CN105599085A - 木材及棉纤维处理剂、其制备方法及应用 - Google Patents
木材及棉纤维处理剂、其制备方法及应用 Download PDFInfo
- Publication number
- CN105599085A CN105599085A CN201610108606.6A CN201610108606A CN105599085A CN 105599085 A CN105599085 A CN 105599085A CN 201610108606 A CN201610108606 A CN 201610108606A CN 105599085 A CN105599085 A CN 105599085A
- Authority
- CN
- China
- Prior art keywords
- cotton fiber
- timber
- inorganic agent
- borax
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
测试内容 | 尺寸(mm) |
增重率、ASE、流失率、吸水率 | 20×20×20 |
弹性模量、抗弯强度及硬度 | 20×20×300(顺纹) |
顺纹抗压强度 | 20×20×30(顺纹) |
实验例 | ASE(%) | 增重率(%) | 流失率(%) | 吸水率(%) |
实验例1 | 56.8 | 43.8 | 6.1 | 61.4 |
实验例2 | 65.8 | 73.8 | 6.2 | 44.6 |
实验例3 | 58.4 | 48.2 | 6.2 | 66.6 |
实验例4 | 60.0 | 56.8 | 6.4 | 64.2 |
对照例1 | - | - | - | 109.0 |
实验例 | MOE(GPa) | MOR(MPa) | CS(MPa) | 硬度(Shore D) |
实验例1 | 6.4 | 68.4 | 73.1 | 54.3 |
实验例3 | 6.6 | 70.7 | 72.4 | 58.1 |
实验例4 | 7.0 | 71.8 | 75.6 | 59.7 |
对照例1 | 4.9 | 75.4 | 46.9 | 43.5 |
实验例 | 增重率(%) | 流失率(%) | 吸湿率(%) |
实验例1 | 106.9 | 14.4 | 10.5 |
实验例5 | 231.5 | 13.4 | 7.2 |
实验例6 | 254.3 | 12.9 | 6.6 |
对照例2 | - | - | 13.9 |
Claims (8)