A kind of industrial waste water purifying agent
Technical field
The present invention relates to a kind of industrial waste water purifying agent.
Background technology
Along with the progress of society, modern technologies are in development, and industrial pollution is also day by day serious, especially industrial wastewater pollution, administer suitable difficulty, the method for traditional improvement water pollutions by filtering-depositing, the pollutent in water is separated, but this kind of method can not deal with problems basic; In development afterwards, it is settlement separate that Industrial Waste Water Treatments uses some chemical reagent to carry out, although achieve some effects, the efficiency of process is low.In addition, also have absorption method, absorption method mainly adopts the modes such as exchange adsorption, physical adsorption or chemisorption, is adsorbed onto sorbent material, to reach the object of removal by pollutent from waste water.Adsorption effect is subject to the impact of the factor such as structures and characteristics and operating procedure of sorbent structure, character and pollutent, and conventional sorbent material has gac, resin, activated carbon fiber, diatomite etc.The advantage of this method is that facility investment is few, treatment effect good, floor space is little.But because the loading capacity of sorbent material is limited, the regeneration after absorption often energy consumption is very large, and after discarded, discharge easily causes secondary pollution, is not suitable for large-scale popularization.
Summary of the invention
The defect that the present invention seeks to exist for prior art provides a kind of industrial waste water purifying agent.
The present invention for achieving the above object, adopt following technical scheme: a kind of industrial waste water purifying agent, is made up of the component of following weight part: polymerize aluminum chloride 5-12 part, bodied ferric sulfate 3-7 part, magnesium chloride 2-5 part, polyacrylamide 6-9 part, clorox 4-8 part, calcium oxide 8-15 part, sulphur 4-6 part, silica 1 1-15 part, tensio-active agent 13-18 part, biological disinfectant 7-10 part and dehydrated alcohol 80-90 part.
Further, be made up of the component of following weight part: polymerize aluminum chloride 5 parts, bodied ferric sulfate 3 parts, 2 parts, magnesium chloride, polyacrylamide 6 parts, clorox 4 parts, 8 parts, calcium oxide, 4 parts, sulphur, silica 11 part, 13 parts, tensio-active agent, biological disinfectant 7 parts and dehydrated alcohol 80 parts.
Further, be made up of the component of following weight part: polymerize aluminum chloride 8 parts, bodied ferric sulfate 5 parts, 3 parts, magnesium chloride, polyacrylamide 7 parts, clorox 6 parts, 12 parts, calcium oxide, 5 parts, sulphur, silica 13 parts, 15 parts, tensio-active agent, biological disinfectant 8 parts and dehydrated alcohol 85 parts.
Further, be made up of the component of following weight part: polymerize aluminum chloride 12 parts, bodied ferric sulfate 7 parts, 5 parts, magnesium chloride, polyacrylamide 9 parts, clorox 8 parts, 15 parts, calcium oxide, 6 parts, sulphur, silica 15 parts, 18 parts, tensio-active agent, biological disinfectant 10 parts and dehydrated alcohol 90 parts.
Further, described tensio-active agent is the mixture of any three kinds in TX-10, FMES, LAS, AEO-9, TX-10, OP-10, QYL-83C and Y-35.
Further, described biological disinfectant is made up of alginate fiber element.
Beneficial effect of the present invention: wastewater purificant of the present invention has very strong throwing out, the clearance of suspended substance and heavy metal is high, and has good biological antibiotic effect, reduces the harm of secondary pollution, more environmental protection.
Embodiment
The present invention relates to a kind of industrial waste water purifying agent, be made up of the component of following weight part: polymerize aluminum chloride 5-12 part, bodied ferric sulfate 3-7 part, magnesium chloride 2-5 part, polyacrylamide 6-9 part, clorox 4-8 part, calcium oxide 8-15 part, sulphur 4-6 part, silica 1 1-15 part, tensio-active agent 13-18 part, biological disinfectant 7-10 part and dehydrated alcohol 80-90 part.
Wherein, described tensio-active agent is the mixture of any three kinds in TX-10, FMES, LAS, AEO-9, TX-10, OP-10, QYL-83C and Y-35.Wherein, described biological disinfectant is made up of alginate fiber element.
Embodiment 1:
The preparation method of above-mentioned wastewater purificant, according to weight parts, comprises the steps:
1) dehydrated alcohol of 80 parts, is got, put in reactor, then the polymerize aluminum chloride of 5 parts, the bodied ferric sulfate of 3 parts and the magnesium chloride of 2 parts is got, and be poured into successively in reactor and carry out mix and blend, stirring velocity is 60 revs/min, whipping temp is 20 degree, and churning time is 10 minutes, obtains mixed liquor A;
2), in reactor, slowly add the calcium oxide of the polyacrylamide of 6 parts, the clorox of 4 parts and 8 parts, and carry out mix and blend, stirring velocity is 50 revs/min, and whipping temp is 30 degree, and churning time is 10 minutes, obtains mixed liquid B;
3), in mixed liquid B, add the sulphur of 4 parts and the silicon-dioxide of 11 parts, and carry out mix and blend, stirring velocity is 60 revs/min, and whipping temp is 22 degree, and churning time is 10 minutes, obtains mixed solution C;
4), add the tensio-active agent of 13 parts and the biological disinfectant of 7 parts in the most backward mixed solution C, and carry out mix and blend, stirring velocity is 30 revs/min, and whipping temp is 50 degree, and churning time is 20 minutes, then 2 hours are left standstill, finally obtained wastewater purificant of the present invention.
During use, get and evenly joined in purification tank for liquid waste by above-mentioned wastewater purificant, after leaving standstill for some time, the removal efficiency detecting waste water reaches more than 80%, and heavy metal removes rate and reaches more than 95%, and degerming rate reaches more than 92%.
Embodiment 2:
The preparation method of above-mentioned wastewater purificant, according to weight parts, comprises the steps:
1) dehydrated alcohol of 85 parts, is got, put in reactor, then the polymerize aluminum chloride of 8 parts, the bodied ferric sulfate of 5 parts and the magnesium chloride of 3 parts is got, and be poured into successively in reactor and carry out mix and blend, stirring velocity is 70 revs/min, whipping temp is 25 degree, and churning time is 12 minutes, obtains mixed liquor A;
2), in reactor, slowly add the calcium oxide of the polyacrylamide of 7 parts, the clorox of 6 parts and 12 parts, and carry out mix and blend, stirring velocity is 55 revs/min, and whipping temp is 35 degree, and churning time is 15 minutes, obtains mixed liquid B:
3), in mixed liquid B, add the sulphur of 5 parts and the silicon-dioxide of 13 parts, and carry out mix and blend, stirring velocity is 65 revs/min, and whipping temp is 27 degree, and churning time is 14 minutes, obtains mixed solution C;
4), add the tensio-active agent of 15 parts and the biological disinfectant of 8 parts in the most backward mixed solution C, and carry out mix and blend, stirring velocity is 40 revs/min, and whipping temp is 55 degree, and churning time is 25 minutes, then 2.5 hours are left standstill, finally obtained wastewater purificant of the present invention.
During use, get and evenly joined in purification tank for liquid waste by above-mentioned wastewater purificant, after leaving standstill for some time, the removal efficiency detecting waste water reaches more than 80%, and heavy metal removes rate and reaches more than 95%, and degerming rate reaches more than 92%.
Embodiment 3:
The preparation method of above-mentioned wastewater purificant, according to weight parts, comprises the steps:
1) dehydrated alcohol of 90 parts, is got, put in reactor, then the polymerize aluminum chloride of 12 parts, the bodied ferric sulfate of 7 parts and the magnesium chloride of 5 parts is got, and be poured into successively in reactor and carry out mix and blend, stirring velocity is 80 revs/min, whipping temp is 30 degree, and churning time is 15 minutes, obtains mixed liquor A;
2), in reactor, slowly add the calcium oxide of the polyacrylamide of 9 parts, the clorox of 8 parts and 15 parts, and carry out mix and blend, stirring velocity is 60 revs/min, and whipping temp is 40 degree, and churning time is 20 minutes, obtains mixed liquid B:
3), in mixed liquid B, add the sulphur of 6 parts and the silicon-dioxide of 15 parts, and carry out mix and blend, stirring velocity is 70 revs/min, and whipping temp is 32 degree, and churning time is 16 minutes, obtains mixed solution C;
4), add the tensio-active agent of 18 parts and the biological disinfectant of 10 parts in the most backward mixed solution C, and carry out mix and blend, stirring velocity is 50 revs/min, and whipping temp is 60 degree, and churning time is 30 minutes, then 3 hours are left standstill, finally obtained wastewater purificant of the present invention.
During use, get and evenly joined in purification tank for liquid waste by above-mentioned wastewater purificant, after leaving standstill for some time, the removal efficiency detecting waste water reaches more than 97%, and heavy metal removes rate and reaches more than 98%, and degerming rate reaches more than 98%.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.