CN105547921A - 改性沥青存储稳定性标准粘度检测法 - Google Patents

改性沥青存储稳定性标准粘度检测法 Download PDF

Info

Publication number
CN105547921A
CN105547921A CN201610000817.8A CN201610000817A CN105547921A CN 105547921 A CN105547921 A CN 105547921A CN 201610000817 A CN201610000817 A CN 201610000817A CN 105547921 A CN105547921 A CN 105547921A
Authority
CN
China
Prior art keywords
steel tube
stainless
height
ball valve
modified asphalt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610000817.8A
Other languages
English (en)
Inventor
王秀芳
张常安
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Northwest Minzu University
Original Assignee
Northwest Minzu University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Northwest Minzu University filed Critical Northwest Minzu University
Priority to CN201610000817.8A priority Critical patent/CN105547921A/zh
Publication of CN105547921A publication Critical patent/CN105547921A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种改性沥青存储稳定性标准粘度检测法，该方法包括以下步骤：⑴在两端开口的不锈钢管的底端、1/3高度处、2/3高度处分别设有出样口，该出样口处均设有球阀；⑵关闭不锈钢管底端的球阀，开启不锈钢管1/3高度处及2/3高度处的球阀；然后将过滤后的改性沥青样品加热并灌入不锈钢管；⑶将不锈钢管放入烘箱加热48±1h后自然冷却至室温；⑷将冷却到室温的改性沥青样品再次加热熔化；然后，通过调节球阀开启或闭合，分别使上部三分一的改性沥青注入标准粘度试验仪Ⅰ中进行标准粘度试验，下部三分一改性沥青注入标准粘度试验仪Ⅱ中进行标准粘度试验；将两个结果进行对比，即可分析其稳定性。本发明结果准确、效率高。

Description

改性沥青存储稳定性标准粘度检测法
技术领域
本发明涉及改性沥青试验技术领域，尤其涉及改性沥青存储稳定性标准粘度检测法。
背景技术
目前，在进行改性沥青离析试验时存在下述缺陷：
⑴试验条件不能很好地模拟改性沥青的存储实际条件，试验温度条件与实际不符（试验条件163℃±5℃烘箱加热48±1h后，再在零度以下冰箱冷冻至少4小时后再经熔融做存储稳定性离析试验，实际改性沥青储存时温度无此急冷急热变化过程）；52小时试验时间，即使试验结果可靠，也只能保证改性沥青在52小时内稳定的，无法保证存储时间大于52小时稳定。
⑵以铝管或玻璃试管作为改性沥青试样容器不能重复利用，浪费资源，再者采用玻璃试管冷冻至少4小时后砸破，还增多了试验环境的不安全因素。
⑶试验容器尺寸长细比和现场沥青存储设备几何尺寸比例不相符。
⑷改性沥青试样在冰箱冷冻过程中，使改性沥青的离析速度变慢，和实际离析过程差别较大。
⑸采用软化点分析改性沥青存储稳定性试验过程中需对改性沥青多次加热冷却（即加热，冷冻，加热，冷却，再加热），反复加热的过程中加速了改性沥青的老化，同时反复加热使试验周期延长，试验效率降低，更重要的是试验冷热循环过程与实际存储冷热过程不一致。不能很好反映实际存储稳定性情况。
发明内容
本发明所要解决的技术问题是提供一种结果准确、效率高的改性沥青存储稳定性标准粘度检测法。
为解决上述问题，本发明所述的改性沥青存储稳定性标准粘度检测法，包括以下步骤：
⑴在两端开口的不锈钢管的底端、1/3高度处、2/3高度处分别设有出样口，该出样口处均设有球阀；
⑵关闭所述步骤⑴所得的不锈钢管底端的所述球阀，开启所述不锈钢管1/3高度处及2/3高度处的所述球阀；然后将0.3mm筛过滤后的200±5g改性沥青样品加热并灌入所述不锈钢管；
⑶将所述步骤⑵所得的不锈钢管放入烘箱，于163℃±5℃加热48±1h后自然冷却至室温；
⑷将冷却到室温的改性沥青样品在163℃±5℃下再次加热熔化；然后，关闭所述不锈钢管上1/3高度处、2/3高度处及底端的所述球阀，使上部三分一的改性沥青注入标准粘度试验仪Ⅰ中进行标准粘度试验；关闭所述不锈钢管上1/3高度处及2/3高度处的所述球阀，开启所述不锈钢管底端的所述球阀，使下部三分一改性沥青注入标准粘度试验仪Ⅱ中进行标准粘度试验；将两个结果进行对比，即可分析其稳定性。
所述步骤⑴中不锈钢管的内径为40mm，长为250mm。
本发明与现有技术相比具有以下优点：
1、本发明试样容器以不锈钢管代替铝管或试管，不但节约试验材料，而且可重复利用，提高实验仪器的利用率及实验的安全性。
2、本发明在不锈钢管的底端、1/3高度处、2/3高度处均设有球阀，因此，当改性沥青在烘箱加热和在自然条件下冷却的过程中1/3高度处、2/3高度处两个球阀处于开启状态，底端球阀处于关闭状态，确保整个管内改性沥青中改性剂自由下沉或上浮；当进行软化点或粘度试验时，通过控制球阀将管内改性沥青分为三段，避免在上下改性沥青倒出时混合，确保试验结果的准确性。
3、本发明将冰箱快速冷却过程改为自然条件下冷却，更好地模拟改性沥青实际储存过程中的离析过程，提高试验效率。
附图说明
下面结合附图对本发明的具体实施方式作进一步详细的说明。
图1为本发明中不锈钢管的结构示意图。
图中：1—球阀2—不锈钢管。
具体实施方式
改性沥青存储稳定性标准粘度检测法，包括以下步骤：
⑴在两端开口的不锈钢管2的底端、1/3高度处、2/3高度处分别设有出样口，该出样口处均设有球阀1（参见图1）。
其中：不锈钢管2的内径为40mm，长为250mm。
⑵关闭步骤⑴所得的不锈钢管2底端的球阀1，开启不锈钢管21/3高度处及2/3高度处的所述球阀1；然后将0.3mm筛过滤后的200±5g改性沥青样品加热并灌入不锈钢管2。
⑶将步骤⑵所得的不锈钢管2放入烘箱，于163℃±5℃加热48±1h后自然冷却至室温。
⑷将冷却到室温的改性沥青样品在163℃±5℃下再次加热熔化；然后，关闭不锈钢管2上1/3高度处、2/3高度处及底端的球阀1，使上部三分一的改性沥青注入标准粘度试验仪Ⅰ中进行标准粘度试验；关闭不锈钢管2上1/3高度处及2/3高度处的球阀1，开启不锈钢管2底端的球阀1，使下部三分一改性沥青注入标准粘度试验仪Ⅱ中进行标准粘度试验；将两个结果进行对比，即可分析其稳定性。

Claims (2)

1.改性沥青存储稳定性标准粘度检测法，包括以下步骤：
⑴在两端开口的不锈钢管（2）的底端、1/3高度处、2/3高度处分别设有出样口，该出样口处均设有球阀（1）；
⑵关闭所述步骤⑴所得的不锈钢管（2）底端的所述球阀（1），开启所述不锈钢管（2）1/3高度处及2/3高度处的所述球阀（1）；然后将0.3mm筛过滤后的200±5g改性沥青样品加热并灌入所述不锈钢管（2）；
⑶将所述步骤⑵所得的不锈钢管（2）放入烘箱，于163℃±5℃加热48±1h后自然冷却至室温；
⑷将冷却到室温的改性沥青样品在163℃±5℃下再次加热熔化；然后，关闭所述不锈钢管（2）上1/3高度处、2/3高度处及底端的所述球阀（1），使上部三分一的改性沥青注入标准粘度试验仪Ⅰ中进行标准粘度试验；关闭所述不锈钢管（2）上1/3高度处及2/3高度处的所述球阀（1），开启所述不锈钢管（2）底端的所述球阀（1），使下部三分一改性沥青注入标准粘度试验仪Ⅱ中进行标准粘度试验；将两个结果进行对比，即可分析其稳定性。
2.如权利要求1所述的改性沥青存储稳定性标准粘度检测法，其特征在于：所述步骤⑴中不锈钢管（2）的内径为40mm，长为250mm。
CN201610000817.8A 2016-01-04 2016-01-04 改性沥青存储稳定性标准粘度检测法 Pending CN105547921A (zh)