CN105524694A - 一种难燃型可降解合成液压油 - Google Patents

一种难燃型可降解合成液压油 Download PDF

Info

Publication number
CN105524694A
CN105524694A CN201510988943.4A CN201510988943A CN105524694A CN 105524694 A CN105524694 A CN 105524694A CN 201510988943 A CN201510988943 A CN 201510988943A CN 105524694 A CN105524694 A CN 105524694A
Authority
CN
China
Prior art keywords
parts
add
stirring
minute
oleic acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201510988943.4A
Other languages
English (en)
Inventor
高恒东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Chuangyuan New Materials Co Ltd
Original Assignee
Wuhu Chuangyuan New Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Chuangyuan New Materials Co Ltd filed Critical Wuhu Chuangyuan New Materials Co Ltd
Priority to CN201510988943.4A priority Critical patent/CN105524694A/zh
Publication of CN105524694A publication Critical patent/CN105524694A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种难燃型可降解合成液压油，由下列重量份的原料制备制成：工业油酸280-285、单质碘12.6-13、丙烯酸72-74、三羟甲基丙烷134-135、甲苯磺酸15-16、纳米碳化硼颗粒15-17、司盘800.8-1、羧甲基纤维素钠2-3、去离子水30-32、羟乙基咪唑啉3.2-3.5、聚甲基丙烯酸酯10-12、二烷基二硫代磷酸锌3.5-4、二甲基硅油0.5-0.6、乙烯丙烯共聚物3-4、硼化硫代磷酸酯胺盐5-6、三聚磷酸钠2.5-3、三异丁基磷酸酯7-8。本发明通过科学合理的成分配比，具有阻燃、耐高温、耐高压、耐低温、环保、可降解等优点，能够广泛用于要求抗燃和接触高温明火的液压系统。

Description

一种难燃型可降解合成液压油
技术领域
本发明涉及液压技术领域，尤其涉及一种难燃型可降解合成液压油。
背景技术
近年来，随着液压系统设计、制造技术的发展和日趋完善，液压技术在新一代机械设备上得到广泛的应用。液压机械作业环境的多变性，给液压油带来了很大的挑战：液压油必须承受高压高温、温度变化、恶劣环境的考验，需要有优良的粘温性能和较高的承载能力，保证机械的工作效率和使用寿命，但现有的抗磨液压油难以完全满足液压系统复杂多变的工况。现在广泛使用的抗磨液压油，粘度指数较低，粘温性能差，适合冬夏长期使用的液压油较少，在温差变化较大时需更换液压油；氧化安定性能不稳定，髙温时氧化产生油泥，堵塞滤油器；承载能力不足，不能承受较大的冲击负荷。
《高性能多级抗磨液压油的研制》一文中通过对多种基础油、粘度调节剂、抗氧剂、润滑添加剂性能评价的基础油上，通过理论和实验研究，研制了一种多级抗磨液压油，拓宽液压油的温度适用性，提髙液压机械的使用寿命，延长液压油使用时间、节约能源。但是随着人们环保意识的加强和环保法规的日益严格，可生物降解润滑油的开发和使用越来越引起人们的广泛关注，大部分的液压基础油的生物降解性差，属生物难降解润滑材料。此文章中没有针对液压油的可降解性以及可降解基础油的抗氧化性进行阐述。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种难燃型可降解合成液压油。
本发明是通过以下技术方案实现的：
一种难燃型可降解合成液压油，由下列重量份的原料制备制成：工业油酸280-285、单质碘12.6-13、丙烯酸72-74、三羟甲基丙烷134-135、甲苯磺酸15-16、纳米碳化硼颗粒15-17、司盘800.8-1、羧甲基纤维素钠2-3、去离子水30-32、羟乙基咪唑啉3.2-3.5、聚甲基丙烯酸酯10-12、二烷基二硫代磷酸锌3.5-4、二甲基硅油0.5-0.6、乙烯丙烯共聚物3-4、硼化硫代磷酸酯胺盐5-6、三聚磷酸钠2.5-3、三异丁基磷酸酯7-8。
所述一种难燃型可降解合成液压油，由以下具体步骤制成：
（1）将工业油酸放入反应釜中，加热至200-210℃，加入单质碘，搅拌均匀后继续加入丙烯酸，以300-400转/分的速度搅拌反应2-2.5小时，自然冷却后对粗产品进行分离精制，得到高纯油酸；将高纯油酸放入反应釜中，加入三羟甲基丙烷、甲苯磺酸，加热至120-130℃，回流反应3-4小时，冷却、过滤、蒸馏，得到基础油，即三羟甲基丙烷油酸酯；
（2）将羧甲基纤维素钠加入去离子水中，搅拌10分钟至完全溶解，然后加入司盘80，以600-800转/分的速度搅拌10分钟，得到分散液，继续加入纳米碳化硼颗粒，搅拌10-15分钟得到悬浮液，再将悬浮液置于超声波清洗仪器中超声分散15-20分钟后喷雾干燥得到改性纳米氮化硼颗粒；
（3）将一半量的三羟甲基丙烷油酸酯放入搅拌中，加入羟乙基咪唑啉，以300-400转/分的速度搅拌15-20分钟后加入步骤（2）得到的改性纳米氮化硼颗粒，继续搅拌30-40分钟，直至分散均匀，得到减摩抗磨增强基础油；
（4）将剩余量的三羟甲基丙烷油酸酯加入调和釜中，加入聚甲基丙烯酸酯、二烷基二硫代磷酸锌、乙烯丙烯共聚物，加热至100-120℃，控温搅拌90-120分钟，降温至60-70℃，加入除减摩抗磨增强基础油之外的其余剩余成分，连续搅拌90-120分钟，直至混合物全部溶解待用；
（5）将步骤（3）得到的减摩抗磨增强基础油与步骤（4）得到的产物混合，以1000-1200转/分的速度搅拌均匀，然后经过三辊磨磨制3次，最后经过3级过滤后装桶，即得成品。
本发明的优点是：本发明通过一系列的反应将工业油酸制成高纯油酸，利用自制高纯油酸再制备成三羟甲基丙烷油酸酯，改善了工业油酸容易发生氧化的缺点，使得制成的基础油具有良好的抗氧化性以及低温性能，同时具有较高的生物降解率；本发明还在基础油中添加羟乙基咪唑啉，降低了油/水界面张力和且加速了微生物生长，从而进一步提高了本发明产品的生物降解性，配合改性纳米氮化硼颗粒的添加，在摩擦副之间起到滚动的“微轴承”作用，从而起到减摩抗磨的作用。
本发明通过科学合理的成分配比，具有阻燃、耐高温、耐高压、耐低温、环保、可降解等优点，尤其是具备良好的氧化安定性，能够广泛用于钢铁行业的连铸、热轧等生产线，煤矿井下输送系统及要求抗燃和接触高温、明火的液压系统，可生物降解，对环境友好，而且本发明液压油的制备方法简单、润滑性能好，且对油泵及液压阀损害小，市场前景广阔。
具体实施方式
一种难燃型可降解合成液压油，由下列重量份（公斤）的原料制备制成：工业油酸280、单质碘12.6、丙烯酸72、三羟甲基丙烷134、甲苯磺酸15、纳米碳化硼颗粒15、司盘800.8、羧甲基纤维素钠2、去离子水30、羟乙基咪唑啉3.2、聚甲基丙烯酸酯10、二烷基二硫代磷酸锌3.5、二甲基硅油0.5、乙烯丙烯共聚物3、硼化硫代磷酸酯胺盐5、三聚磷酸钠2.5、三异丁基磷酸酯7。
所述一种难燃型可降解合成液压油，由以下具体步骤制成：
（1）将工业油酸放入反应釜中，加热至200℃，加入单质碘，搅拌均匀后继续加入丙烯酸，以300转/分的速度搅拌反应2小时，自然冷却后对粗产品进行分离精制，得到高纯油酸；将高纯油酸放入反应釜中，加入三羟甲基丙烷、甲苯磺酸，加热至120℃，回流反应3小时，冷却、过滤、蒸馏，得到基础油，即三羟甲基丙烷油酸酯；
（2）将羧甲基纤维素钠加入去离子水中，搅拌10分钟至完全溶解，然后加入司盘80，以600转/分的速度搅拌10分钟，得到分散液，继续加入纳米碳化硼颗粒，搅拌10分钟得到悬浮液，再将悬浮液置于超声波清洗仪器中超声分散15分钟后喷雾干燥得到改性纳米氮化硼颗粒；
（3）将一半量的三羟甲基丙烷油酸酯放入搅拌中，加入羟乙基咪唑啉，以300转/分的速度搅拌15分钟后加入步骤（2）得到的改性纳米氮化硼颗粒，继续搅拌30分钟，直至分散均匀，得到减摩抗磨增强基础油；
（4）将剩余量的三羟甲基丙烷油酸酯加入调和釜中，加入聚甲基丙烯酸酯、二烷基二硫代磷酸锌、乙烯丙烯共聚物，加热至100℃，控温搅拌90分钟，降温至60℃，加入除减摩抗磨增强基础油之外的其余剩余成分，连续搅拌90分钟，直至混合物全部溶解待用；
（5）将步骤（3）得到的减摩抗磨增强基础油与步骤（4）得到的产物混合，以1000转/分的速度搅拌均匀，然后经过三辊磨磨制3次，最后经过3级过滤后装桶，即得成品。
本发明制成的液压油，经过试验得到数据如下：运动粘度在40℃为48.1mm2/s，100℃为11.1mm2/s；粘度指数为180-211；生物降解率达到97%；腐蚀试验达到1级。

Claims (2)

1.一种难燃型可降解合成液压油，其特征在于，由下列重量份的原料制备制成：工业油酸280-285、单质碘12.6-13、丙烯酸72-74、三羟甲基丙烷134-135、甲苯磺酸15-16、纳米碳化硼颗粒15-17、司盘800.8-1、羧甲基纤维素钠2-3、去离子水30-32、羟乙基咪唑啉3.2-3.5、聚甲基丙烯酸酯10-12、二烷基二硫代磷酸锌3.5-4、二甲基硅油0.5-0.6、乙烯丙烯共聚物3-4、硼化硫代磷酸酯胺盐5-6、三聚磷酸钠2.5-3、三异丁基磷酸酯7-8。
2.根据权利要求1所述一种难燃型可降解合成液压油，其特征在于，由以下具体步骤制成：
（1）将工业油酸放入反应釜中，加热至200-210℃，加入单质碘，搅拌均匀后继续加入丙烯酸，以300-400转/分的速度搅拌反应2-2.5小时，自然冷却后对粗产品进行分离精制，得到高纯油酸；将高纯油酸放入反应釜中，加入三羟甲基丙烷、甲苯磺酸，加热至120-130℃，回流反应3-4小时，冷却、过滤、蒸馏，得到基础油，即三羟甲基丙烷油酸酯；
（2）将羧甲基纤维素钠加入去离子水中，搅拌10分钟至完全溶解，然后加入司盘80，以600-800转/分的速度搅拌10分钟，得到分散液，继续加入纳米碳化硼颗粒，搅拌10-15分钟得到悬浮液，再将悬浮液置于超声波清洗仪器中超声分散15-20分钟后喷雾干燥得到改性纳米氮化硼颗粒；
（3）将一半量的三羟甲基丙烷油酸酯放入搅拌中，加入羟乙基咪唑啉，以300-400转/分的速度搅拌15-20分钟后加入步骤（2）得到的改性纳米氮化硼颗粒，继续搅拌30-40分钟，直至分散均匀，得到减摩抗磨增强基础油；
（4）将剩余量的三羟甲基丙烷油酸酯加入调和釜中，加入聚甲基丙烯酸酯、二烷基二硫代磷酸锌、乙烯丙烯共聚物，加热至100-120℃，控温搅拌90-120分钟，降温至60-70℃，加入除减摩抗磨增强基础油之外的其余剩余成分，连续搅拌90-120分钟，直至混合物全部溶解待用；
（5）将步骤（3）得到的减摩抗磨增强基础油与步骤（4）得到的产物混合，以1000-1200转/分的速度搅拌均匀，然后经过三辊磨磨制3次，最后经过3级过滤后装桶，即得成品。
CN201510988943.4A 2015-12-28 2015-12-28 一种难燃型可降解合成液压油 Withdrawn CN105524694A (zh)