CN105671960A - New environmentally friendly advertising cloth - Google Patents
New environmentally friendly advertising cloth Download PDFInfo
- Publication number
- CN105671960A CN105671960A CN201410657751.0A CN201410657751A CN105671960A CN 105671960 A CN105671960 A CN 105671960A CN 201410657751 A CN201410657751 A CN 201410657751A CN 105671960 A CN105671960 A CN 105671960A
- Authority
- CN
- China
- Prior art keywords
- parts
- lubricant
- silica
- ethyl acetate
- urethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to advertising cloth, and especially relates to new environmentally friendly advertising cloth including base cloth, a coating on both sides of the base cloth, and a PVC film, the PVC film is on one side of the coating, which is the other side of connection side of the coating and the base cloth, and the coating comprises, by mass, 30-60 parts of polyacrylic acid resin, 10-15 parts of silica, 20-30 parts of titanium white pulp, 3-8 parts of a lubricant, 8-15 parts of a plasticizer, 1-3 parts of a dispersant, 10-20 parts of ethyl acetate and 20-30 parts of polyurethane. The new environmentally friendly advertising cloth with the above structure is long in service life and simple in production process, and material stain-resistance and waterproof and fire-retardant and other properties can be reached by addition of different additives.
Description
Technical field
The present invention relates to a kind of advertisement cloth, particularly a kind of novel environment friendly advertisement cloth.
Background technology
Advertising is the industry that information upgrades fast, and the time limit of coming into operation of general outdoor advertising is extremely short, long then half a year, several days at least, it may also be useful to polyvinyl chloride coating folder screen cloth is particularly thorny as the process after a procedure of numerial code spray drawing advertisement cloth. Polyvinyl chloride coating folder screen cloth is taking terylene (PET) cloth as base cloth, is the polyvinyl chloride folder screen cloth at face and the end through coating polyvinyl chloride film. Polyvinyl chloride is bright in colour, corrosion-resistant, firm and durable, but thermostability and photostabilization are poor, more than 100 DEG C or long-time exposure in sunshine start to decomposite hydrogenchloride, need to add some poisonous subsidiary material such as stablizer, softening agent, antiaging agent to strengthen its thermotolerance, toughness, ductility etc. when therefore manufacturing plastics.
China CN102744938A discloses a kind of polypropylene spun fabric environment protection advertisement cloth, adopts polypropylene to be main starting material, makes taking polypropylene cloth as base cloth, there is the novel environment friendly advertisement cloth of multiple characteristic, polypropylene base cloth layer can be comprised, chromatograph in waterproof, polymer ink absorbing layer.
Summary of the invention
The technical issues that need to address of the present invention are to provide a kind of novel environment friendly advertisement cloth.
For solving above-mentioned technical problem, the novel environment friendly advertisement cloth of the present invention comprises the coating of Ji Bu, base cloth both sides, the PVC film of another side that coating is connected with base cloth, the mass fraction of described coating is composed as follows: polyacrylic resin 30-60 part, silica 1 0-15 part, titanium dioxide slurry 20-30 part, lubricant 3-8 part, softening agent 8-15 part, dispersion agent 1-3 part, ethyl acetate 10-20 part, urethane 20-30 part.
Further, the mass fraction of described coating is composed as follows: polyacrylic resin 40 parts, silica 12 parts, titanium dioxide slurry 20 parts, lubricant 8 parts, 10 parts, softening agent, dispersion agent 3 parts, ethyl acetate 15 parts, urethane 25 parts.
Further, described lubricant is the one in hydr ocarbon-based grease, inorganic lubricant fat and organic lubricating grease.
Further, described polyacrylic resin 30 parts, silica 10 part, titanium dioxide slurry 30 parts, lubricant 3 parts, 15 parts, softening agent, dispersion agent 2 parts, ethyl acetate 12 parts, urethane 22 parts.
Further, polyacrylic resin 45 parts, silica 11 part, titanium dioxide slurry 24 parts, lubricant 5 parts, 11 parts, softening agent, dispersion agent 3 parts, ethyl acetate 15 parts, urethane 27 parts.
Further, polyacrylic resin 50 parts, silica 1 03 part, titanium dioxide slurry 22 parts, lubricant 3 parts, 15 parts, softening agent, dispersion agent 2 parts, ethyl acetate 16 parts, urethane 26 parts.
Further, polyacrylic resin 55 parts, silica 14 parts, titanium dioxide slurry 25 parts, lubricant 6 parts, 13 parts, softening agent, dispersion agent 2 parts, ethyl acetate 14 parts, urethane 25 parts.
Adopting after said structure, the novel environment friendly advertisement cloth long service life of the present invention, production technique is simple, reaches the anti-dirt of material, waterproof, the performance such as fire-retardant by different additive simultaneously.
Embodiment
Enforcement mode one:
Polyacrylic resin 40 parts, silica 12 parts, titanium dioxide slurry 20 parts, lubricant 8 parts, 10 parts, softening agent, dispersion agent 3 parts, ethyl acetate 15 parts, urethane 25 parts.
Enforcement mode two:
Described polyacrylic resin 30 parts, silica 10 part, titanium dioxide slurry 30 parts, lubricant 3 parts, 15 parts, softening agent, dispersion agent 2 parts, ethyl acetate 12 parts, urethane 22 parts.
Enforcement mode three:
Polyacrylic resin 45 parts, silica 11 part, titanium dioxide slurry 24 parts, lubricant 5 parts, 11 parts, softening agent, dispersion agent 3 parts, ethyl acetate 15 parts, urethane 27 parts.
Enforcement mode four:
Polyacrylic resin 50 parts, silica 1 03 part, titanium dioxide slurry 22 parts, lubricant 3 parts, 15 parts, softening agent, dispersion agent 2 parts, ethyl acetate 16 parts, urethane 26 parts.
Enforcement mode five:
Polyacrylic resin 55 parts, silica 14 parts, titanium dioxide slurry 25 parts, lubricant 6 parts, 13 parts, softening agent, dispersion agent 2 parts, ethyl acetate 14 parts, urethane 25 parts.
Although the foregoing describing the specific embodiment of the present invention; but those skilled in the art are to be understood that; these are only illustrate; present embodiment can be made various changes or modifications; and not deviating from principle and the essence of the present invention, protection scope of the present invention is only defined by the appended claims.
Claims (7)
1. a novel environment friendly advertisement cloth, comprise the coating of Ji Bu, base cloth both sides, the PVC film of another side that coating is connected with base cloth, it is characterized in that, the mass fraction of described coating is composed as follows: polyacrylic resin 30-60 part, silica 1 0-15 part, titanium dioxide slurry 20-30 part, lubricant 3-8 part, softening agent 8-15 part, dispersion agent 1-3 part, ethyl acetate 10-20 part, urethane 20-30 part.
2. according to novel environment friendly advertisement cloth according to claim 1, it is characterised in that: the mass fraction of described coating is composed as follows: polyacrylic resin 40 parts, silica 12 parts, titanium dioxide slurry 20 parts, lubricant 8 parts, 10 parts, softening agent, dispersion agent 3 parts, ethyl acetate 15 parts, urethane 25 parts.
3. according to novel environment friendly advertisement cloth according to claim 1, it is characterised in that: described lubricant is the one in hydr ocarbon-based grease, inorganic lubricant fat and organic lubricating grease.
4. according to novel environment friendly advertisement cloth according to claim 1, it is characterised in that: described polyacrylic resin 30 parts, silica 10 part, titanium dioxide slurry 30 parts, lubricant 3 parts, 15 parts, softening agent, dispersion agent 2 parts, ethyl acetate 12 parts, urethane 22 parts.
5. according to novel environment friendly advertisement cloth according to claim 1, it is characterised in that: polyacrylic resin 45 parts, silica 11 part, titanium dioxide slurry 24 parts, lubricant 5 parts, 11 parts, softening agent, dispersion agent 3 parts, ethyl acetate 15 parts, urethane 27 parts.
6. according to novel environment friendly advertisement cloth according to claim 1, it is characterised in that: polyacrylic resin 50 parts, silica 1 03 part, titanium dioxide slurry 22 parts, lubricant 3 parts, 15 parts, softening agent, dispersion agent 2 parts, ethyl acetate 16 parts, urethane 26 parts.
7. according to novel environment friendly advertisement cloth according to claim 1, it is characterised in that: polyacrylic resin 55 parts, silica 14 parts, titanium dioxide slurry 25 parts, lubricant 6 parts, 13 parts, softening agent, dispersion agent 2 parts, ethyl acetate 14 parts, urethane 25 parts.