CN105540675A - 宽温低功耗锰锌铁氧体粉料 - Google Patents

宽温低功耗锰锌铁氧体粉料 Download PDF

Info

Publication number
CN105540675A
CN105540675A CN201510976617.1A CN201510976617A CN105540675A CN 105540675 A CN105540675 A CN 105540675A CN 201510976617 A CN201510976617 A CN 201510976617A CN 105540675 A CN105540675 A CN 105540675A
Authority
CN
China
Prior art keywords
parts
weight
power consumption
wide temperature
ferrite powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510976617.1A
Other languages
English (en)
Inventor
杨美华
潘冠军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANTONG HUAXING MAGNETIC MATERIAL CO Ltd
Original Assignee
NANTONG HUAXING MAGNETIC MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG HUAXING MAGNETIC MATERIAL CO Ltd filed Critical NANTONG HUAXING MAGNETIC MATERIAL CO Ltd
Priority to CN201510976617.1A priority Critical patent/CN105540675A/zh
Publication of CN105540675A publication Critical patent/CN105540675A/zh
Priority to PCT/CN2016/102529 priority patent/WO2017107631A1/zh
Pending legal-status Critical Current

Abstract

本申请公开了一种宽温低功耗锰锌铁氧体粉料，包括如下重量份数的各组分：三氧化二铁68.91-70.31份，四氧化三锰21.89-24.86份，氧化锌6.21-9.2份，五氧化二铌0.0-0.08份，氧化钙0.12-0.07份，碳酸钾与碳酸锂的总量小于2份，本发明的宽温低功耗锰锌铁氧体粉料，在25-100℃范围内，具有较高的饱和磁通密度、较低的功率损耗、较高的居里温度和电阻率。

Description

宽温低功耗锰锌铁氧体粉料
技术领域
本公开涉及软磁材料领域，尤其涉及一种宽温低功耗锰锌铁氧体粉料。
背景技术
铁氧体作为一种具有铁磁性的金属氧化物，在电子、通讯等诸多领域有着广泛的应用。随着电子信息产业的迅速发展，行业内对铁氧体各项性能的要求也逐步提高。软磁铁氧体有时必须在高磁通、高频率状态下工作，同时还要求在较大温度范围内磁性能尽可能稳定，因此需要铁氧体材料具有较高的居里温度，且在宽温范围内，尽可能同时提高饱和磁通密度和降低功率损耗。
目前，软磁铁氧体宽温下不能保证饱和磁通密度，锰锌铁氧体材料也不能保证居里温度以及在宽温范围内的磁性能的稳定性，两者的应用范围有限。
发明内容
鉴于现有技术中的上述缺陷或不足，期望提供一种宽温低功耗锰锌铁氧体粉料，本发明的宽温低功耗锰锌铁氧体粉料，具有较高的饱和磁通密度、较低的功率损耗、较高的居里温度和电阻率。
本发明的宽温低功耗锰锌铁氧体粉料，其特征在于，包括如下重量份数的各组分：
三氧化二铁68.91-70.31份，
四氧化三锰21.89-24.86份，
氧化锌6.21-9.2份，
五氧化二铌:0.0-0.08份，
氧化钙0.12-0.07份，
碳酸钾与碳酸锂的总量小于2份。
本发明的宽温低功耗锰锌铁氧体粉料，在25-100℃范围内，具有较高的饱和磁通密度、较低的功率损耗、较高的居里温度和电阻率。
具体实施方式
下面结合实施例对本申请作进一步的详细说明。可以理解的是，此处所描述的具体实施例仅仅用于解释相关发明，而非对该发明的限定。
需要说明的是，在不冲突的情况下，本申请中的实施例及实施例中的特征可以相互组合。下面将实施例来详细说明本申请。
实施例一：
一种宽温低功耗锰锌铁氧体粉料，其特征在于，包括如下重量份数的各组分：
三氧化二铁68.91-70.31份，
四氧化三锰21.89-24.86份，
氧化锌6.21-9.2份，
五氧化二铌:0.0-0.08份，
氧化钙0.12-0.07份，
碳酸钾与碳酸锂的总量小于2份。
进一步的，三氧化二铁的重量份数为69.94份。
进一步的，四氧化三锰的重量份数为23.69份。
进一步的，氧化锌的重量份数为6.37份。
进一步的，五氧化二铌的重量份数为0.06份。
进一步的，氧化钙的重量份数为0.06份。
进一步的，碳酸钾与碳酸锂的总量的重量份数为1份。
实施例二、实施例三、实施例四、实施例五、实施例六：
一种宽温低功耗锰锌铁氧体粉料，按重量份数的配方组成具体见表1：
表1：宽温低功耗锰锌铁氧体粉料按重量份数的配方组成
实施例一至实施例六中宽温低功耗锰锌铁氧体粉料，主要原材料按重量份数的品质及标准对应表2：
表2：主要原材料按重量份数的品质及标准
实施例二至实施例六中宽温低功耗锰锌铁氧体性能见表3：
表3：宽温低功耗锰锌铁氧体性能
实施例六的样品，其初始磁导率μi为3200±25％，饱和磁通密度Bs在H＝1194A/m、25℃时为520mT，饱和磁通密度Bs在H＝1194A/m、100℃时为410mT，居里温度不低于220℃，功率损耗PL在100kHz、200mT、25℃时为400kW/m3，功率损耗PL在100kHz、200mT、100℃时为340kW/m3，电阻率大于7.0Ω·m。在25℃到100℃的宽温范围表现出优良稳定的磁性能，且兼具高饱和磁通密度和低功率损耗的特点。
以上描述仅为本申请的较佳实施例以及对所运用技术原理的说明。本领域技术人员应当理解，本申请中所涉及的发明范围，并不限于上述技术特征的特定组合而成的技术方案，同时也应涵盖在不脱离所述发明构思的情况下，由上述技术特征或其等同特征进行任意组合而形成的其它技术方案。例如上述特征与本申请中公开的(但不限于)具有类似功能的技术特征进行互相替换而形成的技术方案。

Claims (7)

1.一种宽温低功耗锰锌铁氧体粉料，其特征在于，包括如下重量份数的各组分：
三氧化二铁68.91-70.31份，
四氧化三锰21.89-24.86份，
氧化锌6.21-9.2份，
五氧化二铌0.0-0.08份，
氧化钙0.12-0.07份，
碳酸钾与碳酸锂的总量小于2份。
2.根据权利要求1所述的宽温低功耗锰锌铁氧体粉料，其特征在于，所述三氧化二铁的重量份数为69.94份。
3.根据权利要求1所述的宽温低功耗锰锌铁氧体粉料，其特征在于，所述四氧化三锰的重量份数为23.69份。
4.根据权利要求1所述的宽温低功耗锰锌铁氧体粉料，其特征在于，所述氧化锌的重量份数为6.37份。
5.根据权利要求1所述的宽温低功耗锰锌铁氧体粉料，其特征在于，所述五氧化二铌的重量份数为0.06份。
6.根据权利要求1所述的宽温低功耗锰锌铁氧体粉料，其特征在于，所述氧化钙的重量份数为0.06份。
7.根据权利要求1所述的宽温低功耗锰锌铁氧体粉料，其特征在于，所述碳酸钾与碳酸锂的总量的重量份数为1份。
CN201510976617.1A 2015-12-22 2015-12-22 宽温低功耗锰锌铁氧体粉料 Pending CN105540675A (zh)