.004 thousand ns/m, 90 ° of peel strengths between release layer and pet layer are 0.03-0.05 thousand ns/m, and the thickness of PUR rete is 40-60 μm.
3. cloth of coating-type thermoprint electronic tag according to claim 1, it is characterised in that in described inlay layer, the interval between every inlay is equidistant, and above every inlay, all etch equidistant two-way location cursor.
4. the preparation method of the arbitrary described cloth of coating-type thermoprint electronic tag of claim 1-3, it is characterised in that step is as follows:
(1) dribbling film is made
1. one side corona PET is selected;
2. silicon-coating oil reservoir: silicon layer uses compounding machine be coated on the corona surface of pet layer;
3. release layer it is coated with: release layer utilizes compounding machine to be coated at the non-corona surface of pet layer;
4. coated media layer: dielectric layer utilizes compounding machine to be coated in release aspect;
(2) utilize dry compound machine, use two component the medium aspect in the non-chip face of inlay layer Yu dribbling film to be combined with each other;
(3) use solvent-free composite machine at the chip topcoating cloth hot melt adhesive film of inlay layer;
(4) cross cutting: use automatic die cutter to carry out cross cutting, part unnecessary for inlay is drained simultaneously;
(5) bar is divided: use banding machine that the semi-finished product that cross cutting is good are divided into wall scroll and make dribbling thermoprint electronic tag.
5. the preparation method of cloth of coating-type thermoprint electronic tag according to claim 4, it is characterised in that the silicon layer described in step (1) is made up of the raw material of following parts by weight:
6. the preparation method of cloth of coating-type thermoprint electronic tag according to claim 4, it is characterised in that the release layer described in step (1) is made up of the raw material of following parts by weight:
5017 water wax 0.5-1.5 parts
Water 10-15 part
Ethanol 10-15 part.
7. the preparation method of cloth of coating-type thermoprint electronic tag according to claim 4, it is characterised in that the dielectric layer described in step (1) is made up of the raw material of following parts by weight:
8. the preparation method of cloth of coating-type thermoprint electronic tag according to claim 4, it is characterized in that in the silicon-coating oil reservoir described in step (1), coating is to use machine coating in 200 order metallic roll, oven temperature is set to 92 DEG C-130 DEG C-143 DEG C-146 DEG C-115 DEG C, and speed is 50-70 m/min; In coating release layer, coating is that the web coatable roller using 200 orders is coated, coating moisture is 4.6 ± 0.3 grams/, it is coated with the leftover of bolt of cloth and uses and scrapes plain-barreled roll, reversal speed is 550 revs/min, drying tunnel temperature is 95 DEG C-125 DEG C-140 DEG C-145 DEG C-120 DEG C, and coating speed is 50-70m/min; In coated media layer, coating is the web coatable roller using 200 orders, coating moisture is 4.6 ± 0.3 grams/, it is coated with the leftover of bolt of cloth and uses and scrapes plain-barreled roll, reversal speed is 550 revs/min, drying tunnel temperature is 95 DEG C-125 DEG C-140 DEG C-145 DEG C-120 DEG C, and coating speed is 50-70m/min.
9. the preparation method of cloth of coating-type thermoprint electronic tag according to claim 4, it is characterised in that the two component described in step (2) is made up of the raw material of following parts by weight:
YH953010 part
YH9530B10 part
Ethyl acetate 10-20 part.
10. the preparation method of cloth of coating-type thermoprint electronic tag according to claim 4, it is characterised in that the combined temp described in step (2) is 50-60 DEG C, and composite pressure is 1-1.5MPa, and the composite curing time is 12-18 hour.
CN201610009288.8A 2016-01-08 2016-01-08 Cloth of coating-type thermoprint electronic tag and preparation method thereof Active CN105678373B (en)