CN105566782A - Formula of conductor screen anti-ageing cable protective layer material - Google Patents
Formula of conductor screen anti-ageing cable protective layer material Download PDFInfo
- Publication number
- CN105566782A CN105566782A CN201610072113.1A CN201610072113A CN105566782A CN 105566782 A CN105566782 A CN 105566782A CN 201610072113 A CN201610072113 A CN 201610072113A CN 105566782 A CN105566782 A CN 105566782A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- oxide
- cable
- vulcanizing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a formula of a conductor screen anti-ageing cable protective layer material. The conductor screen anti-ageing cable protective layer material is prepared from, by weight, 3.9-5.6 parts of plasticizer, 9.6-12.6 parts of a vulcanizing agent, 18-22 parts of a co-vulcanizing agent, 22-33 parts of zinc oxide, 5.6-6.9 parts of ferric oxide, 30-50 parts of modified nanometer powder, 6.9-15.6 parts of a vulcanizing agent, 15-20 parts of a defoaming agent, 30-38 parts of rare earth oxide, 6-20 parts of modified sepiolite powder, 25-26 parts of magnesium oxide, 20-30 parts of chlorinated polyethylene, 15-20 parts of dimethyl, 22-26 parts of tert-butyl peroxide, 4-6 parts of ethane, 6.5-8.5 parts of a vulcanizing agent, 75-100 parts of filler, 1-2 parts of vinyl triethoxy silane, 1-5 parts of zinc stearate, 1-2 parts of an accelerant CZ, 12-15 parts of aluminium oxide, 15-20 parts of nano calcium carbonate, 1-2 parts of an anti-aging agent RD, 0.2-5.0 parts of a coupling agent and 0.5-5.0 parts of an anti-aging agent. The technological process is simple, the raw material ratio is reasonable, normal use of a cable is ensured, and the cable has good low temperature resistance and flame resistance. The service life of the cable is prolonged, the use effect is good, and quality of the cable product is ensured.
Description
Technical field
The present invention relates to a kind of conductor shielding anti-aging cable covering material prescription.
Background technology
CABLE MATERIALS is the main application fields of insulating material, at present along with the development of the communications field, increasing to the market requirement of CABLE MATERIALS, simultaneously also more and more higher to the performance requriements of CABLE MATERIALS, this cable material, more particularly, the present invention relates in one and presses Plastic-sheathed Cable semiconduction conductor shielding cable material, especially a rubber-type high temperature resistance non halogen semiconduction conductor shielding cable material, belongs to cable material technical field.
In view of the defect existed in above prior art, be necessary it to improve further, make it have more standby practicality, could realistic service condition.
Summary of the invention
In order to overcome the defect of above-mentioned prior art, the object of this invention is to provide a kind of conductor shielding anti-aging cable covering material prescription.
Invention is taked following technical scheme to realize: a kind of conductor shielding anti-aging cable covering material prescription, it is made up of following raw material: get by a point gauge, softening agent 3.9-5.6 part, vulcanizing agent 9.6-12.6 part, co-curing agent 18-22 part, zinc oxide 22-33 part, ferric oxide 5.6-6.9 part, modified Nano powder 30-50 part, vulcanizing agent 6.9-15.6 part, defoamer 15-20 part, rare earth oxide 30-38 part, modified meerschaum powder 6-20 part, magnesium oxide 25-26 part, chlorinatedpolyethylene 20-30 part, dimethyl 15-20 part, tert-butyl hydroperoxide 22-26 part, ethane 4-6 part, vulcanizing agent 6.5-8.5 part, weighting agent 75-100 part, vinyltriethoxysilane 1-2 part, Zinic stearas 1-5 part, accelerant CZ 1-2 part, aluminium sesquioxide 12-15 part, nano-calcium carbonate 15-20 part, anti-aging agent RD 1-2 part, coupling agent 0.2-5.0 part, anti-aging agent 0.5-5.0 part.
Particularly, the present invention it be made up of following raw material: get by a point gauge, 4.2 parts, softening agent, vulcanizing agent 11 parts, co-curing agent 20 parts, 25 parts, zinc oxide, ferric oxide 6.2 parts, 50 parts, modified Nano powder, vulcanizing agent 12.9 parts, defoamer 18 parts, rare earth oxide 32 parts, 18 parts, modified meerschaum powder, 25 parts, magnesium oxide, chlorinatedpolyethylene 30 parts, dimethyl 20 parts, tert-butyl hydroperoxide 25 parts, 5 parts, ethane, vulcanizing agent 7 parts, weighting agent 80 parts, vinyltriethoxysilane 2 parts, Zinic stearas 5 parts, accelerant CZ 2 parts, aluminium sesquioxide 13 parts, nano-calcium carbonate 18 parts, anti-aging agent RD 1 part, coupling agent 3 parts, 2 parts, anti-aging agent.
Beneficial effect of the present invention: present invention process flow process is succinct, reasonable raw material proportioning, preparation method is simple, for cable provides high-quality weighting agent, raw material is easy to get, and has high thermal resistance, there is certain flame retardant resistance simultaneously, avoid core temperature too high and cause security incident, result of use is obvious, ensure that the reasonable employment of feature cable.
Embodiment
For make the present invention existing technique means, creation characteristic, reach object and effect is easy to understand, below in conjunction with embodiment, set forth the present invention further.
The present invention takes following technical scheme to realize: a kind of conductor shielding anti-aging cable covering material prescription, it is made up of following raw material: get by a point gauge, softening agent 3.9-5.6 part, vulcanizing agent 9.6-12.6 part, co-curing agent 18-22 part, zinc oxide 22-33 part, ferric oxide 5.6-6.9 part, modified Nano powder 30-50 part, vulcanizing agent 6.9-15.6 part, defoamer 15-20 part, rare earth oxide 30-38 part, modified meerschaum powder 6-20 part, magnesium oxide 25-26 part, chlorinatedpolyethylene 20-30 part, dimethyl 15-20 part, tert-butyl hydroperoxide 22-26 part, ethane 4-6 part, vulcanizing agent 6.5-8.5 part, weighting agent 75-100 part, vinyltriethoxysilane 1-2 part, Zinic stearas 1-5 part, accelerant CZ 1-2 part, aluminium sesquioxide 12-15 part, nano-calcium carbonate 15-20 part, anti-aging agent RD 1-2 part, coupling agent 0.2-5.0 part, anti-aging agent 0.5-5.0 part.
As preferred version of the present invention, the present invention it be made up of following raw material: get by a point gauge, 4.2 parts, softening agent, vulcanizing agent 11 parts, co-curing agent 20 parts, 25 parts, zinc oxide, ferric oxide 6.2 parts, 50 parts, modified Nano powder, vulcanizing agent 12.9 parts, defoamer 18 parts, rare earth oxide 32 parts, 18 parts, modified meerschaum powder, 25 parts, magnesium oxide, chlorinatedpolyethylene 30 parts, dimethyl 20 parts, tert-butyl hydroperoxide 25 parts, 5 parts, ethane, vulcanizing agent 7 parts, weighting agent 80 parts, vinyltriethoxysilane 2 parts, Zinic stearas 5 parts, accelerant CZ 2 parts, aluminium sesquioxide 13 parts, nano-calcium carbonate 18 parts, anti-aging agent RD 1 part, coupling agent 3 parts, 2 parts, anti-aging agent.
Although give detailed description and explanation to the specific embodiment of the present invention above; but what should indicate is; we can carry out various equivalence according to conception of the present invention to above-mentioned embodiment and change and amendment; its function produced do not exceed that specification sheets contains yet spiritual time, all should within protection scope of the present invention.
Claims (2)
1. a conductor shielding anti-aging cable covering material prescription, it is characterized in that, it is made up of following raw material: get by a point gauge, softening agent 3.9-5.6 part, vulcanizing agent 9.6-12.6 part, co-curing agent 18-22 part, zinc oxide 22-33 part, ferric oxide 5.6-6.9 part, modified Nano powder 30-50 part, vulcanizing agent 6.9-15.6 part, defoamer 15-20 part, rare earth oxide 30-38 part, modified meerschaum powder 6-20 part, magnesium oxide 25-26 part, chlorinatedpolyethylene 20-30 part, dimethyl 15-20 part, tert-butyl hydroperoxide 22-26 part, ethane 4-6 part, vulcanizing agent 6.5-8.5 part, weighting agent 75-100 part, vinyltriethoxysilane 1-2 part, Zinic stearas 1-5 part, accelerant CZ 1-2 part, aluminium sesquioxide 12-15 part, nano-calcium carbonate 15-20 part, anti-aging agent RD 1-2 part, coupling agent 0.2-5.0 part, anti-aging agent 0.5-5.0 part.
2. a kind of conductor shielding anti-aging cable covering material prescription according to claim 1, it is characterized in that, it is made up of following raw material: get by a point gauge, 4.2 parts, softening agent, vulcanizing agent 11 parts, co-curing agent 20 parts, 25 parts, zinc oxide, ferric oxide 6.2 parts, 50 parts, modified Nano powder, vulcanizing agent 12.9 parts, defoamer 18 parts, rare earth oxide 32 parts, 18 parts, modified meerschaum powder, 25 parts, magnesium oxide, chlorinatedpolyethylene 30 parts, dimethyl 20 parts, tert-butyl hydroperoxide 25 parts, 5 parts, ethane, vulcanizing agent 7 parts, weighting agent 80 parts, vinyltriethoxysilane 2 parts, Zinic stearas 5 parts, accelerant CZ 2 parts, aluminium sesquioxide 13 parts, nano-calcium carbonate 18 parts, anti-aging agent RD 1 part, coupling agent 3 parts, 2 parts, anti-aging agent.