CN105541261A - Nano-enhanced environment-friendly baking-free building block - Google Patents
Nano-enhanced environment-friendly baking-free building block Download PDFInfo
- Publication number
- CN105541261A CN105541261A CN201510947794.7A CN201510947794A CN105541261A CN 105541261 A CN105541261 A CN 105541261A CN 201510947794 A CN201510947794 A CN 201510947794A CN 105541261 A CN105541261 A CN 105541261A
- Authority
- CN
- China
- Prior art keywords
- parts
- building block
- nano
- free building
- baking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a nano-enhanced environment-friendly baking-free building block, which uses raw materials of cement, waste fly ash and waste ceramics. The building block has good insulation properties, low cost and simple process, and takes full advantage of solid wastes; and the baking-free building block has the advantages of light weight, good strength, toughness, durability, little energy consumption and no environmental pollution.
Description
Technical field
The present invention relates to a kind of nanometer and strengthen environment-protective baking-free building block, be specifically related to utilize rejected fly ash and pottery to prepare the method for baking-free building block.
Background technology
China has a large amount of rejected fly ashes every year, is mainly derived from power plant, mining area, and flyash is only marginally for fertilizer in recent years, and more flyash goes out of use and causes great destruction to environment.But flyash is attempted it can be used as building materials raw material owing to having certain active people, but poor performance.And flyash is prepared into the burden that baking-free building block not only can alleviate environment, also turn waste into wealth simultaneously, save natural resources, the product performance excellent in toughness be simultaneously made up of it is good, be incubated, heat insulation.
Summary of the invention
The object of this invention is to provide a kind of nanometer and strengthened environment-protective baking-free building block, technique is simple, and high to utilization rate of solid waste, described baking-free building block is lightweight, intensity better, good endurance, to the less environmentally safe of energy consumption.
Technical solution of the present invention is: raw material (by weight) adopts cement 22 parts, 40 parts, flyash, waste ceramic 20 parts, water reducer 0.3 part, water glass 2 parts, 9 parts, vegetable fibre, ether of cellulose 5 parts and 15 parts, water, rubber powder 0.05 part, hardening accelerator 0.5 part, and described rubber powder is obtained by mixing by following raw material: nano-calcium carbonate sodium 5 weight part, nano-calcium carbonate 10 weight part, metasilicate pentahydrate sodium 25 weight part; Described flyash is second class powered coal ash, and its preparation technology is as follows, and above-mentioned raw materials is uniformly mixed by it, then through shaping, maintenance, dry to obtain finished product.Described waste ceramic obtains after break process for discarding architectural pottery, and the performances such as its intensity are well desirable aggregate materials.
advantageous Effects of the present invention:
The present invention can make full use of solid waste, described baking-free building block is lightweight, intensity better, toughness and good endurance, to the less environmentally safe of energy consumption.
Embodiment
Raw material (by weight) adopts cement 22 parts, 40 parts, flyash, waste ceramic 20 parts, water reducer 0.3 part, water glass 2 parts, 9 parts, vegetable fibre, ether of cellulose 5 parts and 15 parts, water, rubber powder 0.05 part, hardening accelerator 0.5 part, and described rubber powder is obtained by mixing by following raw material: nano-calcium carbonate sodium 5 weight part, nano-calcium carbonate 10 weight part, metasilicate pentahydrate sodium 25 weight part; Described flyash is second class powered coal ash, and its preparation technology is as follows, and above-mentioned raw materials is uniformly mixed by it, then through shaping, maintenance, dry to obtain finished product.
Claims (1)
1. a nanometer strengthens environment-protective baking-free building block, it is characterized in that: raw material (by weight) adopts cement 22 parts, 40 parts, flyash, waste ceramic 20 parts, water reducer 0.3 part, water glass 2 parts, 9 parts, vegetable fibre, ether of cellulose 5 parts and 15 parts, water, rubber powder 0.05 part, hardening accelerator 0.5 part, and described rubber powder is obtained by mixing by following raw material: nano-calcium carbonate sodium 5 weight part, nano-calcium carbonate 10 weight part, metasilicate pentahydrate sodium 25 weight part; Described flyash is second class powered coal ash, and its preparation technology is as follows, and above-mentioned raw materials is uniformly mixed by it, then through shaping, maintenance, dry to obtain finished product.