CN105623146A - PVC (polyvinyl chloride) rubber formula - Google Patents
PVC (polyvinyl chloride) rubber formula Download PDFInfo
- Publication number
- CN105623146A CN105623146A CN201610062346.3A CN201610062346A CN105623146A CN 105623146 A CN105623146 A CN 105623146A CN 201610062346 A CN201610062346 A CN 201610062346A CN 105623146 A CN105623146 A CN 105623146A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvc
- rubber
- mixed solvent
- polyvinyl chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a PVC (polyvinyl chloride) rubber formula. The PVC rubber formula comprises 65-85 parts of PVC resin, 1-20 parts of mixed solvent, 0-10 parts of catalyst, 0-5 part of plasticizer, 0-5 parts of stabilizer, 0-5 parts of lubricant, 0-20 parts of foaming agent and 10-40 parts of calcium powder. All properties of PVC rubber prepared by the PVC rubber formula can be enhanced greatly, and an adhesion property of the PVC rubber can be improved to enable the rubber and an object to fit more tightly.
Description
Technical field
The present invention relates to rubber and manufacture field, particularly relate to the formula of a kind of PVC rubber.
Background technology
Rubber is the important component part of Sound-proof material, usually it is pasted onto the surface of Sound-proof material, existing rubber structure is relatively simple, performance is relatively low, and especially viscous stickiness can be relatively low, uses for a long time, its viscous stickiness can be more and more lower, and meeting the viscous stickiness of water can be able to lose efficacy, therefore, the problem solving this class seems particularly very always.
Summary of the invention
For the deficiencies in the prior art, the invention provides a kind of PVC rubber formula, have mixed solvent by arranging, catalyst, plasticizer, stabilizer, lubricant, foaming agent improve the performance of rubber, the problem relatively low to solve existing rubber quality.
In order to solve the problems referred to above, the invention provides a kind of PVC rubber formula, it is characterized in that, the constituent of PVC rubber includes: polyvinyl chloride resin 65-85 part, mixed solvent 1-20 part, catalyst 0-10 part, plasticizer 0-5 part, stabilizer 0-5 part, lubricant 0-5 part, foaming agent 0-20 part, calcium powder 10-40 part.
Further improvement is that: described mixed solvent is mixed after being sufficiently stirred for by 60��70% dimethylbenzene, 25% Ketohexamethylene, 5��15% dibutyl phthalates.
Further improvement is that: the constituent of described PVC rubber includes: polyvinyl chloride resin 77 parts, mixed solvent 10 parts, catalyst 5 parts, plasticizer 2.5 parts, stabilizer 2.5 parts, lubricant 2.5 parts, foaming agent 2.5 parts, calcium powder 20 parts.
Further improvement is that: described mixed solvent is mixed after being sufficiently stirred for by 65% dimethylbenzene, 25% Ketohexamethylene, 10% dibutyl phthalate.
The invention has the beneficial effects as follows: the PVC rubber utilizing this formula to make can greatly strengthen the properties of rubber, and improves the viscous stickiness energy of rubber so that rubber and thing to be pasted laminating are tighter.
Detailed description of the invention
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the present invention being further described, the present embodiment is only used for explaining the present invention, is not intended that limiting the scope of the present invention.
Embodiment one
A kind of PVC rubber formula, the constituent of PVC rubber includes: polyvinyl chloride resin 65 parts, mixed solvent 1 part, catalyst 1 part, plasticizer 1 part, stabilizer 1 part, lubricant 1 part, foaming agent 1 part, calcium powder 10 parts.
Described mixed solvent is mixed after being sufficiently stirred for by 60 dimethylbenzene, 25% Ketohexamethylene, 5 dibutyl phthalates.
Embodiment two
A kind of PVC rubber formula, the constituent of PVC rubber includes: polyvinyl chloride resin 85 parts, mixed solvent 20 parts, catalyst 10 parts, plasticizer 5 parts, stabilizer 5 parts, lubricant 5 parts, foaming agent 20 parts, calcium powder 40 parts.
Described mixed solvent is mixed after being sufficiently stirred for by 70% dimethylbenzene, 25% Ketohexamethylene, 15% dibutyl phthalate.
Embodiment three
A kind of PVC rubber formula, the constituent of described PVC rubber includes: polyvinyl chloride resin 77 parts, mixed solvent 10 parts, catalyst 5 parts, plasticizer 2.5 parts, stabilizer 2.5 parts, lubricant 2.5 parts, foaming agent 2.5 parts, calcium powder 20 parts.
A kind of PVC rubber formula as claimed in claim 1, it is characterised in that: described mixed solvent is mixed after being sufficiently stirred for by 65% dimethylbenzene, 25% Ketohexamethylene, 10% dibutyl phthalate.
Utilize the PVC rubber that this formula is made can greatly strengthen the properties of rubber, and improve the viscous stickiness energy of rubber so that rubber and thing to be pasted laminating are tighter.
Claims (4)
1. a PVC rubber formula, it is characterised in that the constituent of PVC rubber includes: polyvinyl chloride resin 65-85 part, mixed solvent 1-20 part, catalyst 0-10 part, plasticizer 0-5 part, stabilizer 0-5 part, lubricant 0-5 part, foaming agent 0-20 part, calcium powder 10-40 part.
2. a kind of PVC rubber formula as claimed in claim 1, it is characterised in that: described mixed solvent is mixed after being sufficiently stirred for by 60��70% dimethylbenzene, 25% Ketohexamethylene, 5��15% dibutyl phthalates.
3. a kind of PVC rubber formula as claimed in claim 1, it is characterised in that: the constituent of described VC rubber includes: polyvinyl chloride resin 77 parts, mixed solvent 10 parts, catalyst 5 parts, plasticizer 2.5 parts, stabilizer 2.5 parts, lubricant 2.5 parts, foaming agent 2.5 parts, calcium powder 20 parts.
4. a kind of PVC rubber formula as claimed in claim 1, it is characterised in that: described mixed solvent is mixed after being sufficiently stirred for by 65% dimethylbenzene, 25% Ketohexamethylene, 10% dibutyl phthalate.