CN105623494A - Quick-dry deep red paint for metal - Google Patents
Quick-dry deep red paint for metal Download PDFInfo
- Publication number
- CN105623494A CN105623494A CN201610178970.XA CN201610178970A CN105623494A CN 105623494 A CN105623494 A CN 105623494A CN 201610178970 A CN201610178970 A CN 201610178970A CN 105623494 A CN105623494 A CN 105623494A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- red
- metal
- pure water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses quick-dry deep red paint for metal. The paint comprises pure water, pigment permanent red F4R, light fast scarlet BBN, molybdate red 107, sodium pentachlorophenate, a polyamide resin liquid, ethylene glycol monobutyl ether, n-octyl alcohol, tricresyl phosphate, methylcellulose, montmorillonoid, polyethylene microcrystalline wax and sodium orthophosphate. The metal paint is bright in color and high in tinting strength; the expressive force reaches up to 92-95%; the metal paint is full-dry within 1 second and is low in cost; and the metal paint does not go bad after being stored for 8-12 months.
Description
Technical field
The present invention relates to a kind of metal paint, particularly relate to a kind of dark red paint of metal quick-drying.
Background technology
Metal baking finish is a kind of industrial finish. It is divided into water-based metal baking vanish and oiliness metal baking finish two kinds. Water-based metal baking vanish is a kind of environmental protection paint, take water as solvent, and oiliness metal baking finish is then take organic solvent as solvent. Keeping the appearance of metallic paint, waxing is indispensable. But frequent waxing, simply do not wax and the wax of supertition import, it is all imappropriate in fact. Owing to the performance of various car wax is different, its effect is also different with effect, so must be prudent when selecting. Select improper not only to protect vehicle body, car paint variable color can be made on the contrary. Generally, should according to the effect of car wax, feature, the combined factors such as the running environment of the newness degree of vehicle, car paint color and vehicle are considered.
When spraying paint, it is noted that the going out that paint amount, air output, spray fabric width be narrow and walk speed and distance during spray of the instrument that sprays paint, these parameters are the same with paint application viscosity, all adjustable fogging degree. Fogging degree is required different by different paint. Fogging degree is different, can cause the difference of same paint application out color, gloss, decorative pattern, arrangement effect. It is atomized the too end, it is possible to paint film is uneven, the flat not good enough or contracting pin hole eye of stream; Be atomized excessive, may loss of gloss coarse.
It is Polytetrafluoroetylene that high temperature baking vanish has another name called the English full name of Teflon (telon), is called for short Teflon, PTFE, F4 etc. Teflon high-performance special coating take tetrafluoroethylene as the fluoro coatings of matrix resin, English name is Teflon, because pronunciation, usually it is referred to as again Teflon, iron rich dragon, Teflon, teflon etc. (being all the transliteration of Teflon). Teflon (Teflon) coating is a kind of unique high-performance coating, combine insulation stability and the low frictional properties of thermotolerance, unreactiveness and excellence, having the comprehensive advantage that other coating cannot contend with, the handiness of its application makes it can for the product of nearly all shape and size.
Summary of the invention
The technical problem solved: for above-mentioned metal with paint not waterproof, the shortcoming such as dry slow, period of storage is short, glossiness is low and expressive force is poor, it is provided that a kind of dark red paint of metal quick-drying.
Technical scheme: a kind of dark red paint of metal quick-drying, its composition is taking mass fraction representation as pure water 100 parts, forever solid red F4R5-9 part, light-resistant scarlet BBN 4-8 part, 107 molybdenum red 2-6 parts, sodium pentachlorophenate 1-3 part, polyamide resin liquid 20-40 part, ethylene glycol monobutyl ether 1-5 part, n-Octanol 1-5 part, Tritolyl Phosphate 2-8 part, methylcellulose gum 2-4 part, polynite 2-10 part, polyethylene Microcrystalline Wax 4-16 part, ortho-phosphoric acid sodium 0.1-0.8 part.
As a preferred technical solution of the present invention: described metal quick-drying dark red paint composition is taking mass fraction representation as pure water 100 parts, solid red F4R6-8 part forever, light-resistant scarlet BBN 5-7 part, 107 molybdenum red 3-5 parts, sodium pentachlorophenate 1.5-2.5 part, polyamide resin liquid 25-35 part, ethylene glycol monobutyl ether 2-4 part, n-Octanol 2-4 part, Tritolyl Phosphate 3-7 part, methylcellulose gum 2.5-3.5 part, polynite 4-8 part, polyethylene Microcrystalline Wax 6-14 part, ortho-phosphoric acid sodium 0.3-0.5 part.
As a preferred technical solution of the present invention: described metal quick-drying dark red paint composition by: pure water 100 parts of mass fraction representation, solid red F4R6 part, light-resistant scarlet BBN 5 parts, 107 molybdenum red 3 parts, sodium pentachlorophenate 1.5 parts, polyamide resin liquid 25 parts, ethylene glycol monobutyl ether 2 parts, n-Octanol 2 parts, Tritolyl Phosphate 3 parts, methylcellulose gum 2.5 parts, polynite 4 parts, polyethylene Microcrystalline Wax 6 parts, 0.3 part, ortho-phosphoric acid sodium forever.
As a preferred technical solution of the present invention: described metal quick-drying dark red paint composition by: pure water 100 parts of mass fraction representation, solid red F4R8 part, light-resistant scarlet BBN 7 parts, 107 molybdenum red 5 parts, sodium pentachlorophenate 2.5 parts, polyamide resin liquid 35 parts, ethylene glycol monobutyl ether 4 parts, n-Octanol 4 parts, Tritolyl Phosphate 7 parts, methylcellulose gum 3.5 parts, polynite 8 parts, polyethylene Microcrystalline Wax 14 parts, 0.5 part, ortho-phosphoric acid sodium forever.
As a preferred technical solution of the present invention: described metal quick-drying dark red paint composition by: pure water 100 parts of mass fraction representation, solid red F4R7 part, light-resistant scarlet BBN 6 parts, 107 molybdenum red 4 parts, sodium pentachlorophenate 2 parts, polyamide resin liquid 30 parts, ethylene glycol monobutyl ether 3 parts, n-Octanol 3 parts, Tritolyl Phosphate 5 parts, methylcellulose gum 3 parts, polynite 5 parts, polyethylene Microcrystalline Wax 10 parts, 0.4 part, ortho-phosphoric acid sodium forever.
Useful effect: the dark red paint of metal quick-drying provided by the invention, metal is bright in colour with paint, strong coloring force, and expressive force, up to absolutely dry in 92%-95%, 1s and with low cost, store 8-12 month and never degenerates.
Embodiment
Set forth the content of the present invention by the following examples in further detail.
Embodiment 1:
A kind of dark red paint of metal quick-drying, its composition is taking mass fraction representation as pure water 100 parts, forever solid red F4R5 part, light-resistant scarlet BBN 4 parts, 107 molybdenum red 2 parts, sodium pentachlorophenate 1 part, polyamide resin liquid 20 parts, ethylene glycol monobutyl ether 1 part, n-Octanol 1 part, Tritolyl Phosphate 2 parts, methylcellulose gum 2 parts, polynite 2 parts, polyethylene Microcrystalline Wax 4 parts, 0.1 part, ortho-phosphoric acid sodium.
The pure water of n-Octanol, polyethylene Microcrystalline Wax, methylcellulose gum, ortho-phosphoric acid sodium and 2/3rds mass parts is loaded in reactor, with reflux exchanger on reactor, start after opening reflux exchanger water coolant to stir, then polyamide resin liquid, sodium pentachlorophenate and ethylene glycol monobutyl ether is added, heating is stopped after being warming up to 60 DEG C, continue to stir, after insulation 3h, cool the temperature to 40 DEG C; Then add solid red F4R, light-resistant scarlet BBN and 107 molybdenum reds forever to stir evenly, add Tritolyl Phosphate and polynite; Finally add remaining pure water, stir after evenly, filter and obtain the dark red paint of metal quick-drying.
Metal is bright in colour with paint, strong coloring force, and expressive force, up to absolutely dry in 92%, 1s and with low cost, store and never degenerates for 8 months.
Embodiment 2:
A kind of dark red paint of metal quick-drying, its composition is taking mass fraction representation as pure water 100 parts, forever solid red F4R9 part, light-resistant scarlet BBN 8 parts, 107 molybdenum red 6 parts, sodium pentachlorophenate 3 parts, polyamide resin liquid 40 parts, ethylene glycol monobutyl ether 5 parts, n-Octanol 5 parts, Tritolyl Phosphate 8 parts, methylcellulose gum 4 parts, polynite 10 parts, polyethylene Microcrystalline Wax 16 parts, 0.8 part, ortho-phosphoric acid sodium.
The pure water of n-Octanol, polyethylene Microcrystalline Wax, methylcellulose gum, ortho-phosphoric acid sodium and 2/3rds mass parts is loaded in reactor, with reflux exchanger on reactor, start after opening reflux exchanger water coolant to stir, then polyamide resin liquid, sodium pentachlorophenate and ethylene glycol monobutyl ether is added, heating is stopped after being warming up to 60 DEG C, continue to stir, after insulation 3h, cool the temperature to 40 DEG C; Then add solid red F4R, light-resistant scarlet BBN and 107 molybdenum reds forever to stir evenly, add Tritolyl Phosphate and polynite; Finally add remaining pure water, stir after evenly, filter and obtain the dark red paint of metal quick-drying.
Metal is bright in colour with paint, strong coloring force, and expressive force, up to absolutely dry in 94%, 1s and with low cost, store and never degenerates for 10 months.
Embodiment 3:
A kind of dark red paint of metal quick-drying, its composition is taking mass fraction representation as pure water 100 parts, forever solid red F4R7 part, light-resistant scarlet BBN 6 parts, 107 molybdenum red 4 parts, sodium pentachlorophenate 2 parts, polyamide resin liquid 30 parts, ethylene glycol monobutyl ether 3 parts, n-Octanol 3 parts, Tritolyl Phosphate 5 parts, methylcellulose gum 3 parts, polynite 5 parts, polyethylene Microcrystalline Wax 10 parts, 0.4 part, ortho-phosphoric acid sodium.
The pure water of n-Octanol, polyethylene Microcrystalline Wax, methylcellulose gum, ortho-phosphoric acid sodium and 2/3rds mass parts is loaded in reactor, with reflux exchanger on reactor, start after opening reflux exchanger water coolant to stir, then polyamide resin liquid, sodium pentachlorophenate and ethylene glycol monobutyl ether is added, heating is stopped after being warming up to 60 DEG C, continue to stir, after insulation 3h, cool the temperature to 40 DEG C; Then add solid red F4R, light-resistant scarlet BBN and 107 molybdenum reds forever to stir evenly, add Tritolyl Phosphate and polynite; Finally add remaining pure water, stir after evenly, filter and obtain the dark red paint of metal quick-drying.
Metal is bright in colour with paint, strong coloring force, and expressive force, up to absolutely dry in 95%, 1s and with low cost, store and never degenerates for 12 months.
Above-described embodiment is just for setting forth the content of the present invention, instead of restriction, and the therefore any change in the implication suitable with the claim book of the present invention and scope, all it is believed that be included in the scope of claim book.
Claims (5)
1. the dark red paint of metal quick-drying, it is characterised in that: its composition by: pure water 100 parts of mass fraction representation, solid red F4R5-9 part, light-resistant scarlet BBN 4-8 part, 107 molybdenum red 2-6 parts, sodium pentachlorophenate 1-3 part, polyamide resin liquid 20-40 part, ethylene glycol monobutyl ether 1-5 part, n-Octanol 1-5 part, Tritolyl Phosphate 2-8 part, methylcellulose gum 2-4 part, polynite 2-10 part, polyethylene Microcrystalline Wax 4-16 part, ortho-phosphoric acid sodium 0.1-0.8 part forever.
2. a kind of dark red paint of metal quick-drying according to claim 1, it is characterised in that: its composition is taking mass fraction representation as pure water 100 parts, forever solid red F4R6-8 part, light-resistant scarlet BBN 5-7 part, 107 molybdenum red 3-5 parts, sodium pentachlorophenate 1.5-2.5 part, polyamide resin liquid 25-35 part, ethylene glycol monobutyl ether 2-4 part, n-Octanol 2-4 part, Tritolyl Phosphate 3-7 part, methylcellulose gum 2.5-3.5 part, polynite 4-8 part, polyethylene Microcrystalline Wax 6-14 part, ortho-phosphoric acid sodium 0.3-0.5 part.
3. a kind of dark red paint of metal quick-drying according to claim 1, it is characterised in that: its composition is taking mass fraction representation as pure water 100 parts, forever solid red F4R6 part, light-resistant scarlet BBN 5 parts, 107 molybdenum red 3 parts, sodium pentachlorophenate 1.5 parts, polyamide resin liquid 25 parts, ethylene glycol monobutyl ether 2 parts, n-Octanol 2 parts, Tritolyl Phosphate 3 parts, methylcellulose gum 2.5 parts, polynite 4 parts, polyethylene Microcrystalline Wax 6 parts, 0.3 part, ortho-phosphoric acid sodium.
4. a kind of dark red paint of metal quick-drying according to claim 1, it is characterised in that: its composition is taking mass fraction representation as pure water 100 parts, forever solid red F4R8 part, light-resistant scarlet BBN 7 parts, 107 molybdenum red 5 parts, sodium pentachlorophenate 2.5 parts, polyamide resin liquid 35 parts, ethylene glycol monobutyl ether 4 parts, n-Octanol 4 parts, Tritolyl Phosphate 7 parts, methylcellulose gum 3.5 parts, polynite 8 parts, polyethylene Microcrystalline Wax 14 parts, 0.5 part, ortho-phosphoric acid sodium.
5. a kind of dark red paint of metal quick-drying according to claim 1, it is characterised in that: its composition is taking mass fraction representation as pure water 100 parts, forever solid red F4R7 part, light-resistant scarlet BBN 6 parts, 107 molybdenum red 4 parts, sodium pentachlorophenate 2 parts, polyamide resin liquid 30 parts, ethylene glycol monobutyl ether 3 parts, n-Octanol 3 parts, Tritolyl Phosphate 5 parts, methylcellulose gum 3 parts, polynite 5 parts, polyethylene Microcrystalline Wax 10 parts, 0.4 part, ortho-phosphoric acid sodium.