CN105585922A - Novel limestone - Google Patents
Novel limestone Download PDFInfo
- Publication number
- CN105585922A CN105585922A CN201511000343.9A CN201511000343A CN105585922A CN 105585922 A CN105585922 A CN 105585922A CN 201511000343 A CN201511000343 A CN 201511000343A CN 105585922 A CN105585922 A CN 105585922A
- Authority
- CN
- China
- Prior art keywords
- agent
- deionized water
- preparation
- lime stone
- aggregate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of coatings, in particular to novel limestone. The novel limestone comprises aggregate and a main material, wherein the mass ratio of the aggregate to the main material is 1:1.2; the aggregate is a texture coating; the main material is a water-in-water multicolor coating; the texture coating comprises raw materials as follows: deionized water, cellulose, bentonite, a pH regulator, a liquid reinforcing agent, a dispersant, a preservative, an antifoaming agent, a styrene-acrylic emulsion, a coalescing agent, propylene glycol, a thickener, titanium dioxide, talc and heavy calcium. The novel limestone has the benefits as follows: the aggregate of the novel limestone is easy to polish, and the main material has flat color points, is well compatible with the aggregate, has a luxurious decorative effect, is high-grade and has the decorative effect little different from that of natural stone.
Description
Technical field
The present invention relates to technical field of coatings, be specifically related to a kind of Novel lime stone.
Background technology
Natural granite figure colour kind is limited, and cost is high, stone material dry suspending loadOverweight, there is the hidden danger coming off for a long time in year. Natural granite under construction application quantity is larger, butThat natural stone material exploitation and application can cause the societies such as wasting of resources exhaustion and climate warming publicProblem altogether. Along with the development that China requires building energy conservation, building must do outside exterior wallInsulation is to reduce building energy consumption. Adopting the outer external wall being incubated to carry out stone decoration not only executes againWork difficulty is large, and cost is high. Adopt the decoration of exterior wall of water-soluble colorful coating artificial grantie effectCan not be subject to the restriction of outer heat preserving mode, construction simple possible, is widely used in outside multiple exterior wallHeat-preserving wall.
Summary of the invention
In order effectively to address the above problem, the invention provides a kind of Novel lime stone.
Concrete technical scheme is as follows: a kind of Novel lime stone, described Novel lime stone comprises aggregateAnd main material, the mass ratio of described aggregate and described main material is 1:1.2;
Described aggregate is texture coating;
Described main material is water bag water multicolor finish.
Further, the raw material of described texture material comprise deionized water, cellulose, swellingSoil, pH adjusting agent, liquid reinforcing agent, dispersant, anticorrisive agent, defoamer, benzene emulsion,Coalescents, propane diols, thickener, titanium dioxide, talcum powder, coarse whiting;
Described deionized water, cellulose, bentonite, pH adjusting agent, liquid reinforcing agent, pointPowder, anticorrisive agent, defoamer, benzene emulsion, coalescents, propane diols, thickener, titaniumThe component of white powder, talcum powder, coarse whiting is than being 14.25:0.65:0.05:0.06:0.07:0.3：0.26：0.68：17.9：0.68：1.3：0.17：2：5：56.95。
Further, described water bag water multicolor finish comprises basic coating, mixes and help material, allotmentHelp material;
It is 100:90:95 that described basic coating, mixing help material and allotment to help the component ratio of material.
Further, described basic coating comprises deionized water, cellulose, defoamer, pHConditioning agent, wetting agent, dispersant, titanium dioxide, coalescents, propane diols, Silicone acrylic emulsion,Anticorrisive agent, protection sol solution;
Described deionized water, cellulose, defoamer, pH adjusting agent, wetting agent, dispersant,The quality of titanium dioxide, coalescents, propane diols, Silicone acrylic emulsion, anticorrisive agent, protection sol solutionComponent is than being 39.48-40.59:1.36-1.53:0.33:0.14:0.14:0.41:0.1-4.55:1.84-2.35：0.93：41.4-47.05：0.3：7.06。
Further, described mixing helps material to comprise deionized water, cellulose, protection glue, anticorrosionAgent, dispersant and pH adjusting agent, described deionized water, cellulose, protection glue, anticorrisive agent,The component of dispersant and pH adjusting agent is than being 96.63:0.27:2.4:0.3:0.3:0.1.
Further, described allotment helps material to comprise Silicone acrylic emulsion, coalescents, propane diols, increasingThick dose, anticorrisive agent, pH adjusting agent and deionized water;
Described Silicone acrylic emulsion, coalescents, propane diols, thickener, anticorrisive agent, pH regulateThe component of agent and deionized water is than being 89:3.5:1.42:0.15:0.15:0.22:5.56.
A preparation method for Novel lime stone, for the preparation of above-mentioned Novel lime stone, its spyLevy and be, described preparation method comprises the steps:
A) help material to mix basic coating and mixing, and apply comminutor and carry out granulation;
B) after granulation, help material to mix with allotment, mix fully, obtain main material;
C) main material is mixed with aggregate, obtain Novel lime stone.
Further, described preparation method is in described steps A) the front basic coating, mixed that also comprisesClose and help material and allotment to help the preparation process of material, the preparation process of described basic coating comprises:
A11) first defoamer, titanium dioxide and cellulose are added in deionized water to juxtapositionIn mixer, stir, described mixing speed is 200-400r/min, when described stirringBetween be 20-25min;
A12) after stirring completes, be warming up to 70-80 DEG C, add Silicone acrylic emulsion, thirdGlycol, coalescents, dispersant and wetting agent, be incubated and vacuumize stirring, and mixing speed is400-500r/min, the retention time is 1h-1.2h;
A13) completing steps A12) the rear pH adjusting agent of adding, adjusting pH is 7.5-8.0, withAfter add again anticorrisive agent and protection sol solution, vacuumize airtightly, add after nitrogen regulation and control pressureTo 1.5-1.8mpa, and intensification value 120-150 DEG C, and carry out density stirring, with100-120r/min stirs 3-5min, stirring after 20-30min with 200-250r/min,Complete the preparation of basic coating;
Described mixing helps the preparation of material to comprise the steps:
After deionized water, cellulose, protection glue, anticorrisive agent and dispersant are mixed, thenAdd pH adjusting agent, keep pH at 7.2-7.5, at room temperature carry out high-speed stirred, described inMixing speed is 60-120r/min;
Described allotment helps the preparation of material to comprise the steps:
A21) described Silicone acrylic emulsion and deionized water are proportionally mixed, mix laggardRow stirs, and described mixing speed is 100-200r/min, and described mixing time is 10-15min;
A22) to steps A 21) add anticorrisive agent, thickener, film forming in the solution that completes and helpAgent, proceeds to stir, and stirs 3-5min, with 200-250r/min with 100-120r/minStir after 20-30min;
A23) to steps A 22) in add again pH adjusting agent, keep pH at 7.2-7.5, thenAdd propane diols, after at room temperature stirring, leave standstill 10min and prepared.
Further, described steps A) in after basic coating and mixing help material to mix, by makingGrain machine carries out granulation, and the diameter dimension after described granulation is 0.3-0.5mm.
Beneficial effect of the present invention is: the aggregate of Novel lime stone is easily polished, and main wood color point is smooth,Very good with the compatibility of aggregate, decorative effect is luxurious, improves grade, with the decoration of lithotomeEffect is very nearly the same.
The deadweight of Novel lime stone coating only accounts for 1/500 of lithotome, not only fundamentally freesOverweight, year of stone material dry suspending load hidden danger of coming off for a long time, and cost-saving be only stone material1/3, meet energy-conservation requirement completely. It is applicable to mortar, mortar, plasterboard, concrete,The multiple types construction materials such as timber, PC plate, plastics, also can be used for the metal materials such as steelExternal coating.
Detailed description of the invention
Contrasting invention by specific embodiment is below further explained.
Embodiments of the invention provide a kind of Novel lime stone,
Novel lime stone is made up of aggregate and main material two parts, and its aggregate is texture coating, main materialIt is water bag water multicolor finish.
Novel lime stone aggregate is exactly a kind of fine powder material texture coating, and grinability is fine, its proportioningIn table one:
Table one Novel lime stone aggregate
| Material | Proportioning |
| Deionized water | 14.25％ |
| Cellulose | 0.65％ |
| Bentonite | 0.05％ |
| PH adjusting agent | 0.06％ |
| Liquid reinforcing agent | 0.07％ |
| Dispersant | 0.3％ |
| Anticorrisive agent | 0.26％ |
| Defoamer | 0.68％ |
| Benzene emulsion | 17.9％ |
| Coalescents | 0.68％ |
| Propane diols | 1.3％ |
| Thickener | 0.17％ |
| Titanium dioxide | 2％ |
| Talcum powder | 5％ |
| Coarse whiting | 56.95％ |
The main material of Novel lime stone is exactly water bag water multicolor finish, and it is divided into A, B, tri-groups of CPoint, A component formula is in table two:
Table two A component
| Material | Proportioning |
| Deionized water | 39.48-40.59％ |
| Cellulose | 1.36-1.53％ |
| Defoamer | 0.33％ |
| PH adjusting agent | 0.14％ |
| Wetting agent | 0.14％ |
| Dispersant | 0.41％ |
| Titanium dioxide | 0-4.55％ |
| Coalescents | 1.84％-2.35％ |
| Propane diols | 0.93％ |
| Silicone acrylic emulsion | 41.4-47.05％ |
| Anticorrisive agent | 0.3％ |
| 10% protection sol solution | 7.06％ |
This A component is with respect to general water bag water multicolor finish admittedly containing decreasing, and therefore color dot spraysMore smooth on base material, better with the amalgamation of ground.
B component formula is in table three:
Table three B component
C component formula is in table four:
Table four C component
| Material | Proportioning |
| Silicone acrylic emulsion | 89％ |
| Coalescents | 3.5％ |
| Propane diols | 1.42％ |
| Thickener | 0.15％ |
| Anticorrisive agent | 0.15％ |
| PH adjusting agent | 0.22％ |
| Deionized water | 5.56％ |
In A component, select as required suitable titanium dioxide content, add a certain amount of mill base,Can obtain the base paint of different colours. According to A component: B component: C component=100:90:95,A component is joined in B component, select the screen cloth granulator granulation of different sizes, make grainAfter add C component, fully mix, make water bag water multicolor finish.
When construction, first criticize and scrape aggregate with batch cutter, then use sand papering, finally spray again main materialWater bag water multicolor finish.
A preparation method for Novel lime stone, for the preparation of above-mentioned Novel lime stone, its spyLevy and be, described preparation method comprises the steps:
A) help material to mix basic coating and mixing, and apply comminutor and carry out granulation;
B) after granulation, help material to mix with allotment, mix fully, obtain main material;
C) main material is mixed with aggregate, obtain Novel lime stone.
Described preparation method is in described steps A) front also comprise basic coating, mix help material and adjustJoin the preparation process that helps material, the preparation process of described basic coating comprises:
A11) first defoamer, titanium dioxide and cellulose are added in deionized water to juxtapositionIn mixer, stir, described mixing speed is 200-400r/min, when described stirringBetween be 20-25min;
A12) after stirring completes, be warming up to 70-80 DEG C, add Silicone acrylic emulsion, thirdGlycol, coalescents, dispersant and wetting agent, be incubated and vacuumize stirring, and mixing speed is400-500r/min, the retention time is 1h-1.2h;
A13) completing steps A12) the rear pH adjusting agent of adding, adjusting pH is 7.5-8.0, withAfter add again anticorrisive agent and protection sol solution, vacuumize airtightly, add after nitrogen regulation and control pressureTo 1.5-1.8mpa, and intensification value 120-150 DEG C, and carry out density stirring, with100-120r/min stirs 3-5min, stirring after 20-30min with 200-250r/min,Complete the preparation of basic coating;
Described mixing helps the preparation of material to comprise the steps:
After deionized water, cellulose, protection glue, anticorrisive agent and dispersant are mixed, thenAdd pH adjusting agent, keep pH at 7.2-7.5, at room temperature carry out high-speed stirred, described inMixing speed is 60-120r/min;
Described allotment helps the preparation of material to comprise the steps:
A21) described Silicone acrylic emulsion and deionized water are proportionally mixed, mix laggardRow stirs, and described mixing speed is 100-200r/min, and described mixing time is 10-15min;
A22) to steps A 21) add anticorrisive agent, thickener, film forming in the solution that completes and helpAgent, proceeds to stir, and stirs 3-5min, with 200-250r/min with 100-120r/minStir after 20-30min;
A23) to steps A 22) in add again pH adjusting agent, keep pH at 7.2-7.5, thenAdd propane diols, after at room temperature stirring, leave standstill 10min and prepared.
Described steps A) in after basic coating and mixing help material to mix, make by comminutorGrain, the diameter dimension after described granulation is 0.3-0.5mm.
Beneficial effect of the present invention is: the aggregate of Novel lime stone is easily polished, and main wood color point is smooth,Very good with the compatibility of aggregate, decorative effect is luxurious, improves grade, with the decoration of lithotomeEffect is very nearly the same.
Claims (9)
1. a Novel lime stone, is characterized in that, described Novel lime stone comprise aggregate andMain material, the mass ratio of described aggregate and described main material is 1:1.2;
Described aggregate is texture coating;
Described main material is water bag water multicolor finish.
2. a kind of Novel lime stone according to claim 1, is characterized in that, described inThe raw material of texture material comprise deionized water, cellulose, bentonite, pH adjusting agent, liquidBody reinforcing agent, dispersant, anticorrisive agent, defoamer, benzene emulsion, coalescents, propane diols,Thickener, titanium dioxide, talcum powder, coarse whiting;
Described deionized water, cellulose, bentonite, pH adjusting agent, liquid reinforcing agent, pointPowder, anticorrisive agent, defoamer, benzene emulsion, coalescents, propane diols, thickener, titaniumThe component of white powder, talcum powder, coarse whiting is than being 14.25:0.65:0.05:0.06:0.07:0.3：0.26：0.68：17.9：0.68：1.3：0.17：2：5：56.95。
3. a kind of Novel lime stone according to claim 1, is characterized in that, described inWater bag water multicolor finish comprises basic coating, mixes and help material, allotment to help material;
It is 100:90:95 that described basic coating, mixing help material and allotment to help the component ratio of material.
4. a kind of Novel lime stone according to claim 3, is characterized in that, described inBasic coating comprises deionized water, cellulose, defoamer, pH adjusting agent, wetting agent, dividesPowder, titanium dioxide, coalescents, propane diols, Silicone acrylic emulsion, anticorrisive agent, protection sol solution;
Described deionized water, cellulose, defoamer, pH adjusting agent, wetting agent, dispersant,The quality of titanium dioxide, coalescents, propane diols, Silicone acrylic emulsion, anticorrisive agent, protection sol solutionComponent is than being 39.48-40.59:1.36-1.53:0.33:0.14:0.14:0.41:0.1-4.55:1.84-2.35：0.93：41.4-47.05：0.3：7.06。
5. a kind of Novel lime stone according to claim 4, is characterized in that, described inMix and help material to comprise that deionized water, cellulose, protection glue, anticorrisive agent, dispersant and pH adjustJoint agent, described deionized water, cellulose, protection glue, anticorrisive agent, dispersant and pH regulateThe component of agent is than being 96.63:0.27:2.4:0.3:0.3:0.1.
6. a kind of Novel lime stone according to claim 5, is characterized in that, described inAllotment helps material to comprise Silicone acrylic emulsion, coalescents, propane diols, thickener, anticorrisive agent, pHConditioning agent and deionized water;
Described Silicone acrylic emulsion, coalescents, propane diols, thickener, anticorrisive agent, pH regulateThe component of agent and deionized water is than being 89:3.5:1.42:0.15:0.15:0.22:5.56.
7. a preparation method for Novel lime stone, for the preparation of the claims 1-6 itNovel lime stone described in one, is characterized in that, described preparation method comprises the steps:
A) help material to mix basic coating and mixing, and apply comminutor and carry out granulation;
B) after granulation, help material to mix with allotment, mix fully, obtain main material;
C) main material is mixed with aggregate, obtain Novel lime stone.
8. preparation method according to claim 7, is characterized in that, described preparation sideMethod is in described steps A) frontly also comprise basic coating, mix and help material and allotment to help the preparation step of materialSuddenly, the preparation process of described basic coating comprises:
A11) first defoamer, titanium dioxide and cellulose are added in deionized water to juxtapositionIn mixer, stir, described mixing speed is 200-400r/min, when described stirringBetween be 20-25min;
A12) after stirring completes, be warming up to 70-80 DEG C, add Silicone acrylic emulsion, thirdGlycol, coalescents, dispersant and wetting agent, be incubated and vacuumize stirring, and mixing speed is400-500r/min, the retention time is 1h-1.2h;
A13) completing steps A12) the rear pH adjusting agent of adding, adjusting pH is 7.5-8.0, withAfter add again anticorrisive agent and protection sol solution, vacuumize airtightly, add after nitrogen regulation and control pressureTo 1.5-1.8mpa, and intensification value 120-150 DEG C, and carry out density stirring, with100-120r/min stirs 3-5min, stirring after 20-30min with 200-250r/min,Complete the preparation of basic coating;
Described mixing helps the preparation of material to comprise the steps:
After deionized water, cellulose, protection glue, anticorrisive agent and dispersant are mixed, thenAdd pH adjusting agent, keep pH at 7.2-7.5, at room temperature carry out high-speed stirred, described inMixing speed is 60-120r/min;
Described allotment helps the preparation of material to comprise the steps:
A21) described Silicone acrylic emulsion and deionized water are proportionally mixed, mix laggardRow stirs, and described mixing speed is 100-200r/min, and described mixing time is 10-15min;
A22) to steps A 21) add anticorrisive agent, thickener, film forming in the solution that completes and helpAgent, proceeds to stir, and stirs 3-5min, with 200-250r/min with 100-120r/minStir after 20-30min;
A23) to steps A 22) in add again pH adjusting agent, keep pH at 7.2-7.5, thenAdd propane diols, after at room temperature stirring, leave standstill 10min and prepared.
9. preparation method according to claim 7, is characterized in that, described steps A)Middle basic coating and mixing are carried out granulation by comminutor after helping material to mix, after described granulationDiameter dimension is 0.3-0.5mm.