CN105585275A - 一种公路用混凝土外加剂 - Google Patents

一种公路用混凝土外加剂 Download PDF

Info

Publication number
CN105585275A
CN105585275A CN201510978887.6A CN201510978887A CN105585275A CN 105585275 A CN105585275 A CN 105585275A CN 201510978887 A CN201510978887 A CN 201510978887A CN 105585275 A CN105585275 A CN 105585275A
Authority
CN
China
Prior art keywords
parts
concrete
concrete admixture
roads
stearic acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510978887.6A
Other languages
English (en)
Inventor
王兴文
徐荣平
卢祎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU BAIRUIJI NEW MATERIAL CO Ltd
Original Assignee
JIANGSU BAIRUIJI NEW MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU BAIRUIJI NEW MATERIAL CO Ltd filed Critical JIANGSU BAIRUIJI NEW MATERIAL CO Ltd
Priority to CN201510978887.6A priority Critical patent/CN105585275A/zh
Publication of CN105585275A publication Critical patent/CN105585275A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种公路用混凝土外加剂，包括以下重量配比的组分：矿渣70-80份，膨润土10-15份，硅粉8-15份，硬脂酸8-10份，甲基纤维素2-5份，聚丙烯酰氨4-7份，十二烷基硫酸钠8-15份。本发明公路混凝土外加剂对提高混凝土的抗冻能力、抗渗能力和抗腐蚀能力，延长工期有良好的效果，本发明公路混凝土外加剂还具有较高减水率、抗离析性能。

Description

一种公路用混凝土外加剂
技术领域
本发明涉及一种公路混凝土外加剂，属道路交通工程领域。
背景技术
近年来，随着城市化的进程、城乡一体化建设不断加快，混凝土外加剂的作用日趋重要。而众所周知，水泥混凝土材料是当今最大宗的建筑材料之一，在我们生活中，混凝土无处不在。无论是道路、桥梁、建筑、港口、码头、大坝、机场，还是南极的考察站和海洋的钻井平台，人们时时刻刻都可以接触到它，科学家还在研究将水泥混凝土材料用于外层空间。随着科学技术的发展，人们对工程技术、工程质量和建筑物使用寿命的要求愈来愈高。使用混凝土外加剂是提高和改善混凝土各项性能、满足工程耐久性要求的最佳、最有效、最易行的途径之一。
混凝土外加剂品种较多，功能各异。使用各种不同品种的外加剂，可以达到不同的效果，如改善混凝土的工作性、提高硬化混凝土的抗冻融性能、大幅度降低混凝土的用水量，提高混凝土强度、可补偿混凝土干缩，减少混凝土的收缩裂缝、改善混凝土的耐腐蚀性、延长混凝土的使用寿命，提高耐久性等，由此可见混凝土外加剂功效之巨大。但混凝土外加剂的种类品种选用、添加方式等将严重影响其混凝土的工程质量。
目前，市场上供应的混凝土外加剂品种繁多，在实际使用中存在一些缺陷：一是减水效果虽然较好，但泌水率增大，影响其质量均匀性能；二是对水泥品种的适应性差，易造成混凝土的早凝问题，影响工程正常施工，如何既能够在不增大泌水率的前提下提高混凝土的流动性，又能在不会造成混凝土早凝的前提下适应不同水泥品种加工商品混凝土，是解决商品混凝土现代化施工中的一个特出问题。
发明内容
为了解决现有技术中存在的缺陷，本发明提供了一种公路用混凝土外加剂，包括以下重量配比的组分：矿渣70-80份，膨润土10-15份，硅粉8-15份，硬脂酸8-10份，甲基纤维素2-5份，聚丙烯酰氨4-7份，十二烷基硫酸钠8-15份。
上述矿渣、膨润土和硅粉粒径大小为100目-150目。
本发明公路用混凝土外加剂的最佳重量配比为：矿渣70份，膨润土15份，硅粉10份，硬脂酸8份，甲基纤维素3份，聚丙烯酰氨5份，十二烷基硫酸钠12份。
本发明相比现有技术具有以下优点：本发明公路混凝土外加剂对提高混凝土的抗冻能力、抗渗能力和抗腐蚀能力，延长工期有良好的效果，本发明公路混凝土外加剂还具有较高减水率、抗离析性能。
具体实施方式
下面结合具体实施例对本发明进行详细说明。
实施例1
本发明公路用混凝土外加剂的制备：按重量份数取70份矿渣、15份膨润土、10份硅粉混合均匀，将其研磨至100目至150目备用；选硬脂酸8份、甲基纤维素3份、聚丙烯酰氨5份，十二烷基硫酸钠12份，放入封闭式混合机中搅拌混合均匀，密封包装成袋即可。
使用时，在混凝土中添加本发明外加剂，掺量为0.05%-0.10%。添加本发明外加剂后的混凝土性能参数如下：
实施例2
本发明公路用混凝土外加剂的制备：按重量份数取70份矿渣、10份膨润土、8份硅粉混合均匀，将其研磨至100目至150目备用；选硬脂酸8份、甲基纤维素2份、聚丙烯酰氨4份，十二烷基硫酸钠8份，放入封闭式混合机中搅拌混合均匀，密封包装成袋即可。
使用时，在混凝土中添加本发明外加剂，掺量为0.05%-0.10%。添加本发明外加剂后的混凝土性能参数如下：
实施例3
本发明公路用混凝土外加剂的制备：按重量份数取80份矿渣、15份膨润土、15份硅粉混合均匀，将其研磨至100目至150目备用；选硬脂酸10份、甲基纤维素5份、聚丙烯酰氨7份，十二烷基硫酸钠15份，放入封闭式混合机中搅拌混合均匀，密封包装成袋即可。
使用时，在混凝土中添加本发明外加剂，掺量为0.05%-0.10%。添加本发明外加剂后的混凝土性能参数如下：

Claims (3)

1.一种公路用混凝土外加剂，其特征在于：包括以下重量配比的组分：矿渣70-80份，膨润土10-15份，硅粉8-15份，硬脂酸8-10份，甲基纤维素2-5份，聚丙烯酰氨4-7份，十二烷基硫酸钠8-15份。
2.根据权利要求1所述的混凝土外加剂，其特征在于：所述矿渣、膨润土和硅粉粒径大小为100目-150目。
3.根据权利要求1或2所述的混凝土外加剂，其特征在于：包括以下重量配比的组分：矿渣70份，膨润土15份，硅粉10份，硬脂酸8份，甲基纤维素3份，聚丙烯酰氨5份，十二烷基硫酸钠12份。
CN201510978887.6A 2015-12-24 2015-12-24 一种公路用混凝土外加剂 Pending CN105585275A (zh)