CN105566986A - 一种腻子专用纤维素醚 - Google Patents

一种腻子专用纤维素醚 Download PDF

Info

Publication number
CN105566986A
CN105566986A CN201610150296.4A CN201610150296A CN105566986A CN 105566986 A CN105566986 A CN 105566986A CN 201610150296 A CN201610150296 A CN 201610150296A CN 105566986 A CN105566986 A CN 105566986A
Authority
CN
China
Prior art keywords
putty
ether
cellulose ether
cellulose
special
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610150296.4A
Other languages
English (en)
Inventor
张学健
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610150296.4A priority Critical patent/CN105566986A/zh
Publication of CN105566986A publication Critical patent/CN105566986A/zh
Pending legal-status Critical Current

Abstract

一种腻子专用纤维素醚，由以下组份：纤维素醚，有机膨润土，淀粉醚混合配制而成。该发明专门针对腻子系列用的纤维素醚，通过采用高粘度的纤维素醚搭配适量的淀粉醚，既可以保证腻子的保水性的同时也能控制腻子的飞溅程度。配方中添加了有机膨润土，使腻子有合适的粘稠度，另外使得腻子施工时手感更爽滑。该发明的纤维素醚添加到腻子中使用，能有效降低了腻子的成本，并且腻子施工，综合性能优良，值得推广。

Description

一种腻子专用纤维素醚
技术领域
本发明涉及建筑添加剂领域，特别是一种腻子专用纤维素醚。
背景技术
纤维素醚由纤维素制成的具有醚结构的高分子化合物。纤维素大分子中每个葡萄糖基环含有三个羟基，第六碳原子上的伯羟基、第二、三个碳原子上的仲羟基，羟基中的氢被烃基取代而生成纤维醚类衍生物。是纤维素高分子中羟基的氢被烃基取代的生成物。纤维素是一种既不溶解也不熔融的多羟基高分子化合物。纤维素经醚化后则能溶于水、稀碱溶液和有机溶剂，并具有热塑性。
纤维素醚是改善干混砂浆保水性能的关键外加剂，也是决定干混砂浆材料成本的关键外加剂之一。纤维素醚的主要作用就是保水。特别在腻子的批刮中，该组分至关重要，但是由于纤维素醚添加剂的售价较高，直接影响了腻子最终的售价。
发明内容
针对现有技术的不足，本发明提供一种腻子专用纤维素醚，该腻子，施工爽滑，腻子表面易打磨，成本低等特点。
本发明解决技术问题的技术方案如下：
一种腻子专用纤维素醚，其特征在于，由以下组份按照下列重量比配制而成：
纤维素醚70-85份
有机膨润土5-18份
淀粉醚3-8份。
进一步地，所述的纤维素醚是粘度大于20万mpa.s的羟丙基甲基纤维素醚。
进一步地，所述的淀粉醚是醚化度在20-30%的羟丙基淀粉醚。
本发明的有益效果是：该发明专门针对腻子系列用的纤维素醚，
通过采用高粘度的纤维素醚搭配适量的淀粉醚，既可以保证腻子的保水性的同时也能控制腻子的飞溅程度。配方中添加了有机膨润土，使腻子有合适的粘稠度，另外使得腻子施工时手感更爽滑。该发明的纤维素醚添加到腻子中使用，能有效降低了腻子的成本，并且腻子施工，综合性能优良，值得推广。
具体实施方式
以下将结合实施例对本发明的构思、具体组分及产生的技术效果进行清楚、完整地描述，以充分地理解本发明的目的、特征和效果。显然，所描述的实施例只是本发明的一部分实施例，而不是全部实施例，基于本发明的实施例，本领域的技术人员在不付出创造性劳动的前提下所获得的其他实施例，均属于本发明保护的范围。
实施例1：一种腻子专用纤维素醚，其特征在于，由以下组份按照下列重量比配制而成：
纤维素醚82份
有机膨润土12份
淀粉醚6份。
实施例2：一种腻子专用纤维素醚，其特征在于，由以下组份按照下列重量比配制而成：
25万mpa.s的羟丙基甲基纤维素醚78份
有机膨润土15份
醚化度在20-30%的羟丙基淀粉醚7份。
以上对本发明的较佳实施方式进行了具体说明，但本发明创造并不限于所述实施例，熟悉本领域的技术人员在不违背本发明精神的前提下还可作出种种的等同变型或替换，这些等同的变型或替换均包含在本申请权利要求所限定的范围内。

Claims (3)

1.一种腻子专用纤维素醚，其特征在于，由以下组份按照下列重量比配制而成：
纤维素醚70-85份
有机膨润土5-18份
淀粉醚3-8份。
2.根据权利要求1所述的腻子专用纤维素醚，其特征在于，所述的纤维素醚是粘度大于20万mpa.s的羟丙基甲基纤维素醚。
3.根据权利要求1所述的腻子专用纤维素醚，其特征在于，所述的淀粉醚是醚化度在20-30%的羟丙基淀粉醚。
CN201610150296.4A 2016-03-16 2016-03-16 一种腻子专用纤维素醚 Pending CN105566986A (zh)