CN105620162A - Manufacturing method for surface pattern on golf club head/golf club head component - Google Patents
Manufacturing method for surface pattern on golf club head/golf club head component Download PDFInfo
- Publication number
- CN105620162A CN105620162A CN201410705477.XA CN201410705477A CN105620162A CN 105620162 A CN105620162 A CN 105620162A CN 201410705477 A CN201410705477 A CN 201410705477A CN 105620162 A CN105620162 A CN 105620162A
- Authority
- CN
- China
- Prior art keywords
- club head
- glof club
- glof
- thermoplastic film
- head parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a manufacturing method for a surface pattern on a golf club head/golf club head component. The method includes the following steps that (A) a thermoplastic film with a preset pattern and a jig are prepared; (B) the golf club head/golf club head component is placed on the jig, and the thermoplastic film is heated to be softened; (C) the thermoplastic film is made to be tightly attached to the surface of the golf club head/golf club head component; (D) the preset pattern is reserved on the surface of the golf club head/golf club head component; (E) the preset pattern is made to be a set pattern combined to the surface of the golf club head/golf club head component in a solidified mode; and (F) the golf club head/golf club head component is separated from the jig. By means of the design of combination of the thermoplastic film with the preset pattern and the jig, the processing mode is simple, and the manufacturing method can be suitable for golf club heads made of different materials so that cost can be lowered.
Description
Technical field
The present invention relates to the manufacture method of a kind of glof club head, particularly relate to the manufacture method that a kind of glof club head/club head parts exterior view is color.
Background technology
Along with the raising of national life level, the number being engaged in golf is just incrementally increased. Consumer is buying before glof club head, except considering function, also can consider club head exterior design whether attractive in appearance and have texture.
For current glof club head; in order to promote appearance tactile impression; (Physicalvapordeposition would generally be deposited with baking vanish, plating or ion; etc. PVD) process for treating surface carries out painting operation on club head surface, makes club head surface present two or more different gloss or color and luster. Then, then form special picture and text or lines with etching or laser carved technology on club head surface, the glof club head special to make external form.
Etching or laser carved technology not only program are loaded down with trivial details, and owing to how in curved surface glof club head is, related improve etching or laser carved processed complex degree, also improve the manufacturing cost of glof club head simultaneously.
Additionally, existing glof club head material selects composite fibre material or metal material to make mostly. Generally speaking, the glof club head of metal material can select etching or the special picture and text of laser carved processing or lines, but the glof club head of composite fibre material limits for fear of material, causes that processing mode must be different with the glof club head of metal material. For this, manufacturer must select different processing modes for the glof club head of unlike material, and not only inconvenience also can increase the manufacturing cost of manufacturer.
Summary of the invention
It is an object of the invention to provide the manufacture method that a kind of energy is suitable for glof club head/club head parts exterior view coloured silk of multiple unlike material.
The manufacture method that glof club head of the present invention/club head parts exterior view is color, comprise the steps of (A) and prepare a thermoplastic film being formed with a predetermined figure coloured silk, and a tool being used for positioning this glof club head/club head parts, this tool has a body matched with this glof club head/club head parts, (B) this glof club head/club head parts are placed on the body of this tool, and this thermoplastic film of thermoplastic, (C) this thermoplastic film after this tool and thermoplastic is arranged in the mould of a hollow form, and make this mould environment convert between negative pressure and malleation, air pressure is utilized to make this glof club head/club head parts can fit tightly on this body, also make this thermoplastic film can fit tightly in the surface of this glof club head/club head parts simultaneously, (D) open this mould this thermoplastic film and this glof club head/club head parts to be separated from each other, and this predetermined figure coloured silk is that indwelling is in the surface of this glof club head/club head parts, (E) UV-curing technology is utilized to make this predetermined figure coloured silk become the setting figure coloured silk that a solidification is incorporated on the surface of this glof club head/club head parts, and the body of this glof club head/club head parts Yu this tool is separated from each other by (F).
The manufacture method that glof club head of the present invention/club head parts exterior view is color, this setting figure coloured silk in this step (E) has a solidification and is incorporated into the following layer on the surface of this glof club head/club head parts, an ink layer being laminated on this following layer, and a hardened layer being laminated on this ink layer, this solidification is incorporated into thickness color for the setting figure on the surface of this glof club head/club head parts between 0.1um to 60um.
Another object of the present invention, is also to provide the manufacture method that a kind of energy is suitable for glof club head/club head parts exterior view coloured silk of various material.
The manufacture method that glof club head of the present invention/club head parts exterior view is color, comprise the steps of (A) and prepare a thermoplastic film being formed with a predetermined figure coloured silk, and a tool being used for positioning this glof club head/club head parts, this tool has a body matched with this glof club head/club head parts, (B) this glof club head/club head parts are placed on the body of this tool, and this thermoplastic film of thermoplastic, (C) this thermoplastic film after this tool and thermoplastic is arranged in the mould of a hollow form, and make this mould environment convert between negative pressure and malleation, air pressure is utilized to make this glof club head/club head parts can fit tightly on this body, also make this thermoplastic film can fit tightly in the surface of this glof club head/club head parts simultaneously, (D) this mould is opened, material removal technique is utilized to be excised by the thermoplastic film outside this predetermined figure coloured silk, and form the setting figure coloured silk that a solidification is incorporated on the surface of this glof club head/club head parts, and the body of this glof club head/club head parts Yu this tool is separated from each other by (E).
The manufacture method that glof club head of the present invention/club head parts exterior view is color, this setting figure coloured silk in this step (D) has a solidification and is incorporated into the following layer on the surface of this glof club head/club head parts, an ink layer being laminated on this following layer, and a thermoplastic film layer being laminated on this ink layer, and this solidification is incorporated into thickness color for setting figure on the surface of this glof club head/club head parts between 60um to 500um.
The beneficial effects of the present invention is: utilize the thermoplastic film being formed with predetermined figure coloured silk to coordinate the design of this tool, with pressure transfer forming technique and follow-up UV-curing technology/material removal technique, can directly on this glof club head/club head parts surface molding set figure coloured silk, not only processing mode is simple, and can be suitable for unlike material effectively to reduce cost.
Accompanying drawing explanation
Fig. 1 is a flow chart, and the first embodiment of the manufacture method of glof club head of the present invention/club head parts exterior view coloured silk is described;
Fig. 2 is a schematic diagram, the aspect that the predetermined figure illustrated in this first embodiment on this thermoplastic film is color;
Fig. 3 is a schematic diagram, and aspect color for setting figure in this first embodiment is described;
Fig. 4 is a flow chart, and the second embodiment of the manufacture method of glof club head of the present invention/club head parts exterior view coloured silk is described;
Fig. 5 is a schematic diagram, another aspect that the predetermined figure illustrated in this second embodiment on this thermoplastic film is color; And
Fig. 6 is a schematic diagram, illustrates that another kind color for setting figure in this second embodiment constitutes kenel.
Detailed description of the invention
Below in conjunction with drawings and Examples, the present invention is described in detail. Before the present invention is described in detail, it shall be noted that in the following description content, similar assembly is to be identically numbered to represent.
Consult Fig. 1, Fig. 2, the first embodiment of the manufacture method of glof club head of the present invention/club head parts exterior view color (including figure, word, color or combinations of the above) comprises the steps of step 21, prepare a thermoplastic film 3 being formed with a predetermined figure color 31, and a tool 4 being used for positioning a golf club head part 200, this tool 4 has a body 41 matched with this golf club head part 200.
In the present embodiment, this thermoplastic film 3 is thickness polyolefin film (Polyolefin between 0.12mm to 0.15mm, POFilm), and the periphery of this body 41 or turning point are many with fillet process, and this predetermined figure color 31 includes a hardening material 32, being incorporated on this thermoplastic film 3 and is incorporated into the ink 33 on this hardening material 32, and one be incorporated into solid 34 on this ink 33, this solid 34 is PUR or UV glue, is select UV glue in the present embodiment.
Additionally illustrating at this, for convenience of description, the present embodiment is to illustrate with golf club head part 200, certainly, in practical application, as long as there being the tool 4 of correspondence, can also be carry out with whole glof club head, do not limit so that the present embodiment is open.
This golf club head part 200 is placed on the body 41 of this tool 4 by step 22, and this thermoplastic film 3 of thermoplastic. In the present embodiment, it is soften this thermoplastic film 3 with infrared heating.
This thermoplastic film 3 after this tool 4 and thermoplastic is arranged in the mould 5 of a hollow form by step 23, this thermoplastic film 3 is in above this tool 4, then evacuation in this mould 5 is formed negative pressure, then again gas is poured in this mould 5, utilize this golf club head part 200 of air pressure official post can fit tightly on this body 41, also make this thermoplastic film 3 can fit tightly in the surface of this golf club head part 200 simultaneously.
By the pressure transfer forming technique of conversion between negative pressure and malleation, make this golf club head part 200 can fit tightly on this body 41, not only can give full play to this body 41 and support effect of this golf club head part 200, can also be prevented effectively between this thermoplastic film 3 and this golf club head part 200 and produce bag gas phenomenon, promote transfer printing molded effect and stability.
Consulting Fig. 1, Fig. 2, Fig. 3, step 24 opens this mould 5, is separated from each other with this golf club head part 200 by this thermoplastic film 3, and this predetermined figure color 31 is that indwelling is in the surface of this golf club head part 200. Step 25 is to utilize UV-curing technology to make this predetermined figure color 31 become the setting figure coloured silk 201 that a solidification is incorporated on the surface of this golf club head part 200.
This setting figure coloured silk 201 has the following layer 202, that a solidification is incorporated on the surface of this golf club head part 200 and is laminated in the ink layer 203 on this following layer 202, and one be laminated in hardened layer 204 on this ink layer 203, and the thickness of this setting figure coloured silk 201 is between 0.1um to 60um.
In the present embodiment; UV-curing technology is with this predetermined figure color 31 of irradiation under ultraviolet ray; make this solid 34 become and solidify the following layer 202 being attached on the surface of this golf club head part 200; make this ink 33 form the ink layer 203 of specific color and luster simultaneously, and make the hardening of this hardening material 32 become the hardened layer 204 protecting this ink layer 203. And UV-curing technology not only process efficiency is high, more without using solvent can effectively reduce pollution.
Step 26 is to be separated from each other by the body 41 of this golf club head part 200 with this tool 4, and then obtains the golf club head part 200 of tool this setting figure coloured silk 201.
The thermoplastic film 3 being formed with predetermined figure color 31 is utilized to coordinate the design of this tool 4, again with pressure transfer forming technique and follow-up UV-curing technology, can directly on this glof club head/club head parts surface molding set figure color 201, not only processing mode is simple, and can be suitable for the glof club head/club head parts of unlike material effectively to reduce manufacturing cost.
Consult Fig. 4, Fig. 5, second embodiment of the manufacture method that glof club head of the present invention/club head parts exterior view is color is about similar to this first embodiment, the place differed is in that: this predetermined figure color 31 only one is incorporated into the ink 33 on this thermoplastic film 3, and one is incorporated into solid 34 on this ink 33. In the present embodiment, this solid 34 is PUR.
Therefore, the present embodiment can omit the step 25 (being shown in Fig. 1) in first embodiment, and when step 22 heats this thermoplastic film 3, solid 34 can be made simultaneously to produce tackness, and make when step 23 this solid 34 be attached on the surface of this golf club head part 200.
Consult Fig. 4, Fig. 5, Fig. 6, and after step 24 opens this mould 5, it is then utilize material removal technique to be excised by the thermoplastic film 3 outside this predetermined figure color 31, and forms the setting figure coloured silk 201 that a solidification is incorporated on the surface of this golf club head part 200.
This setting figure coloured silk 201 has the following layer 202, that a solidification is incorporated on the surface of this golf club head part 200 and is laminated in the ink layer 203 on this following layer 202, and one is laminated in thermoplastic film layer 205 on this ink layer 203. And the thickness of this setting figure coloured silk 201 is between 60um to 500um.
In the present embodiment, it is by this predetermined Partial Resection schemed outside color 31 in the way of laser cutting, certainly, practical application also is able to utilize cutting die to carry out.
Step 26 is then similar to first embodiment, is separated from each other by the body 41 of this golf club head part 200 with this tool 4, and then obtains the golf club head part 200 of tool this setting figure coloured silk 201.
In sum, the manufacture method of glof club head of the present invention/club head parts exterior view coloured silk utilizes this thermoplastic film 3 being formed with predetermined figure color 31 to coordinate the design of this tool 4, again to bestow the pressure transfer forming technique of malleation and negative pressure, directly can mold this setting figure coloured silk 201 on glof club head/club head parts surface, not only processing mode is simple, and the glof club head/club head parts surface of unlike material can be suitable for, and then effectively reduce manufacturing cost.
Claims (4)
1. the manufacture method that glof club head/club head parts exterior view is color, it is characterized in that comprising the steps of (A) prepares a thermoplastic film being formed with a predetermined figure coloured silk, and a tool being used for positioning this glof club head/club head parts, this tool has a body matched with this glof club head/club head parts, (B) this glof club head/club head parts are placed on the body of this tool, and this thermoplastic film of thermoplastic, (C) this thermoplastic film after this tool and thermoplastic is arranged in the mould of a hollow form, and make this mould environment convert between negative pressure and malleation, air pressure is utilized to make this glof club head/club head parts can fit tightly on this body, also make this thermoplastic film can fit tightly in the surface of this glof club head/club head parts simultaneously, (D) open this mould this thermoplastic film and this glof club head/club head parts to be separated from each other, and this predetermined figure coloured silk is that indwelling is in the surface of this glof club head/club head parts, (E) UV-curing technology is utilized to make this predetermined figure coloured silk become the setting figure coloured silk that a solidification is incorporated on the surface of this glof club head/club head parts, and the body of this glof club head/club head parts Yu this tool is separated from each other by (F).
2. the manufacture method that glof club head/club head parts exterior view is color according to claim 1, it is characterized in that: this setting figure coloured silk in this step (E) has a solidification and is incorporated into the following layer on the surface of this glof club head/club head parts, an ink layer being laminated on this following layer, and a hardened layer being laminated on this ink layer, this solidification is incorporated into thickness color for the setting figure on the surface of this glof club head/club head parts between 0.1um to 60um.
3. the manufacture method that glof club head/club head parts exterior view is color, it is characterized in that comprising the steps of (A) prepares a thermoplastic film being formed with a predetermined figure coloured silk, and a tool being used for positioning this glof club head/club head parts, this tool has a body matched with this glof club head/club head parts, (B) this glof club head/club head parts are placed on the body of this tool, and this thermoplastic film of thermoplastic, (C) this thermoplastic film after this tool and thermoplastic is arranged in the mould of a hollow form, and make this mould environment convert between negative pressure and malleation, air pressure is utilized to make this glof club head/club head parts can fit tightly on this body, also make this thermoplastic film can fit tightly in the surface of this glof club head/club head parts simultaneously, (D) this mould is opened, material removal technique is utilized to be excised by the thermoplastic film outside this predetermined figure coloured silk, and form the setting figure coloured silk that a solidification is incorporated on the surface of this glof club head/club head parts, and the body of this glof club head/club head parts Yu this tool is separated from each other by (E).
4. the manufacture method that glof club head/club head parts exterior view is color according to claim 3, it is characterized in that: this setting figure coloured silk in this step (D) has a solidification and is incorporated into the following layer on the surface of this glof club head/club head parts, an ink layer being laminated on this following layer, and a thermoplastic film layer being laminated on this ink layer, and this solidification is incorporated into thickness color for setting figure on the surface of this glof club head/club head parts between 60um to 500um.