CN105670369A - Fire retardant for paint - Google Patents
Fire retardant for paint Download PDFInfo
- Publication number
- CN105670369A CN105670369A CN201610254563.2A CN201610254563A CN105670369A CN 105670369 A CN105670369 A CN 105670369A CN 201610254563 A CN201610254563 A CN 201610254563A CN 105670369 A CN105670369 A CN 105670369A
- Authority
- CN
- China
- Prior art keywords
- parts
- flame retardant
- fire retardant
- borax
- polyacrylamide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fire retardant for paint. The fire retardant is prepared from the following raw materials in parts by weight: 2-6 parts of phosphoric acid, 10-20 parts of bentonite, 5-10 parts of sodium carboxymethyl cellulose, 6-9 parts of polyacrylamide, 3-5 parts of zinc borate, 6-10 parts of methyl acrylate, 1-3 parts of isocyanuric acid, 5-10 parts of zinc pyrophosphate, 2-6 parts of aluminium hydroxide, 2-6 parts of magnesium hydroxide, 5-13 parts of silicate ester resin, and 7-15 parts of borax. The fire retardant has the beneficial effects such as good flame retarding effect, highly available raw materials, environmental protection and harmlessness.
Description
Technical field
The present invention relates to and flame retardant products technical field, particularly relate to a kind of flame retardant for coating.
Background technology
Fire retardant is as the additive suppressing plastics burning, and development research goes out a lot of kind. General fire retardant can be divided into the big class of interpolation type and response type two, and additive flame retardant is added in ready-made polymkeric substance to use, it be dispersing and mixing in the polymer, namely can not be combined by chemical reaction between polymkeric substance and fire retardant. Reactive flame retardant is used for the fire-retardant of thermosetting resin, the prepolymer generation chemical reaction of this based flame retardant and thermosetting resin and generate thermosetting resin, and give its flame retardant resistance.
Summary of the invention
For the deficiency that prior art exists, technical problem to be solved by this invention is to provide a kind of flame retardant for coating.
For solving the problems of the technologies described above, the technical scheme that the present invention takes is:
A kind of flame retardant for coating, is prepared from by following weight raw material: phosphoric acid 2-6 part, wilkinite 10-20 part, Xylo-Mucine 5-10 part, polyacrylamide 6-9 part, zinc borate 3-5 part, methyl acrylate 6-10 part, isocyanuric acid 1-3 part, zinc pyrophosphate 5-10 part, aluminium hydroxide 2-6 part, magnesium hydroxide 2-6 part, silicon ester resin 5-13 part, borax 7-15 part.
Preferably, a kind of flame retardant for coating, is prepared from by following weight raw material: phosphoric acid 3-5 part, wilkinite 13-17 part, Xylo-Mucine 6-9 part, polyacrylamide 7-8 part, zinc borate 3.5-4.5 part, methyl acrylate 7-9 part, isocyanuric acid 1.5-2.5 part, zinc pyrophosphate 6-9 part, aluminium hydroxide 3-5 part, magnesium hydroxide 3-5 part, silicon ester resin 7-11 part, borax 9-13 part.
More preferably, a kind of flame retardant for coating, is prepared from by following weight raw material: phosphatase 24 part, wilkinite 15 parts, Xylo-Mucine 7.5 parts, polyacrylamide 7.5 parts, zinc borate 4 parts, methyl acrylate 8 parts, isocyanuric acid 2 parts, zinc pyrophosphate 7.5 parts, 4 parts, aluminium hydroxide, magnesium hydroxide 4 parts, silicon ester resin 9 parts, borax 11 parts.
Compared with prior art: the present invention has the useful effects such as flame retardant effect is good, raw material is easy to get, environmentally friendly.
Embodiment
Below embodiments of the invention are described in detail, so that advantages and features of the invention can be easier to be readily appreciated by one skilled in the art, thus protection scope of the present invention are made more explicit defining.
Embodiment 1
A kind of flame retardant for coating, is prepared from by following weight raw material: phosphoric acid 2 parts, wilkinite 10 parts, Xylo-Mucine 5 parts, polyacrylamide 6 parts, zinc borate 3 parts, methyl acrylate 6 parts, isocyanuric acid 1 part, zinc pyrophosphate 5 parts, 2 parts, aluminium hydroxide, magnesium hydroxide 2 parts, silicon ester resin 5 parts, borax 7 parts.
Embodiment 2
A kind of flame retardant for coating, is prepared from by following weight raw material: phosphoric acid 3 parts, wilkinite 13 parts, Xylo-Mucine 6 parts, polyacrylamide 7 parts, zinc borate 3.5 parts, methyl acrylate 7 parts, isocyanuric acid 1.5 parts, zinc pyrophosphate 6 parts, 3 parts, aluminium hydroxide, magnesium hydroxide 3 parts, silicon ester resin 7 parts, borax 9 parts.
Embodiment 3
A kind of flame retardant for coating, is prepared from by following weight raw material: phosphatase 24 part, wilkinite 15 parts, Xylo-Mucine 7.5 parts, polyacrylamide 7.5 parts, zinc borate 4 parts, methyl acrylate 8 parts, isocyanuric acid 2 parts, zinc pyrophosphate 7.5 parts, 4 parts, aluminium hydroxide, magnesium hydroxide 4 parts, silicon ester resin 9 parts, borax 11 parts.
Embodiment 4
A kind of flame retardant for coating, is prepared from by following weight raw material: phosphoric acid 5 parts, wilkinite 17 parts, Xylo-Mucine 9 parts, polyacrylamide 8 parts, zinc borate 4.5 parts, methyl acrylate 9 parts, isocyanuric acid 2.5 parts, zinc pyrophosphate 9 parts, 5 parts, aluminium hydroxide, magnesium hydroxide 5 parts, silicon ester resin 11 parts, borax 13 parts.
Embodiment 5
A kind of flame retardant for coating, is prepared from by following weight raw material: phosphoric acid 6 parts, wilkinite 20 parts, Xylo-Mucine 10 parts, polyacrylamide 9 parts, zinc borate 5 parts, methyl acrylate 10 parts, isocyanuric acid 3 parts, zinc pyrophosphate 10 parts, 6 parts, aluminium hydroxide, magnesium hydroxide 6 parts, silicon ester resin 13 parts, borax 15 parts.
Claims (3)
1. a flame retardant for coating, it is characterised in that be prepared from by following weight raw material: phosphoric acid 2-6 part, wilkinite 10-20 part, Xylo-Mucine 5-10 part, polyacrylamide 6-9 part, zinc borate 3-5 part, methyl acrylate 6-10 part, isocyanuric acid 1-3 part, zinc pyrophosphate 5-10 part, aluminium hydroxide 2-6 part, magnesium hydroxide 2-6 part, silicon ester resin 5-13 part, borax 7-15 part.
2. flame retardant for coating according to claim 1, it is characterised in that be prepared from by following weight raw material: phosphoric acid 3-5 part, wilkinite 13-17 part, Xylo-Mucine 6-9 part, polyacrylamide 7-8 part, zinc borate 3.5-4.5 part, methyl acrylate 7-9 part, isocyanuric acid 1.5-2.5 part, zinc pyrophosphate 6-9 part, aluminium hydroxide 3-5 part, magnesium hydroxide 3-5 part, silicon ester resin 7-11 part, borax 9-13 part.
3. flame retardant for coating according to claim 1 and 2, it is characterised in that be prepared from by following weight raw material: phosphatase 24 part, wilkinite 15 parts, Xylo-Mucine 7.5 parts, polyacrylamide 7.5 parts, zinc borate 4 parts, methyl acrylate 8 parts, isocyanuric acid 2 parts, zinc pyrophosphate 7.5 parts, 4 parts, aluminium hydroxide, magnesium hydroxide 4 parts, silicon ester resin 9 parts, borax 11 parts.