CN105623330A - 一种丙烯酸丁酯涂料 - Google Patents
一种丙烯酸丁酯涂料 Download PDFInfo
- Publication number
- CN105623330A CN105623330A CN201410585692.0A CN201410585692A CN105623330A CN 105623330 A CN105623330 A CN 105623330A CN 201410585692 A CN201410585692 A CN 201410585692A CN 105623330 A CN105623330 A CN 105623330A
- Authority
- CN
- China
- Prior art keywords
- butyl acrylate
- solvent
- polyester resin
- polyacrylic acid
- ethyl cellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种丙烯酸丁酯涂料,以下重量配置而成,包括丙烯酸丁酯15-20kg、二氧化硅10-15kg、乙基纤维素5-10kg、聚酯树脂10-15kg、阻燃剂5-10kg、聚丙烯酸5-10kg、碳化硅5-10kg、氧化铝5-10kg、三聚氰胺15-20kg、溶剂800-1000kg。本发明制备方法具体如下:首先按照各组分原料称取原料,然后将溶剂倒入反应釜中,加热至30-40℃时,加入丙烯酸丁酯、二氧化硅、乙基纤维素、聚酯树脂、阻燃剂、聚丙烯酸、碳化硅、氧化铝、三聚氰胺搅拌,再升温至90℃,保温30分后,即得成品。本发明优点为无毒无味无腐蚀,对坏境无污染,且封闭性好,强度高,无裂纹。
Description
技术领域
本发明涉及涂料领域,特别涉及一种适用于建筑耐高温用涂料及制备方法。
背景技术
涂层对基体材料形成保护,但由于常规的热喷涂技术由于技术本身的原因,很难形成完全致密的涂层,涂层孔隙的存在不仅降低了耐磨效果,对耐腐蚀保护更是致命缺陷。因此尽可能的减少涂层的孔隙或对涂层孔隙进行封闭,以达到将酸、碱、盐与基材隔绝的目的是很多专家努力的方向。
发明内容
本发明的目的在于提供一种绝热性能好、导热系数低、性能稳定、价格低廉、无毒无味的保温原料制成闭孔微孔结构的一种丙烯酸丁酯涂料。
一种丙烯酸丁酯涂料,以下重量配置而成,包括丙烯酸丁酯15—20kg、二氧化硅10—15kg、乙基纤维素5—10kg、聚酯树脂10—15kg、阻燃剂5—10kg、聚丙烯酸5—10kg、碳化硅5—10kg、氧化铝5—10kg、三聚氰胺15—20kg、溶剂800—1000kg。
本发明制备方法具体如下:首先按照各组分原料称取原料,然后将溶剂倒入反应釜中,加热至30—40℃时,加入丙烯酸丁酯、二氧化硅、乙基纤维素、聚酯树脂、阻燃剂、聚丙烯酸、碳化硅、氧化铝、三聚氰胺搅拌,再升温至90℃,保温30分后,即得成品。
本发明优点为无毒无味无腐蚀,对坏境无污染,施工造价低于苯板的30—50%,不怕雨浸日晒和寒冻,同墙体及外罩三聚氰胺砂浆保护层结合性好,使用寿命大于30年可适应任何形状复杂界面上随物成形,且封闭性好,强度高,无裂纹。
具体实施例
实施例一
一种丙烯酸丁酯涂料,以下重量配置而成,包括丙烯酸丁酯18kg、二氧化硅13kg、乙基纤维素8kg、聚酯树脂13kg、阻燃剂8kg、聚丙烯酸8kg、碳化硅8kg、氧化铝8kg、三聚氰胺18kg、溶剂900kg。
本发明制备方法具体如下:首先按照各组分原料称取原料,然后将溶剂倒入反应釜中,加热至30—40℃时,加入丙烯酸丁酯、二氧化硅、乙基纤维素、聚酯树脂、阻燃剂、聚丙烯酸、碳化硅、氧化铝、三聚氰胺搅拌,再升温至90℃,保温30分后,即得成品。
实施例二
实施例二与实施一基本相同,其不同之处是以下重量配置为丙烯酸丁酯15kg、二氧化硅10kg、乙基纤维素5kg、聚酯树脂10kg、阻燃剂5kg、聚丙烯酸5kg、碳化硅5kg、氧化铝5kg、三聚氰胺15kg、溶剂800kg。
实施例三
实施例三与实施一基本相同,其不同之处是以下重量配置为丙烯酸丁酯20kg、二氧化硅15kg、乙基纤维素10kg、聚酯树脂15kg、阻燃剂10kg、聚丙烯酸10kg、碳化硅10kg、氧化铝10kg、三聚氰胺20kg、溶剂1000kg。
Claims (2)
1.一种丙烯酸丁酯涂料,其特征是以下重量配置而成,包括丙烯酸丁酯15—20kg、二氧化硅10—15kg、乙基纤维素5—10kg、聚酯树脂10—15kg、阻燃剂5—10kg、聚丙烯酸5—10kg、碳化硅5—10kg、氧化铝5—10kg、三聚氰胺15—20kg、溶剂800—1000kg;本发明制备方法具体如下:首先按照各组分原料称取原料,然后将溶剂倒入反应釜中,加热至30—40℃时,加入丙烯酸丁酯、二氧化硅、乙基纤维素、聚酯树脂、阻燃剂、聚丙烯酸、碳化硅、氧化铝、三聚氰胺搅拌,再升温至90℃,保温30分后,即得成品。
2.根据权利要求1所述的一种丙烯酸丁酯涂料,其特征在于所述的重量配置为丙烯酸丁酯18kg、二氧化硅13kg、乙基纤维素8kg、聚酯树脂13kg、阻燃剂8kg、聚丙烯酸8kg、碳化硅8kg、氧化铝8kg、三聚氰胺18kg、溶剂900kg。