CN105601179A - 抗裂砂浆 - Google Patents
抗裂砂浆 Download PDFInfo
- Publication number
- CN105601179A CN105601179A CN201410672312.7A CN201410672312A CN105601179A CN 105601179 A CN105601179 A CN 105601179A CN 201410672312 A CN201410672312 A CN 201410672312A CN 105601179 A CN105601179 A CN 105601179A
- Authority
- CN
- China
- Prior art keywords
- fiber
- wall
- crack mortar
- mortar
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗裂砂浆,该抗裂砂浆的组分及重量百分比为:水泥:10%~18%,河沙:50%~58%,粉煤灰:12%~14%,乳胶粉:4%~8%,纤维:0.8%,羟丙基甲基纤维素:0.6%,憎水剂:0.4%,木质纤维:0.8%,淀粉醚:0.5%,余量为水,木质纤维由废报纸或者其它废纸粉碎制成的;所述纤维为基丙烯纤维,本发明抗裂砂浆通过将工业废料进行二次利用用于混合抗裂砂浆,与墙体粘接性、抗流挂性明显增强,提高了施工效率,不仅节约能源,而且在墙体使用过程中不会出现开裂空鼓的现象,提高了墙体的强度。
Description
技术领域
本发明属于含有无机黏结剂或含有无机与有机黏结剂反应产物的砂浆、混凝土或人造石的组合物的技术领域,具体是涉及一种抗裂砂浆。
背景技术
砂浆为建筑用普通材料,属于建筑施工中的必备材料。根据性能划分,砂浆分为很多种,有结合砂浆、嵌缝砂浆、保温砂浆等,其中结合砂浆最为常见,现有的结合砂浆中多存在容易出现空鼓开裂的缺陷,施工性不好易流挂,与墙体粘接性不好,失水太快强度丢失太大,容易留下质量隐患,导致建筑使用寿命较短,为了提高结合砂浆的抗裂效果,普遍的做法是提高结合砂浆中水泥的比率,水泥与沙的比率大,需要添加特质水泥抗裂剂,但是两种抗裂砂浆的使用成本高,能源消耗大。
发明内容
有鉴于此,本发明的目的在于提供一种抗裂砂浆,该抗裂砂浆通过将工业废料进行二次利用用于混合抗裂砂浆,与墙体粘接性、抗流挂性明显增强,提高了施工效率,不仅节约能源,而且在墙体使用过程中不会出现开裂空鼓的现象,提高了墙体的强度。
为了达到上述目的,本发明一种抗裂砂浆,该抗裂砂浆的组分及重量百分比为:
水泥:10%~18%
河沙:50%~58%
粉煤灰:12%~14%
乳胶粉:4%~8%
纤维:0.8%
羟丙基甲基纤维素:0.6%
憎水剂:0.4%
木质纤维:0.8%
淀粉醚:0.5%
余量为水,木质纤维由废报纸或者其它废纸粉碎制成的;所述纤维为基丙烯纤维。
本发明的有益效果在于:
本发明抗裂砂浆通过将工业废料进行二次利用用于混合抗裂砂浆,与墙体粘接性、抗流挂性明显增强,提高了施工效率,不仅节约能源,而且在墙体使用过程中不会出现开裂空鼓的现象,提高了墙体的强度。
具体实施方式
实施例一
抗裂砂浆的具体组分及重量百分比为:
水泥:10%
河沙:50%
粉煤灰:12%
乳胶粉:4%
纤维:0.8%
羟丙基甲基纤维素:0.6%
憎水剂:0.4%
木质纤维:0.8%
淀粉醚:0.5%
余量为水,木质纤维由废报纸或者其它废纸粉碎制成的;所述纤维为基丙烯纤维。
本实施例二
水泥:18%
河沙:58%
粉煤灰:14%
乳胶粉:8%
纤维:0.8%
羟丙基甲基纤维素:0.6%
憎水剂:0.4%
木质纤维:0.8%
淀粉醚:0.5%
余量为水,木质纤维由废报纸或者其它废纸粉碎制成的;所述纤维为基丙烯纤维。
本实施例三
水泥:15%
河沙:55%
粉煤灰:13%
乳胶粉:6%
纤维:0.8%
羟丙基甲基纤维素:0.6%
憎水剂:0.4%
木质纤维:0.8%
淀粉醚:0.5%
余量为水,木质纤维由废报纸或者其它废纸粉碎制成的;所述纤维为基丙烯纤维。
本发明与墙体粘接性、抗流挂性明显增强,提高了施工效率,不仅节约能源,而且在墙体使用过程中不会出现开裂空鼓的现象,提高了墙体的强度。
最后说明的是,以上优选实施例仅用以说明本发明的技术方案而非限制,尽管通过上述优选实施例已经对本发明进行了详细的描述,但本领域技术人员应当理解,可以在形式上和细节上对其作出各种各样的改变,而不偏离本发明权利要求书所限定的范围。
Claims (1)
1.一种抗裂砂浆,其特征在于:该抗裂砂浆的组分及重量百分比为:
水泥:10%~18%
河沙:50%~58%
粉煤灰:12%~14%
乳胶粉:4%~8%
纤维:0.8%
羟丙基甲基纤维素:0.6%
憎水剂:0.4%
木质纤维:0.8%
淀粉醚:0.5%
余量为水,木质纤维由废报纸或者其它废纸粉碎制成的;所述纤维为基丙烯纤维。