CN105632582A - 一种多芯电工缆线 - Google Patents

一种多芯电工缆线 Download PDF

Info

Publication number
CN105632582A
CN105632582A CN201610026152.8A CN201610026152A CN105632582A CN 105632582 A CN105632582 A CN 105632582A CN 201610026152 A CN201610026152 A CN 201610026152A CN 105632582 A CN105632582 A CN 105632582A
Authority
CN
China
Prior art keywords
parts
cable
core
multicore
surplus
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610026152.8A
Other languages
English (en)
Inventor
万明聪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610026152.8A priority Critical patent/CN105632582A/zh
Publication of CN105632582A publication Critical patent/CN105632582A/zh
Pending legal-status Critical Current

Abstract

一种多芯电工缆线，包括铁基合金芯材和铝基合金芯材和铜基合金芯材，三个芯材外各包覆防潮层后形成三个独立导电芯坯，三个芯坯被填充料所包裹成整体，填充料外包覆铝合金金属丝屏蔽网，铝合金金属丝屏蔽网外轻质纤维编织网，轻质编织网外包覆缆料层，铝合金金属丝屏蔽网起到屏蔽作用；轻质编织网保证产品的韧性和强度。

Description

一种多芯电工缆线
技术领域
本发明涉一种多芯电工缆线，属于电工技术领域。
背景技术
现有的电力电缆不具备省能增效的功能和传输信号功能，因此对于需要具备输电和传输光电信号功能的，既要求高导电、重量轻、成本低、省能环保、防腐蚀、抗蠕变、抗疲劳，又要求易弯曲、阻燃的适用场合来说，就必须同时敷设具备以上性能的电力电缆和光缆，这样对一些高层建筑物、国家大型建筑、地铁、轨道交通、城区电力网等来说，加剧了管线铺设的拥挤状况，也相应造成了大量资金的浪费。
发明内容
一种多芯电工缆线，包括铁基合金芯材和铝基合金芯材和铜基合金芯材，三个芯材外各包覆防潮层后形成三个独立导电芯坯，三个芯坯被填充料所包裹成整体，填充料外包覆铝合金金属丝屏蔽网，铝合金金属丝屏蔽网外轻质纤维编织网，轻质编织网外包覆缆料层，
铝基合金芯材各元素组分含量为：Si1-2﹪，Sn0.8-0.9﹪，Nb0.6-0.7﹪，Cu0.5-0.6﹪，Cr0.3-0.4﹪，V0.2-0.3﹪，Mo0.06-0.07﹪，Ag0.05-0.06﹪，Ce0.04-0.05﹪，Pr0.03-0.04﹪，Cd0.01-0.02﹪，余量为Al，
铜基合金芯材各元素组分含量为：Co2-3﹪，Zn0.7-0.8﹪，Ag0.4-0.5﹪，Ta0.3-0.4﹪，Ga0.2-0.3﹪，In0.1-0.2﹪，Ni0.07-0.08﹪，Sc0.04-0.05﹪，Ca0.03-0.04﹪，La0.03-0.04﹪，W0.01-0.02﹪，余量为Cu，
铁基合金芯材各元素组分含量为：C0.03-0.04﹪Al0.8-0.9﹪，Mg0.7-0.8﹪，Sn0.5-0.6﹪，Zn0.4-0.5﹪，Cr0.2-0.3﹪，V0.2-0.3﹪，B0.06-0.07﹪，Sr0.04-0.05﹪，Y0.02-0.03﹪，La0.01-0.02﹪，Bi0.01-0.02﹪，余量为Fe，
防潮层是称取包括：丁基橡胶50份，邻苯二甲酸酯10-20份，二甲苯20-30份，丙二醇甲醚醋酸酯10-20份，双环戊二烯7份，硅藻土40份，氢氧化镁10份，甘油三醋酸酯3份的原料混合固化而成的，
铝合金金属丝屏蔽网各组分元素为：Bi0.3-0.4﹪，Cd0.1-0.2﹪，Sb0.07-0.08﹪，Pr0.04-0.05﹪，Nd0.03-0.04﹪，Ni0.01-0.02﹪，余量为Al，
缆料层是称取包括：乙烯辛烯共聚物100份，甲基乙烯基硅橡胶30-40份，乙烯－醋酸乙烯共聚物20-30份，方解石粉50份，氢氧化铝10份，玻璃粉10份，三羟甲基丙烷三丙烯酸酯4份，硼酸锌3份，硫化锌3份，聚苯硫醚2份的原料混合固化而成的。
所述的一种多芯电工缆线，缆料层是称取包括：乙烯辛烯共聚物100份，甲基乙烯基硅橡胶30份，乙烯－醋酸乙烯共聚物20份，方解石粉50份，氢氧化铝10份，玻璃粉10份，三羟甲基丙烷三丙烯酸酯4份，硼酸锌3份，硫化锌3份，聚苯硫醚2份的原料混合固化而成的。
所述的一种多芯缆线，缆料层是称取包括：乙烯辛烯共聚物100份，甲基乙烯基硅橡胶40份，乙烯－醋酸乙烯共聚物30份，方解石粉50份，氢氧化铝10份，玻璃粉10份，三羟甲基丙烷三丙烯酸酯4份，硼酸锌3份，硫化锌3份，聚苯硫醚2份的原料混合固化而成的。
所述的一种多芯电工缆线，缆料层是称取包括：乙烯辛烯共聚物100份，甲基乙烯基硅橡胶35份，乙烯－醋酸乙烯共聚物25份，方解石粉50份，氢氧化铝10份，玻璃粉10份，三羟甲基丙烷三丙烯酸酯4份，硼酸锌3份，硫化锌3份，聚苯硫醚2份的原料混合固化而成的。
所述的一种多芯缆线，铝合金金属丝屏蔽网各组分元素为：Bi0.3﹪，Cd0.1﹪，Sb0.07﹪，Pr0.04﹪，Nd0.03﹪，Ni0.01﹪，余量为Al。
所述的一种多芯电工缆线，铝合金金属丝屏蔽网各组分元素为：Bi-0.4﹪，Cd0.2﹪，Sb0.08﹪，Pr0.05﹪，Nd0.04﹪，Ni0.02﹪，余量为Al。
所述的一种多芯电工缆线，铝合金金属丝屏蔽网各组分元素为：Bi0.35﹪，Cd0.15﹪，Sb0.075﹪，Pr0.045﹪，Nd0.035﹪，Ni0.015﹪，余量为Al。
所述的一种多芯电工缆线，防潮层是称取包括：丁基橡胶50份，邻苯二甲酸酯15份，二甲苯25份，丙二醇甲醚醋酸酯15份，双环戊二烯7份，硅藻土40份，氢氧化镁10份，甘油三醋酸酯3份的原料混合固化而成的。
所述的一种多芯电工缆线，防潮层是称取包括：丁基橡胶50份，邻苯二甲酸酯10份，二甲苯20份，丙二醇甲醚醋酸酯10份，双环戊二烯7份，硅藻土40份，氢氧化镁10份，甘油三醋酸酯3份的原料混合固化而成的。
所述的一种多芯电工缆线，防潮层是称取包括：丁基橡胶50份，邻苯二甲酸酯20份，二甲苯30份，丙二醇甲醚醋酸酯20份，双环戊二烯7份，硅藻土40份，氢氧化镁10份，甘油三醋酸酯3份的原料混合固化而成的。
上述发明内容相对于现有技术的有益效果在于：1）本发明多芯电工缆线中的铁基合金芯材和铝基合金芯材和铜基合金芯材保证了芯材的强度要求和导电性要求；独立设施保证多产品多功能使用2）防潮层可以提高产品的防水和防潮性能保证材料的使用寿命；3）缆料层有效起到保护作用并且原料简单易获得，4）铝合金金属丝屏蔽网起到屏蔽作用；5）轻质编织网保证产品的韧性和强度。
附图说明
图1为多芯电工缆线截面图。
具体实施方式
为了对本发明的技术特征、目的和效果有更加清楚的理解，现详细说明本发明的具体实施方式。
如图1所示一种多芯电工缆线，包括铁基合金芯材1和铝基合金芯材2和铜基合金芯材3，三个芯材外各包覆防潮层4后形成三个独立导电芯坯，三个芯坯被填充料5所包裹成整体，填充料外包覆铝合金金属丝屏蔽网6，铝合金金属丝屏蔽网外轻质纤维编织网7，轻质编织网外包覆缆料层8。
实施例1
一种多芯电工缆线，包括铁基合金芯材和铝基合金芯材和铜基合金芯材，三个芯材外各包覆防潮层后形成三个独立导电芯坯，三个芯坯被填充料所包裹成整体，填充料外包覆铝合金金属丝屏蔽网，铝合金金属丝屏蔽网外轻质纤维编织网，轻质编织网外包覆缆料层，
铝基合金芯材各元素组分含量为：Si1﹪，Sn0.8﹪，Nb0.6﹪，Cu0.5﹪，Cr0.3﹪，V0.2﹪，Mo0.06﹪，Ag0.05﹪，Ce0.04﹪，Pr0.03﹪，Cd0.01﹪，余量为Al，
铜基合金芯材各元素组分含量为：Co2﹪，Zn0.7﹪，Ag0.4﹪，Ta0.3﹪，Ga0.2﹪，In0.1﹪，Ni0.07﹪，Sc0.04﹪，Ca0.03﹪，La0.03﹪，W0.01﹪，余量为Cu，
铁基合金芯材各元素组分含量为：C0.03﹪Al0.8﹪，Mg0.7﹪，Sn0.5﹪，Zn0.4﹪，Cr0.2﹪，V0.2﹪，B0.06﹪，Sr0.04﹪，Y0.02﹪，La0.01﹪，Bi0.01﹪，余量为Fe，
防潮层是称取包括：丁基橡胶50份，邻苯二甲酸酯10份，二甲苯20份，丙二醇甲醚醋酸酯10份，双环戊二烯7份，硅藻土40份，氢氧化镁10份，甘油三醋酸酯3份的原料混合固化而成的，
铝合金金属丝屏蔽网各组分元素为：Bi0.3﹪，Cd0.1﹪，Sb0.07﹪，Pr0.04﹪，Nd0.03﹪，Ni0.01﹪，余量为Al
缆料层是称取包括：乙烯辛烯共聚物100份，甲基乙烯基硅橡胶30份，乙烯－醋酸乙烯共聚物20份，方解石粉50份，氢氧化铝10份，玻璃粉10份，三羟甲基丙烷三丙烯酸酯4份，硼酸锌3份，硫化锌3份，聚苯硫醚2份的原料混合固化而成的，
实施例2
一种多芯电工缆线，包括铁基合金芯材和铝基合金芯材和铜基合金芯材，三个芯材外各包覆防潮层后形成三个独立导电芯坯，三个芯坯被填充料所包裹成整体，填充料外包覆铝合金金属丝屏蔽网，铝合金金属丝屏蔽网外轻质纤维编织网，轻质编织网外包覆缆料层，
铝基合金芯材各元素组分含量为：Si2﹪，Sn0.9﹪，Nb0.7﹪，Cu0.6﹪，Cr0.4﹪，V0.3﹪，Mo0.07﹪，Ag0.06﹪，Ce0.05﹪，Pr0.04﹪，Cd0.02﹪，余量为Al，
铜基合金芯材各元素组分含量为：Co3﹪，Zn0.8﹪，Ag0.5﹪，Ta0.4﹪，Ga0.3﹪，In0.2﹪，Ni0.08﹪，Sc0.05﹪，Ca0.04﹪，La0.04﹪，W0.02﹪，余量为Cu，
铁基合金芯材各元素组分含量为：C0.04﹪Al0.9﹪，Mg0.8﹪，Sn0.6﹪，Zn0.5﹪，Cr0.3﹪，V0.3﹪，B0.07﹪，Sr0.05﹪，Y0.03﹪，La0.02﹪，Bi0.02﹪，余量为Fe，
防潮层是称取包括：丁基橡胶50份，邻苯二甲酸酯20份，二甲苯30份，丙二醇甲醚醋酸酯20份，双环戊二烯7份，硅藻土40份，氢氧化镁10份，甘油三醋酸酯3份的原料混合固化而成的，
铝合金金属丝屏蔽网各组分元素为：Bi0.4﹪，Cd0.2﹪，Sb0.08﹪，Pr0.05﹪，Nd0.04﹪，Ni0.02﹪，余量为Al
缆料层是称取包括：乙烯辛烯共聚物100份，甲基乙烯基硅橡胶40份，乙烯－醋酸乙烯共聚物30份，方解石粉50份，氢氧化铝10份，玻璃粉10份，三羟甲基丙烷三丙烯酸酯4份，硼酸锌3份，硫化锌3份，聚苯硫醚2份的原料混合固化而成的，
实施例3
一种多芯电工缆线，包括铁基合金芯材和铝基合金芯材和铜基合金芯材，三个芯材外各包覆防潮层后形成三个独立导电芯坯，三个芯坯被填充料所包裹成整体，填充料外包覆铝合金金属丝屏蔽网，铝合金金属丝屏蔽网外轻质纤维编织网，轻质编织网外包覆缆料层，
铝基合金芯材各元素组分含量为：Si1.5﹪，Sn0.85﹪，Nb0.65﹪，Cu0.55﹪，Cr0.35﹪，V0.25﹪，Mo0.065﹪，Ag0.055﹪，Ce0.045﹪，Pr0.035﹪，Cd0.015﹪，余量为Al，
铜基合金芯材各元素组分含量为：Co2.5﹪，Zn0.75﹪，Ag0.45﹪，Ta0.35﹪，Ga0.25﹪，In0.15﹪，Ni0.075﹪，Sc0.045﹪，Ca0.035﹪，La0.035﹪，W0.015﹪，余量为Cu，
铁基合金芯材各元素组分含量为：C0.035﹪Al0.85﹪，Mg0.75﹪，Sn0.55﹪，Zn0.45﹪，Cr0.25﹪，V0.25﹪，B0.065﹪，Sr0.045﹪，Y0.025﹪，La0.015﹪，Bi0.015﹪，余量为Fe，
防潮层是称取包括：丁基橡胶50份，邻苯二甲酸酯15份，二甲苯25份，丙二醇甲醚醋酸酯15份，双环戊二烯7份，硅藻土40份，氢氧化镁10份，甘油三醋酸酯3份的原料混合固化而成的，
铝合金金属丝屏蔽网各组分元素为：Bi0.35﹪，Cd0.15﹪，Sb0.075﹪，Pr0.045﹪，Nd0.035﹪，Ni0.015﹪，余量为Al
缆料层是称取包括：乙烯辛烯共聚物100份，甲基乙烯基硅橡胶35份，乙烯－醋酸乙烯共聚物25份，方解石粉50份，氢氧化铝10份，玻璃粉10份，三羟甲基丙烷三丙烯酸酯4份，硼酸锌3份，硫化锌3份，聚苯硫醚2份的原料混合固化而成的，
实施例4
一种多芯电工缆线，包括铁基合金芯材和铝基合金芯材和铜基合金芯材，三个芯材外各包覆防潮层后形成三个独立导电芯坯，三个芯坯被填充料所包裹成整体，填充料外包覆铝合金金属丝屏蔽网，铝合金金属丝屏蔽网外轻质纤维编织网，轻质编织网外包覆缆料层，
铝基合金芯材各元素组分含量为：Si1.3﹪，Sn0.82﹪，Nb0.61﹪，Cu0.52﹪，Cr0.32﹪，V0.23﹪，Mo0.064﹪，Ag0.053﹪，Ce0.042﹪，Pr0.033﹪，Cd0.011﹪，余量为Al，
铜基合金芯材各元素组分含量为：Co2.4﹪，Zn0.73﹪，Ag0.42﹪，Ta0.31﹪，Ga0.22﹪，In0.11﹪，Ni0.072﹪，Sc0.043﹪，Ca0.034﹪，La0.034﹪，W0.012﹪，余量为Cu，
铁基合金芯材各元素组分含量为：C0.034﹪Al0.84﹪，Mg0.72﹪，Sn0.51﹪，Zn0.42﹪，Cr0.23﹪，V0.24﹪，B0.064﹪，Sr0.043﹪，Y0.022﹪，La0.011﹪，Bi0.013﹪，余量为Fe，
防潮层是称取包括：丁基橡胶50份，邻苯二甲酸酯14份，二甲苯24份，丙二醇甲醚醋酸酯12份，双环戊二烯7份，硅藻土40份，氢氧化镁10份，甘油三醋酸酯3份的原料混合固化而成的，
铝合金金属丝屏蔽网各组分元素为：Bi0.34﹪，Cd0.12﹪，Sb0.072﹪，Pr0.041﹪，Nd0.033﹪，Ni0.013﹪，余量为Al
缆料层是称取包括：乙烯辛烯共聚物100份，甲基乙烯基硅橡胶32份，乙烯－醋酸乙烯共聚物21份，方解石粉50份，氢氧化铝10份，玻璃粉10份，三羟甲基丙烷三丙烯酸酯4份，硼酸锌3份，硫化锌3份，聚苯硫醚2份的原料混合固化而成的，
实施例5
一种多芯电工缆线，包括铁基合金芯材和铝基合金芯材和铜基合金芯材，三个芯材外各包覆防潮层后形成三个独立导电芯坯，三个芯坯被填充料所包裹成整体，填充料外包覆铝合金金属丝屏蔽网，铝合金金属丝屏蔽网外轻质纤维编织网，轻质编织网外包覆缆料层，
铝基合金芯材各元素组分含量为：Si1.6﹪，Sn0.86﹪，Nb0.67﹪，Cu0.58﹪，Cr0.39﹪，V0.27﹪，Mo0.069﹪，Ag0.057﹪，Ce0.048﹪，Pr0.038﹪，Cd0.016﹪，余量为Al，
铜基合金芯材各元素组分含量为：Co2.8﹪，Zn0.76﹪，Ag0.48﹪，Ta0.38﹪，Ga0.28﹪，In0.19﹪，Ni0.076﹪，Sc0.047﹪，Ca0.037﹪，La0.038﹪，W0.017﹪，余量为Cu，
铁基合金芯材各元素组分含量为：C0.036﹪Al0.87﹪，Mg0.78﹪，Sn0.58﹪，Zn0.46﹪，Cr0.27﹪，V0.28﹪，B0.069﹪，Sr0.049﹪，Y0.027﹪，La0.016﹪，Bi0.016﹪，余量为Fe，
防潮层是称取包括：丁基橡胶50份，邻苯二甲酸酯18份，二甲苯29份，丙二醇甲醚醋酸酯16份，双环戊二烯7份，硅藻土40份，氢氧化镁10份，甘油三醋酸酯3份的原料混合固化而成的，
铝合金金属丝屏蔽网各组分元素为：Bi0.37﹪，Cd0.17﹪，Sb0.076﹪，Pr0.046﹪，Nd0.037﹪，Ni0.018﹪，余量为Al
缆料层是称取包括：乙烯辛烯共聚物100份，甲基乙烯基硅橡胶38份，乙烯－醋酸乙烯共聚物28份，方解石粉50份，氢氧化铝10份，玻璃粉10份，三羟甲基丙烷三丙烯酸酯4份，硼酸锌3份，硫化锌3份，聚苯硫醚2份的原料混合固化而成的。

Claims (10)

1.一种多芯电工缆线，包括铁基合金芯材和铝基合金芯材和铜基合金芯材，三个芯材外各包覆防潮层后形成三个独立导电芯坯，三个芯坯被填充料所包裹成整体，填充料外包覆铝合金金属丝屏蔽网，铝合金金属丝屏蔽网外轻质纤维编织网，轻质编织网外包覆缆料层，
铝基合金芯材各元素组分含量为：Si1-2﹪，Sn0.8-0.9﹪，Nb0.6-0.7﹪，Cu0.5-0.6﹪，Cr0.3-0.4﹪，V0.2-0.3﹪，Mo0.06-0.07﹪，Ag0.05-0.06﹪，Ce0.04-0.05﹪，Pr0.03-0.04﹪，Cd0.01-0.02﹪，余量为Al，
铜基合金芯材各元素组分含量为：Co2-3﹪，Zn0.7-0.8﹪，Ag0.4-0.5﹪，Ta0.3-0.4﹪，Ga0.2-0.3﹪，In0.1-0.2﹪，Ni0.07-0.08﹪，Sc0.04-0.05﹪，Ca0.03-0.04﹪，La0.03-0.04﹪，W0.01-0.02﹪，余量为Cu，
铁基合金芯材各元素组分含量为：C0.03-0.04﹪Al0.8-0.9﹪，Mg0.7-0.8﹪，Sn0.5-0.6﹪，Zn0.4-0.5﹪，Cr0.2-0.3﹪，V0.2-0.3﹪，B0.06-0.07﹪，Sr0.04-0.05﹪，Y0.02-0.03﹪，La0.01-0.02﹪，Bi0.01-0.02﹪，余量为Fe，
防潮层是称取包括：丁基橡胶50份，邻苯二甲酸酯10-20份，二甲苯20-30份，丙二醇甲醚醋酸酯10-20份，双环戊二烯7份，硅藻土40份，氢氧化镁10份，甘油三醋酸酯3份的原料混合固化而成的，
铝合金金属丝屏蔽网各组分元素为：Bi0.3-0.4﹪，Cd0.1-0.2﹪，Sb0.07-0.08﹪，Pr0.04-0.05﹪，Nd0.03-0.04﹪，Ni0.01-0.02﹪，余量为Al，
缆料层是称取包括：乙烯辛烯共聚物100份，甲基乙烯基硅橡胶30-40份，乙烯－醋酸乙烯共聚物20-30份，方解石粉50份，氢氧化铝10份，玻璃粉10份，三羟甲基丙烷三丙烯酸酯4份，硼酸锌3份，硫化锌3份，聚苯硫醚2份的原料混合固化而成的。
2.如权利要求1所述的一种多芯电工缆线，缆料层是称取包括：乙烯辛烯共聚物100份，甲基乙烯基硅橡胶30份，乙烯－醋酸乙烯共聚物20份，方解石粉50份，氢氧化铝10份，玻璃粉10份，三羟甲基丙烷三丙烯酸酯4份，硼酸锌3份，硫化锌3份，聚苯硫醚2份的原料混合固化而成的。
3.如权利要求1所述的一种多芯缆线，缆料层是称取包括：乙烯辛烯共聚物100份，甲基乙烯基硅橡胶40份，乙烯－醋酸乙烯共聚物30份，方解石粉50份，氢氧化铝10份，玻璃粉10份，三羟甲基丙烷三丙烯酸酯4份，硼酸锌3份，硫化锌3份，聚苯硫醚2份的原料混合固化而成的。
4.如权利要求1所述的一种多芯电工缆线，缆料层是称取包括：乙烯辛烯共聚物100份，甲基乙烯基硅橡胶35份，乙烯－醋酸乙烯共聚物25份，方解石粉50份，氢氧化铝10份，玻璃粉10份，三羟甲基丙烷三丙烯酸酯4份，硼酸锌3份，硫化锌3份，聚苯硫醚2份的原料混合固化而成的。
5.如权利要求1所述的一种多芯缆线，铝合金金属丝屏蔽网各组分元素为：Bi0.3﹪，Cd0.1﹪，Sb0.07﹪，Pr0.04﹪，Nd0.03﹪，Ni0.01﹪，余量为Al。
6.如权利要求1所述的一种多芯电工缆线，铝合金金属丝屏蔽网各组分元素为：Bi-0.4﹪，Cd0.2﹪，Sb0.08﹪，Pr0.05﹪，Nd0.04﹪，Ni0.02﹪，余量为Al。
7.如权利要求1所述的一种多芯电工缆线，铝合金金属丝屏蔽网各组分元素为：Bi0.35﹪，Cd0.15﹪，Sb0.075﹪，Pr0.045﹪，Nd0.035﹪，Ni0.015﹪，余量为Al。
8.如权利要求1所述的一种多芯电工缆线，防潮层是称取包括：丁基橡胶50份，邻苯二甲酸酯15份，二甲苯25份，丙二醇甲醚醋酸酯15份，双环戊二烯7份，硅藻土40份，氢氧化镁10份，甘油三醋酸酯3份的原料混合固化而成的。
9.如权利要求1所述的一种多芯电工缆线，防潮层是称取包括：丁基橡胶50份，邻苯二甲酸酯10份，二甲苯20份，丙二醇甲醚醋酸酯10份，双环戊二烯7份，硅藻土40份，氢氧化镁10份，甘油三醋酸酯3份的原料混合固化而成的。
10.如权利要求1所述的一种多芯电工缆线，防潮层是称取包括：丁基橡胶50份，邻苯二甲酸酯20份，二甲苯30份，丙二醇甲醚醋酸酯20份，双环戊二烯7份，硅藻土40份，氢氧化镁10份，甘油三醋酸酯3份的原料混合固化而成的。
CN201610026152.8A 2016-01-15 2016-01-15 一种多芯电工缆线 Pending CN105632582A (zh)