CN105523859A - 一种旱地玉米种植保水型肥料及其制备方法 - Google Patents
一种旱地玉米种植保水型肥料及其制备方法 Download PDFInfo
- Publication number
- CN105523859A CN105523859A CN201610097834.8A CN201610097834A CN105523859A CN 105523859 A CN105523859 A CN 105523859A CN 201610097834 A CN201610097834 A CN 201610097834A CN 105523859 A CN105523859 A CN 105523859A
- Authority
- CN
- China
- Prior art keywords
- water
- corn
- fertilizer
- dry
- holding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种旱地玉米种植保水型肥料及其制备方法,由以下重量份的原料制成:膨润土、碳粉、淀粉、环氧树脂、水泥、石膏粉、衣康酸、硼酸、磷酸二氢铵、蚯蚓粪、细孔硅胶、氧化钾、过磷酸钙、磷酸二铵、吲哚丁酸和适量的水;玉米有一定的抗旱能力,但是不能过于干旱,因此玉米常在北方地区种植,土壤一定的吸水保水能力会使得玉米长势更好,这里加入了吸水性的硅胶颗粒,同时膨润土虽然经过改性,但是自身是一种矿质泥土,在加入水泥之后,亦可成为肥料吸水型基质之一。
Description
技术领域
本发明属于肥料的工艺技术领域,具体涉及到一种旱地玉米种植保水型肥料及其制备方法。
背景技术
膨润土是以蒙脱石为主要成分的粘土矿物。蒙脱石具有简单斜晶体的结构,是一种含水的二八面体或三八面体的层状铝硅酸盐矿物,在单晶胞的外面有两层硅氧四面体,中间夹一层氢氧铝八面体,在四面体和八面体中,高价的硅离子和铝离子能被它低价阳离子置换,使蒙脱石晶胞带负电荷,成为一个大的负离子,从而使它具有吸附阳离子的能力,但对阴离子吸附效果欠佳。
鳞片状石墨具有较好的导电性能,但其层状结构使之不适合单独用于导电胶中,通常要和炭黑混合使用。球状的炭黑粒子填充于层状的石墨之间,给石墨层施加一定的压力,使其能够更好的接触。石墨导电胶的最大优点是性能比较稳定,有一定的耐酸碱能力,价格低廉,相对密度小,分散性能好,但是电阻率较高,一般只能用于中阻值浆料。
发明内容
为了更好的发挥改性膨润土在肥料中的吸附性能,本发明利用无机造孔剂在喷润土中制造无数相互连接的微孔管道,因而具有更强的吸附效果,具体方法如下:
一种旱地玉米种植保水型肥料,其特征在于,由以下重量份的原料制成:膨润土20~30、碳粉6~8、淀粉1~2、环氧树脂0.5~0.8、水泥1.5~2.5、石膏粉0.2~0.6、衣康酸2~4、硼酸4~7、磷酸二氢铵10~15、蚯蚓粪20~25、细孔硅胶5~8、氧化钾12~18、过磷酸钙20~25、磷酸二铵15~20、吲哚丁酸0.5~0.8和适量的水;
一种旱地玉米种植保水型肥料的制备方法,其特征在于,包括以下几个步骤:
(1)将环氧树脂与4~5倍其重量份的水混合,加热至70~80℃后搅拌至完全溶解,然后倒入至混合的淀粉和碳粉中,搅拌混匀成粘性匀浆;
(2)对膨润土进行除沙,然后加入(1)所述的粘性匀浆,水泥和石膏粉,边加水边搅拌至成为均匀的浆料,然后放在电压为300~355V的通电场中,缓慢搅拌10~15min使碳粉线型排列,烘干,然后放于500~550℃的高温条件下煅烧30~40min成多孔的固体块状,粉碎筛选过20~30目筛得颗粒剂;
(3)混合过磷酸钙、磷酸二铵、吲哚丁酸及其它以下未涉及的剩余成分,边加水边搅拌至晶体完全溶解;
(4)将(2)所述的颗粒剂加入至(3)所得溶液中,统一放入超声波清洗机中,功率650~750W,作用20~25min使微孔中充满溶液,完成后将颗粒烘干,再次投入到溶液中重复二次吸附,再次烘干得改性颗粒;
(5)混合蚯蚓粪和细孔硅胶,加入(4)所述剩余溶解液和改性颗粒,同时适量加水搅拌成稠膏,最后通过喷浆造粒并烘干即可。
膨润土制备吸附剂的方法基本是:选用非金属矿的优质钠基膨润土为原料,除沙过后在干燥的100g膨润土掺入4g200目易燃微粉碳粉和2g淀粉,再加入适量的水搅匀挤压成直径为3mm的颗粒,烘干,再高温灼烧,由于结晶水的失去和易燃微粉燃烧生成CO2的放出,形成了大量的微孔。
本发明的最终目的是为了吸附化学元素的矿质元素,由碳粉高温燃烧过后留下的微孔过于细小,必须将肥料的无机元素先溶解,再渗透到细小的孔隙中去,但是这里有几个问题:1、水的表面张力很大,渗透到细微的孔隙中很慢且较为困难;2、溶解过后的无机化学元素经过稀释,即使完全渗透,量上面也很小;3、由碳粉微粒组成的微孔制造的是微孔,存在于膨润土内部,因此燃烧过后形成的微孔属于密闭状态,无法进行预留,更谈不上吸附。
本发明的几个措施正好解决以上问题,首先对碳粉进行加工改性,我们将一种粘性较强的且具有导电性能的环氧树脂作为粘结剂稀释过后加入到碳粉中,搅拌过后附着在碳粉表面,成为一种粘性颗粒性的碳粉微粒,然后将碳粉加入喷润土中,在导电的电场作用下自由通电,碳粉在导电情况下自由连接,形成碳粉链,而环氧树脂的作用就在于使链子存在一段时间(环氧树脂作为导电性的粘结剂早已成为先进技术,效果明显),然后在根据步骤,高温灼烧,这样形成微型管道,而不是微孔,然后放入溶解的化学元素中的时候进行超声波作用,大大较小水的表面张力,最后烘干,同时进行二次吸附,这样残留的化学物质量将大大提高,为了提高喷润土颗粒的吸水性能和迅速干燥功能,特别添加一定量的水泥,加强吸水性并维持喷润土颗粒一定的稳定性。
本发明的有益效果:玉米有一定的抗旱能力,但是不能过于干旱,因此玉米常在北方地区种植,土壤一定的吸水保水能力会使得玉米长势更好,这里加入了吸水性的硅胶颗粒,同时膨润土虽然经过改性,但是自身是一种矿质泥土,在加入水泥之后,亦可成为肥料吸水型基质之一,在裂解的过程中还释放吸附的化学元素,复合科学的施肥,干燥的土壤使得一次性施肥,会导致肥料未进入土壤就挥发,或者导致土壤盐度上升,不利于养护,浪费也很严重,最后加入一定的吲哚丁酸可以促进生根,增强玉米根系与土壤的接触面积。
具体实施方式
实施例1:
一种旱地玉米种植保水型肥料,其特征在于,由以下重量份(Kg)的原料制成:膨润土25、碳粉6、淀粉1、环氧树脂0.6、水泥1.8、石膏粉0.4、衣康酸3、硼酸5、磷酸二氢铵12、蚯蚓粪22、细孔硅胶7、氧化钾15、过磷酸钙24、磷酸二铵15、吲哚丁酸0.6和适量的水;
一种旱地玉米种植保水型肥料的制备方法,其特征在于,包括以下几个步骤:
(1)将环氧树脂与4~5倍其重量份的水混合,加热至70~80℃后搅拌至完全溶解,然后倒入至混合的淀粉和碳粉中,搅拌混匀成粘性匀浆;
(2)对膨润土进行除沙,然后加入(1)所述的粘性匀浆,水泥和石膏粉,边加水边搅拌至成为均匀的浆料,然后放在电压为300~355V的通电场中,缓慢搅拌10~15min使碳粉线型排列,烘干,然后放于500~550℃的高温条件下煅烧30~40min成多孔的固体块状,粉碎筛选过20~30目筛得颗粒剂;
(3)混合过磷酸钙、磷酸二铵、吲哚丁酸及其它以下未涉及的剩余成分,边加水边搅拌至晶体完全溶解;
(4)将(2)所述的颗粒剂加入至(3)所得溶液中,统一放入超声波清洗机中,功率650~750W,作用20~25min使微孔中充满溶液,完成后将颗粒烘干,再次投入到溶液中重复二次吸附,再次烘干得改性颗粒;
(5)混合蚯蚓粪和细孔硅胶,加入(4)所述剩余溶解液和改性颗粒,同时适量加水搅拌成稠膏,最后通过喷浆造粒并烘干即可。
采用本发明的一种旱地玉米种植保水型肥料用于旱地玉米的种植试验,结果明显,玉米的长势更加好,产量提高10.5%。
Claims (2)
1.一种旱地玉米种植保水型肥料,其特征在于,由以下重量份的原料制成:膨润土20~30、碳粉6~8、淀粉1~2、环氧树脂0.5~0.8、水泥1.5~2.5、石膏粉0.2~0.6、衣康酸2~4、硼酸4~7、磷酸二氢铵10~15、蚯蚓粪20~25、细孔硅胶5~8、氧化钾12~18、过磷酸钙20~25、磷酸二铵15~20、吲哚丁酸0.5~0.8和适量的水。
2.根据权利要求1所述一种旱地玉米种植保水型肥料的制备方法,其特征在于,包括以下几个步骤:
(1)将环氧树脂与4~5倍其重量份的水混合,加热至70~80℃后搅拌至完全溶解,然后倒入至混合的淀粉和碳粉中,搅拌混匀成粘性匀浆;
(2)对膨润土进行除沙,然后加入(1)所述的粘性匀浆,水泥和石膏粉,边加水边搅拌至成为均匀的浆料,然后放在电压为300~355V的通电场中,缓慢搅拌10~15min使碳粉线型排列,烘干,然后放于500~550℃的高温条件下煅烧30~40min成多孔的固体块状,粉碎筛选过20~30目筛得颗粒剂;
(3)混合过磷酸钙、磷酸二铵、吲哚丁酸及其它以下未涉及的剩余成分,边加水边搅拌至晶体完全溶解;
(4)将(2)所述的颗粒剂加入至(3)所得溶液中,统一放入超声波清洗机中,功率650~750W,作用20~25min使微孔中充满溶液,完成后将颗粒烘干,再次投入到溶液中重复二次吸附,再次烘干得改性颗粒;
(5)混合蚯蚓粪和细孔硅胶,加入(4)所述剩余溶解液和改性颗粒,同时适量加水搅拌成稠膏,最后通过喷浆造粒并烘干即可。