CN105542536A - Pigment with natural tone and stability and preparation method of pigment - Google Patents
Pigment with natural tone and stability and preparation method of pigment Download PDFInfo
- Publication number
- CN105542536A CN105542536A CN201610129581.8A CN201610129581A CN105542536A CN 105542536 A CN105542536 A CN 105542536A CN 201610129581 A CN201610129581 A CN 201610129581A CN 105542536 A CN105542536 A CN 105542536A
- Authority
- CN
- China
- Prior art keywords
- powder
- parts
- ultra
- pigment
- phenylalanine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to pigment with natural tone and stability and a preparation method of the pigment. The pigment comprises components in parts as follows: 30-50 parts of lapis lazuli, 10-20 parts of glass fibers, 20-30 parts of pearl powder, 25-30 parts of polyester fibers, 5-10 parts of phenylalanine and 15-25 parts of talc powder. The preparation method comprises preparation steps as follows: the lapis lazuli, the polyester fibers, the glass fibers and phenylalanine are subjected to first ultramicro grinding and then sieved, remaining material on a sieve are subjected to second ultramicro grinding and then sieved, pearl ultramicro powder, lapis lazuli ultramicro powder, polyester fiber ultramicro powder, glass fiber ultramicro powder, phenylalanine ultramicro powder and the talc powder are mixed and added with warm water, pre-pigment is prepared and finally filtered by a filter net, and the pigment is obtained. The lapis lazuli is added to constituent components of conventional pigment, so that the stability of the pigment is effectively improved, the tone naturality is improved, and fading is not easily caused.
Description
Technical field
The present invention relates to chemical field, be specially and a kind ofly there is Natural color be in harmonious proportion pigment and preparation method thereof of stability.
Background technology
Drawing is on technological layer, and be one and then on it, add the way of color using surface as bearing surface, those surfaces can be paper or cloth, add color instrument can by paintbrush, also can by brush, sponge or cloth etc.Divide by type, comprise oil painting, etching, gouache, mural painting, caricature, inside-paint, sketch, traditional Chinese painting, blue-and-green landscape picture etc., but regardless of that type, pigment is drawn view picture and is all played very important impact, good pigment can play the effect of crucial touch, otherwise pigment inferior then often allows view picture picture therefore die young.
But, in the market most pigment all in various degree there is flaw: tone is pure but lasting, fast light but tone is untrue, and tone is pure fast light lasting but too expensive etc.
Summary of the invention
The object of the invention is to solve the problem, propose a kind ofly there is Natural color to be in harmonious proportion pigment and preparation method thereof of stability, effectively improve the stability of pigment and improve the naturality of tone, and being not easy to fade.
The present invention proposes a kind ofly to be had Natural color and is in harmonious proportion pigment and preparation method thereof of stability.
Calculate by number, comprise following composition: oriental lapis 30-50 part, glass fibre 10-20 part, pearl powder 20-30 part, trevira 25-30 part, phenylalanine 5-10 part and talcum powder 15-25 part;
The described preparation method with the pigment of Natural color mediation stability, carries out according to the following steps:
1) first time micronizing: oriental lapis, trevira, glass fibre and phenylalanine are crushed to respectively granularity≤25 μm of 90.0% through Ultra-Micro Grinding Equipment;
2) sieve: by Pearl and first time micronizing after oriental lapis, trevira, glass fibre and phenylalanine respectively cross 200 mesh sieves, take off material, obtain pearl fine powder, oriental lapis fine powder, trevira fine powder, glass fibre fine powder and phenylalanine fine powder;
3) second time micronizing and sieving: by step 2) clout of oriental lapis, trevira, glass fibre and phenylalanine after Pearl on screen cloth and first time micronizing carries out second time micronizing respectively, after 200 mesh sieves, take off material, obtain pearl ultra-micro powder, oriental lapis ultra-micro powder, trevira ultra-micro powder, glass fibre ultra-micro powder and phenylalanine ultra-micro powder;
4) tentatively modulate: pearl ultra-micro powder, oriental lapis ultra-micro powder, trevira ultra-micro powder, glass fibre ultra-micro powder, phenylalanine ultra-micro powder and talcum powder are mixed, stirs after adding warm water, obtain pre-pigment;
5) filtering net: pour pre-pigment into filter bag, after excluding undesired impurities, obtains pigment.
More specifically, the ratio of pearl ultra-micro powder in described step 4), oriental lapis ultra-micro powder, trevira ultra-micro powder, glass fibre ultra-micro powder, phenylalanine ultra-micro powder and talcous mixture and warm water is 20:1.
Preferred, in described step 4), the water temperature of warm water is 30-35 DEG C.
Preferred, filter bag >=200 order in described step 5).
The present invention adds oriental lapis in conventional pigment moiety, effectively improves the stability of pigment and improves the naturality of tone, and being not easy to fade.
Embodiment
Below provide the specific embodiment of the present invention, be used for being described in further detail formation of the present invention.
embodiment 1
The pigment with Natural color mediation stability of this enforcement, calculates by number, comprises following composition:
Oriental lapis 30 parts, 10 parts, glass fibre, pearl powder 20 parts, 25 parts, trevira, phenylalanine 5 parts and talcum powder 15 parts;
The described preparation method with the pigment of Natural color mediation stability, carries out according to the following steps:
1) first time micronizing: oriental lapis, trevira, glass fibre and phenylalanine are crushed to respectively granularity≤25 μm of 90.0% through Ultra-Micro Grinding Equipment;
2) sieve: by Pearl and first time micronizing after oriental lapis, trevira, glass fibre and phenylalanine respectively cross 200 mesh sieves, take off material, obtain pearl fine powder, oriental lapis fine powder, trevira fine powder, glass fibre fine powder and phenylalanine fine powder;
3) second time micronizing and sieving: by step 2) clout of oriental lapis, trevira, glass fibre and phenylalanine after Pearl on screen cloth and first time micronizing carries out second time micronizing respectively, after 200 mesh sieves, take off material, obtain pearl ultra-micro powder, oriental lapis ultra-micro powder, trevira ultra-micro powder, glass fibre ultra-micro powder and phenylalanine ultra-micro powder;
4) tentatively modulate: pearl ultra-micro powder, oriental lapis ultra-micro powder, trevira ultra-micro powder, glass fibre ultra-micro powder, phenylalanine ultra-micro powder and talcum powder are mixed, stirs after adding warm water, obtain pre-pigment;
5) filtering net: pour pre-pigment into filter bag, after excluding undesired impurities, obtains pigment.
More specifically, the ratio of pearl ultra-micro powder in described step 4), oriental lapis ultra-micro powder, trevira ultra-micro powder, glass fibre ultra-micro powder, phenylalanine ultra-micro powder and talcous mixture and warm water is 20:1.
Preferred, in described step 4), the water temperature of warm water is 30 DEG C.
Preferred, filter bag >=200 order in described step 5).
The present invention adds oriental lapis in conventional pigment moiety, effectively improves the stability of pigment and improves the naturality of tone, and being not easy to fade.
Oriental lapis (English: Lapislazuli, derives from Latin) is CHYOU beautiful jade, aurin, a beautiful gem fine jade, indigo naturalis etc. at Ancient Chinese designate.Buddhism be called bark exert from or ancient piece of jade, round, flat and with a hole in its centre coloured glaze, be one of witness that ancient times, oriental and occidental cultures exchanged, data shows, and oriental lapis imports China by " Silk Road " into from Afghanistan.It typically is aggregate output, in compact mass, granular texture.Color is mazarine, hyacinthine, sky blue, turquoise etc., oriental lapis is in the choice with uniform color flawless, and quality is fine and smooth is good without Venus, takes second place without spilling gold in vain, if spilling gold, to refer to that Venus is uniformly distributed pyrite content lower, do not occur that on surface Venus does not also affect quality.Because oriental lapis has beautiful sky blue, so Ancient Times in China is very early using its blue pigments as colored drawing; And the Dunhuang Caves are that the application oriental lapis pigment time is the longest, one of place that consumption is maximum.Oriental lapis pigment is all applied in the Northern Dynasties to the rock cave mural painting, painted sculptures art of unit.
Glass fibre (English original name is: glassfiber or fiberglass) is a kind of ceramic of excellent performance, and of a great variety, advantage is good insulating, thermotolerance is strong, erosion resistance good, and physical strength is high.Its main component is silicon-dioxide, aluminum oxide, calcium oxide, boron oxide, magnesium oxide, sodium oxide etc., according to the number of alkali content in glass, alkali free glass fibre (sodium oxide 0% ~ 2% can be divided into, belong to aluminium borosilicate glass), medium-alkali glass fibre (sodium oxide 8% ~ 12%, the soda lime glass of genus boracic or not boracic) and high alkali glass fibre (sodium oxide more than 13% belongs to soda lime glass).
Talcum powder, English by name PULVISTALCI, for white or off-white color, fine, without the powder of grittiness, hand touches with greasy feeling, odorless, tasteless.Talcum has oilness, anti-stick, help that stream, resistivity against fire, resistance to acid, insulativity, fusing point are high, chemical torpescence, opacifying power well, softness, good luster, the adsorptive power excellent Wuli-Shili-Renli system approach such as strong, crystal structure due to talcum is stratiform, so have the trend and special slip that easily split into scale, if the content of Fe2O3 is very high, its insulativity can be lowered; Matter is soft, its Mohs' hardness coefficient is 1 ~ 1.5, and have sliding sense, { 001} cleavage is extremely complete, very easily split into thin slice, natural repose angle little (35 ° ~ 40 °), built on the sand, country rock is the magnesite of silication and talcum, magnesite rock, lean ore or dolomitic marble in pole, except minority moderately stable, generally all built on the sand, joint, cranny development, the impact of physico-mechanical properties on production practice of ore and country rock is very large.Talcum powder, as the moiety of pigment, has high temperature nondiscoloration, the effects such as even density, glossiness are good, surface smoothing.
embodiment 2
The pigment with Natural color mediation stability of this enforcement, calculates by number, comprises following composition:
Oriental lapis 50 parts, 20 parts, glass fibre, pearl powder 30 parts, 30 parts, trevira, phenylalanine 10 parts and talcum powder 25 parts;
The described preparation method with the pigment of Natural color mediation stability, carries out according to the following steps:
1) first time micronizing: oriental lapis, trevira, glass fibre and phenylalanine are crushed to respectively granularity≤25 μm of 90.0% through Ultra-Micro Grinding Equipment;
2) sieve: by Pearl and first time micronizing after oriental lapis, trevira, glass fibre and phenylalanine respectively cross 200 mesh sieves, take off material, obtain pearl fine powder, oriental lapis fine powder, trevira fine powder, glass fibre fine powder and phenylalanine fine powder;
3) second time micronizing and sieving: by step 2) clout of oriental lapis, trevira, glass fibre and phenylalanine after Pearl on screen cloth and first time micronizing carries out second time micronizing respectively, after 200 mesh sieves, take off material, obtain pearl ultra-micro powder, oriental lapis ultra-micro powder, trevira ultra-micro powder, glass fibre ultra-micro powder and phenylalanine ultra-micro powder;
4) tentatively modulate: pearl ultra-micro powder, oriental lapis ultra-micro powder, trevira ultra-micro powder, glass fibre ultra-micro powder, phenylalanine ultra-micro powder and talcum powder are mixed, stirs after adding warm water, obtain pre-pigment;
5) filtering net: pour pre-pigment into filter bag, after excluding undesired impurities, obtains pigment.
More specifically, in described step 4), the water temperature of warm water is 35 DEG C.
embodiment 3
The pigment with Natural color mediation stability of this enforcement, calculates by number, comprises following composition:
Oriental lapis 40 parts, 15 parts, glass fibre, pearl powder 25 parts, 28 parts, trevira, phenylalanine 8 parts and talcum powder 20 parts;
The described preparation method with the pigment of Natural color mediation stability, carries out according to the following steps:
1) first time micronizing: oriental lapis, trevira, glass fibre and phenylalanine are crushed to respectively granularity≤25 μm of 90.0% through Ultra-Micro Grinding Equipment;
2) sieve: by Pearl and first time micronizing after oriental lapis, trevira, glass fibre and phenylalanine respectively cross 200 mesh sieves, take off material, obtain pearl fine powder, oriental lapis fine powder, trevira fine powder, glass fibre fine powder and phenylalanine fine powder;
3) second time micronizing and sieving: by step 2) clout of oriental lapis, trevira, glass fibre and phenylalanine after Pearl on screen cloth and first time micronizing carries out second time micronizing respectively, after 200 mesh sieves, take off material, obtain pearl ultra-micro powder, oriental lapis ultra-micro powder, trevira ultra-micro powder, glass fibre ultra-micro powder and phenylalanine ultra-micro powder;
4) tentatively modulate: pearl ultra-micro powder, oriental lapis ultra-micro powder, trevira ultra-micro powder, glass fibre ultra-micro powder, phenylalanine ultra-micro powder and talcum powder are mixed, stirs after adding warm water, obtain pre-pigment;
5) filtering net: pour pre-pigment into filter bag, after excluding undesired impurities, obtains pigment.
More specifically, in described step 4), the water temperature of warm water is 32 DEG C.
embodiment 4
The pigment with Natural color mediation stability of this enforcement, calculates by number, comprises following composition:
Oriental lapis 45 parts, 14 parts, glass fibre, pearl powder 16 parts, 26 parts, trevira, phenylalanine 9 parts and talcum powder 23 parts;
The described preparation method with the pigment of Natural color mediation stability, carries out according to the following steps:
1) first time micronizing: oriental lapis, trevira, glass fibre and phenylalanine are crushed to respectively granularity≤25 μm of 90.0% through Ultra-Micro Grinding Equipment;
2) sieve: by Pearl and first time micronizing after oriental lapis, trevira, glass fibre and phenylalanine respectively cross 200 mesh sieves, take off material, obtain pearl fine powder, oriental lapis fine powder, trevira fine powder, glass fibre fine powder and phenylalanine fine powder;
3) second time micronizing and sieving: by step 2) clout of oriental lapis, trevira, glass fibre and phenylalanine after Pearl on screen cloth and first time micronizing carries out second time micronizing respectively, after 200 mesh sieves, take off material, obtain pearl ultra-micro powder, oriental lapis ultra-micro powder, trevira ultra-micro powder, glass fibre ultra-micro powder and phenylalanine ultra-micro powder;
4) tentatively modulate: pearl ultra-micro powder, oriental lapis ultra-micro powder, trevira ultra-micro powder, glass fibre ultra-micro powder, phenylalanine ultra-micro powder and talcum powder are mixed, stirs after adding warm water, obtain pre-pigment;
5) filtering net: pour pre-pigment into filter bag, after excluding undesired impurities, obtains pigment.
More specifically, in described step 4), the water temperature of warm water is 34 DEG C.
Below know-why of the present invention is described in conjunction with specific embodiments.These describe just in order to explain principle of the present invention, and can not be interpreted as limiting the scope of the invention by any way.Based on explanation herein, those skilled in the art does not need to pay performing creative labour can associate other embodiment of the present invention, and these modes all will fall within protection scope of the present invention.
Claims (7)
1. one kind has pigment of Natural color mediation stability and preparation method thereof, it is characterized in that:
Calculate by number, comprise following composition: oriental lapis 30-50 part, glass fibre 10-20 part, pearl powder 20-30 part, trevira 25-30 part, phenylalanine 5-10 part and talcum powder 15-25 part;
The described preparation method with the pigment of Natural color mediation stability, carries out according to the following steps:
1) first time micronizing: oriental lapis, trevira, glass fibre and phenylalanine are crushed to respectively granularity≤25 μm of 90.0% through Ultra-Micro Grinding Equipment;
2) sieve: by Pearl and first time micronizing after oriental lapis, trevira, glass fibre and phenylalanine respectively cross 200 mesh sieves, take off material, obtain pearl fine powder, oriental lapis fine powder, trevira fine powder, glass fibre fine powder and phenylalanine fine powder;
3) second time micronizing and sieving: by step 2) clout of oriental lapis, trevira, glass fibre and phenylalanine after Pearl on screen cloth and first time micronizing carries out second time micronizing respectively, after 200 mesh sieves, take off material, obtain pearl ultra-micro powder, oriental lapis ultra-micro powder, trevira ultra-micro powder, glass fibre ultra-micro powder and phenylalanine ultra-micro powder;
4) tentatively modulate: pearl ultra-micro powder, oriental lapis ultra-micro powder, trevira ultra-micro powder, glass fibre ultra-micro powder, phenylalanine ultra-micro powder and talcum powder are mixed, stirs after adding warm water, obtain pre-pigment;
5) filtering net: pour pre-pigment into filter bag, after excluding undesired impurities, obtains pigment.
2. a kind of according to according to claim 1 there is Natural color be in harmonious proportion pigment and preparation method thereof of stability, it is characterized in that: the ratio of pearl ultra-micro powder in step 4), oriental lapis ultra-micro powder, trevira ultra-micro powder, glass fibre ultra-micro powder, phenylalanine ultra-micro powder and talcous mixture and warm water is 20:1.
3. a kind of according to according to claim 1 there is Natural color be in harmonious proportion pigment and preparation method thereof of stability, it is characterized in that: in step 4), the water temperature of warm water is 30-35 DEG C.
4. a kind of according to according to claim 1 there is Natural color be in harmonious proportion pigment and preparation method thereof of stability, it is characterized in that: filter bag >=200 order in step 5).
5. a kind of according to according to claim 1 there is Natural color be in harmonious proportion pigment and preparation method thereof of stability, it is characterized in that: calculate by number, comprise following composition: oriental lapis 30 parts, 10 parts, glass fibre, pearl powder 20 parts, 25 parts, trevira, phenylalanine 5 parts and talcum powder 15 parts.
6. a kind of according to according to claim 1 there is Natural color be in harmonious proportion pigment and preparation method thereof of stability, it is characterized in that: calculate by number, comprise following composition: oriental lapis 50 parts, 20 parts, glass fibre, pearl powder 30 parts, 30 parts, trevira, phenylalanine 10 parts and talcum powder 25 parts.
7. a kind of according to according to claim 1 there is Natural color be in harmonious proportion pigment and preparation method thereof of stability, it is characterized in that: calculate by number, comprise following composition: oriental lapis 40 parts, 15 parts, glass fibre, pearl powder 25 parts, 28 parts, trevira, phenylalanine 8 parts and talcum powder 20 parts.