CN105461273A - 一种抽放瓦斯注浆封孔材料 - Google Patents

一种抽放瓦斯注浆封孔材料 Download PDF

Info

Publication number
CN105461273A
CN105461273A CN201510819736.6A CN201510819736A CN105461273A CN 105461273 A CN105461273 A CN 105461273A CN 201510819736 A CN201510819736 A CN 201510819736A CN 105461273 A CN105461273 A CN 105461273A
Authority
CN
China
Prior art keywords
hole
sealing
parts
gas drainage
sealing material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510819736.6A
Other languages
English (en)
Inventor
贾向南
张顺利
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XINXIANG JIAHUI TECHNOLOGY Co Ltd
Original Assignee
XINXIANG JIAHUI TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XINXIANG JIAHUI TECHNOLOGY Co Ltd filed Critical XINXIANG JIAHUI TECHNOLOGY Co Ltd
Priority to CN201510819736.6A priority Critical patent/CN105461273A/zh
Publication of CN105461273A publication Critical patent/CN105461273A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种抽放瓦斯注浆封孔材料，由以下重量组份混合而成，425硅酸盐水泥78～83份、硫铝酸钙9～12份、混凝土膨胀剂6～8份、白方甲托悬浮剂0.5份、稀土稳定剂1份、萘系高效减水剂0.5份。本发明的封孔材料具有加工方便，使用效果好的优点，在使用中凝结速度快，注浆一小时即可进行瓦斯抽采，封孔凝结后抗压强度高，保证封孔的长期效果；还具有良好地渗透性和可塑性，封孔质量可靠，其膨胀性能可使钻孔壁与封孔材料紧密结合，保证瓦斯抽采浓度的持久平稳，即抗静电又阻燃，使用安全性能有保证。

Description

一种抽放瓦斯注浆封孔材料
技术领域：
本发明是一种专门用于抽放瓦斯时注浆封孔的材料。
背景技术：
封孔材料的主要功能是材料本身具有的致密性，同时封孔材料与钻孔壁面之间能形成致密结合体，以便于封堵裂隙。目前抽放瓦斯注浆封孔用的材料主要是聚氨酯和水泥浆料，在封孔段注入水泥浆料，在孔口采用聚氨酯或聚氨酯与水泥浆复合料。这种封孔方式，因聚氨酯是有机材料，与钻孔壁面或岩石之间存在有界面难以致密结合，导致后期密封不严，从而影响瓦斯抽采效果；另外在瓦斯抽采浓度下降后，水泥凝结会产生微小裂隙，使封孔质量下降。
发明内容：
本发明的目的是提供一种封孔致密性好、有利于保证后期封孔质量的抽放瓦斯注浆封孔材料。
本发明的技术方案是以如下方式完成的，一种抽放瓦斯注浆封孔材料，其特征在于：由以下重量组份混合而成，425硅酸盐水泥78～83份、硫铝酸钙9～12份、混凝土膨胀剂6～8份、白方甲托悬浮剂0.5份、稀土稳定剂1份、萘系高效减水剂0.5份。
本发明的封孔材料具有加工方便，使用效果好的优点，在使用中凝结速度快，注浆一小时即可进行瓦斯抽采，封孔凝结后抗压强度高，保证封孔的长期效果；还具有良好地渗透性和可塑性，封孔质量可靠，其膨胀性能可使钻孔壁与封孔材料紧密结合，保证瓦斯抽采浓度的持久平稳，即抗静电又阻燃，使用安全性能有保证。
具体实施方式：
本发明的封孔材料由以下重量组份混合而成，425硅酸盐水泥78～83份、硫铝酸钙9～12份、混凝土膨胀剂6～8份、白方甲托悬浮剂0.5份、稀土稳定剂1份、萘系高效减水剂0.5份。配制时根据地质的松紧和致密情况，适当调整各成分的重量比，混合均匀即可。封孔时，用1份混合粉料加入0.7份的净水，搅拌成浆料，注入钻孔内，初凝时间为10～20分钟，终凝时间为30分钟即可。经检测，封孔时的膨胀率≥4%、抗压强度≥25MP2、膨胀尺寸永久稳定，并且具有抗静电和阻燃的功能，能有效地将封孔材料与钻孔高强度结合成一体。上述实施例中，硅酸盐水泥加入量的多少与抗压强度的正比；硫铝酸盐加入量的多少与初凝和终凝时间成正比，混凝土膨胀剂加入量的多少与膨胀率成正比，总之各种物料加入的比例，可根据用户需要在规定的范围内进行调整。

Claims (1)

1.一种抽放瓦斯注浆封孔材料，其特征在于：由以下重量组份混合而成，425硅酸盐水泥78～83份、硫铝酸钙9～12份、混凝土膨胀剂6～8份、白方甲托悬浮剂0.5份、稀土稳定剂1份、萘系高效减水剂0.5份。
CN201510819736.6A 2015-11-24 2015-11-24 一种抽放瓦斯注浆封孔材料 Pending CN105461273A (zh)