CN105599095A - Herbal smell clearing furniture with high yellowing resistance and preparing method thereof - Google Patents
Herbal smell clearing furniture with high yellowing resistance and preparing method thereof Download PDFInfo
- Publication number
- CN105599095A CN105599095A CN201510974593.6A CN201510974593A CN105599095A CN 105599095 A CN105599095 A CN 105599095A CN 201510974593 A CN201510974593 A CN 201510974593A CN 105599095 A CN105599095 A CN 105599095A
- Authority
- CN
- China
- Prior art keywords
- furniture
- resistance
- xanthochromia
- draft
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses herbal smell clearing furniture with high yellowing resistance and a preparing method thereof. The preparing method includes the following steps that a plate is pretreated; a layer of methanal removing herbal smell clearing seal priming paint is brushed onto the plate; puttying is conducted; grinding is conducted; priming paint is brushed; the dry sand working procedure is performed; a layer of high-yellowing-resistant paint is brushed onto the plate. According to the herbal smell clearing furniture with high yellowing resistance, reasonable auxiliaries are selected for finishing paint, various raw materials difficult to disperse are dispersed ingeniously, and the finishing paint has good aging resisting and formaldehyde removing functions, directly blocks a formaldehyde emission source when brushed onto the surface of the furniture, captures formaldehyde in indoor air under the normal temperature condition and effectively clears the formaldehyde for a long time to keep quality of the indoor air normal; the preparation technology is simple, and the furniture is environmentally friendly, long in service life, attractive, high in practicability and capable of interspersing and beautifying the living environment and saves energy.
Description
Technical field
The present invention relates to furniture processing technology field, be specifically related to a kind of clear taste furniture of the high draft of resistance to xanthochromia andIts preparation method.
Background technology
In the China of 21 century, along with the further opening in market, more and more new styles are there areFurniture. After basic life requirement is met, some start to focus on the quality of life staying idle at home, spyBe not family product for healthy impact, therefore environmental protection furniture is valued by the people gradually, green consumptionAgitation has also promoted the development of environmental protection furniture.
Environmental protection furniture refers on those bases of being based on ecological industry, reasonable development, utilizes nature materialThat produces can meet user's particular demands, is of value to user's health, and has high literary compositionChange the furniture of inside information and scientific and technological content. Wherein comprise which floor implication: one, furniture itself is pollution-free, nontoxicEvil; Two, to there is higher artistic connotation and aesthetic function, echo mutually with indoor design, create one andThe telecommuting environment of humorous grace; Three, be convenient to reclaim, process, recycling, when furniture no longer use intoWhen row is processed, can be to environment.
Plate fitment refers to the assembling-disassembling man taking wood-based plate as main base material, taking plate as basic structureTool. Common artificial board has glued board, core-board, particieboard, medium density fibre board (MDF) etc. GummedPlate (clamping plate) is usually used in making the diastrophic furniture of needs; Core-board performance is subject to board core material matter sometimesImpact; Particieboard (being again particle board, bagasse board) material is loose, only for low-grade furniture. Cost performanceThat high, the most frequently used is medium density fibre board (MDF) (MDF). The common finishing material of plate fitment has veneer (to be commonly called asPaste wooden skin), woodgrained paper (being commonly called as paster), PVC offset plate, polyester lacquer painting (being commonly called as baking vanish) etc.
Furniture lacquer can make woodenware DELICATE AND SIMPLE BAMBOO more attractive in appearance beautiful, improve furniture itself with harsh hand,Make not climate and dry wet variable effect of furniture, not only play the effect of Preservation woodenware DELICATE AND SIMPLE BAMBOO,And can also make whole family life become more comfortable.
The invention provides the clear taste furniture of a kind of high draft of resistance to xanthochromia, there is excellent antibacterial clean taste performance.
Summary of the invention
For above shortcomings in prior art, one of technical problem to be solved by this invention is to carryFor the preparation method of the clear taste furniture of a kind of high draft of resistance to xanthochromia.
It is clear that two of technical problem to be solved by this invention is to provide the height draft of resistance to xanthochromia prepared by said methodTaste furniture.
The present invention seeks to be achieved through the following technical solutions:
A preparation method for the clear taste furniture of the high draft of resistance to xanthochromia, comprises the following steps:
(1) sheet material pretreatment;
(2) brush seal coat: brush one deck and remove the clear taste seal coat of formaldehyde draft on sheet material;
(3) scrape ash;
(4) polishing;
(5) priming;
(6) dry sand;
(7) upper finish paint: brush a floor height paint of resistance to xanthochromia on sheet material.
Preferably,
The described clear taste seal coat of formaldehyde draft that goes is 1:1-3:1 by A component and B component in mass ratioFormulated.
Described A component is prepared from by the raw material of following weight parts: unsaturated polyester resin 85-95 part,Lavender oil 10-20 part, n-butyl acetate 10-20 part, propylene glycol monomethyl ether acetate 5-15 part, formaldehydeCapturing agent 0.5-2.5 part, curing agent 15-30 part.
Described methanal trapping agent is by 40-60wt%1-mesyl-2-imidazolidinone and 40-60wt%1-chloromethaneAcyl group-2-imidazolidinone composition.
Described unsaturated polyester resin is dicyclopentadiene type or propylene ether type unsaturated polyester resin.
Described curing agent is isopropyl benzene hydroperoxide.
Described B component is by 80-90wt% n-butyl acetate and 10-20wt% Toluene-2,4-diisocyanate, 4-bis-[N, N-diformazan ammoniaBase the third urea] composition.
The described height paint of resistance to xanthochromia is 1:0.5:0.3-1:1:1 by main paint, curing agent, diluent in mass ratioFormulated.
Described main paint is prepared from by the raw material of following weight parts: acrylic resin 85-95 part, titanium dioxideTitanium 10-20 part, dodecyl sodium sulfate 2-3 part, dimethicone 0.3-0.8 part, UV absorbers1.5-2.5 part, n-butyl acetate 5-15 part, propylene glycol monomethyl ether acetate 5-15 part.
Described UV absorbers is by 40-60wt%2,2'-dihydroxy-4,4'-dimethoxy-benzophenone-5,5'-Disulfonic acid and 40-60wt%2-hydroxyl-4-methoxybenzophenone-5-sulfonic acid composition.
Described curing agent is by 50-60wt% n-butyl acetate and 40-50wt%1, prepared by hexamethylene-diisocyanateForm.
Described diluent is prepared by 50-60wt% n-butyl acetate and 40-50wt% propylene glycol monomethyl ether acetateForm.
The present invention also provides the preparation method of above-mentioned A component: by unsaturated polyester resin, lavender oil,N-butyl acetate, propylene glycol monomethyl ether acetate, methanal trapping agent, curing agent mix, described in obtainingA component.
The present invention also provides the preparation method of above-mentioned B component: by n-butyl acetate and Toluene-2,4-diisocyanate, and 4-bis-[N, N-dimethylamino the third urea] mixes, and obtains described B component.
The present invention also provides the preparation method of above-mentioned main paint: by acrylic resin, titanium dioxide, 12Sodium alkyl sulfonate, dimethicone, UV absorbers, n-butyl acetate add in high speed dispersor mixedClose evenly; Be 25-35 μ m through sand mill sand milling to fineness again; Add again propylene glycol monomethyl ether acetate to mixEvenly, obtain described main paint.
The present invention also provides the preparation method of above-mentioned curing agent: by oneself two isocyanic acids of butyl acetate and 1,6-Ester mixes, and obtains described curing agent.
The present invention also provides the preparation method of above-mentioned diluent: by n-butyl acetate and propylene glycol monomethyl ether thirdAcid esters mixes, and obtains described diluent.
The present invention also provides a kind of height draft of resistance to xanthochromia clear taste furniture, adopts said method to be prepared from.
Concrete, in the present invention:
N-butyl acetate, No. CAS: 123-86-4.
Propylene glycol monomethyl ether acetate, No. CAS: 148462-57-1.
1-mesyl-2-imidazolidinone, No. CAS: 41730-79-4.
1-Chlorocarbonyl-2-Imidazolidone, No. CAS: 13214-53-4.
Isopropyl benzene hydroperoxide, No. CAS: 80-15-9.
Dodecyl sodium sulfate, No. CAS: 2386-53-0.
Dimethicone, No. CAS: 63148-62-9.
Lavender oil, No. CAS: 97660-01-0.
2,2'-dihydroxy-4,4'-dimethoxy-benzophenone-5,5'-disulfonic acid, No. CAS: 143982-77-8.
2-hydroxyl-4-methoxybenzophenone-5-sulfonic acid, No. CAS: 4065-45-6.
1, hexamethylene-diisocyanate, No. CAS: 822-06-0.
The clear taste furniture of the high draft of resistance to xanthochromia of the present invention, finish paint used, by selecting reasonable auxiliary agent, divides cleverlyThe raw material that the various difficulties of having fallen apart are disperseed, have good anti-aging aldehydes removal function, brush at furniture surface,Not only directly block the root of formaldehyde emission, and possess under normal temperature condition and catch formaldehyde in indoor air,Permanently effective removing formaldehyde, makes IAQ keep normal; Preparation technology of the present invention is simple, isEnvironmental protection, long, a very attractive in appearance furniture of energy-conservation, life-span, practicality is good, can intersperse beautify life ringBorder.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described further, and the following stated is only to of the present inventionPreferred embodiment, not does other forms of restriction to the present invention, is anyly familiar with this professional technologyPersonnel may utilize the technology contents of above-mentioned announcement to be changed to the equivalent embodiment of equal variation. EveryDo not depart from the present invention program's content, any letter of following examples being done according to technical spirit of the present inventionSingle amendment or equivalent variations, all drop in protection scope of the present invention.
Embodiment raw material is introduced:
Titanium dioxide, No. CAS: 13463-67-7, adopts Du Pont, the rutile-type that model is R-960Titanium dioxide.
Acrylic resin, No. CAS: 9003-01-4. Adopt Shenzhen Jin Fengyuan macromolecular material Co., LtdThe model providing is the thermoplastic acrylic resin of RS-68P.
Toluene-2,4-diisocyanate, 4-bis-[N, N-dimethylamino the third urea], can buy or make by oneself, the present invention is big with reference to stone,Zheng Yaping, Hui Feiyuan " the synthetic and cure kinetics research of curing accelerator for EP based powders coating ",China's adhesive, 2010; Prepare Toluene-2,4-diisocyanate, 4-bis-[N, N-dimethylamino the third urea].
Unsaturated polyester resin, the ETERSET of employing Changxing synthetic resin (Changshu) Co., Ltd2307-S。
Medium density fibre board (MDF), adopting the Tian Yemu of Suzhou City industry Co., Ltd specification is 4*10*12, in pineDensity fiber board.
Priming paint, the excellent clear priming paint of PU woodenware of obliging that adopts Zijinghua Paint (Shanghai) Co., Ltd. to produce.
Sand paper, adopts Korea S deer board DEERFOS sand paper, and model is ACM66, granularity is 120,180,400 3 kinds of specifications.
Embodiment 1
A component raw material: unsaturated polyester resin 90kg, lavender oil 15kg, n-butyl acetate 15kg,Propylene glycol monomethyl ether acetate 10kg, methanal trapping agent 2kg, isopropyl benzene hydroperoxide 20kg.
Described methanal trapping agent is by 1kg1-mesyl-2-imidazolidinone and 1kg1-chloroformyl-2-imidazolesAlkane ketone composition.
The preparation method of A component: by unsaturated polyester resin, lavender oil, n-butyl acetate, formaldehydeCapturing agent, isopropyl benzene hydroperoxide add the linear velocity high speed dispersion 30 minutes of 20m/s in high speed dispersorMix, then be 30 μ m through sand mill sand milling to fineness; Add again propylene glycol monomethyl ether acetate to stirMix, obtain described A component.
B component is by 60.35kg n-butyl acetate and 10.65kg Toluene-2,4-diisocyanate, 4-bis-[N, N-dimethylamino the third urea]Composition. By n-butyl acetate and Toluene-2,4-diisocyanate, 4-bis-[N, N-dimethylamino the third urea] adds stirrer for mixing equalEven, obtain described B component.
Main raw materials for varnish: acrylic resin 90kg, titanium dioxide 15kg, dodecyl sodium sulfate 2.5g part,Dimethicone 0.5kg UV absorbers 2kg, n-butyl acetate 10kg, propylene glycol monomethyl ether acetate10kg。
Described UV absorbers is by 1kg2,2'-dihydroxy-4,4'-dimethoxy-benzophenone-5,5'-disulfonic acidForm with 1kg2-hydroxyl-4-methoxybenzophenone-5-sulfonic acid.
The preparation method of main paint: by acrylic resin, titanium dioxide, dodecyl sodium sulfate, dimethylSilicone oil, UV absorbers, n-butyl acetate add the linear velocity of 20m/s in high speed dispersor to divide at a high speedLoose mixing for 30 minutes; Be 30 μ m through sand mill sand milling to fineness again; Add again propylene glycol monomethyl etherPropionic ester mixes, and obtains described main paint.
Described curing agent is by 50.82kg n-butyl acetate and 41.58kg1, and hexamethylene-diisocyanate is prepared from.By butyl acetate and 1, hexamethylene-diisocyanate adds stirrer for mixing even, obtains described curing agent.
Described diluent is prepared from by 36.3kg n-butyl acetate and 29.7kg propylene glycol monomethyl ether acetate.Add stirrer for mixing even n-butyl acetate and propylene glycol monomethyl ether acetate, obtain described diluent.
The preparation method of the clear taste furniture of the high draft of resistance to xanthochromia, comprises the following steps:
(1) sheet material pretreatment, the sand paper that is 120 by granularity by medium density fibre board (MDF) carries out sanding polishing,Polishing rear surface dedusting;
(2) brush seal coat, will go the clear taste seal coat of formaldehyde draft A component and B component by qualityThan mixing for 2:1, adopt painting way on sheet material, to brush one deck and remove the clear taste seal coat of formaldehyde draft,Japanning amount 100g/m2；
(3) scrape ash, by fresh pig blood and titanium dioxide in mass ratio for 9:1 mixes, on sheet materialFresh pig blood and titanium dioxide after brush one deck mixes, applying amount 50g/m2；
(4) polishing; The sand paper that is 180 by granularity carries out sanding polishing, polishing rear surface dedusting;
(5) priming, the excellent PU woodenware of obliging that Zijinghua Paint (Shanghai) Co., Ltd. is produced is clearThe main paint of priming paint, curing agent, diluent mix for 2:1:0.8 in mass ratio, adopt painting way to existUniform priming on sheet material, japanning amount 100g/m2；
(6) dry sand: the sand paper that is 400 by granularity carries out sanding polishing, polishing rear surface dedusting;
(7) upper finish paint, is 1:0.7:0.5 by the main paint of the height paint of resistance to xanthochromia, curing agent, diluent in mass ratioMix, adopt painting way on sheet material, to brush uniformly the antibacterial damage resistant paint of one deck, japanning amount200g/m2, adopt Halogen lamp LED uniform irradiation 1h on sheet material, dry,, can make height of the present inventionThe clear taste furniture of the draft of resistance to xanthochromia.
Embodiment 2
Prepare the clear taste furniture of the high draft of resistance to xanthochromia by the raw material proportioning of embodiment 1 and method, difference is only:Described methanal trapping agent is 2kg1-mesyl-2-imidazolidinone. Obtain the height grass of resistance to xanthochromia of embodiment 2This clear taste furniture.
Embodiment 3
Prepare the clear taste furniture of the high draft of resistance to xanthochromia by the raw material proportioning of embodiment 1 and method, difference is only:Described methanal trapping agent is 2kg1-chloroformyl-2-imidazolidinone. Obtain the height grass of resistance to xanthochromia of embodiment 3This clear taste furniture.
Embodiment 4
Prepare the clear taste furniture of the high draft of resistance to xanthochromia by the raw material proportioning of embodiment 1 and method, difference is only:Described UV absorbers is 2kg2,2'-dihydroxy-4,4'-dimethoxy-benzophenone-5,5'-disulfonic acid. ?To the clear taste furniture of the height draft of resistance to xanthochromia of embodiment 4.
Embodiment 5
Prepare the clear taste furniture of the high draft of resistance to xanthochromia by the raw material proportioning of embodiment 1 and method, difference is only:Described UV absorbers is 2kg2-hydroxyl-4-methoxybenzophenone-5-sulfonic acid. Obtain embodiment's 5The clear taste furniture of the high draft of resistance to xanthochromia.
Test case 1
The furniture that makes of above-described embodiment 1-5 is carried out to performance test.
Press the purifying formaldehyde performance of JC/T1074-2008 mensuration paint film, wherein purifying formaldehyde performance >=75%For I class, >=80% be II class, clean-up effect persistence >=60% is I class, >=65% is II class;Yellowing resistance is pressed IOS11507:1997 test; Concrete result of the test is as shown in table 1:
Table 1: clean furniture performance test results table
Comparing embodiment 1-3, embodiment 1 (methanal trapping agent adopt 1-mesyl-2-imidazolidinone and1-Chlorocarbonyl-2-Imidazolidone is composite) purifying formaldehyde successful is better than embodiment 2-3 (methanal trappingAgent adopts single raw material in 1-mesyl-2-imidazolidinone and 1-Chlorocarbonyl-2-Imidazolidone); RelativelyEmbodiment 1 and embodiment 4-5, (UV absorbers adopts 2,2'-dihydroxy-4,4'-dimethoxy to embodiment 1Base benzophenone-5,5'-disulfonic acid and 2-hydroxyl-4-methoxybenzophenone-5-sulfonic acid are composite) yellowing resistance(UV absorbers adopts 2,2'-dihydroxy-4,4'-dimethoxy-benzophenone to be obviously better than embodiment 4-5Single raw material in-5,5'-disulfonic acid and 2-hydroxyl-4-methoxybenzophenone-5-sulfonic acid).
The storage stability of the present invention's woodcare paint used is good, and the content of harmful substance is all at GB18581-2009Claimed range within, the present invention has enough safety in utilization; Paint film water white transparency, smooth smooth,Resistance to acids and bases is good, and coated family is had to good defencive function, be applicable to such as family, office,The places such as school; The purifying property of PARA FORMALDEHYDE PRILLS(91,95) and clean-up effect persistence all meet JC/T1074-2008'sRequirement, illustrates clean aldehyde excellent, the free formaldehyde in can purifying air rapidly, efficiently, enduringly.
Claims (7)
1. a preparation method for the clear taste furniture of the high draft of resistance to xanthochromia, is characterized in that, comprises the following steps:
(1) sheet material pretreatment;
(2) on sheet material, brush one deck and remove the clear taste seal coat of formaldehyde draft;
(3) scrape ash;
(4) polishing;
(5) priming;
(6) dry sand;
(7) on sheet material, brush a floor height paint of resistance to xanthochromia.
The described clear taste seal coat of formaldehyde draft that goes is 1:1-3:1 by A component and B component in mass ratioFormulated;
Described A component is prepared from by the raw material of following weight parts: unsaturated polyester resin 85-95 part,Lavender oil 10-20 part, n-butyl acetate 10-20 part, propylene glycol monomethyl ether acetate 5-15 part, formaldehydeCapturing agent 0.5-2.5 part, curing agent 15-30 part;
Described methanal trapping agent is by 40-60wt%1-mesyl-2-imidazolidinone and 40-60wt%1-chloromethaneAcyl group-2-imidazolidinone composition.
Described unsaturated polyester resin is dicyclopentadiene type or propylene ether type unsaturated polyester resin; DescribedCuring agent is isopropyl benzene hydroperoxide.
2. the preparation method of the clear taste furniture of the height draft of resistance to xanthochromia as claimed in claim 1, is characterized in that,Described B component is by 80-90wt% n-butyl acetate and 10-20wt% Toluene-2,4-diisocyanate, 4-bis-[N, N-dimethylamino thirdUrea] composition.
3. the preparation method of the clear taste furniture of the height draft of resistance to xanthochromia as described in any one in claim 1-2,It is characterized in that:
The described height paint of resistance to xanthochromia is 1:0.5:0.3-1:1:1 by main paint, curing agent, diluent in mass ratioFormulated;
Described main paint is prepared from by the raw material of following weight parts: acrylic resin 85-95 part, titanium dioxideTitanium 10-20 part, dodecyl sodium sulfate 2-3 part, dimethicone 0.3-0.8 part, UV absorbers1.5-2.5 part, n-butyl acetate 5-15 part, propylene glycol monomethyl ether acetate 5-15 part.
4. the preparation method of the clear taste furniture of the height draft of resistance to xanthochromia as claimed in claim 3, is characterized in that,Described UV absorbers is by 40-60wt%2,2'-dihydroxy-4,4'-dimethoxy-benzophenone-5,5'-bis-sulphursAcid and 40-60wt%2-hydroxyl-4-methoxybenzophenone-5-sulfonic acid composition.
5. the preparation method of the clear taste furniture of the height draft of resistance to xanthochromia as claimed in claim 3, is characterized in that,Described curing agent is by 50-60wt% n-butyl acetate and 40-50wt%1, and hexamethylene-diisocyanate is prepared from;Described diluent is by the preparation of 50-60wt% n-butyl acetate and 40-50wt% propylene glycol monomethyl ether acetateBecome.
6. the preparation method of the clear taste furniture of the height draft of resistance to xanthochromia as claimed in claim 3, is characterized in that,The preparation method of described main paint: by acrylic resin, titanium dioxide, dodecyl sodium sulfate, dimethylSilicone oil, UV absorbers, n-butyl acetate add in high speed dispersor and mix; Again through sand millSand milling to fineness is 25-35 μ m; Add again propylene glycol monomethyl ether acetate to mix, obtain described main paint.
7. the clear taste furniture of the high draft of resistance to xanthochromia, is characterized in that, adopts in claim 1-6 arbitraryThe described method of item is prepared from.