Abstract

The invention relates to a manufacturing method of a metal carved window. The manufacturing method comprises the process steps of mold making, mold assembling, forming, surface treatment and the like. The metal carved window is manufactured through a die-casting machine according to an integrated die-casting formation method, so that the process steps of welding, screw locking, nailing, bonding and the like in the prior art are omitted; meanwhile, the overall structural strength of the carved window is greatly improved, and the situation of leakage of connecting points is eradicated. The metal carved window manufactured through the manufacturing method is attractive in appearance and long in service life; meanwhile, the metal carved window can be melted to be used repeatedly and has the advantage of being environmentally friendly.

Description

A kind of manufacture method of metallic carved window

Technical field

The present invention relates to the manufacture method of metal window, particularly relate to the manufacture method of a kind of metallic carved window.

Background technology

Existing window is typically all to be made up of materials such as timber, iron and steel, plastics, aluminium section bars, and its essential structure is at least by four root type materials, or plastics or timber or iron and steel combine, in joint all seams. Some traditional timber window family increases carving decoration materials on frame, or with the various decorative pattern of metal casting, then by the decorative pattern screw lock of timber or metal, welding or be fixed on window frame with iron nail. During this existing window production costs, expense is expected, is taken a lot of work, and because the joint of window too many (include bonding part etc.) between the bonding part between carving and the bonding part of window frame, carving, window frame, easily produce to loosen at this joint, thus affecting its overall construction intensity, simultaneously, also affect the barrier properties of window, aesthetic property and service life thereof, in addition, due also to the window frame of most of existing carving windows is not use commaterial with carving, therefore, it is difficult to recycle.

Summary of the invention

Defect that the purpose of the present invention is contemplated to overcome above-mentioned prior art to exist and provide that a kind of method for making is simple, the manufacture method of the metallic carved window of sound construction, good looking appearance.

The purpose of the present invention can be achieved through the following technical solutions: the manufacture method of a kind of metallic carved window, it is characterized in that, the method comprises the following steps that: a. molding, adopts heat resisting steel to make mould shock-resistant, resistant to elevated temperatures through machining, electro-discharge machining, heat treated mode; B. die-filling, prepared mould is arranged on die casting machine, the operating pressure of this die casting machine is 300��500kg/cm2; C. molding, pours in mould by the non-ferrous metal through high-temperature fusion, and the melt temperature of this non-ferrous metal is 400��700 DEG C, through die casting machine die cast, and rapidly cooling after, hydraulic press finished product is ejected; D. surface treatment, carries out the finished product after molding deburring polishing, then carries out surface treatment, namely obtains the carved window product of global formation.

Described non-ferrous metal is selected from the one in the aluminium alloy of corrosion resistance, magnesium alloy, zinc alloy material.

Described process of surface treatment can adopt plating or surface spraying.

Due to the fact that and have employed above technical scheme, namely the method adopting die casting machine integrated die-casting molding manufactures metallic carved window, it is integrated with decoration carved on paste that this carving protects the window frame of window, therefore the processing steps such as welding, screw lock, nail be solid, bonding are eliminated, simultaneously, substantially increase the overall construction intensity of carved window, the situation having stopped contact seepage occurs, the product prepared by the inventive method, it is specious, long service life, simultaneously, can melt down and reuse, the advantage with environmental protection.

Claims

1. the manufacture method of a metallic carved window, it is characterised in that the method comprises the following steps that: a. molding, adopts heat resisting steel to make mould shock-resistant, resistant to elevated temperatures through machining, electro-discharge machining, heat treated mode; B. die-filling, prepared mould is arranged on die casting machine, the operating pressure of this die casting machine is 300��500kg/cm2; C. molding, pours in mould by the non-ferrous metal through high-temperature fusion, and the melt temperature of this non-ferrous metal is 400��700 DEG C, through die casting machine die cast, and rapidly cooling after, hydraulic press finished product is ejected; D. surface treatment, carries out the finished product after molding deburring polishing, then carries out surface treatment, namely obtains the carved window product of global formation.

2. the manufacture method of a kind of metallic carved window according to claim 1, it is characterised in that described non-ferrous metal is selected from the one in the aluminium alloy of corrosion resistance, magnesium alloy, zinc alloy material.

3. the manufacture method of a kind of metallic carved window according to claim 1, it is characterised in that described process of surface treatment can adopt plating or surface spraying.