CN105672622A - 玻璃地板的制作工艺 - Google Patents

玻璃地板的制作工艺 Download PDF

Info

Publication number
CN105672622A
CN105672622A CN201610106114.3A CN201610106114A CN105672622A CN 105672622 A CN105672622 A CN 105672622A CN 201610106114 A CN201610106114 A CN 201610106114A CN 105672622 A CN105672622 A CN 105672622A
Authority
CN
China
Prior art keywords
glass
glue
surface layer
grams
back layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610106114.3A
Other languages
English (en)
Inventor
王通
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610106114.3A priority Critical patent/CN105672622A/zh
Publication of CN105672622A publication Critical patent/CN105672622A/zh
Pending legal-status Critical Current

Abstract

一种玻璃地板的制作工艺，包括以下步骤：步骤1、将环氧透明玻璃漆100克，玻璃漆固化剂50克，搅拌均匀没有气泡；步骤2、在玻璃面上倒上调配好的面层配胶，把石纹纸扑在胶上面，扑平之后用刮板刮制，刮至没有气泡为止；步骤3、取191玻璃钢树脂1000g，325目滑石粉1000~1500？g，蓝水促进剂15~20？g，搅拌均匀之后加入固化剂（白色）15~20？g，再搅拌均匀制成背层胶；步骤4、将步骤2制作后的玻璃上铺上网格布，把背层胶倒在网格布上，用刮板把胶刮均匀凉干，凉干之后用铲刀把四边铲掉，修好即可，由于石纹纸的多样化，比较传统的地砖，可实现花纹自选定制，硬度高耐磨，托盘安装施工简单，可重复使用，同时因为背层的处理，通过网格布和背层胶的配合，使地板较为传统的地砖更加的防爆。

Description

玻璃地板的制作工艺
技术领域
本发明涉及一种装饰材料技术领域，尤其是一种玻璃地板的制作工艺。
背景技术
传统的装饰地砖、墙砖，一半都是采用陶瓷、大理石等材料制造，其表面的图案、色彩不够逼真，表现力差，同时，陶瓷和大理石材料还存在反射性，防污效果差等缺点，尤其是陶瓷和大理石材料的反射性，对人体健康会产生一定的损害及影响。
目前，市场上出现了几种玻璃地砖，主要分为两种形式，一种直接在玻璃板底面采用玻璃漆喷涂或移印等技术方法，在玻璃表面形成一层色彩丰富、立体感强的装饰涂层；其存在的不足是：由于玻璃板表面光滑，作为地砖使用时防滑性能不好且容易磨花，而且玻璃破碎后会形成大量的碎渣，存在安全隐患，第二种是在第一种的基础上，在装饰涂层外部增设一层由高分子材料与玻璃纤维网组成的复合材料层，解决了第一种存在的安全隐患，但是这种防滑及强度依然不够。
发明内容
本发明的目的在于提供一种多样化、可以自选定制、硬度高、耐磨、托盘安装施工简单、重复率高的玻璃地板的制作工艺。
为解决上述技术问题，本发明提供一种玻璃地板的制作工艺，包括以下步骤：
步骤1、将环氧透明玻璃漆100克，玻璃漆固化剂50克，搅拌均匀没有气泡，配置成面层配胶；
步骤2、在玻璃面上倒上调配好的面层配胶，把石纹纸扑在胶上面，扑平之后用刮板刮制，刮至没有气泡为止，之后将其在阴凉处晾干；
步骤3、取191玻璃钢树脂1000g，325目滑石粉1000~1500g，蓝水促进剂15~20g，搅拌均匀之后加入固化剂（白色）15~20g，再搅拌均匀制成背层胶；
步骤4、将步骤2制作后的玻璃上铺上网格布，把背层胶倒在网格布上，用刮板把胶刮均匀凉干，凉干之后用铲刀把四边铲掉，修好即可。
2、根据权利要求1所述的玻璃地板的制作工艺，其特征在于，在步骤2之前还包括面层处理步骤：在玻璃做面层的哪一面擦试改性剂2~3分钟，凉干。
本发明的有益效果为：新型工艺制作出的玻璃地板，由于石纹纸的多样化，比较传统的地砖，可实现花纹自选定制，硬度高耐磨，托盘安装施工简单，可重复使用，同时因为背层的处理，通过网格布和背层胶的配合，使地板较为传统的地砖更加的防爆。
具体实施方式
为详细说明本发明的技术内容、构造特征、所实现目的及效果，以下结合实施方式详予说明。
本发明提供一种玻璃地板的制作工艺，包括以下步骤：
步骤1、将环氧透明玻璃漆100克，玻璃漆固化剂50克，搅拌均匀没有气泡，配置成面层配胶，根据外界气温的高低可以稍微增加或减小；
步骤2、在玻璃面上倒上调配好的面层配胶，把石纹纸扑在胶上面，扑平之后用刮板刮制，刮至没有气泡为止，之后将其在阴凉处晾干。
为了保证玻璃面的干净及光滑，可以在倒面层配胶之前做面层处理，具体如下，在玻璃做面层的哪一面擦试改性剂2~3分钟，凉干即可。
步骤3、取191玻璃钢树脂1000-1200g，325目滑石粉1000~1500g，蓝水促进剂15~20g，搅拌均匀之后加入固化剂（白色）15~20g，再搅拌均匀制成背层胶；
优选的，191玻璃钢树脂1000g，325目滑石粉1200g，蓝水促进剂18g，搅拌均匀之后加入固化剂（白色）17g，再搅拌均匀制成背层胶，效果最好。
步骤4、将步骤2制作后的玻璃上铺上网格布，把背层胶倒在网格布上，用刮板把胶刮均匀凉干，凉干之后用铲刀把四边铲掉，修齐。
采用新型工艺制作出来的玻璃地板，由于石纹纸的多样化，比较传统的地砖，可实现花纹自选定制，硬度高耐磨，托盘安装施工简单，可重复使用。
同时因为背层的处理，通过网格布和背层胶的配合，由于网格布的拉伸性能及背层胶的牢固性，使地板较为传统的地砖更加的防爆。
进一步的，可以在玻璃面层上在设置防滑层，具体的，防滑层可以通过对面层玻璃进行喷砂、拉丝、蚀刻、雕刻等工艺，增加其外表面的凹凸感，粗糙度和阻滞感觉，以起到防滑和装饰的效果。
当然，在其他实施例中，所述防滑层还可以采用油墨涂料等，通过喷涂、涂镀、印刷等方法土附鱼玻璃表面，或经过高温烘烤、光固化等化学工艺，实现防滑的效果，达到装饰的效果。或者采用防滑纸、膜等材料通过无害环保的有机、无机粘合剂粘结与面层的玻璃上。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (2)

1.一种玻璃地板的制作工艺，其特征在于，包括以下步骤：
步骤1、将环氧透明玻璃漆100克，玻璃漆固化剂50克，搅拌均匀没有气泡，配置成面层配胶；
步骤2、在玻璃面上倒上调配好的面层配胶，把石纹纸扑在胶上面，扑平之后用刮板刮制，刮至没有气泡为止，之后将其在阴凉处晾干；
步骤3、取191玻璃钢树脂1000g，325目滑石粉1000~1500g，蓝水促进剂15~20g，搅拌均匀之后加入固化剂（白色）15~20g，再搅拌均匀制成背层胶；
步骤4、将步骤2制作后的玻璃上铺上网格布，把背层胶倒在网格布上，用刮板把胶刮均匀凉干，凉干之后用铲刀把四边铲掉，修好即可。
2.根据权利要求1所述的玻璃地板的制作工艺，其特征在于，在步骤2之前还包括面层处理步骤：在玻璃做面层的哪一面擦试改性剂2~3分钟，凉干。
CN201610106114.3A 2016-02-26 2016-02-26 玻璃地板的制作工艺 Pending CN105672622A (zh)