CN105620162B - The manufacturing method of glof club head/club head component exterior view coloured silk - Google Patents
The manufacturing method of glof club head/club head component exterior view coloured silk Download PDFInfo
- Publication number
- CN105620162B CN105620162B CN201410705477.XA CN201410705477A CN105620162B CN 105620162 B CN105620162 B CN 105620162B CN 201410705477 A CN201410705477 A CN 201410705477A CN 105620162 B CN105620162 B CN 105620162B
- Authority
- CN
- China
- Prior art keywords
- club head
- glof
- head component
- glof club
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A kind of manufacturing method of glof club head/club head component exterior view coloured silk contains the following steps：Step (A) prepares one and is formed with a predetermined figure color thermoplastic film and a jig.One glof club head/club head component is placed on the jig by step (B), and heats and softens the thermoplastic film.Step (C) enables the thermoplastic film to fit closely in the surface of the glof club head/club head component.Step (D) makes the predetermined figure coloured silk be indwelling in the surface of the glof club head/club head component.Step (E) keeps the color setting figure being incorporated into as a solidification on the surface of the glof club head/club head component of the predetermined figure color.The glof club head/club head component is separated from each other by step (F) with the jig.Coordinate the design of the jig using the thermoplastic film for being formed with predetermined figure coloured silk, not only processing method is simple, and can be applicable in the glof club head of unlike material to reduce cost.
Description
Technical field
The present invention relates to a kind of manufacturing methods of glof club head, more particularly to a kind of glof club head/club
The manufacturing method of head part exterior view coloured silk.
Background technology
With the raising of national life level, the number for being engaged in golf is just incrementally increased.Consumer is purchasing
Before buying glof club head, other than considering function, it is whether beautiful and there is texture also to consider club head exterior design.
For current glof club head, for appearance tactile impression to be promoted, it will usually be steamed with baking vanish, plating or ion
It plates process for treating surface such as (Physical vapor deposition, PVD) and carries out painting operation in club head surface, make ball
Head surface shows two or more different gloss or color and luster.Then, then with etching or laser carved technology in club head table
Face forms special picture and text or lines, to make the special glof club head of external form.
Not only program is cumbersome for etching or laser carved technology, and since how in curved surface glof club head is, related raising
Etching or laser carved processing complexity, while also improving the manufacturing cost of glof club head.
In addition, existing glof club head material selects composite fibre material or metal material to be made mostly.In general,
The glof club head of metal material can select etching or the special picture and text of laser carved processing or lines, but composite fibre material
Glof club head for fear of material limit, cause processing method different with the glof club head of metal material.
For this purpose, the glof club head that manufacturer must be directed to unlike material selects different processing methods, it is not only inconvenient also to increase factory
The manufacturing cost of quotient.
Invention content
The purpose of the present invention is to provide a kind of glof club head/club head component tables that can be applicable in a variety of unlike materials
The manufacturing method of face figure coloured silk.
The manufacturing method of glof club head of the present invention/club head component exterior view coloured silk, comprises the steps of：(A) it prepares
There are one the color thermoplastic films of predetermined figure and one to be used to position the glof club head/club head component for one formation
Jig, the jig there are one and the glof club head/matched ontology of club head component, (B) by the glof club head/
Club head component is placed on the ontology of the jig, and heats and softens the thermoplastic film, and (C) is by the jig and after heating and softening
The thermoplastic film be set in the molding die of a hollow form, to form negative pressure by being vacuumized in the molding die, then
Gas is poured into the molding die again, environment in the molding die is made to be converted between negative pressure and positive pressure, makes the height using air pressure
Golf ball head/club head component can be fitted closely on the ontology, while the thermoplastic film also being enable to fit closely in this
The surface of glof club head/club head component, (D) open the molding die by the thermoplastic film and the golf club
Head/club head component is separated from each other, and the predetermined color indwelling of figure is in the surface of the glof club head/club head component, (E) profit
Make the color surface for becoming a solidification and being incorporated into the glof club head/club head component of the predetermined figure with UV-curing technology
On setting figure it is color, and the glof club head/club head component and the ontology of the jig be separated from each other by (F).
The manufacturing method of glof club head of the present invention/club head component exterior view coloured silk, this in the step (E) are set
Following layer that the fixed color tool of figure is incorporated into there are one solidification on the surface of the glof club head/club head component, one be laminated in
Ink layer on the following layer and a hardened layer being laminated on the ink layer, the solidification be incorporated into the glof club head/
The thickness of setting figure coloured silk on the surface of club head component is between 0.1um between 60um.
Another object of the present invention is also to provide a kind of glof club head/club head component that can be applicable in various material
The manufacturing method of exterior view coloured silk.
The manufacturing method of glof club head of the present invention/club head component exterior view coloured silk, comprises the steps of：(A) it prepares
There are one the color thermoplastic films of predetermined figure and one to be used to position the glof club head/club head component for one formation
Jig, the jig there are one and the glof club head/matched ontology of club head component, (B) by the glof club head/
Club head component is placed on the ontology of the jig, and heats and softens the thermoplastic film, and (C) is by the jig and after heating and softening
The thermoplastic film be set in the molding die of a hollow form, to form negative pressure by being vacuumized in the molding die, then
Gas is poured into the molding die again, environment in the molding die is made to be converted between negative pressure and positive pressure, makes the height using air pressure
Golf ball head/club head component can be fitted closely on the ontology, while the thermoplastic film also being enable to fit closely in this
The surface of glof club head/club head component, (D) open the molding die, using material removal technique that the predetermined figure is color
Outer thermoplastic film excision, and form a solidification and be incorporated into setting on the surface of the glof club head/club head component
Fixed figure is color, and the glof club head/club head component and the ontology of the jig are separated from each other by (E).
The manufacturing method of glof club head of the present invention/club head component exterior view coloured silk, this in the step (D) are set
Following layer that the fixed color tool of figure is incorporated into there are one solidification on the surface of the glof club head/club head component, one be laminated in
Ink layer on the following layer and a thermoplastic film layer being laminated on the ink layer, and the solidification is incorporated into the Gao Er
The thickness of setting figure coloured silk on the surface of husband's club head/club head component is between 60um between 500um.
The beneficial effects of the present invention are：Coordinate the design of the jig using the thermoplastic film for being formed with predetermined figure coloured silk,
It, can be directly in the golf with pressure transfer forming technique and subsequent UV-curing technology/material removal technique
Molding setting figure is color on head/club head parts surface, and not only processing method is simple, and can be applicable in unlike material effectively to reduce
Cost.
Description of the drawings
Fig. 1 is a flow chart, illustrates the of the manufacturing method of glof club head of the present invention/club head component exterior view coloured silk
One embodiment；
Fig. 2 is a schematic diagram, illustrates the aspect of the predetermined figure coloured silk in the first embodiment on the thermoplastic film；
Fig. 3 is a schematic diagram, illustrates the aspect of setting figure coloured silk in the first embodiment；
Fig. 4 is a flow chart, illustrates the of the manufacturing method of glof club head of the present invention/club head component exterior view coloured silk
Two embodiments；
Fig. 5 is a schematic diagram, illustrates another aspect of the predetermined figure coloured silk in the second embodiment on the thermoplastic film；And
Fig. 6 is a schematic diagram, illustrates another composition kenel that setting figure is color in the second embodiment.
Specific implementation mode
The following describes the present invention in detail with reference to the accompanying drawings and embodiments.Before the present invention is described in detail, it should note
In the following description content, similar component is indicated with being identically numbered to meaning.
Refering to fig. 1, Fig. 2, glof club head of the present invention/club head component exterior view coloured silk (including figure, word, color
Or combinations of the above) the first embodiment of manufacturing method comprise the steps of：Step 21, it prepares one and is formed with a predetermined figure
The thermoplastic film 3 of coloured silk 31 and one for position the jig 4 of a golf club head part 200, the jig 4 have one and
The 200 matched ontology 41 of golf club head part.
In this present embodiment, which is thickness between 0.12mm to the polyolefin film between 0.15mm
(Polyolefin, PO Film), and the periphery of the ontology 41 or turning point are mostly handled with fillet, and the predetermined figure coloured silk 31 includes
The ink 33 and one that the one hardening material 32, one being incorporated on the thermoplastic film 3 is incorporated on the hardening material 32 is incorporated into the oil
Solid 34 on ink 33, the solid 34 are hot melt adhesive or UV glue, are to select UV glue in this present embodiment.
In addition to illustrate herein, for convenience of description, the present embodiment is said with golf club head part 200
It is bright, can also be to be carried out with entire glof club head, not as long as there is corresponding jig 4 in practical application certainly
It is disclosed and is limited with the present embodiment.
The golf club head part 200 is placed on the ontology 41 of the jig 4 by step 22, and heats and softens the thermoplastic
Property film 3.In this present embodiment, it is that the thermoplastic film 3 is softened with infrared heating.
The jig 4 is set to the molding die 5 of a hollow form by step 23 with the thermoplastic film 3 after heating and softening
Interior, which is to be located at 4 top of jig, then will vacuumize to form negative pressure in the molding die 5, then again will
Gas pours into the molding die 5, and using air pressure official post, the golf club head part 200 can be fitted closely in the ontology 41
On, while the thermoplastic film 3 also being enable to fit closely in the surface of the golf club head part 200.
By the pressure transfer forming technique converted between negative pressure and positive pressure, keep the golf club head part 200 tight
It is closely connected together on the ontology 41, can not only give full play to the ontology 41 support the golf club head part 200 the effect of, moreover it is possible to
It effectively avoids generating packet gas phenomenon between the thermoplastic film 3 and the golf club head part 200, promotes transfer printing molded effect
Fruit and stability.
Refering to fig. 1, Fig. 2, Fig. 3, step 24 opens the molding die 5, by the thermoplastic film 3 and the glof club head
Component 200 is separated from each other, and the predetermined figure coloured silk 31 is indwelling in the surface of the golf club head part 200.Step 25 is profit
Make the predetermined figure coloured silk 31 become a solidification with UV-curing technology to be incorporated on the surface of the golf club head part 200
Setting figure coloured silk 201.
The setting figure coloured silk 201 is incorporated into the following layer on the surface of the golf club head part 200 with a solidification
202, an ink layer 203 and one being laminated on the following layer 202 is laminated in the hardened layer 204 on the ink layer 203, and should
The thickness of setting figure coloured silk 201 is between 0.1um between 60um.
In this present embodiment, UV-curing technology is the predetermined figure coloured silk 31 with ultraviolet light, make the solid 34 at
It is attached to the following layer 202 on the surface of the golf club head part 200 for solidification, while the ink 33 being made to form special color
The ink layer 203 in pool, and the hardening material 32 hardening is made to become the hardened layer 204 for protecting the ink layer 203.And ultraviolet light cures
Not only process efficiency is high for technology, more can effectively reduce pollution without using solvent.
Step 26 is to be separated from each other the ontology 41 of the golf club head part 200 and the jig 4, and then obtaining tool should
The golf club head part 200 of setting figure coloured silk 201.
Coordinate the design of the jig 4 using the thermoplastic film 3 for being formed with predetermined figure coloured silk 31, then skill is molded with pressure transfer
Art and subsequent UV-curing technology can be molded setting figure directly on the glof club head/club head parts surface
Coloured silk 201, not only processing method is simple, and the glof club head/club head component that can be applicable in unlike material is made with effective reduction
Cause this.
Refering to Fig. 4, Fig. 5, the second of the manufacturing method of glof club head of the present invention/club head component exterior view coloured silk implements
Example is generally similar to the first embodiment, and different place is：The predetermined figure coloured silk 31 only one is incorporated into the thermoplasticity
Ink 33 and one on film 3 is incorporated into the solid 34 on the ink 33.In this present embodiment, which is hot melt
Glue.
Therefore, the present embodiment can omit the step 25 (being shown in Fig. 1) in first embodiment, and heat the heat in step 22
When plastic films 3, solid 34 can be made to generate tackness simultaneously, and so that the solid 34 is attached to the Gao Er in step 23
On the surface of husband's club head component 200.
Refering to Fig. 4, Fig. 5, Fig. 6, and after step 24 opens the molding die 5, then being should using material removal technique
Thermoplastic film 3 outside predetermined figure coloured silk 31 is cut off, and is formed a solidification and be incorporated on the surface of the golf club head part 200
Setting figure coloured silk 201.
The setting figure coloured silk 201 is incorporated into the following layer on the surface of the golf club head part 200 with a solidification
202, an ink layer 203 and one being laminated on the following layer 202 is laminated in the thermoplastic film layer on the ink layer 203
205.And the thickness of the setting figure coloured silk 201 between 60um between 500um.
In this present embodiment, it is to cut off the part outside the predetermined figure coloured silk 31 in such a way that laser is cut, certainly, in reality
It can also be carried out using cutting die using upper.
And step 26 is then similar to first embodiment, by 41 phase of ontology of the golf club head part 200 and the jig 4
Mutually separation, and then obtain the golf club head part 200 for having the setting figure coloured silk 201.
In conclusion the manufacturing method of glof club head of the present invention/club head component exterior view coloured silk is pre- using being formed with
The thermoplastic film 3 of fixed figure coloured silk 31 coordinates the design of the jig 4, then is molded skill with the pressure transfer for bestowing positive pressure and negative pressure
Art can directly mold the setting figure coloured silk 201 on glof club head/club head parts surface, not only processing method letter
It is single, and it can be applicable in glof club head/club head parts surface of unlike material, and then effectively reduce manufacturing cost.
Claims (4)
1. a kind of manufacturing method of glof club head/club head component exterior view coloured silk, it is characterised in that comprise the steps of：
(A) preparing a formation, there are one the color thermoplastic films of predetermined figure and one to be used to position the glof club head/club head
The jig of component, the jig there are one and the glof club head/matched ontology of club head component, (B) is by the golf
Club head/club head component is placed on the ontology of the jig, and heats and softens the thermoplastic film, and (C) is by the jig and adds
The thermoplastic film after thermal softening is set in the molding die of a hollow form, will be vacuumized in the molding die to be formed it is negative
Pressure, then gas is poured into the molding die, so that environment in the molding die is converted between negative pressure and positive pressure, utilize air pressure again
So that the glof club head/club head component is fitted closely on the ontology, while the thermoplastic film also being enable closely to paste
Together in the surface of the glof club head/club head component, (D) opens the molding die by the thermoplastic film and the golf
Club head/club head component is separated from each other, and the predetermined color indwelling of figure is in the surface of the glof club head/club head component,
(E) the predetermined figure coloured silk is made to be incorporated into the glof club head/club head component as a solidification using UV-curing technology
Surface on setting figure it is color, and the glof club head/club head component and the ontology of the jig be separated from each other by (F).
2. the manufacturing method of glof club head/club head component exterior view coloured silk according to claim 1, it is characterised in that：
There are one solidifications to be incorporated on the surface of the glof club head/club head component for setting figure coloured silk tool in the step (E)
Following layer, an ink layer being laminated on the following layer and a hardened layer being laminated on the ink layer, the solidification combine
In the color thickness of the setting figure on the surface of the glof club head/club head component between 0.1um between 60um.
3. a kind of manufacturing method of glof club head/club head component exterior view coloured silk, it is characterised in that comprise the steps of：
(A) preparing a formation, there are one the color thermoplastic films of predetermined figure and one to be used to position the glof club head/club head
The jig of component, the jig there are one and the glof club head/matched ontology of club head component, (B) is by the golf
Club head/club head component is placed on the ontology of the jig, and heats and softens the thermoplastic film, and (C) is by the jig and adds
The thermoplastic film after thermal softening is set in the molding die of a hollow form, will be vacuumized in the molding die to be formed it is negative
Pressure, then gas is poured into the molding die, so that environment in the molding die is converted between negative pressure and positive pressure, utilize air pressure again
So that the glof club head/club head component is fitted closely on the ontology, while the thermoplastic film also being enable closely to paste
Together in the surface of the glof club head/club head component, (D) opens the molding die, using material removal technique that this is pre-
Thermoplastic film excision outside fixed figure coloured silk, and form one and cure the surface for being incorporated into the glof club head/club head component
On setting figure it is color, and the glof club head/club head component and the ontology of the jig be separated from each other by (E).
4. the manufacturing method of glof club head/club head component exterior view coloured silk according to claim 3, it is characterised in that：
There are one solidifications to be incorporated on the surface of the glof club head/club head component for setting figure coloured silk tool in the step (D)
Following layer, an ink layer being laminated on the following layer and a thermoplastic film layer being laminated on the ink layer, and should
Cure the thickness for being incorporated into the setting figure coloured silk on the surface of the glof club head/club head component between 60um between 500um.